熔盐法合成红色荧光粉CaWO_4∶Eu~(3+)及其发光性能的研究

采用熔盐法在800℃条件下合成了红色荧光粉CaWO4:Eu3+。通过多种手段对样品进行了表征,并与固相法样品进行了对比。XRD结果表明所合成的荧光粉衍射峰位置和标准卡77-2233一致,为单一四方晶系的白钨矿结构;SEM结果表明荧光粉形貌规则,粒度分布均匀,分散性较好;光谱结果显示荧光粉的发射主峰位于614 nm处,激发主峰位于393 nm处,为近紫外激发,色坐标为(0.661,0.343),且色纯度与商品粉相当。由于CaWO4∶Eu3+用熔盐法合成具有工艺简单、能耗低、周期短等特点,合成样品粉体形貌好、粒度分布均匀、结晶度高,样品质量不低于固相法样品,因此,该方法值得研究者关注。     

共沉淀法制备白光LED用CaMO_4:Eu~(3+),Bi~(3+)(M=Mo,W)红色荧光粉及其发光性能的研究

采用共沉淀法制备了Ca_(0.93-x)(Mo_(0.9)W_(0.1))O_4∶Eu_(0.07)~(3+),Bi_x~(3+)(0≤x≤0.05)系列样品,通过XRD、SEM及荧光光谱仪对粉体的晶体结构、形貌及荧光性能进行测试和表征。结果表明,Bi~(3+)、Eu~(3+)及WO_4~(2-)的掺杂没有改变CaMoO_4原有的四方晶系体心结构,且样品粒径分布较均匀,无明显团聚现象。随着Bi~(3+)的掺杂,Ca_(0.93-x)(Mo_(0.9)W_(0.1))O_4∶Eu_(0.07)~(3+),Bi_x~(3+)样品的激发光谱带边会发生红移,且激发强度呈现先增强后减弱的趋势,其发射光谱也具有相应的规律,Bi~(3+)的最佳掺杂浓度为x=0.02 mol,在395 nm激发下,样品的发光强度提升至134%;较之商用红色荧光粉Y_2O_2S∶Eu~(3+),Ca_(0.91)(Mo_(0.9)W_(0.1))O_4∶Eu_(0.07)~(3+),Bi_(0.02)~(3+)样品显现出更好的色纯度和发光强度,适合于近紫外LED用红色荧光粉。     

白光LED用氮化物荧光粉的研究现状及发展趋势

对白光LED(发光二极管)用氮化物荧光粉目前的研究状况、存在问题及发展趋势进行了分析和论述。重点介绍了M2Si5N8∶Eu(M=Ca,Sr,Ba)氮化物荧光粉,展望了新型氮化物荧光粉的应用前景,并指出开发新型氮化物荧光粉的关键在于高纯金属Eu、Ca、Sr等原料的制备及氮化物粉的合成这两个方面。     

红色荧光粉NaBaPO_4:Eu~(3+)的制备及其性能研究

采用高温固相法制备单一六方晶系红色荧光粉NaBaPO4:Eu3+。利用XRD、SEM和荧光光谱等对NaBaPO4:Eu3+粉末的理化特性进行表征,考察了激活剂Eu3+的浓度和助熔剂NH4F用量对粉末的晶体结构和发光性能的影响。结果表明:激活剂Eu3+最大掺入量为20%,助熔剂NH4F的最大掺入量为10%,采用该配比合成得到的荧光粉NaBa0.8PO4具有最好的发光性能。在最强激发波长的近紫外光(≈393nm)激发下,样品发射强的红光(≈613nm)和橙光(≈591nm)。     

白光LED用LaPO4:Eu3+红色荧光粉的合成与表征

利用水热法制备了性能稳定的红色荧光粉LaPO4:Eu3+,同时研究了不同的Eu3+浓度、煅烧温度对荧光粉发光性能的影响.通过X射线粉末衍射(XRD)和扫描电子显微镜(SEM)来表征荧光粉的晶体结构和颗粒大小及形貌;用激发光谱和发射光谱以及荧光衰减曲线来表征荧光粉的荧光性能.结果表明:未煅烧时前躯体主要是六方晶相LaPO4·0.5H2O,煅烧温度在900℃时,所制备样品为单斜相LaPO4:Eu3+;SEM图像显示5 at.%Eu3+掺杂LaPO4呈椭球形,颗粒长约为500 nm,宽约为300 nm.最大发射波长和激发波长分别为592 nm和393 nm,发射光谱中592 nm和612 nm的发射峰对应的是Eu3+离子的5D0→7F1和5D0→7F2跃迁.其荧光寿命为3.32 ms.     

绿色荧光粉Na_(1-x)Li_xCaPO_4:0.02Eu~(2+)的制备及其性能的研究

采用高温固相反应法制备了稀土掺杂荧光粉NaCa0.98PO4:Eu2+0.02,在波长360nm激发光激发下,荧光粉发射波长在500nm左右的绿光。采用Li+为掺杂离子取代基质晶格中的Na+位,通过杂质离子掺杂量对发光性能影响的研究,获得Li+的最佳掺杂量为5mol%。在波长为360mm近紫外光激发下,Na0.95Li0.05Ca0.98PO4:0.02Eu2+的发射强度是NaCa0.98PO4:Eu0.022+的2.5倍,该荧光粉为适用于近紫外激发的白光LED的绿色荧光粉。     

白光LED用YAG：Ce^3＋荧光粉的研究进展

介绍了近年来自光YAG：Ce^3＋荧光粉发光特性和合成方法,并展望该领域的发展前景及今后的研究趋势。     

助熔剂对LiGd(W_(0.4)Mo_(0.6)O_4)_2:Eu~(3+)红色荧光粉性能的影响

采用高温固相法制备了LiGd(W_(0.4)Mo_(0.6)O_4)_2:Eu~(3+)白光LED用红色荧光粉。通过扫描电子显微镜、X射线衍射仪、荧光光谱仪考察了不同助熔剂对荧光粉的形貌、结构、光学性能的影响,探讨了不同助熔剂的作用机理。结果表明,不同种类助熔剂未改变LiGd(W_(0.4)Mo_(0.6)O_4)_2的四方晶系白钨矿结构;396nm激发下,添加质量分数为2%的H_3BO_3,LiF或NH_4F使样品的发光强度分别提高了21%,17%,9.6%;而添加2%的Na_2CO_3样品发光强度下降了10.9%。同时,H_3BO_3可有效地减少样品颗粒的团聚,其最佳用量为3%;由于F-声子能量低,可减少能量的无辐射跃迁概率的原因,当以1%H_3BO_3与2%LiF同时作为助熔剂制备荧光粉时,相比未添加助熔剂的样品发光强度提高40%。     

高亮度白光LED用YAG∶Ce~(3+)荧光粉的研制

根据蓝光芯片的发光特性,从激活剂、助熔剂、基质Y3+的替代物等方面较系统地研究了YAG∶Ce3+荧光粉的制备。最终的荧光粉产品制成5mm封装20mA蓝光激发的白光LED后,光效可达70 lm/W,显色指数≥80。     

F~-掺杂对红色荧光粉NaGd(WMo)O_(8-x/2)F_x:Eu~(3+)的结构和发光特性的影响

采用高温固相法合成了NaGd(WMo)O_(8-x/2)F_x:Eu~(3+)(x=0、0.1、0.2、0.3、0.4、0.5)系列红色荧光粉。分别采用X射线衍射、荧光光谱测试手段对所得粉末的晶型及其发光性能进行了表征分析。结果表明,该系列红色荧光粉均为白钨矿四方晶系结构,空间点群结构为I41/a(88),可被近紫外光395 nm有效激发,其最强发射峰位于616 nm处,属于Eu~(3+)的~5D_0→~7F_2电偶极跃迁。F-离子掺杂量为0.2 mol时发光强度最强,与未掺杂F-相比其发光强度提高了41%,其色坐标为(0.653,0.336)。由此可见,NaGd(WMo)O_(7.9)F_(0.2):Eu~(3+)是一种具有潜在应用价值的白光LED红色荧光粉。     

高亮度白光LED用YAG:Ce3+荧光粉的研制

根据蓝光芯片的发光特性,从激活剂、助熔剂、基质Y3+的替代物等方面较系统地研究了YAG:Ce3+荧光粉的制备.最终的荧光粉产品制成φ5mm封装20mA蓝光激发的白光LED后,光效可达70lm/W,显色指数≥80.     

Luminescence Properties of Green-Emitting Phosphor (Ba1-x,Srx)2SiO4:Eu2+ for White LEDS

The (Ba1-xSrx)2SiO4∶Eu2 green-emitting phosphors were synthesized by conventional solid-state reaction in a CO-reductive atmosphere, and their luminescent properties were investigated. The XRD data show that the Ba/Sr ratio not only affects the lattice parameters, but also influences the emission peak. The excitation spectra indicate that this phosphor can be effectively excited by UV light from 370 to 470 nm. The emission band is due to the 4f65d1→4f7 transition of the Eu2 ion. With an increase in x, the emission band shifts to longer wavelength and the reason was discussed. The emission spectra exhibit a satisfactory green performance under different excitation wavelength(380, 398, 412, 420, 460 nm). (Ba1-xSrx)2SiO4∶Eu2 is a promising phosphor for green white-lighting-emission diode by ultraviolet chip.     

熔盐电解法制备Al-Sc应用合金的工艺研究

研究了熔盐电解法生产Al-Sc合金的工艺参数对合金中Sc含量的影响.结果表明.合金中Sc的含量随电解温度的升高呈先升后降的趋势,最佳电解温度为960℃;随冰晶石分子比的增大,Sc含量逐渐下降;采用工业电流密度(J=1 A·cm-2)电解90 min,合金中的Sc含量高达0.8%左右;为保证电解过程稳定并降低能耗,电流强度应为2-4 A,极距应为3 cm.     

Characterization of (Y,Gd) BxV1-xO4-x:Eu Phosphor Prepared by Coprecipitation Reaction

White body-color (Y, Gd)BxV1- xO4-x :Eu3 phosphors were prepared by coprecipitation reaction. Under VUV excitation at 147 nm, the red emission colorimetric purity of (Y, Gd)BxV1- xO4-x :Eu3 phosphor is much better than that of commercial PDP (plasma display panels) phosphor (Y, Gd)BO3:Eu3 . But its relative emission intensity is only about 90% of the commercial phosphor.     

熔盐电解制备金属钒

以氧化物为原料,采用熔盐电解的方法,制备了金属钒。研究了电解温度、电解电压、电解时间和阳极面积等参数对电解电流的影响规律。用扫描电镜、微区分析和X-射线表征了未完全还原及完全还原的试样的形貌、结构和组成。在850～900℃温度范围、2.9～3.0 V电压范围实验室规模上电解获得了金属钒。该方法具有温度低、流程短、设备简单,适合小规模化生产的优点。     

熔盐电解法制备镨钕铈合金的研究

利用500A规模电解槽,在氟化锂-氟化镨钕-氟化铈熔盐体系中,以氧化铈与氧化镨钕混合物为电解原料,制备了不同金属配分的镨钕铈合金。研究了不同电解质组成、电解温度(980～1 060℃)以及加料速度对电解过程的影响。研究表明,电解质组成是控制合金中金属配分的关键因素,同时电解温度对金属配分的影响不大。但电解温度偏低或者加料速度偏慢会使电解质液面上升,导致"熔盐外溢"现象的发生。     

熔盐电解法制备硼粉的研究

研究了在KCl-KBF4体系和KCl-KBF4-B2O3体系中熔盐电解法制备硼粉的工艺条件。对KCl-KBF4体系采用正交试验法研究了熔盐配比、温度、阴极电流密度和电解时间对硼粉纯度及电流效率的影响,得到的最佳实验条件为:KCl∶KBF4为5∶1,温度750℃,阴极电流密度1.5A.cm-2,电解时间3h。该条件下能得到纯度95%以上的球形非晶态硼粉,电流效率可达到80%以上。KCl-KBF4-B2O3体系熔盐电解得到超细球形硼粉,但电流效率低,产品难以收集,杂质含量较高。     

熔盐电解法制备高纯铟

以还原ITO废料得到的铟锡合金为原料,氯化铟和氯化锌的混合盐为电解质,采用熔盐电解法经过两次电解,可以制备出纯度达到4N5的高纯铟,相对于湿法电解工艺,产率提高至少2倍,且工艺过程不产生废水。     

Luminescence and Preparation of LED Phosphor Ca8Mg(SiO4)4Cl2:Eu2+

Calcium magnesium chlorosilicate doped by europium, Ca8Mg(SiO4)4Cl2:Eu2 , was prepared by the solid state reaction at high temperature. The compound obtained is pure Ca8Mg(SiO4)4Cl2 phase with cubic structure. Its average particle size is 5 μm, and it has good dispersity and morphological form. The excitation spectrum of Ca8Mg(SiO4)4Cl2:Eu2 is a wide band, which covers from 270 to 480 nm. The emission spectrum is also a wide band peaked at 510 nm. The luminescent intensity reaches to the maximum when the concentration of Eu2 is 2%. The wavelength of emission and excitation of the phosphor with various Eu2 contents keeps constant. This spectrum range matches violet and blue LED chips very well, and its strong luminescence intensity is suitable for a green phosphor of tricolor phosphor of white light LED.     

熔盐电解制备稀土铝合金的研究

铝中加入一定量的稀土金属后,铝合金的导电性、机械强度、耐腐蚀性和耐热性等方面都有明显的提高。稀土金属在铝合金中具有净化、细化和合金化效果。稀土铝合金因有上述的特点,而广泛地应用在电工铝的生产上。研究稀土铝合金的制取方法对稀土铝合金的广泛应用具有积极的推动作用。本实验使用熔盐电解法制备了稀土铝合金。