载体焙烧气氛对环氧乙烷银催化剂性能的影响

在不同组成的焙烧气氛中制备了氧化铝载体,对其进行XRD、压汞和SEM表征。将载体浸渍在银氨络合溶液中制得银催化剂,对制备的催化剂进行CO脉冲吸附和O₂-TPD表征,并采用固定床反应器对比评价了反应性能。结果表明,空气混合氮气气氛下焙烧的载体,孔径呈多级分布,氧化铝微观形貌呈“块”状。氮气比例的提升,有利于Ag颗粒的分散和提高催化剂表面低温脱附氧的比例。以70%空气+30%氮气气氛所焙烧载体制备的催化剂相比传统空气焙烧气氛,反应温度降低1.7 ℃,选择性提高1.6%,但更高的氮气比例会造成催化剂的性能劣化。     

焙烧温度对合成吗啉催化剂性能的影响

利用共沉淀法制备了合成吗啉催化剂,用差热分析（TG/DTA）和XRD分析技术研究了合成吗啉的催化剂性能,特别考察了焙烧温度对催化剂性能的影响。通过几种曲线的分析,初步确定了催化剂的最佳焙烧温度在400 ℃左右。     

焙烧温度对加氢脱氮催化剂性能的影响

A series of Mo/Ni-based hydrotreating catalysts calcined at different temperatures was prepared by impregnation method,and characterized by means of N₂ adsorption-desorption,NH₃-TPD and TPR techniques.The HDN performance of the catalysts was investigated in a microreactor.The results indicated that with the increase of calcination temperatures,the specific surface area of the catalysts was decreased,the average pore size was gradually increased,and the pore volume change was very small.The acid amount on the surface of the catalysts showed a tendency to ascend firstly, and then to descend with the increase of calcination temperatures, and the acid amount reached the maximum at 500 ℃. The activity of the hydrotreating catalysts was enhanced firstly and then reduced with the increase of calicination temperature,and the optimal calcination temperature was 500 ℃.On the whole,the activity of the catalysts could be improved prepared under suitable calcination temperature,and be suppressed obtained under high calcination temperature.     

载体焙烧温度对Ni-Mo/TiO2催化剂的影响

采用碳源助剂改性载体TiO2,制备催化剂Ni-Mo/TiO2催化剂,考察载体焙烧温度对催化剂性能的影响,并采用透射电镜(TEM)、X射线能谱(EDS)、X射线衍射(XRD)和X射线光电子能谱(XPS)等对载体及催化剂进行表征.结果表明,焙烧温度为500～600℃时,TiO2晶粒大小适中,活性元素分布均匀,焙烧温度为550℃的载体制备的催化剂加氢性能较好.     

焙烧温度对Cu-Zn-Al-Mg甲醇合成催化剂结构与性能的影响

采用共沉淀法制备Cu-Zn-Al-Mg甲醇合成催化剂,并用XRD、N2低温吸附、H2-TPR、SEM、TG-DTG等手段对催化剂进行表征,着重考察焙烧温度对催化剂结构与性能的影响.结果表明,随着焙烧温度的增加,铜锌间的相互作用增强,有利于催化反应进行;但过高的焙烧温度又会导致催化剂中CuO晶粒过大,不利于铜的分散.35...     

二氧化碳和抑制剂浓度对银催化剂反应性能的影响

研究了反应气中CO_2和抑制剂浓度对YS-8520银催化剂反应性能的影响规律。在其它组成不变情况下,反应气中CO_2的浓度增加,银催化剂活性下降,选择性变化不明显。CO_2浓度变化一个百分点,催化剂活性变化相当于反应温度变化3.0～4.0℃。反应气中CO_2浓度升高,银催化剂的活性下降速率也就是反应温度上升速率明显加快。降低反应气中CO_2浓度对提高银催化剂的反应活性和改进稳定性有明显的效果。反应气中抑制剂浓度对银催化剂稳定性影响明显。银催化剂在较低的抑制剂浓度条件下长期运行,反应温度上升较快;在长期反应过程中不断增加反应气中抑制剂浓度,能够延缓催化剂反应温度的上升速率,延长催化剂的使用寿命。在银催化剂使用初期,反应气中抑制剂浓度过高对催化剂的活性和稳定性都不利。在银催化剂的使用过程中,反应气中抑制剂的浓度应先保持在较低水平,根据反应温度的变化情况逐渐增加,可以明显改进催化剂的反应性能。上述结论在工业应用过程中得到了验证。     

焙烧及还原温度对Ni-Mg甲烷化催化剂的影响

采用共沉淀-水热复合法制备Ni-Mg/Al2O3催化剂,考察焙烧和还原温度对其结构和甲烷化催化性能的影响,通过XRD,H2-TPR,TEM等表征,发现随焙烧温度升高,催化剂中NiAl2O4物相呈增多趋势,至900℃时,催化剂中镍物种完全以NiAl2O4形式存在,催化剂表面积从500℃焙烧的130m2/g降至900℃焙烧的34m2/g.针对600℃焙烧的催化剂,反应活性随还原温度升高呈现先增加后降低的趋势,其最佳还原温度为650℃,这主要是受Ni物种还原度、还原后Ni晶粒尺寸等多重因素影响.通过关联甲烷化性能与催化剂结构发现,NiO与载体之间相互作用适中,还原后表面能够形成较小的镍晶粒,催化剂具有较好的甲烷化活性和稳定性.     

载体预处理工艺对乙烯氧化银催化剂性能的影响

采用预浸渍和预焙烧联合预处理工艺处理载体,制备系列乙烯氧化的银催化剂。对催化剂进行孔结构、吸水率和比表面积等表征,结果表明,预处理工艺能增加载体的比表面积,改善活性组分的分散状况并提高活性组分银的负载量,同时除去载体表面钠,预处理工艺制备的银催化剂活性、选择性和稳定性均得到改进。     

载体助剂对环氧乙烷银催化剂性能的影响

采用Zr和Cr助剂改性银催化剂载体氧化铝,探索影响环氧乙烷合成银催化剂初期选择性的关键因素。结果表明,载体中添加的Zr和Cr助剂,负载的银粒子及协同助剂均未在氧化铝表面形成较强的酸性中心,Zr和Cr组分间存在协同效应,促进高价态的Re元素的形成,Zr组分能激发出特征峰信号更强的Cr 2p峰。添加Zr助剂的载体与不加Zr的载体相比,在强化负荷条件下,制成的银催化剂初期选择性高出约2%,初期反应温度高出约6℃。     

焙烧温度对改性钒基催化剂载体性能的影响

采用硅溶胶和微波法对堇青石蜂窝陶瓷载体进行表面改性,并在改性载体基础上制备了钒系催化剂。通过BET比表面积、TG-DTA和XRD等手段研究了焙烧温度对改性载体的比表面积、结构和催化剂反应活性的影响。实验表明,改性载体在经400℃焙烧后比表面积达到最大值72.74 m2/g,同时焙烧温度的变化并没有影响改性载体的结构,相应的使用经400℃焙烧的改性载体所制成的催化剂在最佳反应温度350℃时也拥有最大的NO转化率,说明了400℃是改性载体的最佳焙烧温度。     

钢化温度对可钢双银Low-E玻璃性能影响

主要研究了目前典型的离线双银Low-E低辐射玻璃在钢化过程中的温度变化对其性能的影响,通过实验,总结出生产过程中温度变化对光学和电学性能影响的规律,为完善钢化过程中工艺参数设定提供参考依据。     

Influence of Heating Rate and Calcining Temperature on Properties of 95 Polycrystalline Alumina Fiber

The swung gel fibers were heated to 400 ℃ at 0.5, 1, 1.5, 2, 2.5, 3 and 4 ℃·min-1 of heating rate, respectively, and soaked for 1 h; then heated to 600 ℃ at 3 ℃·min-1 of heating rate and soaked for 1 h; at last calcined at 1 000, 1 100, 1 200, 1 300, and 1 400 ℃ for 1 h, respectively. The average single fiber tensile strengths of fibers after calcining at 600 ℃ or higher temperatures were determined and their surface morphology was observed. The results show that: (1) when the heating rate below 400 ℃ is 0.5-1 ℃·min-1, the average single fiber tensile strengths of 95 polycrystalline alumina fibers after calcining at 600 ℃ and 1 000-1 100 ℃ exceed 1 000 and 800 MPa, respectively, surface of the fibers after calcining at 1 000-1 100 ℃ is smooth, α-Al2O3 appears at 1 200 ℃, and a large amount of α-Al2O3 forms above 1 300 ℃; (2) when the heating rate exceeds 3 ℃·min-1, the fibers pulverize obviously.     

Mn-Ce催化剂低温脱硝性能的研究

采用浸渍法和共沉淀法制备了Mn-Ce/TiO2-SnO2、MnCeTiOx及MnCeSnTiOx催化剂.考察了催化剂在80～180℃之间的脱硝性能以及在180℃下通入150 ppm SO2300 min后催化剂的抗硫性能.通过XRD、BET、NH3-TPD等方法对催化剂的理化性质进行了表征.结果表明,浸渍法制备的Mn-Ce/TiO2-SnO2催化剂表现出了最佳的低温脱硝性能,在100℃时,可达90％以上,但其抗硫性能最差,在180℃下通入150 ppm SO2300 min后,脱硝效率由最初的约100％,下降为40％.在掺杂Sn之后,共沉淀法制备的MnCeTiOx催化剂的低温活性及抗硫性能均有得到了有效提高.MnCeSnTiOx催化剂表现出了最佳的抗硫性能,在180℃下通入150 ppm SO2300 min后,脱硝效率由最初的约100％,下降为65％.     

Surface Fractal Dimension of Perovskite-Doped Alumina Membrane: Influence of Calcining Temperature

The surface fractal dimension, D , and pore size distribution of perovskite-doped alumina membrane prepared via the sol–gel method were determined from their nitrogen adsorption isotherms. The D value was calculated using the Frenkel–Halsey–Hill method. The D value increased with increasing temperature due to membrane shrinkage. The pore size distribution pattern of perovskite-doped alumina membrane showed a narrow pore size when the temperature was increased from 400° to 800°C. The isotherm type was characterized as Type IV. Smoothing and sintering effects contributed to the decreasing trend of surface fractal dimension at a high temperature. The surface fractal dimension increased when the perovskite ratio in alumina membrane was increased.     

催化剂性能对煤炭燃烧产生的影响

中国现今对于煤炭产业的长期发展战略离不开发展洁净煤技术,以提高煤炭的资源利用率。然而在煤炭燃烧利用过程中存在燃烧不完全,热能利用效率低,利用过程中产生大量容易对大气产生污染的有害物质如烟尘、一氧化碳、二氧化硫等气体,因此,提高煤炭的燃烧利用率对整个社会及国家都会产生极其重要的意义。以氧化铁废渣为原料,把评价指标侧重点放在烧失率、热值释放率和硫释放率上,研究对煤炭燃烧具有催化作用的Fe2O3对于燃烧性能的影响。通过一系列实验研究,最后得出结论 :煤炭的燃烧性可通过添加合适的催化剂得到提高,在整个燃烧过程中煤炭的燃尽率在催化剂的作用下有了明显的提高。但是煤炭的燃烧性能也会受到会阻碍,通过多次实验发现,催化剂量的加入应该适量并且少量,否则只能适得其反。在实验中,对结果进行多次量化,对于添加量进行调整,得到了对于提高燃尽率最为合适的添加量。     

不同制备条件对镍基催化剂性能的影响研究

通过不同制备方法制取NiO-Ce0.75Zr0.25O2/Al2O3催化剂,考察制备条件对CH4/CO2重整反应催化性能的影响。催化性能尤其结构特性的研究,采用H2-TPR、BET手段进行表征。结果表明:沉淀-浸渍法与共沉淀法和溶胶凝胶法相比较,所制得催化剂活性组分NiO在载体表面分散度更高,此时催化剂抗积炭、抗烧结性能增强,催化剂稳定性提高,活性评价中CH4、CO2转化率和H2收率分别可达85.5%、86.4%和93.8%。     

哌啶对负载型Pt催化剂加氢脱硫性能的影响

将ZSM-5溶于偏硅酸钠水溶液,用水热合成法以十六烷基三甲基溴化铵作模板剂自组装合成了ZSM-5/MCM-41介孔硅铝分子筛(ZM)。以二苯并噻吩(DBT)和哌啶作为模型含硫和含氮化合物,考察了含氮化合物对ZM担载的Pt催化剂加氢脱硫(HDS)反应性能的影响。结果表明,DBT在Pt/ZM催化剂上主要通过直接脱硫(DDS)反应路径脱硫,引入哌啶显著抑制了DBT的HDS反应。与DDS相比,哌啶对加氢路径(HYD)抑制作用更强,并且几乎完全抑制了HYD路径含硫中间体的脱硫。动力学分析表明,DBT的HDS反应和DDS路径级数为一级而其HYD路径则为零级,说明DDS和HYD反应可能是在Pt/ZM不同活性中心上进行的。     

中温变换催化剂中氧化铝添加效应研究

实验室研究了添加氧化铝对中温变换催化剂堆密度、机械强度、活性和热稳定性的影响。 研究表明,添加适量的氧化铝可明显改善铁铬系中温变换催化剂的性能。     

Influence of Light Calcining Hydration of Magnesite on MgO Sintering

Sintered magnesia clinker(also called sintered MgO) was prepared with Mg(OH)2(prepared by light calcining hydration of magnesite) and magnesite as starting materials,respectively,by the technical process:light calcining(850 ℃ 1 h) → grinding → molding → firing(1 600 ℃ 3 h).The morphology and structure of light calcined MgO powders prepared with magnesite or Mg(OH)2 were analyzed by XRD,SEM and FT-IR.The sinterability and microstructure of sintered magnesia prepared with magnesite or Mg(OH)2 were researched....     

催化剂对环氧丙烯酸水性烤漆性能的影响

以环氧丙烯酸水性树脂为主基料,以甲醚化氨基树脂为辅基料配制水性丙烯酸氨基烤漆。讨论水性烤漆配方中催化剂的种类及用量对水性烤漆涂膜的硬度、附着力和耐水性等性能的影响。