Comparative study of EMI shielding effectiveness for carbon fiber pultruded polypropylene/poly(lactic acid)/multiwall CNT composites prepared by injection molding versus screw extrusion

The electrical conductivity and electromagnetic interference (EMI) shielding effectiveness of the composites of polypropylene/poly(lactic acid) (PP/PLA) (70/30, wt %) with single filler of multiwall carbon nanotube (CNT) or hybrid fillers of nickel‐coated carbon fiber (CF) and CNT were investigated. For the single filler composite, higher electrical conductivity was observed when the PP‐g‐maleic anhydride was added as a compatibilizer between the PP and PLA. For the composite of the PP/PLA (70/30)/CF (20 phr)/CNT (5 phr), the composite prepared by injection molding observed a higher EMI shielding effectiveness of 50.5 dB than the composite prepared by screw extrusion (32.3 dB), demonstrating an EMI shielding effectiveness increase of 49.8%. The higher values in EMI shielding effectiveness and electrical conductivity of the PP/PLA/CF (20 phr)/CNT (5 phr) composite seemed mainly because of the increased CF length when the composites were prepared using injection molding machine, compared with the composites prepared by screw extrusion. This result suggests that the fiber length of the conductive filler is an important factor in obtaining higher values of electrical conductivity and EMI shielding effectiveness of the PP/PLA/CF/CNT composites. © 2017 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2017 , 134, 45222.     

Effects of hybrid fillers on the electrical conductivity,EMI shielding effectiveness,and flame retardancy of PBT and PolyASA composites with carbon fiber and MWCNT

The effects of hybrid fillers of carbon fiber (CF) and multiwall carbon nanotube (MWCNT) on the electrical conductivity, electromagnetic interference shielding effectiveness (EMI SE), flame retardancy, and mechanical properties of poly(butylene terephthalate) (PBT)/poly(acrylonitrile-co-styrene-co-acrylate) (PolyASA) (70/30, wt %) with conductive filler composites were investigated. The CF was used as the main filler, and MWCNT was used as the secondary filler to investigate the hybrid filler effect. For the PBT/PolyASA/CF (8 vol %)/MWCNT (2 vol %) composite, a higher electrical conductivity (1.4 × 10⁰ S cm⁻¹) and EMI SE (33.7 dB) were observed than that of the composite prepared with the single filler of CF (10 vol %), which were 9.0 × 10⁻² S cm⁻¹ and 23.7 dB, respectively. This increase in the electrical properties might be due to the longer CF length and hybrid filler effect in the composites. From the results of aging test at 85 °C, 120 h, the electrical conductivity and EMI SE of the composites decreased slightly compared to that of the composite without aging. The results of electrical conductivity, EMI SE, and flame retardancy suggested that the composite with the hybrid fillers of CF and MWCNT showed a synergetic effect in the PBT/PolyASA/CF (8 vol %)/MWCNT (2 vol %) composite. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019 , 136, 48162.     

High electromagnetic interference shielding with high electrical conductivity through selective dispersion of multiwall carbon nanotube in poly (ε‐caprolactone)/MWCNT composites

This study presents the preparation of electrically conducting poly(ε‐caprolactone) (PCL)/multiwall carbon nanotube (MWCNT) composites with very low percolation threshold (p_c). The method involves solution blending of PCL and MWCNT in the presence of commercial PCL beads. The PCL beads were added into high viscous PCL/MWCNT mixture during evaporation of solvent. Here, the used commercial PCL polymer beads act as an ‘excluded volume’ in the solution blended PCL/MWCNT region. Thus, the effective concentration of the MWCNT dramatically increases in the solution blended region and a strong interconnected continuous conductive network path of CNT−CNT is assumed throughout the matrix phase with the addition of PCL bead which plays a crucial role to improve the electromagnetic interference shielding effectiveness (EMI SE) and electrical conductivity at very low MWCNT loading. Thus, high EMI SE value (∼23.8 dB) was achieved at low MWCNT loading (1.8 wt %) in the presence of 70 wt % PCL bead and the high electrical conductivity of ∼2.49×10⁻² S cm⁻¹ was achieved at very low MWCNT loading (∼0.15 wt %) with 70 wt % PCL bead content in the composites. The electrical conductivity gradually increased with increasing the PCL bead concentration, as well as, MWCNT loading in the composites. © 2015 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015 , 132, 42161.     

Graphene nanoplate and multiwall carbon nanotube–embedded polycarbonate hybrid composites: High electromagnetic interference shielding with low percolation threshold

This study has reported the preparation of polycarbonate (PC)/graphene nanoplate (GNP)/multiwall carbon nanotube (MWCNT) hybrid composite by simple melt mixing method of PC with GNP and MWCNT at 330°C above the processing temperature of the PC (processing temperature is 280°C) followed by compression molding. Through optimizing the ratio of (GNP/MWCNT) in the composites, high electromagnetic interference shielding effectiveness (EMI SE) value (∼21.6 dB) was achieved at low (4 wt%) loading of (GNP/MWCNT) and electrical conductivity of ≈6.84 × 10⁻⁵ S.cm⁻¹ was achieved at 0.3 wt% (GNP/MWCNT) loading with low percolation threshold (≈0.072 wt%). The high temperature melt mixing of PC with nanofillers lowers the melt viscosity of the PC that has helped for better dispersion of the GNPs and MWCNTs in the PC matrix and plays a key factor for achieving high EMI shielding value and high electrical conductivity with low percolation threshold than ever reported in PC/MWCNT or PC/graphene composites. With this method, the formation of continuous conducting interconnected GNP‐CNT‐GNP or CNT‐GNP‐CNT network structure in the matrix polymer and strong π–π interaction between the electron rich phenyl rings and oxygen atom of PC chain, GNP, and MWCNT could be possible throughout the composites. POLYM. COMPOS., 37:2058–2069, 2016. © 2015 Society of Plastics Engineers     

Electrical and thermal conductivity and tensile and flexural properties: Comparison of carbon black/polycarbonate and carbon nanotube/polycarbonate resins

Adding conductive carbon fillers to thermoplastic polymers increases the resulting composite's electrical conductivity. Carbon black (CB) is very effective at increasing composite electrical conductivity at low loading levels. In this study, varying amounts (2 to 10 wt %) CB were added to polycarbonate (PC) and the resulting composites were tested for electrical conductivity (1/electrical resistivity), thermal conductivity, and tensile and flexural properties. These results were compared with prior work done for carbon nanotubes (CNT) in polycarbonate. The percolation threshold was ～ 2.3 vol % CB compared to between 0.7 and 1.4 vol % CNT. At 8 wt % filler, the CNT/PC composite had an electrical resistivity of 8 ohm‐cm compared to 122 ohm‐cm for the CB/PC composite. The addition of CB to polycarbonate increased the composite electrical and thermal conductivity and tensile and flexural modulus. The 8 wt % (5.5 vol %) CB in polycarbonate composite had a good combination of properties for semiconductive applications. Ductile tensile behavior is noted in pure polycarbonate and in samples containing up to 8 wt % CB. © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2011     

Electrical,rheological and electromagnetic interference shielding properties of thermoplastic polyurethane/carbon nanotube composites

Electrically conducting rubbery composites based on thermoplastic polyurethane (TPU) and carbon nanotubes (CNTs) were prepared through melt blending using a torque rheometer equipped with a mixing chamber. The electrical conductivity, morphology, rheological properties and electromagnetic interference shielding effectiveness (EMI SE) of the TPU/CNT composites were evaluated and also compared with those of carbon black (CB)‐filled TPU composites prepared under the same processing conditions. For both polymer systems, the insulator–conductor transition was very sharp and the electrical percolation threshold at room temperature was at CNT and CB contents of about 1.0 and 1.7 wt%, respectively. The EMI SE over the X‐band frequency range (8–12 GHz) for TPU/CNT and TPU/CB composites was investigated as a function of filler content. EMI SE and electrical conductivity increased with increasing amount of conductive filler, due to the formation of conductive pathways in the TPU matrix. TPU/CNT composites displayed higher electrical conductivity and EMI SE than TPU/CB composites with similar conductive filler content. EMI SE values found for TPU/CNT and TPU/CB composites containing 10 and 15 wt% conductive fillers, respectively, were in the range ?22 to ?20 dB, indicating that these composites are promising candidates for shielding applications. © 2013 Society of Chemical Industry     

Hybrid composites of ABS with carbonaceous fillers for electromagnetic shielding applications

This work evaluates the influence of two types of carbonaceous fillers, carbon black (CB) and carbon nanotubes (CNTs), on the electrical, electromagnetic, and rheological properties of composites based on poly(acrylonitrile‐co‐butadiene‐co‐styrene) (ABS) prepared by the melt mixing. Electrical conductivity, electromagnetic shielding efficiency (EMI SE) in the X‐band frequency range (8–12.4 GHz), and melt flow index (MFI) results showed that ABS/CNT composites exhibit higher electrical conductivity and EMI SE, but lower MFI when compared to ABS/CB composites. The electrical conductivity of the binary composites showed an increase of around 16 orders of magnitude, when compared to neat ABS, for both fillers. Binary composites with 5 and 15 wt % of filler showed an EMI SE of, respectively, ?44 and ?83 dB for ABS/CNT, and ?9 and ?34 dB for ABS/CB. MFI for binary composites with 5 wt % were 15.45 and 0.55 g/10 min for CB and CNT, respectively. Hybrid composites ABS/CNT.CB with 3 wt % total filler and fraction 50:50 and 75:25 showed good correlation between EMI SE and MFI. © 2018 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2018 , 135, 46546.     

Electrical conductivity modeling of carbon black/polycarbonate,carbon nanotube/polycarbonate,and exfoliated graphite nanoplatelet/polycarbonate composites

Adding conductive carbon fillers to electrically insulating thermoplastic polymers increases the resulting composite's electrical conductivity, which would enable them to be used in electrostatic dissipative and semiconductive applications. In this study, varying amounts of carbon black (CB: 2 to 10 wt %), multiwalled carbon nanotubes (CNT: 0.5 to 8 wt %), or exfoliated graphite nanoplatelets (GNP: 2 to 15 wt %) were added to polycarbonate (PC) and the resulting composites were tested for electrical conductivity (EC = 1/electrical resistivity). The percolation threshold was ～ 1.2 vol % CNT, ～ 2.4 vol % CB, and ～ 4.6 vol % GNP. In addition, three EC models (Mamunya, additive, and general effective media) were developed for the CB/PC, CNT/PC, and GNP/PC composites. The general effective media (GEM) model showed the best agreement with the experimental results over the entire range of filler concentrations (above and below the percolation threshold) for all three composite systems. In addition, the GEM model can be easily adapted for composites containing combinations of different conductive fillers. © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2012     

CNT基木塑复合材料的力学性能、电磁屏蔽性能

采用碳纤维(CF)和碳纳米管(CNT)通过模压工艺制备出具有电磁屏蔽功能的丙烯酸酯木塑复合材料。借助材料试验机、动态热机械分析仪、微欧计和电磁屏蔽测量仪等详细研究CNT质量分数对丙烯酸酯木塑复合材料弯曲性能、动态力学性能、电阻率和电磁屏蔽效能的影响。结果表明,添加质量分数为2%的CNT,使得复合材料的弯曲强度和弯曲弹性模量分别增加了10%和16%。复合材料的储能模量也在CNT质量分数为2%时达到最大值,之后储能模量随着CNT的增加而逐渐下降,损耗因子在CNT质量分数多于2%时也逐渐增加。复合材料的吸水率和导电性能随着CNT含量的增加而增加。同时复合材料的电磁屏蔽效能也随着CNT含量增加而递增。在30~1 500 MHz范围内,电磁屏蔽效能从27 d B增加到40 d B。结果证明,当CNT质量分数在2%时,丙烯酸酯木塑复合材料具有较佳的力学性能和较好的电磁屏蔽效能(30 d B),能满足商业要求。     

Electrical and thermal conductivity and tensile and flexural properties of carbon nanotube/polycarbonate resins

Adding conductive carbon fillers to insulating thermoplastic polymers increases the resulting composite's electrical conductivity. Carbon nanotubes (CNTs) are very effective at increasing composite electrical conductivity at low loading levels without compromising composite tensile and flexural properties. In this study, varying amounts (2–8 wt %) of CNTs were added to polycarbonate (PC) by melt compounding, and the resulting composites were tested for electrical conductivity (1/electrical resistivity), thermal conductivity, and tensile and flexural properties. The percolation threshold was less than 1.4 vol % CNT, likely because of CNTs high aspect ratio (1000). The addition of CNT to PC increased the composite electrical and thermal conductivity and tensile and flexural modulus. The 6 wt % (4.2 vol %) CNT in PC resin had a good combination of properties for electrical conductivity applications. The electrical resistivity and thermal conductivity were 18 Ω‐cm and 0.28 W/m · K, respectively. The tensile modulus, ultimate tensile strength (UTS), and strain at UTS were 2.7 GPa, 56 MPa, and 2.8%, respectively. The flexural modulus, ultimate flexural strength, and strain at ultimate flexural strength were 3.6 GPa, 125 MPa, and 5.5%, respectively. Ductile tensile behavior is noted in pure PC and in samples containing up to 6 wt % CNT. © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2010     

Electrical conductivity and EMI shielding effectiveness of polyurethane foam–conductive filler composites

The morphological, electrical, and thermal properties of polyurethane foam (PUF)/single conductive filler composites and PUF/hybrid conductive filler composites were investigated. For the PUF/single conductive filler composites, the PUF/nickel‐coated carbon fiber (NCCF) composite showed higher electrical conductivity and electromagnetic interference shielding effectiveness (EMI SE) than did the PUF/multiwall carbon nanotube (MWCNT) and PUF/graphite composites; therefore, NCCF is the most effective filler among those tested in this study. For the PUF/hybrid conductive fillers PUF/NCCF (3.0 php)/MWCNT (3.0 php) composites, the values of electrical conductivity and EMI SE were determined to be 0.171 S/cm and 24.7 dB (decibel), respectively, which were the highest among the fillers investigated in this study. NCCF and MWCNT were the most effective primary and secondary fillers, and they had a synergistic effect on the electrical conductivity and EMI SE of the PUF/NCCF/MWCNT composites. From the results of thermal conductivity and cell size of the PUF/conductive filler composites, it is suggested that a reduction in cell size lowers the thermal conductivity of the PUF/conductive filler composites. © 2016 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2017 , 134, 44373.     

Tensile modulus modeling of carbon black/polycarbonate,carbon nanotube/polycarbonate,and exfoliated graphite nanoplatelet/polycarbonate composites

Conductive fillers are often added to thermoplastic polymers to increase the resulting composite's electrical conductivity (EC) which would enable them to be used in electrostatic dissipative and semiconductive applications. The resulting composite also exhibits increased tensile modulus. The filler aspect ratio plays an important role in modeling composite EC, and tensile modulus. It is difficult to measure the filler aspect ratio after the manufacturing process (often extrusion followed by injection molding) in the composite, especially when nanomaterials are used. The EC percolation threshold is a function of the filler aspect ratio; hence, knowledge of this percolation threshold provides a means to extract the filler aspect ratio. In this study, the percolation threshold of the composite was determined from EC measurements and modeling, which in turn was used to determine the filler aspect ratio for tensile modulus modeling. Per the authors' knowledge, this approach has not been previously reported in the open literature. The fillers; carbon black (CB: 2–10 wt %), multiwalled carbon nanotubes (CNT: 0.5–8 wt %), or exfoliated graphite nanoplatelets (GNP: 2–12 wt %); were added to polycarbonate (PC) and the resulting composites were tested for EC and tensile modulus. With the filler aspect ratio determined from EC values for CNT/PC and GNP/PC composites, the three‐dimensional randomly oriented fiber Halpin‐Tsai model accurately estimates the tensile modulus for the CNT/PC composites and the Nielsen model predicts the tensile modulus well for the CB/PC and GNP/PC composites. © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2012     

Comparative study of electromagnetic interference shielding properties of injection molded versus compression molded multi-walled carbon nanotube/polystyrene composites

This study compares electromagnetic interference (EMI) shielding properties of injection molded versus compression molded multi-walled carbon nanotube/polystyrene (MWCNT/PS) composites, i.e., properties such as EMI shielding effectiveness (EMI SE), electrical conductivity, real permittivity and imaginary permittivity. The injection molded (MWCNT-aligned) samples showed lower EMI shielding properties than compression molded (randomly distributed MWCNT) samples that was attributed to lower probability of MWCNTs contacting each other due to MWCNT alignment. The compression molded samples showed higher electrical conductivity and lower electrical percolation threshold than the injection molded samples. The compression molded samples at MWCNT concentrations of 5.00 and 20.0 wt.% showed real permittivity two times and imaginary permittivity five times greater than the injection molded samples. The EMI SE for the compression molded samples at MWCNT concentrations of 5.00 and 20.0 wt.% was 15.0 and 30.0 dB, respectively, significantly greater than EMI SE for the injection molded samples. Lower EMI SE for the injection molded samples was ascribed to lower electrical conductivity, real permittivity (polarization loss) and imaginary permittivity (Ohmic loss). Comparison of the EMI shielding properties of the compression molded versus injection molded samples confirmed that EMI shielding does not require filler connectivity; however it increases with filler connectivity.     

Synergistic effects of carbon nanotubes and exfoliated graphite nanoplatelets for electromagnetic interference shielding and soundproofing

Polypropylene/carbon nanotube/exfoliated graphite nanoplatelet (PP/CNT/xGnP) composites have been fabricated to evaluate their electromagnetic interference shielding effectiveness (EMI SE) and soundproofing. An EMI SE of 36.5 dB at 1250 MHz was measured for the 80/10/10 wt % PP/CNT/xGnP composite; its sound transmission loss was more than 5 dB higher than that for pure PP at low frequencies (520–640 Hz). These results indicate simultaneous EMI SE and soundproofing. Transmission electron microscopy was used to study the microstructure and to probe synergetic effects between the CNTs and xGnPs. © 2013 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 130: 3947–3951, 2013     

Synthesis of carbon nanotube/epoxy composite films with a high nanotube loading by a mixed-curing-agent assisted layer-by-layer method and their electrical conductivity

A mixed-curing-agent assisted layer-by-layer method is reported to synthesize carbon nanotube (CNT)/epoxy composite films with a high CNT loading from ∼15 to ∼36 wt.%. The mixed-curing-agent consists of two types of agents, one of which is responsible for the partial initial curing at room temperature to avoid agglomeration of the CNTs, and the other for complete curing of epoxy resin at high temperature to synthesize epoxy composite films with good CNT dispersion. The electrical conductivity of the composites shows a value up to ∼12 S/m, which is much higher than that for CNT/epoxy composites with a low CNT loading prepared using conventional methods.     

Substantially improving mechanical property of double percolated poly(phenylene sulfide)/poly(arylenesulfide sulfone)/graphene nanoplates composites with superior electromagnetic interference shielding performance

The electrical conductivity and electromagnetic interference (EMI) shielding effectiveness (SE) can be conspicuously enhanced at low conductive filler contents with the formation of segregated structure in the conductive polymer composites (CPCs). Nevertheless, poor interface adhesion of segregated composites results in poor mechanical properties due to the selective distribution of conductive fillers. In this work, a flexible approach was applied to fabricate the poly(phenylene sulfide)/poly(arylene sulfide sulfone)/graphene nanoplates (GNPs) composite with a unique double percolated structure. This composite exhibits an outstanding EMI SE of 38.8 dB with only 3 wt % GNPs, which is comparable to that of the conventional segregated structure counterpart. What is more, the tensile strength and Young's modulus of double percolated composites with 3 wt % GNPs are remarkably improved by ~892 and ~274% compared to conventional segregated structure, achieving 37.7 and 1788.3 MPa, respectively. This work provides a valuable method for producing CPCs with high EMI shielding performances and outstanding mechanical properties. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019 , 137, 48709.     

Flexible poly(styrene-b-(ethylene-co-butylene)-b-styrene) nanocomposites for electromagnetic interference shielding

In this report, multiwalled carbon nanotubes (CNT) embedded poly(styrene-b-(ethylene-co-butylene)-b-styrene) (SEBS) microspheres (CNT/SEBS) were prepared by solvent evaporation method. Reduced graphene oxide (rGO) nanosheets were used to cover the surface of CNT/SEBS microspheres. The CNT/SEBS/rGO nanocomposites with special segregated conductive network were fabricated by hot pressing these as-prepared complex microspheres. The morphology, electrical percolation threshold, electrical conductivity, and electromagnetic interference (EMI) shielding effectiveness (SE) of CNT/SEBS/rGO composites were characterized. The shielding mechanisms were discussed in detail. Analysis of electrical conductive performance shows that the electrical percolation threshold of rGO is 0.22 vol %. Results of EMI shielding test confirmed the synergistic effect between CNT and rGO. The EMI SE of the composite filled by 2.1 vol % CNT and 3.35 vol % rGO can achieve 26 dB in 8.2− 12.4 GHz (X band), which exceeds the basic requirement for commercial application (20 dB). Its reflectance coefficient (19–41%) indicates that the most part of incident electromagnetic (EM) wave energy is attenuated through absorption mechanism. This kind of absorptive EMI shielding material can be applied without serious secondary EM radiation pollution problems. The effects of filler content, molding temperature on EMI SE, and shielding mechanism were also investigated. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2020 , 137, 48542.     

Highly filled multilayer thermoplastic/graphene conducting composite structures with high strength and thermal stability for electromagnetic interference shielding applications

Polyvinyl chloride (PVC)/graphene and poly(methyl methacrylate) (PMMA)/graphene nanocomposites were made by solution casting technique with graphene weight fractions of 1, 5, 10, 15, and 20%. Multilayer structures of the composites were made by hot compression technique to study their electromagnetic interference shielding effectiveness (EMI SE). Tensile strength, hardness, and storage modulus of the nanocomposites were studied in relation with graphene weight fraction. There has been a substantial increase in the electrical conductivity and EMI SE of the composites with 15–20% filler loading. Differential thermal analysis of the composites shows improved thermal stability with an increase in graphene loading. PMMA/graphene composites have better thermal stability, whereas PVC/graphene composites have superior mechanical properties. About 2 mm thick multilayer structures of PMMA/graphene and PVC/graphene composites show a maximum EMI SE of 21 dB and 31 dB, respectively, in the X band at 20 wt % graphene loading. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019 , 136, 47792.     

Electrical, morphological and rheological properties of carbon nanotube composites with polyethylene and poly(phenylene sulfide) by melt mixing

Electrical, morphological and rheological properties of polyethylene (PE)/multi-walled carbon nanotube (MWCNT) and poly(phenylene sulfide) (PPS)/MWCNT composites were studied with the MWCNT content using vector network analyzer, scanning electron microscopy and rotational rheometry. From the results of electrical conductivity and electromagnetic interference shielding efficiency (EMI SE) of the PE/MWCNT and PPS/MWCNT composites, the electrical percolation threshold of the composites has found to be 5 and 3 wt% MWCNT, respectively. From the results of the EMI SE of the composites, it was suggested that the increase in homogeneous dispersion of the MWCNT in the PPS matrix has been attributed to the increase in connectivity of the MWCNT-MWCNT network structure of the composite. Therefore, the higher values of the EMI SE with the MWCNT content were observed in the PPS/MWCNT than the PE/MWCNT composites. From the results of the rheological properties of the PE/MWCNT and PPS/MWCNT composites, the increase in the complex viscosity was observed for the PPS/MWCNT than the PE/MWCNT composites. The increase in complex viscosity maybe due to the increase in homogeneous dispersion of the MWCNT in the PPS matrix than that in the PE matrix. From the results of the rheological properties of the PE/MWCNT and PPS/MWCNT composites, it was suggested that the homogeneous dispersion of the MWCNT in the polymer matrix has affected the increase in complex viscosity of the PPS/MWCNT composite. This result of rheological behavior is consistent with the results of the EMI SE of the PE/MWCNT and PPS/MWCNT composites.     

Shielding effectiveness of carbon‐filled polycarbonate composites

In this project, varying amounts of three different carbons [carbon black (CB), carbon nanotubes (CNT), and graphene nanoplatelets (GNP)] were added to polycarbonate (PC). The resulting single filler composites were tested for shielding effectiveness (SE). The effects of single fillers and combinations of two different carbon fillers were studied via a factorial design. At the highest single filler loadings, the following SE results were obtained at 800 MHz: 18.9 dB for 10 wt % CB/PC, 18.4 dB for 8 wt % CNT/PC, and 6.3 dB for 15 wt % GNP/PC. The highest SE value of 21.4 dB was measured for the 5 wt % CB/5 wt % CNT/PC composite and could be used in SE applications (typically > 20 dB is needed). Statistically significant equations were developed that could be used to predict the SE of composites containing these fillers. In addition, it was determined that the composite SE is higher than what would be expected from the additive effect of each single filler for the CB/GNP/PC composites. © 2015 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015 , 132, 42719.