粉煤灰泡沫玻璃的性能研究

以粉煤灰和废平板玻璃为基础原料,以发泡剂、助熔剂、稳泡剂为辅助原料,用粉末烧结法制备了泡沫玻璃。通过对样品有关性能的检测,分析了影响泡沫玻璃质量的工艺因素。     

双氧水发泡法制备泡沫陶瓷外墙保温板

本文以粉煤灰和铜尾矿为主要原料,掺加膨润土和赤泥,以长石为助熔剂,双氧水为发泡剂,聚乙烯醇为稳泡剂,采用浆料发泡烧结法制备泡沫陶瓷外墙保温板.确定了适宜的原料组成为粉煤灰40％％铜尾矿38％％长石10％％膨润土10％％赤泥2％％双氧水的加入量为5％％所制备的泡沫陶瓷的性能为:吸水率0.90％％体积密度1.10g/cm3、显气孔率为0.70％％抗压强度为8MPa、导热系数为0.15 W/m·k.     

浆料发泡烧结法制备泡沫陶瓷外墙保温板

本文以粉煤灰和铜尾矿为主要原料,掺加膨润土和赤泥,以长石为助熔剂,松香皂为发泡剂,聚乙烯醇为稳泡剂,采用浆料发泡烧结法制备泡沫陶瓷外墙保温板。确定了适宜的原料组成为粉煤灰40％、铜尾矿38％、长石10％、膨润土10％、赤泥2％;用松香皂发泡后泡沫引入量为15％时具有较好的综合性能。所制备的泡沫陶瓷的性能为：吸水率0．95％、体积密度1．00g／cm3、显气孔率为0．61％、抗压强度为7MPa、导热系数为0．1W／m·K。     

以废平板玻璃为原料研制泡沫玻璃

以废平板玻璃制备泡沫玻璃,不仅能节约原料,还能变废为宝,达到资源的综合利用。本实验以废平板玻璃为基料,碳黑为发泡剂,添加适量助熔剂和稳泡剂,采用粉体烧结,高温发泡工艺研制出了泡沫玻璃。研究表明:当废玻璃用量达到75.7%,碳黑加入9.80%,加入适量的助熔剂和稳泡剂,预热升温速度为5℃/min,快速升温速度为10℃/min,发泡温度为800℃,发泡时间为30min,可得到较为理想的泡沫玻璃。     

粉煤灰泡沫玻璃的试验研究

以粉煤灰和玻璃粉为主要原料,添加适量的发泡剂、稳泡剂等助剂,可制得粉煤灰泡沫玻璃。通过对制品体积密度、表观密度、开口孔孔隙率、吸水率等性能的测定,分析了发泡剂、粉煤灰掺量对泡沫玻璃性能的影响。实验表明,适量添加粉煤灰和玻璃粉,可制得性能较好的粉煤灰泡沫玻璃。     

稳泡剂对粉煤灰泡沫玻璃性能影响研究

以粉煤灰和玻璃粉为主要原料,分别以二氧化钛、氧化铁、磷酸三钠、磷酸三钾、硼酸为稳泡剂制备泡沫玻璃,并对制品的力学性能、表观密度、孔隙率、孔径分布、平均孔径、导热系数进行了测定,研究探讨了稳泡剂种类及掺量对粉煤灰泡沫玻璃物理性能的影响。实验结果表明,磷酸三钠为稳泡剂时,材料的表观密度最低可达0.212 g/cm~3,导热系数的最低可达0.0499 W/(m·K),孔径大小适中,分布均匀,是制备粉煤灰泡沫玻璃较为合适的稳泡剂。     

低密度泡沫玻璃的制备及其微观结构研究

泡沫玻璃是以废玻璃为主要原料,以发泡剂、助溶剂和促进剂等为添加剂,经过细碎、粉磨而形成配合料,再经过低温预热、高温熔融、发泡、稳泡、退火等工序形成的内部充满连通或封闭气孔的无机非金属材料。笔者选用(绿色)废瓶罐玻璃为主要原料,以纯碳和CaCO_3为发泡剂,Na_2CO_3、(NaPO_3)_6为添加剂,采用粉末烧结法制备了低密度泡沫玻璃。实验结果表明:以纯碳和CaCO_3为发泡剂,且碳酸钙掺量3.0%,纯碳掺量0.4%,发泡温度840℃,保温时间70min时,制备的泡沫玻璃密度为240kg/m~3左右,样品内部孔径大小均匀一致,孔壁厚度也较薄。     

粉煤灰泡沫玻璃工艺性能的研究

以粉煤灰和废玻璃为主要原料，添加适量发泡剂、助熔剂等制备粉煤灰泡沫玻璃。讨论分析了成型压力和退火制度等工艺过程对泡沫玻璃性能的影响。     

利用煤粉炉渣制备微晶泡沫玻璃的研究

以煤粉炉渣为主要原料,以碳酸钙作为发泡剂,磷酸钠作为稳泡剂,再加入其他辅助原料制备了微晶泡沫玻璃,研究了碳酸钙和磷酸钠的掺入量、发泡温度、保温时间对微晶泡沫玻璃性能的影响,并且采用XRD分析其物相组成,结果表明,当发泡剂和稳泡剂的掺量分别为4.5%和5%,发泡温度为1000℃,发泡时间为20min时,试样已经完全转化为微晶泡沫玻璃,主晶相为硅灰石,次晶相为钙长石和辉石,平均泡径达2.03mm,表观密度为938 kg/m3,气孔率达52.6%,抗压强度达17.95MPa,抗弯强度达12.51 Mpa,热膨胀系数达5.67×10-6/℃,导热系数达0.20 W/(m.K)。     

烧结时间对高钛高炉渣-粉煤灰微晶泡沫玻璃的影响

以高钛高炉渣、粉煤灰和废玻璃粉为主要原料,硼砂为助熔剂,碳酸钙为发泡剂,十二水磷酸钠为稳泡剂,通过烧结法制备了微晶泡沫玻璃.研究了烧结时间对微晶泡沫玻璃析出相、微观形貌、体积密度、抗压强度、吸水率及热导率的影响.结果表明,在900℃下,烧结时间变化对析出相影响不显著,主要为透辉石Ca(Mg,Al)(Si,Al)2O6,富铝普通辉石Ca(Mg,Fe,Al)(Si,Al)2 O6以及普通辉石Ca(Mg,Fe)Si2 O6.随烧结时间从0 min延长至30 min,材料孔径大小变得越来越均匀,抗压强度、体积密度、热导率先升高后降低,吸水率逐渐降低;烧结时间在30～60 min时材料孔径大小不均匀,抗压强度下降,体积密度、热导率逐渐升高,吸水率先升高后降低.综合而言,当烧结时间为30 min时,微晶泡沫玻璃具备最优综合性能.     

Orthophosphates and Diphosphates Containing Zinc and Copper and Zinc and Cobalt

Solid solutions of diphosphates of zinc and copper and of zinc and cobalt were synthesized from mixtures of pure diphosphates at temperatures up to 1000°C. Their X-ray diffractometry patterns varied continuously from one end member to the other. Solid solutions of orthophosphates of composition Zn_3−xCox(PO₄)2, with x = 0.4–1.6, were formed at temperatures up to 950°C; all exhibited the structure of γ-Zn₃(PO₄)2. Solid solutions of orthophosphates of composition Zn_3−xCu_x(PO₄)2 exhibited more-complex behavior. At 1000°C and copper contents of 20–80 mol%, a phase that is related to Cu₃(PO₄)2, termed here the "ε-phase," predominated. At 850°–950°C and in the region from 20 mol% to ∼33 mol% of copper, the solid solutions (the "η-phase") adopted the structure of graftonite. At 800°–900°C and 10–15 mol% of copper, the solid solutions exhibited a new structure (the "δ-phase"), which we found to be related to the mineral sarcopside. At temperatures 950°C, the solutions that contained 5–15 mol% of copper (the "β-phase") had the structure of β-Zn₃(PO₄)2, whereas at 800°–850°C, solutions with 5 mol% of copper (the "-phase") exhibited the structure of γ-Zn₃(PO₄)2. Attempts to synthesize Cu⁺ZnPO₄ and Cu⁺Cu²⁺Zn₃(PO₄)3 were unsuccessful.     

油气储运系统中油气的回收及腐蚀与防护问题

油气储运系统已经与保障国家经济的发展息息相关,介绍了油气储运系统中油气回收问题及腐蚀与防护问题,并提出了相应的解决措施。     

油气集输处理工艺及工艺流程

为了提高油田的生产效率,设计最佳的油气集输处理的工艺流程,更好地完成油气水分离处理的任务。对油气集输工艺技术进行优化,发挥高效油气水分离处理设备的优势,提高油气水处理的质量,保证油气集输工艺顺利实施,获得最佳的油田产量外输。     

Gemini型表面活性剂结构性能与应用

Gemini型表面活性剂的结构和性质与传统的表面活性剂有很大的不同,例如Gemini型表面活性剂可以视为两个普通表面活性剂在亲水基或者靠近亲水基处由连接基团通过化学键连接而成;Gemini表面活性剂的C20值和cmc值都比传统表面活性剂的值要低很多。着重介绍了Gemini型表面活性剂的特性,结构与表面活性的关系以及应用。     

科技创新与钢铁科技进步

建设创新型国家是我们中华民族的历史责任。“自主创新、重点突破、支撑发展、引领未来”的16字方针应当成为我们未来创新活动的指南。建设创新型国家把自主创新放在首位,并提出了引领未来的高标准要求。钢铁科技创新必须突出重点,抓住创新成果产业化这个关键,支撑起行业和国民经济的发展。     

油气管道及储运设施安全保障技术发展现状及展望

相比已经完善丰富的开采和勘探技术,油气的运输以及储存却仍然存在不足之处。我国对能源安全提出更加严格要求的同时,对区域经济的发展规划也有足够重视。因此,保障油气管道的安全则成为了我国能源安全战略的重中之重。在阐释油气管道现阶段在储运安全保障技术发展状况的基础上,分析了现存的问题及解决问题的手段,并指出未来可能使用的目标策略,为今后研究者提供一定程度上的借鉴经验。     

石油与天然气地质与勘探开发措施

石油天然气的地质勘探开发目的是为了获得最佳的油气产能而进行的地质研究工作。石油天然气地质勘探工作具有非常重要的意义,通过地质勘探获得有价值的地层信息资料,对储层油气的显示进行评价和分析,确定具有工业开采价值,才能投入开发生产,为油田创造最佳的经济效益。     

膜的污染和劣化及其防治对策

较为系统地介绍了膜污染和劣化的定义和特点,因膜污染和劣化而造成的膜性能变化,以及如何预防、减少或清除膜污染和劣化的一些通用方法。     

国内外天然橡胶产销分析及趋势预测

2009年,对中国橡胶行业来说,机遇和挑战并存。国际金融危机、全球经济增长放缓、国际市场需求持续走弱,产品出口大幅度下降,国内市场压力增大等各种不利因素的挑战日益尖锐。然而国家大规模投资,实施积极的财政政策和适度宽松的货币政策,并出台十大产业调整振兴规划,都给橡胶工业带来发展机遇。 目前,2009年时间已过半,在经历过最冷的“寒冬”后,国内外橡胶业现况如何、天然胶和合成胶的市场走势如何,成为上下游企业关注的热点。 从本期开始,本刊推出《金融危机下的世界橡胶市场》专题,从天然橡胶产销、贸易概况和主要合成橡胶产品（丁苯、乙丙、氯丁、丁腈、丁基、异戊等）的市场分析及前景两个角度,对国内外橡胶业的现况和发展进行分析及预测,供业内人士参考。