FeCo/SnO_(2)复合纳米纤维的制备及其吸波性能EI北大核心CSCD

用静电纺丝和氢气还原法制备FeCo/SnO_(2)复合纳米纤维并使用X射线衍射、扫描电子显微镜、振动样品磁强计和矢量网络分析仪等手段分析表征其结构、形貌、磁性及电磁特性,研究了SnO_(2)含量对复合纳米纤维的吸波性能的影响。结果表明,添加适量的SnO_(2)可显著提高FeCo纳米纤维的吸波性能。用SnO_(2)摩尔含量为20%的复合纳米纤维制备的厚度仅为1.4 mm的涂层,在频率10.95 GHz处最小反射损耗(RL)为-40.2 dB,有效吸收带宽(RL≤-10 dB)为2.64 GHz (9.75-12.39 GHz),厚度减小到1.0 mm的涂层其最大有效吸收带宽为4.16 GHz,频率范围为13.84~18.00 GHz。涂层吸波性能优异的主要原因,是阻抗匹配的改善、磁性FeCo合金与介电SnO_(2)的电磁损耗协同作用、加强的界面极化驰豫以及纳米纤维形成的三维网络结构产生的多重反射与散射。     

Co含量对轻质微波吸收剂C/Co纳米纤维吸波性能的影响

采用静电纺丝法结合热处理制备了一种可应用于2~18 GHz频段的高性能轻质微波吸收剂C/Co纳米纤维, 详细研究了金属Co含量对纳米纤维的电磁特性及微波吸收性能的影响。相对于纯碳纳米纤维, C/Co纳米纤维的微波吸收性能得到显著加强, 其主要吸波机制仍是介电损耗。随着Co含量的增加, C/Co纳米纤维的电磁衰减能力逐渐下降, 而微波吸收却先增强后减弱, 含37.8wt% Co的C/Co-5纳米纤维因金属Co粒子和纳米碳纤维的良好结合与协同效应, 以及纤维中特殊的Co粒子@石墨核壳结构所带来的良好阻抗匹配与足够高的电磁衰减能力而表现出最好的吸波性能。模拟计算结果表明, 涂层厚度在1.1~5.0 mm间变化时, 填充5wt% C/Co-5纳米纤维的硅胶吸波涂层的反射损耗(RL)值超过-20 dB的频率范围在3.2~18 GHz, 最小RL值达到-78.8 dB, 其中当涂层厚度仅为1.5 mm时, RL值低于-20 dB的吸收带宽可达6.0 GHz (12~18 GHz)。C/Co纳米纤维优异的微波吸收性能表明, 这些磁性碳杂化纳米纤维有望成为一种极具应用前景的新型吸波材料。     

静电纺制备Fe3O4/PEK-C纳米复合膜及其吸波性能

静电纺丝技术是一种新颖、高效且简单的制备连续纳米纤维的方法,纳米复合纤维膜的优异特点赋予了纳米吸波剂新的吸波通道。本文采用静电纺丝工艺制备Fe3O4/PEK-C纳米复合纤维膜,利用SEM和TGA表征纳米复合纤维膜的微观形貌和热稳定性,用矢量网络分析仪测试样品在8.2~12.4 GHz的电磁参数与吸波性能。结果表明,Fe3O4/PEK-C纳米复合纤维膜呈现出超细纤维彼此交织构成的立体网络结构,其热稳定性、复介电常数和复磁导率均随着Fe3O4含量的增加而增加,介电损耗和磁损耗得到加强。当纳米复合纤维膜的厚度为1.8 mm时,其反射损耗在整个测试波段均处于-5 dB以下,-10 dB以下有效吸收频宽为2 GHz,频率在8.6 GHz处吸收强度达到最大值-15.4 dB。预期可作为隐身复合材料的吸波功能层。     

单壁碳纳米管-CoFe2O4双层复合材料的微波吸收特性

通过直流电弧放电法制备了高结晶性单壁碳纳米管（SWCNTs）,采用溶胶凝胶自燃法制备CoFe₂O₄,并将两种材料复合制成SWCNTs-CoFe₂O₄双层吸波材料。使用Raman光谱、XRD、SEM、TEM和矢量网络分析仪对SWCNTs和CoFe₂O₄的形貌、结构和电磁性能进行了表征,并利用传输线理论分析了SWCNTs-CoFe₂O₄双层吸波材料在2~18 GHz频带内的微波吸收性能。结果表明,相对于单一材料,SWCNTs-CoFe₂O₄双层复合材料的吸波性能得到了极大提高。当CoFe₂O₄作为匹配层、SWCNTs作为吸收层时,通过调节匹配层和吸收层的厚度,SWCNTs-CoFe₂O₄双层复合材料的最强反射损耗可以达到-61.13 dB,低于-10 dB的吸收带宽达到7 GHz （8~15 GHz）。因此,SWCNTs-CoFe₂O₄双层复合材料是一种新型的有应用前景的高吸收宽频带吸波材料。     

活性炭纤维/树脂复合吸波材料的研究

研究了活性炭纤维/树脂吸波复合材料的微波吸收特性.实验结果表明:活性炭纤维吸波材料的吸波性能与吸波层中纤维的含量、分布方式密切相关.在本实验条件下吸波层中四个结构层纤维含量(质量分数)分别为0.2%,0.4%,0.6%和0.8%时,材料在4.2～18GHz频率范围内对电磁波有-10dB以下的吸收,7.12GHz时取得最...     

SiO2对羰基铁/炭黑双层吸波涂层吸波性能的影响

以羰基铁和炭黑分别用于匹配层和吸收层制备了具有阻抗渐变结构(匹配层+吸收层)的1.2 mm厚环氧树脂基吸波涂层。通过在匹配层中加入透波剂SiO2,改善了吸波涂层的阻抗匹配性。随着SiO2在匹配层中含量的增加,涂层的反射损耗(RL)得到增强。当匹配层中SiO2与羰基铁及环氧树脂的比值为2∶5∶1时,涂层的吸收峰值达到-17.3 dB,涂层有效带宽(RL<-4 dB)达到5.7 GHz。     

核壳结构LaOCl/LaFeO3纳米纤维的阻抗匹配设计及其电磁吸波性能研究(英文)

电磁波在无线通信等领域的广泛应用导致了严重的电磁污染,迫切需要研发高性能电磁波吸收材料.本文针对吸波材料阻抗不匹配等关键问题,设计并成功制备了新型核壳LaOCl/LaFeO₃纳米纤维电磁波吸收剂.这种独特的一维多级结构由导电LaFeO₃磁性壳层和离子化合物LaOCl核层组成.基于介电-磁损耗耦合和阻抗匹配的协同作用,LaOCl/LaFeO₃纳米纤维在超低负载条件下(4 w t%),表现出-40.1 d B (2.0 mm)的反射损耗和6.4 GHz (2.4 mm)的有效吸收带宽.该工作提出了一种新型LaOCl/LaFeO₃纳米纤维吸波材料,并为阻抗匹配调控和电磁吸波性能优化开辟了新策略.     

外贴Fe3O4/CNTs杂化碳纳米纸的碳纳米管复合材料吸波性能

通过对Fe₃O₄纳米粒子接枝碳纳米管的单分散水溶液真空吸滤制备出一种新型的杂化碳纳米纸, 它与树脂浸润良好, 可以与复合材料一体成型。分别借助FE-SEM、EDS、BJH法和振动样品磁强计表征杂化碳纳米纸及其复合材料的微观形貌、元素组成、平均孔径分布和磁性能。在8.2~18 GHz频段内利用波导法测量碳纳米管共混复合材料和外贴杂化碳纳米纸/碳纳米管共混复合材料的电磁参数和吸波反射率。研究结果表明: 外贴一层杂化碳纳米纸(厚0.1 mm)后, 碳纳米管共混复合材料的磁损耗明显增加, 在8.2~18 GHz微波频段内吸波反射率基本上全部小于-10 dB(频宽大于9.7 GHz), 在15.42 GHz位置, 反射损耗峰达-43.18 dB, 远优于碳纳米管共混复合材料。     

碳包覆铁/丙烯酸树脂水性纳米复合涂料的制备及电磁波吸收性能

以"壳/核"型碳包覆铁(Fe(C))纳米颗粒为填料、水性丙烯酸树脂为基体,制备了纳米复合电磁波吸收涂料.采用不同含量的十二烷基苯磺酸钠(SDBS)对纳米颗粒改性,提高了纳米颗粒在基体中的分散性.选用吸收剂填充量为25%(质量分数)的涂料,测定了不同厚度涂层的电磁波吸波性能.涂层具有很好的吸波性能,当厚度为5mm时,反射损耗峰值为-17.2dB,吸收带宽为3.2GHz(7～10.2GHz).首次用实验结果证明了传输线理论对铁磁性纳米颗粒吸波性能的模拟结果.     

聚苯胺纳米纤维/锂锌铁氧体复合吸波材料的制备与性能

采用溶胶-凝胶法制备锂锌铁氧体(Li_0.435Zn_0.195Fe_2.37O₄,LZFO),界面聚合法制备纯聚苯胺(PANI)和PANI纳米纤维/LZFO复合材料。通过SEM、XRD、FTIR和矢量网络分析(PNA)等对材料的物相、结构和吸波性能进行了表征和分析。结果表明:制备出的样品分别为PANI、LZFO和不同配比的PANI纳米纤维/LZFO复合材料。在2~18 GHz范围内,PANI纳米纤维/LZFO复合材料的电磁波反射率<-10 dB的波段有2个,吸波性能较纯PANI和LZFO有了很大提高,并且拓宽了吸波频带,当PANI纳米纤维/LZFO复合材料中PANI纳米纤维的质量分数为10%,其综合吸波性能最佳,电磁波反射率<-10 dB的波段分别为2.5~5.5 GHz波段和14.5~16.5 GHz波段,最大吸收峰可达到-33.8 dB。而PANI和LZFO在电磁波反射率<-10 dB的波段只有1个。因此通过PANI纳米纤维接枝铁氧体,可调节电磁参数,提高材料的吸波性能。      

Microwave absorption properties of double-layer absorbers based on spindle magnetite nanoparticles and flower-like copper sulfide microspheres

In this work, the spindle magnetite nanoparticles (SMNPs) and flower-like copper sulfide microspheres (FCSMSs) were synthesized via hydrothermal method. The structures, chemical composition and morphologies of samples were analyzed and characterized in detail. The microwave absorption properties of single-layer and double-layer absorbers were investigated based on the electromagnetic transmission line theory in the frequency range from 2 to 18 GHz. The results show that the double-layer absorbers consisting of FCSMSs as matching layer and SMNPs as absorbing layer display superior microwave absorbing performance compared to the single-layer ones due to the proper combination of magnetic loss of SMNPs and dielectric loss of FCSMSs, and the improved impedance matching characteristics. When the thicknesses of the absorbing layer and the matching layer are 1.6 and 0.4 mm, respectively, the minimum reflection loss reaches ??74.3 dB at 10.9 GHz, and the efficient absorption bandwidth is up to 5.34 GHz (8.46–13.8 GHz). The optimal SMNPs/FCSMSs double-layer absorbers can become a novel microwave absorption material with strong-absorption and broad-band.     

Influence of SiO2 fillers on microwave absorption properties of carbonyl iron/carbon black double-layer coatings

Epoxy resin (ER) based double-layer composite coatings were prepared with the thickness of 1.2 mm, employing carbonyl iron (CI) and carbon black (CB) as absorbents in the matching layer and absorption layer respectively. Especially, SiO₂ was introduced into the matching layer as wave-transmission material to improve the matching impendence. The complex permittivity, complex permeability and absorption properties were investigated in 2–18 GHz. With increasing SiO₂ content in the matching layer, the reflection loss (RL) was enhanced in the range 2–18 GHz. When the coating with the optimized SiO₂ and CI weight concentration (SiO₂:CI:ER) of 2:5:1, the optimal RL got to −17.3 dB and the effective absorption band (RL better than −4 dB) reached 5.7 GHz. In comparison, the minimum RL value was only −5.9 dB and the bandwidth (RL better than −4 dB) was just 4.1 GHz for the SiO₂-free composite coating.     

Effects of Multi-walled Carbon Nanotubes on the Electromagnetic Absorbing Characteristics of Composites Filled with Carbonyl Iron Particles

The electromagnetic(EM) wave absorbing property of silicone rubber filled with carbonyl iron particles(CIPs) and multi-walled carbon nanotubes(MWCNTs) was examined.Absorbents including MWCNTs and spherical/flaky CIPs were added to silicone rubber using a two-roll mixer.The complex permittivity and complex permeability were measured over the frequency range of 1-18 GHz.The two EM parameters were verified and the uniform dispersion of MWCNTs and CIPs was confirmed by comparing the measured reflection loss(RL) with the calculated one.As the MWCNT weight percent increased,the RL of the spherical CIPs/silicone rubber composites changed insignificantly.It was attributed to the random distribution of spherical CIPs and less content of MWCNTs.On the contrary,for composites filled with flaky CIPs the absorption bandwidth increased at thickness 0.5 mm(RL value lower than-5 dB in 8-18 GHz) and the absorption ratio increased at lower frequency(minimum-35 dB at 3.5 GHz).This effect was attributed to the oriented distribution of flaky CIPs caused by interactions between the two absorbents.Therefore,mixing MWCNTs and flaky CIPs could achieve wider-band and higher-absorption ratio absorbing materials.     

Enhanced microwave absorption performance of graphene/doped Li ferrite nanocomposites

In the present study, Microwave absorbing Li-Sr, Li-Co ferrite nanoparticles and RGO/Li-Sr, RGO/Li-Co ferrite nanocomposites containing Li ferrite and reduced graphene oxide (RGO) were synthesized to further improve the microwave absorption performance of Li ferrite nanoparticles (LiFe₅O₈). The Li-Sr and Li-Co nanoparticles were synthesized by thermal treatment method, the RGO/Li-Sr and RGO/Li-Co nanocomposites were obtained by a polymerization method and were characterized by different techniques. The electromagnetic wave absorption properties of the samples were evaluated by vector network analyzer (VNA) in the frequency range of 2–18 GHz. The magnetic and dielectric loss, impedance matching, and electromagnetic wave absorption of the samples are significantly improved through the addition of RGO. Experimental results revealed that the RGO/Li-Co nanocomposite considerably increased microwave absorption. The minimum reflection loss (RL) of RGO/Li-Co also was found to reach −46.80 dB at the thickness of 3 mm and the effective absorption bandwidth (≤-10 dB) amounted to 6.80 GHz (from 10.52 to 17.32 GHz), which was much higher in comparison with pure Li and Li-Co ferrites nanoparticles. Due to the synergistic effect between magnetic loss and dielectric loss and the good impedance matching, the RGO/Li-Co nanocomposite may be regarded as a new candidate for microwave absorbing materials characterized with a broad effective absorption bandwidth at thin thicknesses.     

Electromagnetic characteristic and microwave absorbing performance of different carbon-based hydrogenated acrylonitrile–butadiene rubber composites

Hydrogenated acrylonitrile–butadiene rubber (HNBR) was mixed with carbon fiber (CF), conductive carbon black (CCB) and multi-walled carbon nanotubes (MWCNT) to prepare microwave absorbing composites, their complex permittivity was measured in microwave frequencies (2–18 GHz), and their electromagnetic characteristics and microwave absorbing performance were studied. The real part and imaginary part of permittivity of the composites increased with increasing carbon filler loading, showing dependency on filler type. The microwave reflection loss of the composites also depended on the loading and type of fillers. The matching thickness of the absorber layer decreased with increasing permittivity, while the matching frequency decreased with increasing layer thickness. The minimum reflection loss was −49.3 dB for HNBR/MWCNT (100/10) composite, while −13.1 dB for HNBR/CCB (100/15) composite and −7.1 dB for HNBR/CF (100/30) composite. The efficient microwave absorption of HNBR/MWCNT composites is accounted from high conduction loss and dielectric relaxation of MWCNT, and strong interface scattering.     

双层吸波材料吸波特性研究

依据阻抗匹配原理与电磁波传播规律,设计了具有阻抗渐变结构的双层吸波材料.实验表明,匹配层对提高吸收率起着重要作用;需精确控制其吸波剂含量,以实现吸波效果.经测试:4#试样厚度为6mm,测试频段为8-18GHz,最大吸收峰值在14.1GHz(R=-28.14dB),R＜-10dB的频宽为6.7GHz;7#试样厚度为5.5mm,最大吸收峰值在9.6GHz(R=-27.48dB),R＜10dB的频宽为8.6GHz,R＜-15dB的频宽为7.6GHz;8#试样厚度为6mm,最大吸收峰值在16.8GHz(R=-24.24dB),R＜-10dB的频宽为8.6Hz.该结果具有一定工程应用价值.     

Investigation of adjacent spacing dependent microwave absorption properties of lamellar structural Ti3C2Tx MXenes

Ti₃C₂Tx MXenes and their composites play a vital role in the research on microwave absorbing materials. Herein, the different interlamellar spaces of Ti₃C₂Tx MXene materials were prepared by an etching process. The dependence of the microwave absorbing properties of the Ti₃C₂Tx MXene nanosheets on different interlamellar spaces was studied. The complex permittivity, dielectric loss, impedance matching characteristic and the minimum reflection loss (RL) value with the variation in interlamellar space were systematically investigated. Results showed that 40% ratio paraffin-bonded composites (S3) have a strong electromagnetic wave absorption performance and large effective absorbing bandwidth. The maximum RL reaches −36.3 dB at 4.67 GHz with the thickness of 4.5 mm, ascribed to its a high dielectric loss and good impedance matching characteristics. The RL value of Ti₃C₂Tx MXenes is strongly dependent on the inter-lamellar space. The enhanced microwave absorption originates from the unique 2-D structure, good impedance matching characteristics, and enhanced space-charge polarization effects. This work provides a new avenue for exploring high-performance microwave absorbers based on MXene materials.     

Microwave absorption properties of FSS-impacted composites as a broadband microwave absorber

The development of a cost-effective microwave absorber with wide bandwidth corresponding to reflection loss (RL)?≤??10 dB is still a very challenging task. A sugarcane bagasse-based agricultural waste composite has been analyzed for its elemental contents. The combination of elements is suitable for its possible usage as a cost-effective microwave absorbing material. Therefore, this composite has been subjected to morphological and electromagnetic studies to analyze its microwave absorbing behavior. The frequency dependent complex dielectric permittivity and complex magnetic permeability values were obtained using a transmission/reflection waveguide approach in the X-band. Furthermore, the effect of the Minkowski loop frequency selective surface (FSS) was studied over the absorption capability of the composite. It was found that the application of FSS leads to a reduction in thickness up to 2.9 mm and an enhancement in absorption bandwidth up to 3.6 GHz. The FSS patterned composite shows a remarkable performance with peak RL of ?28.4 dB at 10.7 GHz and absorption bandwidth of 3.6 GHz.