聚丙烯/凹凸棒土复合材料的结晶行为

通过双螺杆挤出机熔融共混制备了聚丙烯(PP)/凹凸棒土(ATP)复合材料样品,分别采用偏光显微镜和差示扫描量热仪对其结晶行为进行了研究。研究表明,复合材料样品的偏光显微镜照片呈现球晶所特有的十字消光现象,球晶尺寸与纯PP球晶的尺寸相比有所减小。非等温结晶测试结果表明,复合材料样品的结晶温度随着ATP含量的增加向高温方向移动,而且半结晶期缩短,PP/ATP复合材料的总体结晶速率增加;ATP的加入改变了PP成核的机制,起到了异相成核的作用。随着降温速率的增大,PP及PP/ATP(95/5)复合材料的结晶起始温度和结晶峰值温度均向低温方向移动,半结晶期变短。     

聚丙烯/木粉/纳米凹凸棒土复合材料性能研究

采用双螺杆挤出机制备了一系列聚丙烯(PP)/木粉/纳米凹凸棒土(AT)木塑复合材料(WPC.研究了AT用量对复合材料力学性能、热性能、加工性能的影响.结果表明,随着AT用量的增加,复合材料拉伸强度逐渐增加、冲击强度逐渐减小,硬度先增加后减小,AT用量为5份时复合材料硬度最大;复合材料维卡软化点不断提高;熔体流动速率(M...     

聚丙烯/凹凸棒土纳米复合材料力学性能的研究

利用超声波分散方法将凹凸棒土分散在水中，采用硅烷偶联剂KH—570对凹凸棒土纳米棒品进行表面处理将经表面处理的凹凸棒土与聚丙烯复合制成纳米复合材料；研究了纳米复合材料的结品行为与力学性能。结果表明超声波有利于凹凸棒土的分散；凹凸棒土质量分数较低时，复合材料的力学性能有一定程度的提高。     

聚丙烯/凹凸棒土复合材料的制备与性能研究

以聚丙烯(PP)为基体,凹凸棒土(AT)为无机粒子填充剂,通过熔融共混的方法制备PP/AT复合材料,探讨了AT对PP/AT复合材料的热行为、机械性能及流动性能的影响.结果表明:AT能起到一定增强的效果,当AT的含量为2 wt.%时,PP/AT复合材料的抗拉强度可达到35.5MPa,但其冲击强度随AT含量的增加而呈现阶梯...     

硅烷偶联剂改性凹凸棒土对PVC/ABS合金性能影响

研究了经硅烷偶联剂(KH550)湿法和干法改性后的凹凸棒土对聚氯乙烯(PVC)/丙烯腈-丁二烯-苯乙烯共聚物(ABS)合金力学性能及维卡软化温度的影响,利用SEM观察了合金的冲击断面微观形貌和凹凸棒土的分散情况.结果表明:经KH550干法改性后的凹凸棒土对合金力学性能的影响要好于湿法改性和未改性的;经KH550湿法改性处理的凹凸棒土对合金维卡软化温度有较大的提高,当凹凸棒土添加量为70份时维卡软化温度可以达到99.3℃.     

PP/凹凸棒土纳米复合材料的制备与性能研究

采用超声波分散方法将凹凸棒土在甲苯中进行分散，然后采用硅烷偶联剂KH—570对凹凸棒土纳米棒晶进行表面处理，将经表面处理的凹凸棒土与聚丙烯复合制备纳米复合材料，研究了纳米复合材料的晶体结构与性能。结果表明，当凹凸棒土含量为10％时，复合材料的拉伸强度达最大值；而冲击强度在凹凸棒土含量为2％时出现峰值。凹凸棒土的加入并没有改变聚丙烯的晶型，复合材料的加工性能在一定程度上得到改善。     

液体石蜡与凹凸棒土对聚丙烯力学性能影响的研究

以液体石蜡与凹凸棒土加入到聚丙烯并对力学性能的影响进行研究。将凹土与液体石蜡和聚丙烯在高速混合机中进行混合,再在挤出机中熔融挤出,注塑成型,研究液体石蜡与凹凸棒土对聚丙烯力学性能的影响。研究结果表明：液体石蜡和经硅烷偶联剂处理过的凹土能比较显著的提高PP的综合力学性能,当PP的用量为100份,凹土的用量为20份,LP为10份时拉伸强度及硬度性能最好。此时,拉伸强度为34.63 MPa,硬度为63.30。当PP的用量为100份,凹土的用量为20份,LP为20份时冲击强度最好,为11.11 kJ/m^2。     

甲基乙烯基硅橡胶/凹凸棒土复合材料的紫外老化性能

以硅烷偶联剂KH 570改性凹凸棒土(AT),制备了甲基乙烯基硅橡胶(MVQ)/AT复合材料,考察了紫外辐射对MVQ/AT复合材料物理机械性能及热性能的影响,并通过扫描电子显微镜表征了复合材料的微观形貌。结果表明,随着辐照时间的延长,MVQ/AT复合材料的邵尔A硬度和拉伸强度先增大后减小,扯断伸长率先减小后增加,热稳定性先提高后下降;MVQ/AT复合材料经紫外辐照后,表面颜色加深并出现裂纹,随着辐照时间的延长,裂纹数量逐渐增加,表面变得粗糙,并且有部分填料暴露在材料表面。     

偶联剂对凹凸棒土/三元乙丙橡胶复合材料性能的影响

研究偶联剂品种和用量对凹凸棒土（AT）/三元乙丙橡胶（EPDM）复合材料性能的影响。结果表明：与未用偶联剂改性的AT/EPDM复合材料相比,偶联剂改性的AT/EPDM复合材料物理性能明显提高;采用偶联剂Si69改性的AT/EPDM复合材料物理性能最好;偶联剂Si69用量为1份时,AT用量为50份的AT/EPDM复合材料物理性能较好。     

凹凸棒土对PVC/ABS复合材料性能的影响

主要研究了经表面处理和未经表面处理的凹凸棒土对PVC/ABS复合材料力学性能及维卡软化温度的影响,用SEM观察了PVC/ABS复合材料的冲击断面微观形貌和凹凸棒土的分散情况。结果表明:经偶联剂改性后的凹凸棒土对复合材料力学性能的影响要好于未改性的凹凸棒土;未经处理的凹凸棒土对复合材料维卡软化温度有较大的提高。     

不同硅烷偶联剂在聚丙烯/KD膨胀型阻燃剂复合体系中的作用研究

考察了硅烷偶联剂(KH-SSO,KH-560)在聚丙烯( PP) /KD膨胀型阻燃剂(KDIFR)复合体系中的偶联作用。X射线衍射研究表明,KDIFR可促进PP形成R晶,KH-550增强KDIFR粒子的R成核作用,而KH-560则降低这种作用。扫描电镜分析表明硅烷偶联剂的加人使粒子与基体间的薪结作用增强。偏光显微镜分析表明,随着硅烷偶联剂的增加,球晶的大小趋于一致,KDIFR的分散趋于均匀。KH-550和KH-560的加人均可提高复合体系的力学性能,PP/KDIFR/KH-560 = 70 /30 /5(质量份数,下同)复合体系综合性能最佳,冲击强度和拉伸强度比PP/KDIFR分别提高了24.2%和9.6%。阻燃性能的测试结果表明硅烷偶联剂的加人可提高材料的阻燃性。     

偶联剂对玻纤增强PP复合材料力学性能的影响

选取5种不同型号的偶联剂,采用湿法改性对玻纤表面进行处理,制备聚丙烯/玻纤(PP/GF)复合材料。通过PP/GF的界面行为表征,分析了不同偶联剂对PP/GF复合材料的影响规律。结果表明:GF经偶联剂改性的PP/GF复合材料与未改性的相比,材料力学性能得到大幅度提高。其中以偶联剂KH560改性效果最理想,拉伸强度达到59.14 MPa,压缩强度为70.69 MPa,冲击强度为10.14 kJ/m2。     

不同硅烷偶联剂对电子布性能影响

电子布的化学处理离不开硅烷偶联剂的作用,分析了电子布常用3种硅烷偶联剂的特性,并分析了其对电子布以及半固化片性能的影响。同时呼吁行业内不断改进偶联剂Z-032、Z-132的性能,使其能更好的满足电子布及半固化片的需要。     

Influence of Reactice Processing on the Properties of PP/Glass Fiber Composites Compatibilized with Silane

Summary: Composites of PP reinforced with 20 wt.‐% of short glass fibers were prepared by extrusion using VTES as a coupling agent. The addition of VTES was performed via in‐situ functionalization of PP and by a two‐step process in which PP was functionalized before the composite preparation. The obtained samples were characterized using rheometry, mechanical tests and microscopy. Both processes allowed the fiber/matrix interaction to increase. It was found that the VTES content affected the viscosity of the system by means of three different mechanisms: reduction of β‐scission reactions, decrease of fiber sliding and plasticizing effect on the matrix. Whereas the first two mechanisms increased the viscosity of the final composite after unreacted VTES removal, the third one reduced the viscosity during the process and contributed to fiber‐length preservation. The effects of VTES and peroxide contents on the Young's modulus were closely related to their effects on the final fiber length, indicating the effectiveness of using VTES as a coupling agent. Comparison between in‐situ functionalization and the two‐step process with prefunctionalization showed that in‐situ functionalization led to a lower degree of chain breakage, even when it was performed in the presence of peroxide.

Scanning electron micrographs of PP/glass fiber composite prepared without coupling agent.     

硅烷偶联剂对白炭黑胶料性能的影响

研究硅烷偶联剂Si75和NXT对白炭黑胶料性能的影响。结果表明,与偶联剂Si75胶料相比,偶联剂NXT胶料的门尼粘度较低,硫化时间较长,定伸应力和拉伸强度较小,拉断伸长率较大,动态性能差别不大。     

硅烷偶联剂在玻纤增强复合材料领域中的应用

介绍了玻纤生产中常用硅烷偶联剂的种类、结构、偶联机理及使用方法。着重介绍了硅烷偶联剂在玻纤增强复合材料中的应用,特别是硅烷结构类型、用量对复合材料性能的影响。同时,对硅烷偶联剂的作用及其在玻纤增强热固性和热塑性树脂中的应用进行了阐述。     

硅烷偶联剂预处理PANI对水性涂料性能的影响

借助不同硅烷偶联剂[苯胺甲基三乙氧基硅烷(ND-42)、3-氨丙基三乙氧基硅烷(KH-550)、3-(2,3-环氧丙氧)丙基三甲氧基硅烷(KH-560)和3-甲基丙烯酰氧基丙基三甲氧基硅烷(KH-570)]预处理聚苯胺(PANI),制备出具有不同分散性的PANI。红外测试表明,偶联剂成功掺杂到PANI上;粒径分析表明,预处理后的PANI粒径增加;采用自制分散测试装置进行沉降体积测试,结果表明,经ND-42处理的PANI单位质量沉降体积(0.3m L/g)比未经偶联剂处理的PANI下降83.3%。将PANI加入水性环氧涂料中制成涂层后进行机械性能测试,结果表明,涂层附着力、硬度和耐冲击性均有不同程度的提升。其中,添加ND-42改性PANI的涂层,其腐蚀电位为-0.484 V,相对于未经偶联剂处理的PANI涂层右移0.131 V,腐蚀电流密度下降55.0%,盐雾实验120 h后无明显生锈现象。     

不同偶联剂改性RM对PVCW/RM复合材料性能的影响

分别采用A0800、NDZ102、DL411三种不同偶联剂对赤泥(RM)进行改性,并以之为填料、聚氯乙烯废弃物(PVCW)为基体,通过熔融共混制备了PVCW/RM复合材料。研究了各种偶联剂及其改性RM用量对复合材料力学性能的影响,同时考察了由不同偶联剂改性RM所得PVCW/RM复合材料的微观形貌及尺寸稳定性。结果表明:三种偶联剂中,A0800对RM的改性效果最好,当A0800偶联剂用量为RM质量的1.5%,且由其改性的RM(A0800-RM)用量为PVCW/RM复合材料质量的15%时,复合材料的力学性能达到最佳;当偶联剂用量均为1.5%时,由不同偶联剂改性RM得到的PVCW/RM复合材料,其冷收缩率和与热膨胀率均小于由未改性RM填充得到的复合材料。     

硅烷偶联剂对HDPE/木粉复合材料性能的影响

使用经硅烷偶联剂HP-172和HP-174改性的木粉制备了HDPE/木粉复合材料,研究了偶联剂用量对其性能的影响。实验结果表明:当使用1.5%的HP-172处理木粉后,可使复合材料的各项力学性能提高30%以上;HP-174的用量为1%~1.5%也得到了较好的改性效果。通过FIR和SEM分析发现,硅烷偶联剂可与木粉表面发生化学反应,从而提高了HDPE与木粉的界面粘合强度,使复合材料的力学性能得以提高     

偶联剂对聚乳酸/蔗渣纤维复合材料力学性能的影响

采用了4种硅烷偶联剂处理甘蔗渣,研究了偶联剂品种和含量对聚乳酸/甘蔗渣复合材料力学性能的影响,并运用扫描电子显微镜对复合材料的冲击断面进行了观察。结果表明,甘蔗渣经过硅烷偶联剂表面处理后,聚乳酸/甘蔗渣复合材料的力学性能较未处理体系有不同程度的提升,其中Z-6032的处理效果最佳。聚乳酸/甘蔗渣复合材料的力学强度受甘蔗渣粒径和含量的影响;甘蔗渣的粒径越小,复合材料的冲击强度越大;随着甘蔗渣含量的增大,复合材料的冲击强度和拉伸强度均呈下降趋势。