The effect of oxidation on the mechanical properties and dielectric properties of porous Si3N4 ceramics

The effect of oxidation temperature and time on the microstructures, phase compositions, mechanical properties, and dielectric properties of porous Si₃N₄ ceramics was investigated in the temperature range from 900 °C to 1300 °C for 1 h, 5 h, and 24 h. The weight gain measured either at lower temperature (900 °C) for long time (24 h) or at higher temperature (1300 °C) for 1 h demonstrated that the porous Si₃N₄ ceramics were easily oxidized under the current test conditions. Results showed that the amount of open pores, flexural strength, compressive strength, and dielectric constant all decreased with the increase of oxidation temperature independent upon the oxidation time. The oxidation product SiO₂ was low-temperature quartz in mild condition (low temperature, short time) and cristobalite in severe condition (high temperature, long time). The existence of cracks on the oxide scale was due to the phase transformation of SiO₂ and thermal expansion coefficient mismatch between SiO₂ and Si₃N₄.     

Effect of boron nitride nanosheets addition on the mechanical and dielectric properties of magnesium oxide ceramics

Boron nitride nanosheets (BNNSs)/magnesium oxide (MgO) composites were prepared via hot pressing. Mechanical properties of MgO ceramics were improved obviously in virtue of adding BNNSs. The bending strength of the 1 wt% BNNSs/MgO composite increased by about 85% than that of the monolithic MgO. The fracture toughness increased by 34% with the addition of 1.5 wt% BNNSs. Microstructural analyzes have shown that the toughening mechanisms are combinations of the pull-out and bridging of BNNSs, crack deflection, and crack bypassing mechanisms. The addition of a small amount of BNNSs don't destroy the excellent dielectric properties of composites. The dielectric constant of the sample doped with 1 wt% BNNSs was about 9.5 in the whole X-band and the vast majority of P-band, and the loss tangent was less than 5 × 10⁻³ in 10–15.8 GHz.     

Effect of TiO2 addition on the microstructures,mechanical and dielectric properties of porous Si3N4-based ceramics

Porous Si₃N₄-based ceramics with different TiO₂ contents were prepared by gas pressure sintering method. The effects of TiO₂ addition ranging from 0 to 25?wt-% on the phase compositions, microstructures, mechanical performance and dielectric properties were investigated. The addition of TiO₂ significantly promoted the density which increased from 1.64 to about 2.3?g?cm^?3. The mechanical properties of porous Si₃N₄-based ceramics with TiO₂ addition decreased first and then increased with the increase of TiO₂ content, and the flexural strength and elastic modulus are more than 167.4?MPa and 72.8?GPa, respectively, which were higher than that of the Si₃N₄ ceramic without TiO₂ addition. With the increase of TiO₂ content, both the dielectric constant and dielectric loss increased, and the dielectric constant enhanced obviously. These results suggested that the TiO₂ was beneficial for the improvement of mechanical properties and dielectric constant of porous Si₃N₄-based ceramics.     

Effect of SiO2 content on the microstructure,mechanical and dielectric properties of Si3N4 ceramics

This study investigated the effect of SiO₂ content in the Y₂O₃–Al₂O₃ additive system on the microstructure, mechanical and dielectric properties of silicon nitride (Si₃N₄) ceramics. The total sintering additive content was fixed at 8 wt% and the amount of SiO₂ was varied from 0 to 7 wt%. The crystalline phases of the samples were determined by X-ray diffraction analysis. Complete α-to-β transformation of the Si₃N₄ occurred during sintering of all of the samples, which indicated that the phase transformation was unaffected by the SiO₂ content. However, the microstructures showed that the aspect ratio of the β-Si₃N₄ grains decreased and the residual porosity increased with increasing SiO₂ content. Additionally, the flexural strength and the dielectric constant decreased with increasing SiO₂ content because of the residual porosity and the formation of the Si₂N₂O phase via a reaction of SiO₂ with Si₃N₄.     

Effects of heat treatment on mechanical and dielectric properties of 3D Si3N4f/BN/Si3N4 composites by CVI

In this study, three-dimensional silicon nitride fiber-reinforced silicon nitride matrix (3D Si₃N_4f/BN/Si₃N₄) composites with a boron nitride (BN) interphase were fabricated through chemical vapor infiltration. Through comparing the changes of microstructure, thermal residual stress, interface bonding state, and interface microstructure evolution of composites before and after heat treatment, the evolution of mechanical and dielectric properties of Si₃N_4f/BN/Si₃N₄ composites was analyzed. Flexural strength and fracture toughness of composites acquired the maximum values of 96 ± 5 MPa and 3.8 ± 0.1 MPa·m^1/2, respectively, after heat treatment at 800 °C; however, these values were maintained at 83 ± 6 MPa and 3.1 ± 0.2 MPa·m^1/2 after heat treatment at 1200 °C, respectively. The relatively low mechanical properties are mainly attributed to the strong interface bonding caused by interfacial diffusion of oxygen and subsequent interfacial reaction and generation of turbostratic BN interphase with relatively high fracture energy. Moreover, the Si₃N_4f/BN/Si₃N₄ composites also displayed moderate dielectric constant and dielectric loss fluctuating irregularly around 5.0 and 0.04 before and after heat treatment, respectively. They were mainly determined based on the intrinsic properties of materials system and complex microstructure of composites.     

Preparation,mechanical, dielectric and microwave absorption properties of hierarchical porous SiCnw-Si3N4 composite ceramics

Herein, hierarchical porous SiC_nw-Si₃N₄ composite ceramics with good electromagnetic absorption properties were prepared. A porous Si₃N₄ matrix with different pore structures was first prepared by gelcasting-pressureless sintering (G-PLS) and gelcasting combined with particle stabilized foam-pressureless sintering (G-PSF-PLS). SiC_nw was then introduced by catalytic chemical vapor deposition (CCVD). An increase in solid loading (25–40 vol%) decreased apparent porosity (47.7–41.3%) and improved flexural strength (142.19–240.36 MPa) and fracture toughness (2.25–3.68 MPa·m^1/2). The addition of foam stabilizer propyl gallate (PG, 0.5–1.0 wt%) significantly increased apparent porosity (73.2–86.4%) and realized large-sized spherical pores, reducing flexural strength (58.23–38.56 MPa) and fracture toughness (0.75–0.41 MPa·m^1/2). High apparent porosity and large-sized pores facilitated the introduction of SiC_nw. The 25 vol% sample exhibited a reflection loss of ? 14.67 dB with an effective absorption bandwidth of 3.47 GHz, suggesting a development potential in the electromagnetic wave absorption field.     

Mechanical and dielectric properties of spark plasma sintered Si3N4/SiO2/Eu2O3 composite

In this work, effect of Eu₂O₃ (by 0, 3, 5, and 7 wt%) on mechanical and dielectric properties of Si₃N₄–SiO₂ composites (denoted by E0, E3, E5, E7) was studied. Samples were sintered by spark plasma at 1750 °C - 15 min by 100 °C/min heating rate and 40 MPa pressure under a vacuum atmosphere. The SEM micrographs confirmed the β-Si₃N₄ rod-shaped grains growth. The α to β phase transformation was completed in samples. The E5 and E7 samples have about 180.8 MPa flexural strength due to β-Si₃N₄ rod-shaped grains and increased grain aspect ratio compared to other samples. With the increase of Eu₂O₃ additive, due to an increase in grain size and β phase concentration the average dielectric constant and dielectric loss at 10 GHz frequency growth from 6.6 to 8 and from 0.125 to 0.160, respectively. High hardness values due to the dissolution, diffusion, and precipitation mechanism, and the α phase concentration was developed in these samples.     

Effect of sintering activation energy on Si3N4 composite ceramics

This study investigated the activation energy and kinetic characteristics of silicon nitride (Si₃N₄) composite ceramics produced using different preparation methods. The effects of the linear shrinkage, expansion ratio, and heating rate on the sintering process were analysed in detail. The obtained results reveal that the finer particle size produced using the urea homogeneous precipitation method obviously enhanced the densification rate and reduced the atomic diffusion distance. Moreover, the densification sintering process was carried out efficiently, and the largest densification rate was achieved in advance. According to the Arrhenius curve, the activation energy of the Si₃N₄ composite ceramics calculated using the urea homogeneous precipitation method (310.94 kJ/mol) was lower than that achieved using the mechanical ball-milling method (365.11 kJ/mol). Additionally, the flexural strength and hardness of the Si₃N₄ composite ceramic prepared using the urea homogeneous precipitation method were 740 ± 42 MPa and 16.20 ± 30 GPa, respectively, which is attributed to this composite ceramic's higher diffusion rate and small grain size.     

Effect of BN content on microstructures,mechanical and dielectric properties of porous BN/Si3N4 composite ceramics prepared by gel casting

Porous BN/Si₃N₄ composite ceramics with different BN contents have been fabricated by gel casting. The rheological behaviors of the suspensions, microstructure, mechanical properties, dielectric properties and critical temperature difference of thermal shock (ΔT_C) of porous BN/Si₃N₄ composite ceramics with different BN contents were investigated. With BN contents increasing, the mechanical properties of the porous BN/Si₃N₄ composite ceramics were partially declined, but the dielectric properties and thermal shock resistances were enhanced at the same time. For the porous Si₃N₄ ceramic without BN addition, the porosity, flexural strength, dielectric constant and critical temperature difference were 48.1%, 128 MPa, 4.1 and 395 °C, while for the 10 vol% BN/Si₃N₄ porous composite ceramics, they were 49.4%, 106.6 MPa, 3.8, and 445 °C, respectively. The overall performance of the obtained porous BN/Si₃N₄ composite ceramics indicated that it could be one of the ideal candidates for high-temperature wave-transparent applications.     

Evaluation of cure characteristic,physico-mechanical,and dielectric properties of calcium copper titanate filled acrylonitrile-butadiene rubber composites: Effect of calcium copper titanate loading

Calcium copper titanate (CCTO) has been synthesized by high temperature solid-state reaction from calcium carbonate, copper (II) oxide, and titanium dioxide as the starting materials. The formation and morphology of CCTO were confirmed by X-ray diffraction, Fourier-transformed infrared spectrophotometry, scanning electron microscopy (SEM), and particle size analysis. In order to develop flexible dielectric materials, acrylonitrile-butadiene rubber (NBR)-based composites were prepared with CCTO content varied from 0 to 120 phr (parts per hundred rubber). The cure characteristics of composites were assessed. High-dielectric constant CCTO particles were blended into NBR to make composites with improved dielectric constant. Results showed that the NBR/CCTO composites had a high dielectric constant (10–20) with low dielectric loss (<0.4) and low conductivity (<10⁻³ μS/cm) at frequencies up to 10⁶ Hz. However, the higher CCTO loadings had agglomeration in the NBR matrix, and thus tensile strength and elongation at break sharply deteriorated due to poor rubber-filler interactions. The results showed lower storage modulus E′ and a reduction in T_g with the incorporation of CCTO in NBR matrix. Moreover, improved thermal stability of the NBR/CCTO composites was achieved. SEM was used to observe the dispersion of CCTO particles in NBR matrix.     

Microstructure development in (Co,Ta)-doped SnO2-based ceramics with promising varistor and dielectric properties

Following the $\mathit{3}Sn{\mathit{(}IV\mathit{)}}_{Sn\mathit{(}IV\mathit{)}}^{\times }\leftrightharpoons Co{\mathit{(}II\mathit{)}}_{Sn\mathit{(}IV\mathit{)}}^{\mathrm{″}}+2Ta{\mathit{\left(}V\mathit{\right)}}_{Sn\mathit{(}IV\mathit{)}}^{\cdot }$ charge compensation mechanism we optimized densification and electrical properties of Ta₂O₅-doped SnO₂–CoO ceramics. We show that incorporation of acceptor dopant Co²⁺ in SnO₂ is promoted after the addition of donor dopant like Ta⁵⁺, whereas any surplus of Co would form secondary Co₂SnO₄ phase. A balanced addition of both dopants is needed to promote densification, and any surplus of donor dopants that remain present at the grain boundaries retard the grain growth and deteriorate electrical properties. Varistor and dielectric properties are then strongly influenced by donor doping. Optimum varistor properties (α = 40, U_T = 272 V/mm, I_L = 1.2 μA) were measured for the sample with 1 mol% Ta₂O₅ and the best dielectric properties (ε = 6525; tan(δ) = 0.057@1kHz) were measured for the sample with 0.10 mol% Ta₂O₅ with the largest SnO₂ grain sizes.     

Tuning the dielectric properties of porous BN/Si3N4 composites by controlling porosity

To solve the shortcomings of traditional layered structure for broadband wave-transmitting applications, a novel porosity gradient structure is proposed. The precise turning of the relative permittivity of each layer and their simultaneous shrinkage during sintering are the keys to design and fabrication. Porous BN/Si₃N₄ composites with different porosities were prepared by incorporation of pore former, tape casting and gas pressure sintering. Results show that the obtained composites with different porosities exhibit low and similar shrinkage after sintering at 1900 °C, which is mainly due to the bridging effect between rapidly growing β-Si₃N₄ rod. When the porosity increases from 33.2% to 59.4%, the relative permittivity decreases from 4.00 to 2.38. Moreover, the composites with different porosities have excellent mechanical properties, with bending strength and fracture toughness of 180 ± 10–36 ± 4 MPa and 3.2 ± 0.30–0.85 ± 0.10 MPa·m^?1/2, respectively, which is attributed to the bridging and pull-out strengthening effects of the elongated β-Si₃N₄ grains.     

Vanadium doping effects on microstructure and dielectric properties of barium titanate ceramics

V-doped barium titante ceramics were prepared by conventional solid state reaction method. XRD patterns show that V⁵⁺ ions have entered into the tetragonal perovskite structure of solid solution to substitute for Ti⁴⁺ ions on the B sites. Addition of vanadium accelerates grain growth of BTO ceramics and there is abnormal grain growth of barium titanate ceramics with higher vanadium concentration. Vanadium doping can increase the Curie temperature and decrease the dielectric loss of barium titanate ceramics. As vanadium concentration increases, the remnant polarization of V-doped BTO ceramics begins to increase and reaches the maximum and then decreases. The coercive electric field for V-doped barium titanate ceramics decreases with the increasing of vanadium concentration. As temperature rises, the remnant polarization and the coercive electric field of V-doped barium titanate ceramics decrease simultaneously.     

Microstructure and mechanical properties of Si3N4f/Si3N4 composites with different coatings

The Si₃N₄ coating and Si₃N₄ coating with Si₃N₄ whiskers as reinforcement (Si₃N_4w-Si₃N₄) were prepared by chemical vapor deposition (CVD) on two-dimensional silicon nitride fiber reinforced silicon nitride ceramic matrix composites (2D Si₃N_4f/Si₃N₄ composites). The effects of process parameters of as-prepared coating including the preparation temperature and volume fraction of Si₃N_4w on the microstructure and mechanical properties of the composites were investigated. Compared with Si₃N₄ coating, Si₃N_4w-Si₃N₄ coating shows more significant effect on the strength and toughness of the composites, and both strengthening and toughening mechanism were analyzed.     

Effects of doping Al-metal powder on thermal,mechanical and dielectric properties of AlN ceramics

In this work, the influence of Al-metal powder addition upon that thermal, mechanical and dielectric properties of aluminium nitride (AlN) ceramic was studied. The findings show that adding Al-metal powder improves not only the mechanical and thermal properties of the AlN ceramic but also has no negative impact on its dielectric properties. Based on Y₂O₃ as sintering aid, the AlN ceramic with 1.0 wt% Al doping were 14.35% higher thermal conductivity, 11.73% higher flexural strength and 59.50% higher fracture toughness than those doped without Al, respectively. This study showed that the addition of Al-metal powder may favor the purifying of the AlN lattice and the formation of homogenous and isolated second phase, which would increase the AlN–AlN interfaces and improve the thermal conductivity. Furthermore, the grain boundaries of AlN ceramics might be strengthened by the isolated second phases due to the thermal mismatch between the second phases and AlN grains, thus strengthening and toughening the AlN ceramic doped with Al. However, the large additive amount of Al powder (>1.0 wt%) was not help the isolation and homogenization of the second phase, giving a deterioration in an AlN ceramic's mechanical and thermal properties. These results suggest that the introduction of an appropriate dose of aluminium metal powder is a simple method that can be used to improve the AlN ceramic's mechanical and thermal properties simultaneously.     

Mechanical and dielectric properties of reduced graphene oxide nanosheets/alumina composite ceramics

Reduced graphene oxide (rGO) nanosheets/alumina (Al₂O₃) composite ceramics were fabricated by hot-pressing sintering. The density, porosity, microhardness, flexural strength and complex permittivity were investigated to study their mechanical and dielectric properties. The results revealed that the rGO nanosheets were uniformly distributed in the Al₂O₃ matrix and that the composite ceramics were highly dense at 3.67–3.99 g/cm³. Due to low rGO hardness and elevated porosity, the microhardness exhibits a decreasing trend as the rGO content increases. The flexural strength first increased and then decreased with the escalation of rGO content, and the highest strength of 313.75 MPa was obtained at 3 wt%, increasing by 37.61% relative to that of the hot-pressing sintered Al₂O₃ ceramic. Owing to the enhanced interfacial polarization, dipole polarization, polarization relaxation loss and conductance loss, the real part and imaginary part of complex permittivity increase from 10.40 to 52.73 and from 0.08 to 28.86 as the rGO content rose from 0 wt% to 4 wt%, respectively.     

Microstructure,high-temperature mechanical and dielectric properties of novel Si3N4 f/SiNO wave-transparent composites

Continuous Si₃N₄ fiber reinforced SiNO matrix composites (Si₃N_4 f/SiNO composites) were innovatively prepared for long-time high-temperature resistant wave-transparent materials of hypersonic aircraft. The microstructure, high-temperature mechanical and dielectric properties of Si₃N_4 f/SiNO composites were investigated in detail. The as-fabricated Si₃N_4 f/SiNO composites have homogeneous SiNO matrix distribution for the special winding process, which is beneficial for the mechanical strength and wave-transparent properties. The average tensile strength and flexural strength at room temperature is 87.8 MPa and 171.2 MPa respectively, which suggests Si₃N_4 f/SiNO composites have excellent mechanical strength. The tensile strength value decreases to 54.6 MPa after heat-treated at 1000 ℃ for the surface reactions between the SiNO matrix and Si₃N₄ fibers. After heat-treated at 1550 ℃, the composites have the tensile strength value of 24.2 MPa for the high strength retention rate of Si₃N₄ fibers at this temperature. Si₃N_4 f/SiNO composites have excellent room temperature dielectric properties and excellent dielectric stability in different frequency bands (7–18 GHz). The dielectric constant values vary from 3.69 to 3.75 while the dielectric loss attains the order of 10^?3. The dielectric constants and dielectric loss of Si₃N_4 f/SiNO composites are relatively stable from RT to 800 ℃. The as-fabricated Si₃N_4 f/SiNO composites that have excellent high temperature resistance and dielectric properties are the ideal high temperature wave-transparent composites.     

Effects of boron content on the microstructures and mechanical properties of reactive hot-pressed BxC-TiB2-SiC composites

B_xC-TiB₂-SiC ceramic composites were fabricated via reactive hot pressing using TiC, B, and Si as the raw materials. The phase transition process was studied by heating powder mixtures to different temperatures in combination with X-ray diffraction analysis. The stoichiometric ratio between B and C in boron carbide is variable. A series of powder mixtures containing excess boron (0 wt%, 10 wt%, 20 wt%, or 30 wt% B) were sintered, and the microstructures and mechanical properties of the composites were investigated. The results showed that the B_6.1C-TiB₂-SiC composite prepared from the starting powders with 30 wt% excess boron had the best comprehensive mechanical properties, with a relative density, hardness, bending strength, and fracture toughness of 98.32%, 33.2 GPa, 840 MPa, and 5.22 MPa m^1/2, respectively. Excessive boron substitution may cause lattice distortion in boron carbide, and the boron carbide grains in this state may form a large number of twins under the compressive stress generated by the TiB₂ grains, which will affect the properties of the composites.     

Effect of ball milling treatment on the microstructures and properties of Cr2AlC powders and hot pressed bulk ceramics

Ball milling was used on synthesized Cr₂AlC powders, and dense Cr₂AlC bulk ceramics with almost pure phase were fabricated by hot pressing these ball milled Cr₂AlC powders at 1300 °C for 2 h under 30 MPa. The phase compositions and the microstructures of powders and bulk ceramics were characterized. The mechanical properties and dislocation analysis of bulk ceramics were also investigated. Our results indicated that the grain size of powders became uniform and smaller after ball milling, which was also inherited in the bulk ceramics. Moreover, the mechanical properties of hot pressed Cr₂AlC ceramics, including flexural strength, fracture toughness, and Vickers hardness, significantly increased by using ball milled powders treated at speed 200 rpm. The organization of hexagonal dislocation networks during hot pressing and reduction of grain size both had a positive effect on improving mechanical properties.     

Microstructure and dielectric properties of Ag-BaTiO3 composite ceramics

Di-phase composite ceramics based on BaTiO₃ with 5?vol% of Ag filler have been prepared by sintering the mixture of powders at temperatures above the silver melting point (1000?°C–1300?°C/2?h). As predicted by finite element calculations, the addition of metallic particles should produce a field concentration in some regions of the BaTiO₃ matrix and therefore, an enhanced dielectric response with respect to pure BaTiO₃. The role of oxygen vacancies on the dielectric relaxation mechanisms of Ag-BaTiO₃ composites has been investigated. The sintering temperature of 1200?°C provided optimized ceramics with excellent dielectric properties, i.e. with low losses (tanδ?<?3%) and room temperature permittivity measured at 50?kHz exceeding 6500 (and above 13,000 at the Curie temperature), as result of a good densification (94% relative density) and a synergy effect of the metallic particles inclusions and ceramic grain size in the range of ≈1?μm, where BaTiO₃ has a well-known maximum of its permittivity.