热等静压处理技术在燃机叶片上的应用

为减少叶片内部显微疏松等冶金缺陷,提高铸件合格率,将热等静压处理技术应用于某高温合金大尺寸精铸导向叶片。研究表明,热等静压处理对某高温合金导向叶片内部显微疏松具有明显闭合效果,疏松体积分数较大部位的闭合程度达80%。建立了热等静压处理过程中显微疏松闭合机制模型。热等静压处理合金高温力学性能高于技术指标要求。热等静压处理导向叶片通过某燃机600h试车考核。     

热等静压处理对铸造高温合金涡轮叶片的影响

为解决铸造高温合金涡轮叶片由于工艺固有特性而在内部产生的疏松、气孔及残余共晶等冶金缺陷的问题,采用标准热处理和热等静压处理(HIP)+标准热处理两种工艺对铸造涡轮叶片及其同炉试样进行试验,并对试样进行了差热分析、密度测试、力学性能测试及X射线三维成像,对比分析不同工艺的处理效果。结果表明：相比标准热处理,热等静压处理+标准热处理试样的屈服强度上升3%,抗拉强度上升1.4%,延伸率和断面收缩率分别上升28.1%和51.5%,持久寿命上升16.6%,内部显微疏松和气孔等缺陷的闭合程度达99.8%;铸造涡轮叶片增加热等静压处理可有效闭合铸件内部疏松,提高合金致密度、力学性能,进而提高铸件合格率。     

重型燃机叶片熔模精密铸造陶瓷型芯开发

文章介绍了一种重型燃机叶片用硅基陶瓷型芯制备方法,测试了型芯显气孔率、吸水率、体积密度、抗弯强度和热变形性能。结果表明,制备的硅基陶瓷型芯显气孔率为32%~36%,吸水率为21%~24%,体积密度为1.48~1.56 g/cm3,室温强度为15~25 MPa,1 450℃高温强度为18~26 MPa,热变形量小于0.3 mm,满足燃机叶片精密铸造要求。     

差速器壳体铸造工艺设计及改进

主要介绍工程机械差速器壳体铸件的工艺改进过程。此零件由于结构复杂,零件本身存在较多热节处,零件材料又是球墨铸铁,所以出现缩松的倾向较大。在生产过程中确实发现大量零件出现缩松,从而导致零件报废,给企业造成了较大的损失。通过工艺方案的逐渐改进,最终消除了缩松缺陷的过程,为相关零件的铸造提供了经验依据。     

改进模具冷却消除铝活塞组织缩松

目前,国内铝活塞毛坯的铸造,仍以金属型人工浇注为主。多采用顶注上抽芯,这在很大程度上限制了铝活塞的顺序凝固,因此,铸造废品主要为组织缩松。 为了确保产品质量,提高经济效益,消除活塞组织缩松,是大家所共同关心的问题。借鉴国外先进技术及我厂生产实践,我们认为;以磷变质金属型铸造的铝活塞,采用水冷,或水、气冷相结合的方法,对降低铸造废品率,提高产品质量,是行之有效的方法。     

热等静压对Mar M247合金组织及力学性能的影响

研究了热等静压处理对Mar M247合金精密铸件微观组织和力学性能的影响。结果表明:热等静压处理可以消除铸件显微疏松,提高致密度,改善显微组织,降低合金偏析,大幅度提高了铸件的冲击性能、拉伸性能和持久性能;热等静压处理减小了致密度和力学性能等数据的离散度。     

如何减少合金铸铁油环心部缩松

1 引言 在单体合金油环机加工过程中,挖了油槽后,往往在油槽的心部可看到细小的孔洞,有时是一个,有时一连几个.这就是我们所说的心部缩松(宏观).缩松有宏观、微观两种,宏观缩松是用眼或放大镜可看到的小孔,多分布在铸件心部,微观缩松是分布在晶粒之间的微小孔洞,可遍及整个截面.环的心部缩松必然降低环的机械性能,这样可降低其使用性、安全性.因此对活塞环(油环)的心部缩松问题,一定要高度重视并加以控制,尽量减少或避免使油环产生心部缩松.     

建立合理凝固顺序消除活塞缩松缺陷

本文简要介绍了汽油机铝活塞的铸造缩松缺陷产生的原因和影响因素，并以一个典型产品为例对比了冒口设置对活塞宏观质量的影响。铸件中建立起合理的凝固顺序不仅可以保证铸件的内在质量，还可提高铝液的工艺出品率和生产效率，产生的经济效益将十分显著。     

砂型单体合金活塞环铸造缩松缺陷分析研究

本文研究和分析了单体舍金活塞环铸造产生缩松的原因,并提出了合理的解决措施。研究表明,生铁的遗传性、原材料中的微量元素（如Te,As等）及集流包包颈处热节对活塞环的缩松产生较大的影响。其解决措施是,在钒钛生铁中加入一定比例的本溪生铁（30％-40％）,消弱生铁遗传性影响。另外加入稀土中和有害元素的影响,并在工艺上采取相应的改进措施。同时本文也讨论了单体活塞环铸造的凝固特点,并分析了生铁遗传性影响以及借助质谱分析和俄歇分析结果,探讨了合金中加入稀土的作用。     

燃气轮机叶片热裂缺陷的应力形成及演化研究

为揭示精铸过程中应力对热裂缺陷的影响,选取某重型燃气轮机透平导向叶片作为研究对象,采用熔模精密铸造工艺成型该叶片.通过观测叶片热裂的宏观和微观形貌,结合数值模拟软件Procast计算叶片不同位置凝固过程的应力,研究了应力的形成及演化过程,对比了铸件变形的数值计算结果与实测值.结果 表明:数值计算结果与实测值吻合较好;热...     

Unerroric of control of mutual compliance of the efficiency of hydrogen engines of unmanned vehicles in the conditions of mass production

The issues related to the reliability of hydrogen engines of unmanned vehicles and increasing the efficiency of using hydrogen as fuel when using the method of its production during the decomposition of hydrogen-containing molecules of liquid-phase organic compounds in a plasma discharge under the action of intense ultrasonic exposure are considered. Experiments have shown that as a result of decomposition in the acoustoplasma discharge of liquid hydrocarbons, solid-phase carbon-containing products are formed, chemical transformations occur in the liquid phase and hydrogen-containing combustible gas is formed. Hydrogen-containing gas can be used as fuel immediately after synthesis, i.e. it does not require separation, since in addition to hydrogen it contains only impurities of CO₂ and water vapor. The purpose of the study is to formalize the basic conditions for tightening the control of mutual compliance with the efficiency of hydrogen engines of the same series in the conditions of their mass production. Methods of mathematical statistics and hardware-software modeling were used in the study. The term “unerroric of quality mutual compliance control” is introduced to describe a set of hardware and software tools for such control. The principle of in-depth testing of the technical condition of such engines of one series is described in a multidimensional formulation of the quality control problem for three of their operating parameters at once. The conditions for increasing the mutual correspondence of the measured values of such parameters in the conditions of serial production of hydrogen engines are formalized.     

气门锁夹槽位置检测

气门圆弧形锁夹槽中心至杆端面以及至盘锥面量规线的距离(如图1中L、H). 在过程检验中如用普通量具难以测量,如用仪器测量则速度慢,效率低.为便于生产过程控制,确保工序质量,我们采用锁夹槽定位,用标准件比较测量的专用检具(如图2)进行测量.为保证锁夹槽定位准确以适应不同型号的气门,并防止气门测量时轴向窜动和左右摆动,采用了V型定位叉,使锁夹槽以四点定位,V型叉口的宽度,根据锁夹槽圆弧半径大小确定:约为圆弧的三分之二处(图3,图4).     

小型锅炉烟尘测试时锅炉出力的计算

锅炉烟尘测试时,必须对锅炉出力进行测试。但监测中,许多小型锅炉往往不具备相关的计量装置和仪表,为解决这一问题,文章提出了用烟气量和空气过剩系数来计算锅炉的出力的公式,在实际使用中,该方法简单易行,其结果和实测值具有很好的一致怀。     

煤焦混烧时粉尘化学成分和比电阻对静电除尘效率的影响

文章介绍了在煤焦混粉燃烧的情况下，粉尘化学成分和粉尘比电阻的变化对静电除尘器效率的影响。     

关于发展天然气电厂的讨论

世界发电燃料结构在不断的转换过程中。18世纪60年代从薪柴转到煤炭,19世纪到20世纪初大量发展燃煤电厂;20世纪20年代又从煤炭转向石油和天然气,20年代上半叶又大量发展燃油电厂;20世纪末由于天然气生产的发展,天然气因环境影响小,受到工业发达国家的青睐,加速发展天然气电厂。我国70年代初和90年代曾两次发展燃油电厂,由于石油危机和石油价格暴涨而受到制约,不得不实行以煤代油,改造燃油电厂。现在似乎认为燃油电厂不能再搞,但又出现发展燃气电厂的热流,发展燃气电厂确实是当今的世界潮流,但是同当年发展燃油电厂一样,要研究是否符合中国的国情?     

活塞车床设计方案探讨--ECK25异形活塞车床设计分析

本文从新型活塞设计的趋势及其对活塞车床的功能要求，讨论活塞车床的设计方案，并从机床功能、造型和宜人性上进行分析。     

中国煤炭地下气化技术的发展

本文综述了煤炭地下汽化技术的国内外发展现状,对我国“长通道、大断面”煤炭地下气化新工艺给予了技术经济评述,并提出了发展煤炭地下汽化技术的政策建议。     

分选机制砂对混凝土性能影响试验研究

平江抽水蓄能电站泵送混凝土使用的花岗岩为主的人工细骨料,云母含量较高.通过分选工艺降低游离云母的机制砂配制混凝土,性能试验结果表明:分选后机制砂混凝土拌和物混凝土用水量减少,混凝土工作性能提高,混凝土的抗冻性能得到改善.     

MgO膨胀剂细度对MgO水化和水泥浆体膨胀的影响

基于《水工混凝土掺用氧化镁技术规范》中的Ⅰ型氧化镁（MgO）,研究了该型MgO膨胀剂（MEA）细度对掺粉煤灰水泥浆体膨胀性能的影响。即采用X射线衍射分析(XRD)及同步热分析（TG DSC）分析了掺MEA水泥浆体中MgO的水化性。结果表明,养护温度相同时,MEA的细度对水泥浆体内MEA中MgO的水化和水泥浆体的膨胀无显著影响,产生的膨胀均能补偿水泥浆体的收缩;MEA的细度可从试验设计采用的45 μm筛筛余15%左右增加到30%左右,这将有利于MEA生产企业的节能降耗。     

柴油理化性能的分析与质量指标的控制

对柴油的化学组成及物理性质进行了分析,叙述了柴油理化性能与柴油机工作状态的关系,探讨了柴油质量指标的控制措施,为今后的柴油检验和机车检修工作提供了实用的理论依据。