Sintering and Electrical Properties of Lead-Free Na0.5K0.5NbO3 Piezoelectric Ceramics

Lead-free Na_0.5K_0.5NbO₃ (NKN) piezoelectric ceramics were fairly well densified at a relatively low temperature under atmospheric conditions. A relative density of 96%–99% can be achieved by either using high-energy attrition milling or adding 1 mol% oxide additives. It is suggested that ultra-fine starting powders by active milling or oxygen vacancies and even liquid phases from B-site oxide additives mainly lead to improved sintering. Not only were dielectric properties influenced by oxide additives, such as the Curie temperature ( T _c) and dielectric loss ( D ), but also the ferroelectricity was modified. A relatively large remanent polarization was produced, ranging from 16 μC/cm² for pure NKN to 23 μC/cm² for ZnO-added NKN samples. The following dielectric and piezoelectric properties were obtained: relative permittivity ɛ ^T ₃₃/ɛ ₀ =570–650, planar mode electromechanical coupling factor, k _p=32%–44%, and piezoelectric strain constant, d ₃₃=92–117 pC/N.     

Nanopowders of Na0.5K0.5NbO3 Prepared by the Pechini Method

A Pechini-based chemical synthesis route was used to produce powders of Na_0.5K_0.5NbO₃ (NKN). The thermochemistry of the gel was investigated using thermogravimetric analysis-fourier transform infrared (TGA-FTIR) evolved gas analysis; in addition, powder FTIR was used to analyze the gel residues after different heat treatments. The final decomposition of the organic components occurred at ∼650°C. However, hydrated–carbonated secondary phase(s) were detected by FTIR in powders that had been heated at 700°C, indicating that the NKN nanopowders are susceptible to a reaction with atmospheric moisture and carbon dioxide. The NKN particle sizes were in the range 50–150 nm after decomposition at 700°C.     

Effect of CuO on the Sintering Temperature and Piezoelectric Properties of (Na0.5K0.5)NbO3 Lead-Free Piezoelectric Ceramics

When a small amount of CuO was added to (Na_0.5K_0.5)NbO₃ (NKN) ceramics sintered at 960°C for 2 h, a dense microstructure with increased grains was developed, probably due to liquid-phase sintering. The Curie temperature slightly increased when CuO exceeded 1.5 mol%. The Cu²⁺ ion was considered to have replaced the Nb⁵⁺ ion and acted as a hardener, which increased the E _c and Q _m values of the NKN ceramics. High piezoelectric properties of k _p=0.37, Q _m=844, and ɛ₃ ^T /ɛ₀=229 were obtained from the specimen containing 1.5 mol% of CuO sintered at 960°C for 2 h.     

Low-Temperature Sintering of K0.5Na0.5NbO3 Ceramics

The objective of this work was to lower the sintering temperature of K_0.5Na_0.5NbO₃ (KNN) without reducing its piezoelectric properties. The KNN was sintered using 0.5, 1, 2, and 4 mass% of (K, Na)-germanate. The influence of the novel sintering aid, based on alkaline germanate with a melting point near 700°C, on the sintering, density, and piezoelectric properties of KNN is presented. The alkaline-germanate-modified KNN ceramics reach up to 96% of theoretical density at sintering temperatures as low as 1000°C, which is approximately 100°C less than the sintering temperature of pure KNN. The relative dielectric permittivity (ɛ/ɛ₀) and losses (tanδ), measured at 10 kHz, the piezo d ₃₃ coefficient, the electromechanical coupling and mechanical quality factors ( k _p, k _t, Q _m) of KNN modified with 1 mass% of alkaline germanate are 397, 0.02, 120 pC/N, 0.40, 0.44, and 77, respectively. These values are comparable to the best values obtained for KNN ceramics sintered above 1100°C.     

Low-Temperature Sintering and Piezoelectric Properties of (Na0.5K0.5)NbO3 Lead-Free Piezoelectric Ceramics

(Na_0.5K_0.5)NbO₃ (NKN) ceramic with 1.5 mol% CuO added (NKNC) was well sintered even at a low temperature of 900°C with the addition of ZnO. Most of the ZnO reacted with the CuO and formed the liquid phase that assisted the densification of the specimens at 900°C. A few Zn²⁺ ions entered the matrix of the specimens and increased the coercive field ( E _c) and Q _m values of the specimens. High-piezoelectric properties of k _p=0.37, Q _m=755, and ɛ₃ ^T /ɛ₀=327 were obtained from the NKNC ceramics containing 1.0 mol% ZnO sintered at 900°C for 2 h.     

Microstructural Evolution of Crystalline-Oriented (K0.5Na0.5)NbO3 Piezoelectric Ceramics with a Sintering Aid of CuO

The microstructural development of crystalline-oriented (K_0.5Na_0.5)NbO₃ (KNN)-based piezoelectric ceramics during sintering was investigated. The addition of CuO as a sintering aid was found to be effective for fabricating highly oriented and dense KNN ceramics. KNN specimens containing 0.5–1.0 mol% CuO sintered at 1100°C for 1 h were found to have relative densities and pseudo-cubic {100} orientation degrees of 95% or higher. In the early stages of sintering, KNN is formed in the reaction between complementary reactants NaNbO₃ and KNbO₃, after which oriented grain growth proceeds at a relative density of more than 90%. In addition, the results of transmission electron microscopy observation showed that textured KNN ceramics have a unique pectinate-like domain structure with domain walls consisting of {101} planes.     

(Na0.8K0.2)0.5Bi0.5TiO3 Nanowires: Low-Temperature Sol–Gel–Hydrothermal Synthesis and Densification

The sol–gel–hydrothermal processing of (Na_0.8K_0.2)_0.5Bi_0.5TiO₃ (NKBT) nanowires as well as their densification behavior were investigated. The morphology and structure analyses indicated that the sol–gel–hydrothermal route led to the formation of phase-pure perovskite NKBT nanowires with diameters of 50–80 nm and lengths of 1.5–2 μm, and the processing temperature was as low as 160°C, but the conventional sol–gel route tended to lead to the formation of NKBT agglomerated porous structured nanopowders, and the processing temperature was higher than 650°C. It is believed that the gel precursor and hydrothermal environment play an important role in the formation of the nanowires at a low temperature. Owing to the better packing efficiency and therefore a good sinterability of the freestanding nanowhiskers, the pressed pellets made by NKBT nanowires showed >98% theoretical density at 1100°C for 2 h. The sol–gel–hydrothermal-derived ceramics have typical characteristics of relaxor ferroelectrics, and the piezoelectric properties were better than the ceramics prepared by the conventional sol–gel and solid-state reaction.     

Processing and Electromechanical Properties of (Bi0.5Na0.5)(1−1.5x)LaxTiO3 Ceramics

Bismuth sodium titanate (Bi_0.5Na_0.5TiO₃, BNT) with 0–6 at.% lanthanum was prepared by the conventional mixed oxide method. Each composition was calcined at 800–900°C for 2–5 h to form a pure perovskite phase. Green pellets were sintered at 1050–1150°C for 1–4 h to obtain dense ceramics with at least 95% of theoretical density. X–ray diffraction (XRD) showed phase distortion as lanthanum was added to this system. Meanwhile, a small amount of La was found to affect the grain size and had an influence on the poling conditions and electrical properties. The BNT–based composition with 1 at.% La doping provided a dielectric constant ( K ) of 560, a piezoelectric charge constant ( d ₃₃) of 92 pC/N, and a hydrostatic piezoelectric coefficient ( d _h) of 72 pC/N.     

Effect of Calcination Conditions and Excess Alkali Carbonate on the Phase Formation and Particle Morphology of Na0.5K0.5NbO3 Powders

Sodium-potassium niobate [Na_0.5K_0.5NbO₃] powders were prepared following the conventional mixed oxide method. An orthorhombic XRD pattern, consistent with single-phase Na_0.5K_0.5NbO₃, was obtained after calcination at 900°C for 6 h. Introducing 5 mol% excess Na₂CO₃ and K₂CO₃ into the starting mixture allowed milder calcination conditions to be used, for example 800°C for 2 h. Primary particles in 5 mol% excess samples were cuboid, with maximum sizes of ∼2.5 μm. Equiaxed 0.3–0.4-μm particles were formed for non-excess powders, and also for powders prepared with 1 and 3 mol% excess alkali carbonates. The results suggest liquid formation during calcination of the excess 5-mol% starting powders.     

Microstructure and Piezoelectric Properties of (1−x)(Na0.5K0.5)NbO3–xLiNbO3 Ceramics

(1− x )(Na_0.5K_0.5)NbO₃– x LiNbO₃ [(1− x )NKN– x LN] ceramics were produced by the conventional solid-state sintering method, and their microstructure and piezoelectric properties were investigated. The formation of the liquid phase and K₆Li₄Nb₁₀O₃₀ second phase that were observed in the (1− x )NKN– x LN ceramics was explained by the evaporation of Na₂O during the sintering. A morphotropic phase boundary (MPB) was observed in the specimens with 0.05< x <0.08. Promising piezoelectric properties were obtained for the specimens with x =0.07. Therefore, the piezoelectric properties of this 0.93NKN–0.07LN ceramic were further investigated and were found to be influenced by their relative density and grain size. In particular, grain size considerably affected the d ₃₃ value. Two-step sintering was conducted at different temperatures to increase the grain size. Piezoelectric properties of d ₃₃=240 (pC/N) and k _p=0.35 were obtained for the 0.93NKN–0.07LN ceramics sintered at 1030°C and subsequently annealed at 1050°C.     

Low-Temperature Sintering and Piezoelectric Properties of CuO-Added 0.95(Na0.5K0.5)NbO3–0.05BaTiO3 Ceramics

The sintering temperature of 0.95(Na_0.5K_0.5)NbO₃–0.05BaTiO₃ (NKN–BT) ceramics needs to be decreased below 1000°C to prevent Na₂O evaporation, which can cause difficulties in poling and may eventually degrade their piezoelectric properties. NKN–BT ceramics containing CuO were well sintered at 950°C with grain growth. Poling was easy for all specimens. Densification and grain growth were explained by the formation of a liquid phase. The addition of CuO improved the piezoelectric properties by increasing the grain size and density. High piezoelectric properties of d ₃₃=230 pC/N, k _p=37%, and ɛ₃^T/ɛ₀=1150 were obtained from the specimen containing 1.0 mol% of CuO synthesized by the conventional solid-state method.     

Microwave Dielectric Properties of a New A5B4O15-Type Cation-Deficient Perovskite Ba2La3Ti3TaO15

High dielectric constant and low loss ceramics with composition Ba₂La₃Ti₃TaO₁₅ have been prepared by a conventional solid-state ceramic route. This compound adopts A₅B₄O₁₅ cation-deficient hexagonal perovskite structure. The dielectric properties of dense ceramics sintered in air at 1520°C have been characterized at microwave frequencies. It shows a relative dielectric constant of ∼45, quality factor Q _u× f of ∼26 828 GHz and temperature variation of resonant frequency of −0.97 ppm/°C.     

A Novel Hybrid Method of Sol–Gel and Ultrasonic Atomization Synthesis and Piezoelectric Properties of SrBi4Ti4O15 Ceramics

SrBi₄Ti₄O₁₅(SBTi) powders were synthesized by a novel hybrid method of sol–gel and ultrasonic atomization. TiO₂ particle was used as a starting material to replace other expensive soluble titanium salts. X-ray diffraction results showed that the pure-phase SBTi powders were obtained at 700°C for 2 h, which is much lower than the calcination temperature (800°–850°C) required in solid-state reactions. The ceramics sintered at 1100°C for 1 h exhibited 94.5% of relative density and a piezoelectric coefficient of 21 pC/N. The results showed that this hybrid method could lead to an attractive method for the industrial fabrication of SBTi materials.     

Alkoxide Route to La0.5Sr0.5CoO3 Films and Powders

An all-alkoxide route to films and nano-phase powders of the La_0.5Sr_0.5CoO₃ perovskite is described. To our knowledge, this is the first purely alkoxide-based route to (La_{1− x} Sr _x )CoO₃, and it yields phase-pure and elementally homogeneous perovskite at 700°C by heating at 2°C/min. At 700°C, a cubic unit cell was obtained with a _c=3.853Å, and after further heating to 1000°C, a rhombohedral cell could be indexed: a _r=5.417 Å, α_r=59.94°. Ninety to 130 nm thick films of La_0.5Sr_0.5CoO₃ were obtained by spin coating. The gel-to-oxide conversion was studied in some detail, using thermo-gravimetric analysis, differential scanning calorimetry, powder X-ray diffraction, IR spectroscopy, and transmission electron microscope equipped with an energy-dispersive X-ray spectrometer.     

Ferroelectric and Piezoelectric Properties of Fine-Grained Na0.5K0.5NbO3 Lead-Free Piezoelectric Ceramics Prepared by Spark Plasma Sintering

Lead-free piezoelectric ceramics have received attention because of increasing interest in environmental protection. Niobate ceramics such as NaNbO₃ and KNbO₃ have been studied as promising Pb-free piezoelectric ceramics, but their sintering densification is fairly difficult. In the present study, highly dense Na_0.5K_0.5NbO₃ ceramics were prepared using spark plasma sintering (SPS). Although the SPS temperature was as low as 920°C, the density of the Na_0.5K_0.5NbO₃ solid solution ceramics was raised to 4.47 g/cm³ (>99% of the theoretical density). After post-annealing in air, reasonably good ferroelectric and piezoelectric properties were obtained in the Na_0.5K_0.5NbO₃ ceramics with submicron grains. The crystal phase of the Na_0.5K_0.5NbO₃ has an orthorhombic structure. The Curie temperature is 395°C and the piezoelectric parameter ( d ₃₃) of the Na_0.5K_0.5NbO₃ ceramics reached 148 pC/N.     

Microstructure and Mechanical Properties of Hot-Pressed α-Al2O3-Seeded γ-Alumina Ceramics

High-quality alumina ceramics were fabricated by a hot pressing with MgO and SiO₂ as additives using α-Al₂O₃-seeded nanocrystalline γ-Al₂O₃ powders as the raw material. Densification behavior, microstructure evolution, and mechanical properties of alumina were investigated from 1250°C to 1450°C. The seeded γ-Al₂O₃ sintered to 98% relative density at 1300°C. Obvious grain growth was observed at 1400°C and plate-like grains formed at 1450°C. For the 1350°C hot-pressed alumina ceramics, the grain boundary regions were generally clean. Spinel and mullite formed in the triple-grain junction regions. The bending strength and fracture toughness were 565 MPa and 4.5 MPa·m^1/2, respectively. For the 1300°C sintered alumina ceramics, the corresponding values were 492 MPa and 4.9 MPa·m^1/2.     

Electrical Properties of Sr0.7Ba0.3TiO3 Ceramics Doped with Nb2O5, 3Li2O · 2SiO2, and Bi2O3

The electrical properties of Sr_0.5Ba_0.3TiO₃ in the presence of Nb₂O₅ as a donor, 3Li₂O · 2SiO₂ as a sintering agent, and Bi₂O₃ as a dopant have been studied. When the compositions of the ceramics were 1 mol Sr_0.7Ba_0.3TiO₃+ 0.5 mol% Nb₂O₅+ 2 mol% 3Li₂O · 2SiO₂+ 0.2 mol% Bi₂O₃, the ceramics were sintered at 1100°C and exhibited the following characteristics: apparent dielectric constant ɛ, 25000; loss factor tan δ, 2%; insulating resistivity ρ_j, 10¹⁰Ω· cm; variation of dielectric constant with temperature Δɛ/ɛ (−25° to +85°C), +10%, −14%. ɛ and tan δ show only small changes with frequency. The study shows this ceramic can be used in multilayer technology.     

Direct Synthesis and Hydration of Calcium Aluminosulfate (Ca4Al6O16S)

Calcium aluminosulfate (Ca₄Al₆O₁₆S or C₄A₃̄) was prepared by direct synthesis from calcium and aluminum nitrates, and aluminum sulfate. CaAl₄O₇(CA₂) formed as an intermediate at 900°C, and C₄A₃̄ was the main phase after calcination at 1100°C. The specific surface areas after calcination at 1100° and 1300°C were ∼2.5 and 1 m²/g, respectively. Hydration was investigated using XRD, DSC, SEM, conduction calorimetry, and solid-state ²⁷Al MAS-NMR spectroscopy. Calorimetry showed that the induction period was longer than that of a sample prepared using conventional solid-state sintering, and this was attributed to the formation of amorphous coatings. Crystalline hydration products, principally calcium monoaluminosulfate hydrate and aluminum hydroxide, appeared subsequently. Although the induction period was very long, complete hydration occurred as early as 3 d in the sample calcined at 1100°C and was 91% complete in the sample calcined at 1300°C.     

Effect of Cation Substitution and Non-Stoichiometry on the Microwave Dielectric Properties of Sr(B'0.5Ta0.5)O3 [B'=Lanthanides] Perovskites

The Sr(B'_0.5Ta_0.5)O₃ ceramics where B'=La, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Y, Er, and Yb have been prepared by the conventional solid-state ceramic route and their microwave dielectric properties have been investigated. The structure and microstructure of the ceramics have been characterized by X-ray diffraction and scanning electron microscope techniques. The relative permittiviy (ɛ_r) varies linearly with B'-site ionic radii, except for La, and the temperature coefficient of resonant frequency (τ_f) varies linearly with the tolerance factor. The Sr(B'_0.5Ta_0.5)O₃ ceramics have ɛ_r in the range 25.9–32, Q _u× f =4500–54 300 GHz, and τ_f=−79 to −42 ppm/°C. A slight deviation from stoichiometry affects the dielectric properties of these double perovskites. Partial substitution of Ba for Sr could tune the dielectric properties. Addition of rutile (TiO₂) lowered the sintering temperature and improved the dielectric properties of Sr(B'_0.5Ta_0.5)O₃ ceramics.     

Intrinsic Nonstoichiometry in Single-Phase Pb(Zr0.5Ti0.5)O3

Two-phase crucibles made of Pb(Zr,Ti)O₃ with small additions of either PbO or (Zr _x Ti _1-x )O₂, which provide atmospheres of constant PbO activity, permit study of intrinsic nonstoichiometry by thermogravimetry. The width of the single-phase region can be determined by alternate equilibration of a sample with crucible atmospheres of high and low PbO activity. The width of this region for Pb(Zr_0.5Ti_0.5)O₃ is 2.48 mol% PbO at 1100°C.