小尺寸混凝土试件双K断裂参数试验研究

采用最大尺寸为680mm×160mm×40mm的标准三点弯曲梁试件,利用在初始裂缝两侧粘贴电阻应变片并利用混凝土裂缝扩展到此处时其应变回缩的方法测得了起裂荷载Pini,在此基础上根据Pini及初始缝长a0得到了起裂断裂韧度KIiCni;根据在试验中测得的最大荷载Pmax及对应的裂缝口张开位移CMODC计算了混凝土等效裂缝长度aC,据此计算了失稳断裂韧度KIuCn。结果表明:采用电阻应变片法可准确测定混凝土的起裂荷载Pini,且方法简单。试验结果还表明:在本试验范围内,三点弯曲梁法测得的混凝土双K断裂参数KIiCni、KIuCn与试件高度无关,进一步说明了混凝土双K断裂参数可以作为描述混凝土裂缝扩展的断裂参数。     

砼非标准三点弯曲梁试件双Ｋ断裂参数

采用跨高比为２．５的非标准三点弯曲梁试件,利用在试验中测得的最大荷载Pmax对应的裂缝口张开位移ＣＭＯＤc,根据渐近线性叠加假设,求得了砼缝亚临界扩展量△ac.在此基础上,采用虚拟裂缝模型计算了不同初始缝长,不同试件高度的砼非标准三点弯曲梁试件的起裂断裂韧度Ｋ^iniIC,失稳断裂度Ｋ^umIC及临界裂缝尖端张开位移ＣＴＯＤc,计算结果表明,砼Ｋ^umIC与试件高度及初始缝高比无关,而Ｋ^iniIC在初始缝高比a0/h=0.3-0.5内,也是一稳定的常数且试件高度无关,这说明砼双Ｋ断裂参数可作为砼的材料常数。     

大初始缝高比混凝土试件双K断裂参数的试验研究

双K 断裂准则能够定量描述混凝土裂缝的起裂、稳定扩展和失稳断裂。该文采用混凝土三点弯曲梁试件,通过在试验中测得的起裂荷载P_ini、最大荷载P_max及临界裂缝口张开位移CMOD_C计算了初始缝高比为0.3~0.9共7组试件的起裂断裂韧度K_ICini 和失稳断裂韧度K_ICun 。结果表明,当初始缝高比为0.3~0.7时,混凝土裂缝扩展经历起裂、稳定扩展和失稳破坏3 个阶段,双K 参数均是与初始缝高比无关的材料参数;当初始缝高比大于或等于0.8 时,混凝土裂缝起裂后便进入失稳扩展阶段,起裂荷载即为最大荷载,且计算得到的K_ICini 仍与初始缝高比无关。因此,在确定K_ICini 时,仅需测得初始缝高比大于或等于0.8试件的P_max,将P_max作为P_ini直接计算得到K_ICini。同以往的试验方法相比,其结果更为准确且试验方法简单。     

岩石-混凝土界面拉伸断裂性能的率相关性研究EI北大核心CSCD

该文弯曲断裂试验获得了不同应变率下界面的抗拉强度、荷载-加载点位移曲线、荷载-裂缝口张开位移曲线、起裂荷载和峰值荷载,通过夹式引伸计法和DIC法获得了临界裂缝扩展长度。并计算了界面断裂能及双K断裂参数,分析了不同应变率下界面断裂过程区演化规律及特征长度的变化。结果表明:随应变率的增大,断裂能和起裂韧度增大,临界裂缝长度和失稳韧度先增加后减小,断裂过程区长度及特征长度随应变率的提高而减小。该文从裂缝发展路径、自由水粘性、惯性效应三方面探讨了岩石-混凝土界面断裂参数的率效应。     

电测法确定低强混凝土裂缝起裂和等效裂缝长度

该文设计了3种低强度混凝土三点弯曲切口梁,测试研究其双K断裂参数。试验中采用标距为5 mm和10 mm的应变片以半桥连接方式测量预制裂缝的起裂荷载,比较其工作性,发现应变片测量起裂荷载具有强度敏感性,短标距应变片更适宜测量本试验用低强度混凝土的裂缝起裂。试验中另沿韧带方向布置4组半桥应变片,根据各测点处拉应变回缩时的荷载与裂缝口张开位移,计算裂缝发展至测点高度时刻的等效裂缝长度,并与此时的实际缝长比较,结果表明双K断裂模型在预测裂缝长度方面具有较好的适用性。     

全级配混凝土I型裂缝扩展全过程数值模拟

该文将起裂断裂韧度作为裂缝扩展的判定依据,应用ANSYS软件,对全级配混凝土I型裂缝扩展过程进行数值模拟,分别计算了混凝土楔入劈拉试件的荷载-裂缝口张开位移曲线、临界裂缝长度和双K 断裂韧度,并与溪洛渡大坝的断裂试验结果进行比较,吻合良好。同时,结合试验数据,将该文计算结果与《水工混凝土断裂试验规程》规定的标准尺寸试件断裂参数计算结果进行对比。结果表明:规程规定的方法也适用于大尺寸非标准试件双K 断裂参数的计算,其误差率在5%以内。此外,对于全级配混凝土,只要通过试验测得其弹性模量、抗拉强度、抗压强度和起裂荷载,即可用该文提出的方法计算混凝土的双K 断裂韧度和裂缝扩展全过程。应用该方法还可以得到全级配混凝土的K_R阻力曲线。     

权函数法计算的混凝土断裂韧度

在采用解析方法确定混凝土的双K断裂韧度时,粘聚断裂韧度计算的准确性直接影响起裂韧度断裂控制参数计算的准确性。根据权函数法,给出了基于CEB-FIP粘聚应力软化函数计算的粘聚断裂韧度的表达式。使用最大高度为1000mm的五组楔入劈拉紧凑拉伸试件测量的最大荷载和临界裂缝嘴张开口位移,计算了混凝土的双K断裂韧度,并与积分解析计算公式进行了对比。结果表明,两种解析计算方法较为吻合,最大误差不超过2%。     

混凝土裂缝扩展的断裂过程准则与解析

该研究工作对混凝土这一多相的复合材料,通过实验和理论相结合的科学手段,建立了一套完整的描述混凝土裂缝发展的断裂理论以及分析方法。根据实验观测结果提出了双K断裂参数,可以反映混凝土裂缝发展特性。在线形渐进叠加假定基础上,给出了双K断裂参数的解析表达式。根据分布于断裂过程区上粘聚力对裂缝扩展阻力的增强作用,得到了双K断裂参数适用的解析解,并通过实验分析了各种可能因素对双K断裂参数的影响。在考虑粘聚力影响条件下,提出了裂缝扩展阻力的新KR曲线,并将双K断裂参数与之对应起来。研究工作又通过能量的观点提出了与双K断裂参数相对应的以能量释放率为参数的双G断裂参数。通过数值计算和实验分析证实了能量法和应力场法在描述混凝土断裂性能方面的等效性。     

基于非接触式观测技术的再生骨料混凝土断裂性能分析

采用非接触式观测技术(DIC)和传统电测法,对不同再生粗骨料取代率(0％、30％、50％、70％、100％)的混凝土进行三点弯曲梁断裂性能试验,得到双K断裂参数、裂缝口张开位移(CMOD)、裂缝尖端张口位移(CTOD)、裂缝扩展长度(△a)以及裂缝扩展路径,验证DIC非接触观测技术的有效性.结果表明:当再生骨料取代率为...     

基于虚拟裂缝模型的混凝土断裂过程区研究

利用虚拟裂缝模型对混凝土断裂过程区进行了研究.以无限大板中心拉伸裂缝模型为例,将过程区裂缝张开位移采用多项式级数形式表示,求得了断裂过程区上的位移分布和粘聚力分布.进而分析了材料参数对断裂过程区上的位移、粘聚力、断裂过程区长度以及峰值外荷载的影响.结果表明:断裂过程区上的位移和粘聚力均为非线性分布.断裂过程区长度随骨料最大粒径增大而逐渐增大,随抗压强度增大而逐渐减小.峰值外荷载随骨料最大粒径和抗压强度增大均逐渐增大.     

混凝土软化本构关系对双K断裂参数的影响

混凝土裂缝扩展的双K 断裂准则，用于描述混凝土结构裂缝的起裂、稳定扩展和失稳断裂。其相 应的双K 断裂参数ini c K I 、un c K I 可通过简便的实验和基于虚拟裂缝扩展粘聚力的解析方法确定。已取得的 研究结果表明，起裂韧度ini c K I 的解析解与所确定的混凝土软化本构关系有关。对于简单实用的双线性软化 本构曲线而言，参数s s 、s w 、0 w 的取值直接影响软化本构关系的确定。根据本课题组新近所做楔入劈 拉实验，经分析对比得到了与实测结果相符合、为确定双K 断裂参数所使用的双线性软化本构曲线的相应 参数。     

低热水泥全级配混凝土断裂试验及尺寸效应分析

该文分析了低热水泥全级配混凝土断裂性能的尺寸效应规律。通过在大坝工程施工现场浇筑成型试件有效高度为0.75 m、1.5 m和2.25 m的楔入劈拉试件并开展试验,获得低热水泥全级配混凝土稳定的双K断裂参数。基于试验结果,采用理论方法推求全级配混凝土无尺寸效应的失稳和起裂韧度,预测任意尺寸试件的最大和起裂水平荷载。研究发现,当韧带高度与骨料最大粒径比值大于等于6.0后,双K断裂参数趋于稳定。尺寸效应模型及其演化形式可用于确定全级配混凝土无尺寸效应的起裂和失稳断裂韧度,定量分析强度与韧度对裂缝扩展的影响,并可通过引入等效几何参数,分别建立任意尺寸试件最大和起裂水平荷载的预测方程。     

Determination of double-Determination of double-K criterion for crack propagation in quasi-brittle fracture Part I: experimental investigation of crack propagation

The results of experimental investigations using laser speckle interferometry on small size three-point bending notched beams and using photoelastic coating and the strain gauges on very large size compact tension specimens of concrete are presented in detail. The investigations showed that there exists a stage of stable crack propagation before unstable fracture occurs. The results are in agreement with other researchers' investigations using moire interferometry, holographic interferometry, dye-impregnation method and microscope. Further detailed study shows that the three different states, i.e., crack initiation, stable crack propagation and unstable fracture can be distinguished in the fracture process in concrete structures. In order to predict the crack propagation during the fracture process in quasi-brittle materials a double-K criterion is proposed. The double-K criterion consists of two size-independent parameters. Both of them are expressed in terms of the stress intensity factors. One of them reflects the initial cracking toughness, denoted with Kⁱⁿⁱ, which can be directly evaluated by the initial cracking load, P_ini, and the precast crack length, a₀, using a formula of LEFM. The other one refers to the unstable fracture toughness, denoted with K^un, which can be obtained inserting the maximum load, P_max, and the effective crack length, a, into the same formula of LEFM. The values of the two parameters, K _Ic ⁱⁿⁱ and K _Ic ^un , obtained from the small size three-point bending notched beams and the large size compact tension specimens show that K _Ic ⁱⁿⁱ and K _Ic ^un are size-independent. Evaluating with the K-resistance curves obtained from the same test data, it is found that the proposed double-K criterion is equivalent to it in basic principle, but, the double-K criterion can be applied more easily than the K-resistance curve. Finally, as a practical example, the application of the double-K criterion to the prediction of the crack propagation in a concrete dam is discussed.     

Equivalence between stress intensity factor and energy approach based fracture parameters of concrete

The paper presents numerical study and relationship between the double-K fracture parameters and the double-G fracture parameters using two standard tests. The data required for calculation is obtained using cohesive crack model. It is observed that both the corresponding parameters of the double-K fracture model and the double-G fracture model at the onset of crack initiation and unstable fracture are equivalent. This observation agrees well with experimental results available in literature. It is also found that the fracture parameters of double-K fracture criterion and double-G fracture criterion are influenced by initial notch-length/depth ratio, specimen shape, size and softening function.     

基于等效纯弯曲梁的混凝土双K断裂参数研究

因四点弯曲梁跨中裂缝截面附近处于纯弯段,故其从理论上更符合Ι型断裂模式。基于此,该文通过开展跨中带缝的四点弯曲梁试验,将荷载作用下的四点弯曲梁纯弯曲段等效为纯弯曲梁,基于线性叠加原理给出了计算混凝土四点弯曲梁双K断裂参数的计算公式,并研究了不同初始缝高比（0.2、0.3、0.4、0.5及0.6）对四点弯曲梁双K断裂参数的影响,结果表明:随着初始缝高比的增大,试件起裂荷载P_ini,最大荷载P_max及相对临界有效裂缝扩展长度（a_c-a₀）/H均逐渐减小;起裂断裂韧度K_ICini和失稳断裂韧度K_ICun基本保持不变。可见,四点弯曲梁可以用于研究混凝土的双K断裂参数。     

采用峰值荷载法确定全级配水工混凝土断裂参数

该文采用峰值荷载法研究了全级配水工混凝土试件的断裂参数。通过有限元方法,得到了适用于全级配水工混凝土的非标准楔入劈拉试件的应力强度因子K、裂缝嘴张开口位移CMOD计算公式以及裂缝张开位移COD与CMOD比值COD/CMOD的相关曲线。基于相关断裂试验,通过该文所提公式得到了全级配水工混凝土的等效断裂韧度与临界裂缝尖端张开口位移CTOD_c等断裂参数。研究结果表明:峰值荷载法可应用于截面尺寸不同而缝高比相同的全级配水工混凝土试件,峰值荷载法只需实测各试件的峰值荷载,就可方便确定全级配水工混凝土的断裂参数。