UV固化水性含氟聚氨酯的制备及其性能研究

选用异佛尔酮二异氰酸酯（IPDI）、聚酯多元醇（PCDL）、二羟甲基丙酸（DMPA）、甲基丙烯 酸羟乙酯（HEMA）、季戊四醇三丙烯酸酯（PETA）、三乙胺（TEA）、甲基丙烯酸十二氟庚酯（DFHMA）为 主要原料合成了一种UV固化水性含氟聚氨酯。采用FT-IR、1H NMR、光学接触角测量仪、粒度分析 仪、热重分析仪、电子拉力机等对涂膜的结构与性能进行了表征与测试。结果表明:随着甲基丙烯酸 十二氟庚酯的加入,乳液粒径变大,分布变宽,涂膜接触角明显变大,吸水率明显降低,热稳定性有所 提升,拉伸强度变大。当甲基丙烯酸十二氟庚酯添加量为6%时,涂膜综合性能最好。     

UV固化超支化水性聚氨酯涂料的制备

以自制单体6[N-氨乙基-2,2'-二羟甲基丙酰胺]、甲苯-2,4-二异氰酸酯(TDI)和2,2'-二羟甲基丙酸(DMPA)为主要原料,采用准一步法制备了新型WHBPU(水性超支化聚氨酯);然后以此为基体,通过接枝活性稀释剂(羟乙基丙烯酸酯)引入了光活性基团,制备出一种可UV(紫外光)固化的WHBPU涂料。研究结果表明:以固化速率为考核指标,采用单因素试验法优选出制备WHBPU涂料的最佳工艺条件是冰盐浴(-5℃)反应时间为2.0 h、油浴温度为60℃、油浴时间为2.0 h、w(活性稀释剂)=20%(相对于WHBPU乳液质量而言)、w(光引发剂)=3%(相对于干固乳液质量而言)和干燥条件为室温(25℃)干燥2 h→50℃干燥2 h;此时,胶膜的固化速率相对较快、凝胶含量相对最大。     

改性UV固化水性聚氨酯丙烯酸酯合成研究

采用异佛尔酮二异氰酸酯(IPDI)、聚醚硅氧烷二元醇(WACKER IM 22、IM15)/聚酯二元醇(7112)混合软段、二羟甲基丙酸( DMPA)/聚乙二醇(PEG600)混合亲水基(扩链剂)、季戊四醇三丙烯酸酯(PETA)等原料合成多官能度的综合改性UV固化水性聚氨酯丙烯酸酯(WPUA);实验结果表明:采用阴/非离子混合型亲水基能提高WPUA产品稳定性,改性产品固化后膜的耐水性、耐碱性、耐溶剂性能明显提高,综合性能优良.     

紫外光固化碳纳米管改性水性聚氨酯涂膜

以异佛尔酮二异氰酸酯(IPDI)、聚乙二醇(PEG400)、2,2-双羟甲基丙酸(DMPA)和甲基丙烯酸-2-羟乙酯(HEMA)为主要原料,合成光固化水性聚氨酯丙烯酸酯预聚体,以三乙醇胺中和后,原位引入经浓硝酸处理过的碳纳米管(CNTs),制备了光固化水性聚氨酯碳纳米管复合乳液(WPU/CNTs),加入光引发剂后交联固...     

紫外光固化水性聚氨酯丙烯酸酯的制备及其性能分析

由于传统的溶剂型涂料存在一定的有毒有害物质,为此必须要积极探索溶剂型涂料的替代品通过利用低含量溶剂化、水性化、无溶剂化、粉末化、光固化涂料的研究与发展,不仅能够继承传统的紫外光固化技术和水性技术,而且还能够实现绿色健康环保无污染。紫外光固化技术和水性技术的结合也能够保证材料的防火性能和安全性能在涂料行业得到了快速的发展。本文通过对紫外光固化水性聚氨酯丙烯酸酯的制备,以及性能进行深入的研究,并且异氟尔酮二异氰酸酯为应对聚乙二醇为软段,同时以氢甲基丙酸作为亲水扩链剂加入到烃基之中,利用甲基丙烯酸-β-羟乙酯通过封端引入碳碳双键作为双固化的功能团,实现了多步骤聚反应制备紫外光固化水性聚氨脂、丙烯酸酯。     

影响UV固化聚酯型水性聚氨酯-丙烯酸酯涂层性能的因素

选用异佛尔酮二异氰酸酯(IPDI)、聚酯二元醇、二羟甲基丙酸(DMPA)、甲摹丙烯酸-β-羟乙酯(HEMA)等为原料,采用阴离子自乳化法制备了紫外光(UV)固化聚酯型水性聚氨酯-丙烯酸酯预聚体,并配以光引发剂,其涂层经紫外光固化.讨论了光引发剂和n(-NCO):n(-OH)对涂层性能的影响.研究结果表明,复配光引发剂种类及比例为m(光引发剂B):m(光引发剂c)=1:1,用量为HEMA质量分数的10%时,涂层性能最好.     

水性UV固化树脂的研究进展

介绍了近年来水性UV(紫外光)固化树脂的研究进展,重点综述了水性UV固化树脂的特点、分类及其在不同领域的应用研究。最后就水性UV固化树脂现存的问题展望了其未来的研究方向。     

阳离子型水性UV固化含氟聚氨酯树脂的制备及性能研究

以二乙醇胺、甲基丙烯酸十三氟辛酯为原料,通过迈克尔加成反应合成一种含氟二元醇(F-DEA),并以此为含氟单体,通过缩合共聚的方法与异佛尔酮二异氰酸酯(IPDI)、聚四亚甲基醚二醇(PTMG-1000)、N-甲基二乙醇胺(MDEA)以及季戊四醇三丙烯酸酯(PETA)反应合成一种阳离子型水性UV固化含氟聚氨酯树脂。利用FT-IR、1H-NMR等手段对产物的分子结构进行表征。采用粒径分析、接触角、X射线光电子能谱(XPS)以及各种性能测试手段,对乳液、光固化过程及涂膜性能进行分析研究。结果表明:在一定条件下,该树脂能稳定分散在水中,随着含氟量的增加,乳液粒径增大,但光固化效率有所降低,同时热处理后的氟碳链迁移至涂膜表面,所得的光固化涂膜各种性能较好,特别是耐水和耐酸碱性有明显改善。     

新型含氟UV固化水性聚氨酯的合成及其性能研究

文章以三羟甲基丙烷、马来酸酐为原料合成出一种新型的亲水二元醇(T.M),将其与聚丙二醇(PPG-1000)、甲苯-2,4-二异氰酸酯(TDI),和全氟辛醇等合成出含氟UV固化水性聚氨酯(TPTMF),并通过傅立叶红外光谱(FTIR)对其进行了表征,并通过热重分析等仪器对乳液和涂膜性能进行测试。结果表明:所合成的树脂具有具有光固化性能;将含氟辛醇引入主链中,所得到的固化膜具有良好的疏水性、耐热性、自清洁性等[1-2]。     

纳米氧化锡锑/UV固化水性聚氨酯隔热涂料的制备及其性能表征

以聚酯二元醇、异佛尔酮二异氰酸酯、二羟甲基丙酸、季戊四醇三丙烯酸酯(PETA)等为原料,制备了具有感光性能的水性聚氨酯丙烯酸酯预聚体(PUA),通过溶胶-凝胶法对采用硅烷偶联剂KH570对纳米氧化锡锑(ATO)进行改性,然后将改性纳米ATO与PUA加水乳化制得纳米WPUA/ATO复合乳液,最后通过UV固化制得WPUA/ATO涂膜,研究了ATO含量对WPUA/ATO涂膜性能的影响。结果表明,随着纳米ATO含量增加,可见光平均透过率降低,红外光平均屏蔽率增加;其中当纳米WPUA/ATO复合乳液中ATO质量含量为9%时,可见光平均透过率为71.43%,红外光平均屏蔽率高达为79.69%,隔热性能较好,特别适合制备涂膜隔热玻璃。     

聚氯乙烯/粉煤灰复合材料的制备与性能研究

制备了聚氯乙烯/粉煤灰复合材料,研究了粉煤灰的不同表面处理方式对共混物的力学性能和耐温性能的影响。结果表明:湿法处理粉煤灰的效果最好,不做处理的效果最差;粉煤灰会降低PVC材料的缺口冲击强度;添加5份处理过的粉煤灰可以提高PVC材料的拉伸强度;添加粉煤灰可以提高PVC材料的弯曲强度和弯曲模量,同时,耐温性也有一定的提高。     

Comparative Study on Selected Properties of Modified Polyurethane Foam with Fly Ash

The aim of the article is to compare two types of fly ash (from the fluidized and pulverized coal combustion process) as a filler for rigid polyurethane foam. Pulverized fly ash (PFA) is widely used in building materials, while fluidized fly ash (FFA) is not currently recycled, but landfilled. The produced rigid polyurethane foams were reinforced with 5 and 10% by weight addition of fly ash from two different types of boilers. The foaming process, physical properties, morphologies and thermal degradation were subject to comparative analysis. The research indicated that fly ash intensifies the reactions of foam synthesis, most commonly, polyurethane (PU) foam with an addition of 10% PFA. What is interesting is that both ashes can be used in PU foam technology as they do not cause deterioration of the physical parameters. As shown, the addition of filler affects the morphology and impairs the brittleness. Additionally, the use of fly ash from coal combustion in the technology of polyurethane materials complies with the guidelines of the circular economy stated in the European Union legislation. Partial replacement of petrochemical components with waste filler also reduces the total energy consumption in the production of PU composites.     

UV固化水性聚氨酯丙烯酸酯木器涂料的研究

利用2种软硬程度不同的UV固化水性树脂,对UV固化水性木器涂料的复配及工艺进行研究.探讨了助剂(特别是硅溶胶)对水性木器涂料涂膜性能及施工工艺性等的影响.实验结果表明:UV固化水性木器清漆涂膜硬度高,具有很好的附着性、耐刮擦、耐化学品等性能,适合于工业化生产板材的涂饰.     

粉煤灰制备多孔水处理材料的试验研究

针对粉煤灰粒度细小带来的分离困难等问题,研究了一种粉煤灰制备多孔水处理材料的方法。对成型过程中石灰添加量、铝粉添加量、粉煤灰粒度以及搅拌速度等影响因素进行了研究。分别考察了成型试件的吸水率、COD去除率、氨氮去除率、抗压强度、干体积密度以及抗冻性能。结果表明最佳制备条件为：粉煤灰：石灰：石膏：水泥：铝粉：水：十二烷基苯磺酸钠为34．5：10．5：2：4：0．056：35：0．15,粉煤灰、石灰、石膏、水泥粒度为O．075mm,搅拌速度为400r／min。制得的多孔试件各项指标为：于体积密度约为540-590kg／m^3,抗压强度为0．7～0．9MPa,吸水率为70％-80％,COD去除率为22％左右,氨氮去除率为38％左右,冻融后质量损失为2．5％左右,冻后抗压强度为0．5MPa,均达到较优水平,是一种很好的水处理材料。     

不同聚醚二元醇软段对光固化水性聚氨酯乳液性能的影响

以不同聚醚二元醇、异佛尔酮二异氰酸酯、2,2-双羟甲基丙酸、甲基丙烯酸-2-羟基乙酯为主要原料,通过丙酮法合成光固化水性聚氨酯(WPU)乳液,讨论了不同聚醚软段对光固化WPU乳液性能的影响.结果表明,由聚四氢呋喃醚二元醇PTMG1000和PTMG2000制备的光固化WPU乳液具有较小的粒径和粘度,其交联后的膜具有较高储...     

粉煤灰填充双组分聚氨酯防水涂料的制备

研究了粉煤灰填充双组分聚氨酯防水涂料的效果。粉煤灰的细度对防水涂料的固化速度和涂膜性能都有影响。当粉煤灰的细度为300目时能得到性能优良的双组分聚氨酯防水涂料。     

氧化剂浓度对漂珠/聚苯胺复合材料的制备及其性能影响研究

本文采用乳液聚合法制备了十六烷基三甲基溴化铵改性漂珠/聚苯胺复合材料(FAFB-HDTMA/PAn),利用FTIR、SEM对产物的结构与形貌进行分析,并讨论了不同氧化剂过硫酸铵(APS)浓度对FAFB-HDTMA/PAn复合材料的产物颜色及其电学性能的影响.实验结果表明:利用FTIR和SEM分析证明HDTMA对FAFB修饰改性成功,FAFB-HDTMA被PAn包覆;通过观察复合产物颜色可知,随着APS:An浓度比的增加,产物颜色更趋近于掺杂态PAn的颜色;利用四探针技术测试发现,聚苯胺的电导率随着改性粉煤灰漂珠(FAFB-HDTMA)的加入而降低了近100倍;利用LCR数字电桥测试发现,在100 kHz～2 MHz的频率范围内,FAFB-HDTMA/PAn复合材料的相对介电常数和介电损耗随外加频率的增大而减小,进而可知当APS::An浓度比为0.8时,FAFB-HDTMA/PAn复合材料的电导率和相对介电性能均为最优效果.     

乳液型紫外光固化聚氨酯丙烯酸酯的涂膜性能及其影响因素

合成了一系列乳液型紫外光(UV)固化聚氨酯丙烯酸酯,针对其涂膜性能进行研究,考察了辐射时间、膜厚、光引发剂用量、分子结构等因素对涂膜性能的影响;通过对各种影响因素的研究,得到了具有优良的涂膜性能和装饰性的乳液型UV固化聚氨酯丙烯酸酯,附着力在0~1级,正反耐冲击性都在50 cm以上,铅笔硬度可以达到3H以上。     

粉煤灰陶粒制备试验研究

粉煤灰是燃煤电厂排出的主要固体废物,粉煤灰主要用于混凝土添加剂,附加值较低.为了提高粉煤灰的利用价值,本研究利用粉煤灰制备轻质高强陶粒.在1100 ℃煅烧时,粉煤灰陶粒烧结出现新物相钙长石,在1200 ℃煅烧时,石英相溶解到烧结物相中,粉煤灰陶粒烧结出现新物相普通辉石,煅烧温度控制在1100~1200 ℃范围较适宜.煅烧温度增加到1200 ℃时,筒压强度达到6.3 MPa左右,体积密度达到1.6 g/cm3左右.当P值较低时,粉煤灰陶粒的烧成温度降低,陶粒容易烧胀,当P值超过10时,粉煤灰陶粒的烧成温度过高,粉煤灰陶粒不易发生膨胀.