Preparation and properties of mullite-bonded porous fibrous mullite ceramics by an epoxy resin gel-casting process

Porous fibrous mullite ceramics with a narrow range of pore size distribution have been successfully prepared utilizing a near net-shape epoxy resin gel-casting process by using mullite fibers, Al₂O₃ and SiC as raw materials. The effects of sintering temperatures, different amounts of fibers and Y₂O₃ additive on the phase compositions, linear shrinkage, apparent porosity, bulk density, microstructure, compressive strength and thermal conductivity were investigated. The results indicated that mullite-bonded among fibers were formed in the porous fibrous mullite ceramics with a bird nest pore structure. After determining the sintering temperatures and the amount of fibers, the tailored porous fibrous mullite ceramics had a low linear shrinkage (1.36–3.08%), a high apparent porosity (61.1–71.7%), a relatively high compressive strength (4.4–7.6 MPa), a low thermal conductivity (0.378–0.467 W/m K) and a narrow range of pore size distribution (around 5 µm). The excellent properties will enable the porous ceramics as a promising candidate for the applications of hot gas filters, thermal insulation materials at high temperatures.     

Theoretical and experimental analyses of Young's modulus and thermal expansion coefficient of the alumina-mullite system

Young's moduli (E) and thermal expansion coefficients (TECs) of the alumina–mullite–pore system (96.4–99.5% relative density) were measured for a wide mullite fraction range from 0 to 100 vol%. Both E and TEC values decreased at high mullite fractions. These properties were theoretically analyzed with four proposed model structures that were constructed by three-phase systems of mullite (or alumina) continuous phase 2–pore dispersed phase 1–alumina (or mullite) dispersed phase 3. The ratios of E(theoretical)/E(experimental) and TEC(theoretical)/TEC(experimental) were very close to unity, depending on the mullite fraction. That is, the measured E and TEC values are closely related to the change in the composite microstructure as a function of mullite fraction.     

In-situ growth of mullite whiskers and their effect on the microstructure and properties of porous mullite ceramics with an open/closed pore structure

Porous mullite ceramics with an open/closed pore structure were prepared by protein foaming method combined with fly ash hollow spheres. Both the open porosity and total porosity of samples were enhanced by increasing the hollow sphere content. Mullite whiskers with a diameter of 0.2–4 μm were grown in-situ in the porous mullite ceramics with an AlF₃ catalyst, conforming to a vapor-solid growth mechanism. The pore structure of the porous mullite ceramics was significantly affected by the mullite whiskers which increased the open porosity and total porosity. Moreover, the median pore size was reduced from 65.05 μm to 36.92 μm after the introduction of mullite whiskers. The flexural strength and the thermal conductivity of the samples decreased with increasing total porosity. The porosity dependence of the thermal conductivity was well described by the universal model, providing a reference for the prediction of thermal conductivity of porous ceramics with open/closed pores.     

Porous fibrous ZrO2-mullite ceramics prepared via tert-butyl alcohol-based gel-casting

Mullite fiber was used to fabricate ZrO₂-mullite based porous ceramic via tert-butyl alcohol (TBA)-based gel-casting process using zirconite and bauxite as raw materials. Phase compositions, microstructure, pore size distribution, linear shrinkage, bulk density, apparent porosity, thermal conductivity, and compressive strength were analyzed to investigate influences of mullite fiber content and added Y₂O₃ on prepared porous ceramics. Results show that bird nest-like three-dimensional fibrous reticular skeleton structure was constructed with mullite fibers that evenly enwrapped rod-like mullite and ZrO₂ grains. Prepared porous fibrous ZrO₂-mullite ceramics had narrow pore size distribution that consisted of mullite and m-ZrO₂. With an increase in mullite fiber content, linear shrinkage and bulk density decreased, apparent porosity increased, and relatively good thermal conductivity was obtained. In addition, added Y₂O₃ reacted with Al₂O₃ and SiO₂ to form Y-Al-Si-O glass phase, which promoted sintering and densification of the ceramic, thus improving its compressive strength.     

High gas permeability and directional channels of mullite porous ceramics prepared by pectin-based freeze-drying method

New gel system for preparing mullite porous ceramics by gel-casting freeze-drying was proposed, using pectin as gel source and alumina and silica as raw materials. Directional channels were formed due to sublimation of water during freeze-drying and decomposition of pectin during high temperature sintering to prepare porous mullite ceramic membranes. Effects of solid content on the properties of mullite ceramics in terms of phase composition, microstructure, apparent porosity, bulk density, pore size distribution, compressive strength, thermal conductivity, pressure drop, and gas permeability were investigated. It was found that prepared porous mullite possessed high apparent porosity (56.04%–75.34%), low bulk density (.77–1.37 g/cm³), uniform pore size distribution, relatively high compressive strength (.61–3.03 MPa), low thermal conductivity (.224–.329 W/(m·K)), high gas permeability coefficient (1.11 × 10⁻¹⁰–4.73 × 10⁻¹¹ m²), and gas permeance (2.18 × 10⁻²–9.32 × 10⁻³ mol⋅m⁻²⋅s⁻¹⋅Pa⁻¹). These properties make prepared lightweight mullite ceramic membranes promising for application in high temperature flue gas filtration. Proposed gel system is expected to provide a new route to prepare porous ceramics with high porosity and directional channels.     

Preparation of Porous Mullite Ceramics Using Fly Ash Cenosphere as a Pore‐Forming Agent by Gelcasting Process

Porous mullite ceramics were fabricated from an industrial grade mullite powder by gelcasting process using fly ash cenospheres (FAC) as a pore‐forming agent. The influence of content of FAC and sintering temperature on the density and strength was evaluated. The microstructure showed that FAC can act as a sintering aid and a pore‐forming agent. When the sintering temperature at 1200°C, porous mullite ceramics with a relatively high porosity (48.1–72.2%), low density (0.84–1.64 g/cm³), low thermal conductivity (0.16–0.22 W/m · K), and high compressive strength (6.21–14.70 MPa) have been obtained.     

Porous mullite ceramics with enhanced compressive strength from fly ash-based ceramic microspheres: Facile synthesis,structure, and performance

Porous mullite ceramics are widely used in heat insulation owing to their high temperature and corrosion resistant properties. Reducing the thermal conductivity by increasing porosity, while ensuring a high compressive strength, is vital for the synthesis of high-strength and lightweight porous mullite ceramics. In this study, ceramic microspheres are initially prepared from pre-treated high-alumina fly ash by spray drying, and then used to successfully prepare porous mullite ceramics with enhanced compressive strength via a simple direct stacking and sintering approach. The influence of sintering temperature and time on the microstructure and properties of porous mullite ceramics was evaluated, and the corresponding formation mechanism was elucidated. Results show that the porous mullite ceramics, calcined at 1550 °C for 3 h, possess a porosity of 47%, compressive strength of 31.4 MPa, and thermal conductivity of 0.775 W/(m?K) (at 25 °C), similar to mullite ceramics prepared from pure raw materials. The uniform pore size distribution and sintered neck between the microspheres contribute to the high compressive strength of mullite ceramics, while maintaining high porosity.     

Fabrication and properties of mullite fiber matrix porous ceramics by a TBA-based gel-casting process

A bird nest-like structure was designed by using the mullite fiber as the matrix and SiO₂ as the high temperature binder. This special material was successfully prepared by a TBA-based gel-casting process. The randomly arranged fiber laps bonded by SiO₂ binder was the most important structure characteristic of this porous material. The effect of sintering temperature on the properties, i.e. porosity, bulk density, linear shrinkage, compressive strength, thermal conductivity and the microstructure was studied. The composite exhibited significant pseudoductility. The fracture mechanism of this composite under compression was discussed. The results indicated that the sintering temperature ranging from 1500 to 1600 °C was suitable for yielding mullite fiber matrix porous ceramics which had a low thermal conductivity (0.19–0.22 W/m K), a relatively high compressive strength (3–13 MPa) and a high resilience (66–70%) for applications in the thermal insulators and high-temperature elastic seal field.     

Design and preparation of high permeability porous mullite support for membranes by in-situ reaction

The natural mineral kaolin combined with alumina additives Al(OH)₃,α-Al₂O₃ and AlF₃ was used to prepare porous mullite ceramic membrane supports using an in-situ reaction. The effects of composition and sintering temperature on the sintering behavior, pore structure, permeability and microstructure of the resulting porous mullite supports were extensively investigated. The experimental results showed that excess SiO₂ in kaolin can be consumed by adding alumina precursors, which resulted in a stiff skeleton of interlinked needle-like mullite crystals in-situ during the sintering. The needle-like mullite crystals touched each other and formed a short network, which acted as a porous skeletal network structure. This network resulted in a highly permeable porous structure. The resulting support is suitable for the preparation of asymmetric ceramic membranes. The densification and pore structure of the support can be effectively adjusted by control of the quantity of alumina precursors in the composition and the sintering temperature. Sintering the subject mullite compositions at 1500 °C for two hours resulted in support structures with an average porosity of 45.9%, an average pore size of 1.3 µm and a penetrating porosity of 35.9%.     

Effect of mullite phase formed in situ on pore structure and properties of high-purity mullite fibrous ceramics

Porous mullite ceramics are potential advanced thermal insulating materials. Pore structure and purity are the main factors that affect properties of these ceramics. In this study, high performance porous mullite ceramics were prepared via aqueous gel-casting using mullite fibers and kaolin as the raw materials and ρ-Al₂O₃ as the gelling agent. Effects of addition of mullite fibers on the pore structure and properties were examined. The results indicated that mullite phase in situ formed by kaolin, and ρ-Al₂O₃ ensured the purity of mullite samples and mullite fibers bonded together to form a nest-like structure, greatly improving the properties of ceramic samples. In particular, the apparent porosity of mullite samples reached 73.6%. In the presence of 75% of mullite fibers, the thermal conductivity was only 0.289 W/m K at room temperature. Moreover, the mullite samples possessed relatively high cold compressive strength in the range of 4.9–9.6 MPa. Therefore, porous mullite ceramics prepared via aqueous gel-casting could be used for wide applications in thermal insulation materials, attributing to the excellent properties such as high cold compressive strength and low thermal conductivity.     

Controllable preparation of porous ZrB2–SiC ceramics via using KCl space holders

In this work, a novel and facile technique based on using KCl as space holders, along with partial sintering (at 1900 °C for 30 min), was explored to prepare porous ZrB₂–SiC ceramics with controllable pore structure, tunable compressive strength and thermal conductivity. The as-prepared porous ZrB₂–SiC samples possess high porosity of 45–67%, low average pore size of 3–7 μm, high compressive strength of 32–106 MPa, and low room temperature thermal conductivity of 13–34 W m⁻¹ K⁻¹. The porosity, pore structure, compressive strength and thermal conductivity of porous ZrB₂–SiC ceramics can be tuned simply by changing KCl content and its particle size. The effect of porosity and pore structure on the thermal conductivity of as-prepared porous ZrB₂–SiC ceramics was examined and found to be consistent with the classical model for porous materials. The poring mechanism of porous ZrB₂–SiC samples via adding pore-forming agent combined with partial sintering was also preliminary illustrated.     

The preparation and properties of high-strength porous mullite ceramics by a novel non-toxic gelcasting process

A novel approach to fabricate porous mullite ceramics with homogeneous pore size and high-strength using green non-toxic and cost-effective poly-γ-glutamic acid (γ-PGA) gelling system was reported for the first time. Effect of γ-PGA addition, additive amount and solid loading on rheological behavior of the slurries, and microstructure and properties of samples were investigated systematically. By optimizing the solid loading of mullite samples, we are able to get the sample with small pores (< 200 µm) dominating (93.3% of the total pores), and compressive strength of the sample reaches up to 26.62 MPa. In addition, the mullite ceramics exhibited high porosity of 75.7% with low thermal conductivity of 0.279 W/(m·K) at room temperature. This study not only provides a green and non-toxic gelling system but also offers porous mullite ceramics with low thermal conductivity and excellent mechanical strength as an energy-saving thermal insulation material.     

Fabrication and characterization of anorthite–mullite–corundum porous ceramics from construction waste

In this work, anorthite–mullite–corundum porous ceramics were prepared from construction waste and Al₂O₃ powders by adding AlF₃ and MoO₃ as mineralizer and crystallization catalyst, respectively. The effects of the sintering temperature and time on open porosity, mechanical properties, pore size distribution, microstructure, and phase composition were characterized in detail. The results showed that the formation of the mullite whiskers and the properties of the anorthite–mullite–corundum porous ceramics depended more on the sintering temperature than the holding time. By co-adding 12 wt% AlF₃ and 4 wt% MoO₃, mullite whiskers were successfully obtained at sintering temperatures upon 1350 °C for 1 h. Furthermore, the resultant specimens exhibited excellent properties, including open porosity of 66.1±0.7%, biaxial flexural strength of 23.8±0.9 MPa, and average pore size of 1.32 µm (the corresponding cumulative volume percent was 37.29%).     

Investigating the effect of SPRM on mechanical strength and thermal conductivity of highly porous alumina ceramics

For recycling waste refractory materials in metallurgical industry, porous alumina ceramics were prepared via pore forming agent method from α-Al₂O₃ powder and slide plate renewable material. Effects of slide plate renewable material (SPRM) on densification, mechanical strength, thermal conductivity, phase composition and microstructure of the porous alumina ceramics were investigated. The results showed that SPRM effectively affected physical and thermal properties of the porous ceramics. With the increase of SPRM, apparent porosity of the ceramic materials firstly increased and then decreased, which brought an opposite change for the bulk density and thermal conductivity values, whereas the bending strength didn’t decrease obviously. The optimum sample A2 with 50 wt% SPRM introducing sintered at 1500 °C obtained the best properties. The water absorption, apparent porosity, bulk density, bending strength and thermal conductivity of the sample were 31.7%, 62.8%, 1.71 g/cm³, 47.1 ± 3.7 MPa and 1.73 W/m K, respectively. XRD analysis indicated that a small quantity of silicon carbide and graphite in SPRM have been oxidized to SiO₂ during the firing process, resulting in rising the porous microstructures. SEM micrographs illustrated that rod-like mullite grains combined with plate-like corundum grains to endow the samples with high bending strength. This study was intended to confirm the preparation of porous alumina ceramics with high porosity, good mechanical properties and low thermal conductivity by using SPRM as pore forming additive.     

Ultra-low cost porous mullite ceramics with excellent dielectric properties and low thermal conductivity fabricated from kaolin for radome applications

Near-net-shape mullite ceramics with high porosity were prepared from ultra-low cost natural aluminosilicate mineral kaolin as raw material and polystyrene micro-sphere (PS) as pore-forming agent. Microstructure, flexural strength, thermal conductivity and dielectric properties of the ceramics were systematically researched. Results show that the porous mullite ceramics possess fibrous skeleton structure formed by a large quantity of interlocked mullite whiskers, which results in good mechanical properties and low-to-zero sintering shrinkage. Flexural strength of the porous mullite ceramics can be up to 41.01 ± 1.12 MPa, even if the porosity is as high as 62.44%. The dielectric constant and loss tangent of the porous mullite ceramics at room temperature are lower than 2.61 and 5.9 × 10⁻³, respectively. Besides, dielectric constant is very stable with the rising of temperature, and the dielectric loss can be consistently lower than 10⁻² when the temperature is not higher than 800 °C. In addition, thermal conductivity at room temperature is as low as 0.163 W/m/K when the porosity of mullite ceramics is 80.05%. The infiltration of SiO₂ aerogels (SiO₂ AGs) can further decrease the thermal conductivity to 0.075 W/m/K, while has just little effects on the dielectric properties. Excellent mechanical, thermal and dielectric properties show that the porous mullite ceramics have potential applications in radome fields. The porous mullite ceramics prepared from kaolin not only have low cost, but also can achieve near-net-shape.     

Effects of firing temperature on the microstructures and properties of porous mullite ceramics prepared by foam-gelcasting

Porous mullite ceramics were prepared at 1300–1600°C for 2?h via a foam-gelcasting route using industrial-grade mullite powders as the main raw material, Isobam 104 as the dispersing and gelling agent, triethanolamine lauryl sulphate as the foaming agent and sodium carboxymethyl cellulose as the foam stabilising agent. The effects of firing temperature on the sintering behaviour of green samples as well as microstructures and properties of final porous mullite products were investigated. With increasing the temperature from 1300 to 1600°C, linear shrinkage and bulk density values of fired samples increased, whereas their porosity decreased. Mechanical strength and thermal conductivity values of fired samples decreased with increasing their porosities. Even at a porosity level as high as 79.4%, compressive and flexural strengths of fired samples (with average pore size of 314?μm) remained as high as 9.0 and 3.7?MPa, respectively, and their thermal conductivity (at 200°C) remained as low as 0.21?W?(m^?1?K^?1).     

Low sintering shrinkage porous mullite ceramics with high strength and low thermal conductivity via foam-gelcasting

Excessive sintering shrinkage leads to severe deformation and cracking, affecting the microstructure and properties of porous ceramics. Therefore, reducing sintering shrinkage and achieving near-net-size forming is one of the effective ways to prepare high-performance porous ceramics. Herein, low-shrinkage porous mullite ceramics were prepared by foam-gelcasting using kyanite as raw material and aluminum fluoride (AlF₃) as additive, through volume expansion from phase transition and gas generated from the reaction. The effects of AlF₃ content on the shrinkage, porosity, compressive strength, and thermal conductivity of mullite-based porous ceramics were investigated. The results showed that with the increase of content, the sintering shrinkage decreased, the porosity increased, and mullite whiskers were produced. Porous mullite ceramics with 30 wt% AlF₃ content exhibited a whisker structure with the lowest shrinkage of 3.5%, porosity of 85.2%, compressive strength of 3.06 ± 0.51 MPa, and thermal conductivity of 0.23 W/(m·K) at room temperature. The temperature difference between the front and back sides of the sample reached 710°C under high temperature fire resistance test. The low sintering shrinkage preparation process effectively reduces the subsequent processing cost, which is significant for the preparation of high-performance porous ceramics.     

Effects of porosity on electrical and thermal conductivities of porous SiC ceramics

The effects of porosity on the electrical and thermal conductivities of porous SiC ceramics, containing Y₂O₃–AlN additives, were investigated. The porosity of the porous SiC ceramic could be controlled in the range of 28–64 % by adjusting the sacrificial template (polymer microbead) content (0–30 wt%) and sintering temperature (1800–2000 °C). Both electrical and thermal conductivities of the porous SiC ceramics decreased, from 7.7 to 1.7 Ω⁻¹ cm⁻¹ and from 37.9 to 5.8 W/(m·K), respectively, with the increase in porosity from 30 to 63 %. The porous SiC ceramic with a coarser microstructure exhibited higher electrical and thermal conductivities than those of the ceramic with a finer microstructure at the equivalent porosity because of the smaller number of grain boundaries per unit volume. The decoupling of the electrical conductivity from the thermal conductivity was possible to some extent by adjusting the sintering temperature, i.e., microstructure, of the porous SiC ceramic.     

Studies on processing of layered oxide-bonded porous sic ceramic filter materials

Oxide-bonded porous SiC ceramic filter supports were prepared using SiC powder (d₅₀ = 212 µm), Al₂O₃, and clay as bond forming additives and graphite as pore former following reaction bonding of powder compacts at 1400°C in air. Reaction bonding characteristics, phase composition, porosity, pore size, mechanical strength, and microstructure of porous SiC ceramic supports were investigated. Mullite bond phase formation kinetics was studied following the Johnson–Mehl–Avrami–Kolmogorov (JMAK) model using non-isothermal differential thermal analysis (DTA) data. Compared to porous SiC ceramic filter supports having no needle-like mullite bond phase, materials processed by the mullite bonding technique exhibited higher average strength (22.1%) and elastic modulus (5.4%) at a similar porosity level of ~38%, with upper and lower bounds of their strength, modulus, and porosity being 39.1 MPa, 40.2 GPa, and 36.3% and 34.2 MPa, 31.3 GPa, and 33.0%, respectively. Spray coating method was applied for preparation of oxidation-bonded SiC filtration layer having thickness of ~150 µm and pore size of ~5–20 µm over the porous SiC support compacts using aqueous slurry made of fine SiC powder (d₅₀ = 15 µm) followed by sintering. The layered ceramics thus prepared are potential materials for gas filter applications.     

Fibrous porous mullite ceramics modified by mullite whiskers for thermal insulation and sound absorption

In order to meet the demand for thermal insulation and sound absorption, fibrous porous mullite ceramics (FPMC) with high porosity and an interconnected pore structure were prepared, followed by a pore structure modification with in situ grown mullite whiskers on the three-dimensional framework of the FPMC. The resultant hierarchical material exhibited superior sound absorption performance in the low-to-medium frequency to most reported sound-absorbing materials, as well as a sufficient compressive strength of 1.26 MPa with low thermal conductivity of 0.117 W·m^?1·K^?1. Moreover, the effects of solid content and mullite whiskers on the microstructure and physical properties of the material were analyzed. The increase of solid content led to increased compressive strength and thermal conductivity and decreased frequency corresponding to the first sound absorption peak. The thermal conductivity and compressive strength of the material increased as the mullite whiskers grew, while the median pore size decreased.