环氧树脂与丙烯酸酯单体的接枝共聚及其汽车阴极电泳涂料的性能

用环氧树脂与丙烯酸酯单体接枝共聚合,制备汽车阴极电泳涂料.研究了聚合条件对接枝体系的单体转化率(CR)、接枝率(GR)及接枝效率(GE),对产物环氧-丙烯酸酯树脂及其涂料漆膜性能的影响.用热重法(TG)和扫描电镜(SEM)对环氧-丙烯酸树脂及其涂料漆膜进行了分析.结果表明,在适宜的聚合条件下,接枝体系的CR、GR和GE分别达到100%、37.3%和87.0%;接枝率较高的环氧-丙烯酸树脂的外观,水溶性,其涂料的稳定性及漆膜的综合性能较好.环氧-丙烯酸酯树脂涂膜可在烘烤温度下自交联,漆膜的综合性能和外观均优于用三聚氰胺-甲醛树脂作交联剂的环氧-胺树脂漆膜.     

阴极电泳涂料用基料树脂及其制备工艺以及含有该种树脂的阴极电泳涂料组合物

一种新颖的碱性树脂,最好是环氧-胺体系树脂,可用于阴极电泳涂料的制备。该树脂的数均相对分子质量为1000～3 000,胺值为150～250 mg KOH/g,含有50～230毫当量/100g树脂的β-羟烷基氨基甲酸酯基团,此基团的结构式为OHC_2H_(2n)OC(O)NH-(n=2～3)。本发明同时提供了制备该树脂的工艺,以及用该树脂制成的提高泳透率的电泳涂料组合物及其工艺。该电泳涂料尤其适用于汽车车身及零部件。     

紫外光固化环氧丙烯酸酯涂料

合成了涂料用紫外光固化环氧丙烯酸酯树脂,并对其固化时间、铅笔硬度、附着力、柔韧性、耐磨性及耐化学品性进行测试,获得了预期的效果。     

光固化改性环氧丙烯酸酯阴极电泳涂料的制备与性能研究

用聚乙二醇、甲苯-2,4-二异氰酸酯及丙烯酸羟乙酯合成半封端聚氨酯丙烯酸酯,再以它对环氧丙烯酸酯进行改性,然后与光引发剂配制成阴极电泳涂料。考察了不同分子量的聚乙二醇对固化膜性能的影响。结果表明,电泳后光固化膜的玻璃化温度最高达58°C,附着力1级,柔韧性小于2 mm,耐冲击性(1 kg)大于40 cm,耐丙酮擦拭超过500次,光固化时间在12 s内,光泽优异。随着嵌入的聚乙二醇链段长度增加,水性树脂的黏度降低,固化膜的柔韧性增强,但光泽、耐丙酮擦拭性和铅笔硬度都降低。     

丙烯酸酯改性环氧阴极电泳涂料的研究

制备了一种以聚丙二醇增韧改性的环氧树脂为母体，接枝丙烯酸单体所形成主体树脂，经离子化反应得到阴极电泳涂料。详细研究了环氧增韧改性和丙烯酸单体接枝共聚合反应的引发剂种类及用量、反应温度、溶剂种类及用量等因素对漆膜性能的影响，发现与未进行增韧改性的环氧树脂产物比较，涂膜光泽和柔韧性均有显著改善。     

聚乙二醇改性环氧丙烯酸阴极电泳涂料用乳液的制备

以聚醚多元醇改性环氧丙烯酸酯为主体树脂制备了阴极电泳涂料用乳液。讨论了聚醚多元醇的种类和用量对改性环氧丙烯酸乳液及其涂膜性能的影响,以及扩链反应温度和时间对环氧基转化率的影响。通过红外光谱(FT-IR)和热重分析(TG)对改性前后的环氧丙烯酸阳离子树脂进行了表征。试验发现,以PEG1000为扩链剂,用量为13%~14%,在90°C下反应4h,制得的改性环氧丙烯酸乳液平均粒径65.49nm,ζ电位58.3mV,乳液黏度0.21Pa.s,常温下放置300d未分层。改性后的阴极电泳涂料漆膜柔韧性为0.5mm,附着力0级,硬度2H,冲击强度50kg.cm,耐水性达到208h,性能明显优于改性前的漆膜。     

装饰性丙烯酸阴极电泳涂料的合成

介绍了采用甲基丙烯酸缩水甘油酯与常用丙烯酸酯单体溶液共聚，通过对配方和工艺进行研究和优选，成功合成具高装饰性的丙烯酸阴极电泳漆的方法。对电泳漆膜的各项性能测试表明，它具有较高的高浊耐黄变性，可着色性，高装饰性，高耐候性等特点，可广泛应用于五金，家俱等装饰行业。     

丙烯酸系阴极电泳涂料研究进展

电泳涂料的合成与应用是涂料行业的一个突破性进展.综述了丙烯酸共聚物的合成原理,当今丙烯酸阴极电泳涂料研究的发展方向及所取得的进展.     

丙烯酸酯系阴极电泳涂膜性能研究

研究了丙烯酸酯系阴极电泳涂料主体树脂的原料配比、膜固化时间、温度及胺化剂等因素对漆膜性能的影响,并优化了试验条件.结果表明,甲基丙烯酸环氧酯系树脂作为阴极电泳涂料的主体树脂性能优越.     

环氧丙烯酸阴极电泳涂料的研究

通过接枝共聚的方法在环氧树脂主链上接枝合适的丙烯酸酯类单体,制备出自交联型阴极电泳涂料.研究了合成树脂的配方和工艺,同时对所得漆膜性能进行了测试.结果表明:选用E-44环氧树脂,用丙烯酸酯单体对其改性,以BPO作引发剂,用量为单体总量的0.4%-0.5%,接枝反应温度为110℃左右,反应时间为6 h左右时,树脂和漆膜均具有良好的性能.     

Preparation and surface characteristics of low-temperature curing fluorinated cathodic electrodeposition coating

Fluorinated cationic cathodic electrodepositing (CED) resins were synthesized by copolymerization of several acrylic monomers including Zonyl. Water dispersible cationic blocked-diisocyanate (denoted as TId) was also synthesized from isophorone diisocyanate (IPDI), cationic triethanolamine (TEOA), and dimethylpyrazole as the cross-linker for the low temperature curing at 90–120 °C. The emulsion stability of the cationic fluorinated CED resin was improved by ionization of the cross-linker TId, showing a mean particle diameter of 140–150 nm and a narrow distribution. 0.5 wt% of curing catalyst dibutyltin dilaurate (DBTL) was enough to accelerate the curing reaction and the gel content of the TId cured fluorinated CED film was higher than 90 wt% after being cured at 130 °C for 40 min. The contact angle and XPS spectrum of the CED film demonstrated that the surface enrichment of C–F₂ and C–F₃ groups effectively reduced the surface tension of the fluorinated CED coating and its surface tension γ_sv is even lower than 15 mN m⁻¹ for PTFE. The preheating of the CED film above T_g but below curing temperature promoted this surface enrichment of the fluorinated groups. Thermal fragmentation of the fluorinated side chains in the CED resins was successfully avoided due to using TId for low temperature curing.     

阴极电泳涂装生产线中的废气处理

介绍了阴极电泳漆烘干过程中废气的来源,提出了废气处理设备的设计原则。     

单组分丙烯酸阴极电泳涂料的研制

阴极电泳涂料由于其优异的耐蚀性能、高的泳透力和库仓效率而广泛用作防锈底漆。在此采用封闭不饱和异氰酸酯与常用的丙烯酸酯类单体共聚制备单组分丙烯酸阴极电泳涂料。探讨了合成树脂的配方及反应条件 ,并对所得阴极电泳涂料的性能进行了测试。该阴极电泳涂料克服了外加交联剂固化电泳涂料的缺点 ,具有可着色性、高耐蚀性和装饰性等优点。     

耐磨阴极电泳涂料的研究

利用专用水性阳离子颜料分散树脂,选择环保型颜料、助剂和耐磨填料,设计出耐磨阴极电泳涂料的色漆配方和分散工艺.采用PTFE乳液对传统乳液进行改性,当PTFE乳液用量为30%时,获得了具有优异耐磨性能的阴极电泳涂料.     

改性丙烯酸型阴极电泳涂料的研究

以PVB(聚乙烯醇缩丁醛)改性丙烯酸乳液,合成了一种新的阴极电泳涂料。研究了搅拌速度和引发剂的滴加速度对乳液聚合反应的影响。分别讨论了反应温度、引发剂用量对乳液性能以及固化温度和熟化时间对涂膜性能的影响。结果表明,乳液合成时,搅拌速度与引发剂的滴加速度分别以120～240r/min和1～1.5d/s为佳;反应温度为75～85°C,引发剂用量占单体用量的6%～8%时,乳液性能较佳。当固化温度为150°C和160°C时,所合成的改性丙烯酸型阴极电泳涂料涂膜外观平整,附着力0级,冲击强度50kg·cm,柔韧性1mm,光泽(60°)70°,耐盐雾时间超过1000h。     

阴极电泳涂料用阳离子丙烯酸树脂的合成与应用研究

通过溶液自由基聚合合成了用于阴极电泳涂料的阳离子丙烯酸树脂,研究了影响树脂水溶性、电沉积效果和涂膜性能的因素,并详细阐述了在应用方面的研究。     

环氧丙烯酸树脂合成工艺对阴极电沉积涂膜外观的影响

在110℃下、于一定溶剂中以偶氮二异丁腈和过氧化苯甲酰(BPO)为引发剂,引发由甲基丙烯酸甲酯、丙烯酸丁酯、甲基丙烯酸缩水甘油酯和甲基丙烯酸羟乙酯组成的反应体系,并以二乙醇胺为胺化剂、冰醋酸为中和剂合成了可用于阴极电沉积涂料的环氧丙烯酸阳离子树脂。研究了胺化温度、不同胺化工艺、不同醋酸中和工艺、中和温度以及不同DH值对电泳液粒径、电导率和阴极电沉积涂膜外观的影响。结果表明,选择胺化工艺Ⅱ,在90℃下胺化,同时选用冰醋酸在90℃下直接中和,当pH值为5．8左右时,所得的阴极电沉积涂料电泳液的外观呈乳白带蓝、电导率约为0．7ms／cm、槽液粒径约为95nm,所得涂膜厚度超过20μm,涂膜外观均匀、平滑。     

阴极电泳漆的工作液参数管理探讨

着眼于阴极电泳漆涂装的工艺过程控制,从一定的理论角度出发,重点阐述了槽液稳定性及几个常见的涂装弊病的控制,调整方法。