Separation of aluminosilicates and diaspore from diasporic-bauxite by selective flocculation

The flocculation tests of four pure minerals (diaspore, kaolinite, illite, pyrophyllite) and bauxite ore were investigated by the sedimentation. The dispersion behavior of the four pure minerals shows a very good consistency with the variation of zeta potential. The concentrate with the mass ratio of Al2O3 to SiO2 (m(Al2O3)/m(SiO2)) 8.90 and the recovery of Al2O3 86.98% is obtained from bauxite ore (m(Al2O3)/m(SiO2)=5.68) in pH range of 9.5-10.0 by using sodium carbonate (5 kg/t) and sodium polyacrylate (7 g/t) as dispersant and flocculant respectively. Sodium carbonate acts as both pH modifier and favorable dispersant for aluminosilicates. The high performance of sodium polyacrylate on flocculation for diaspore is contributed to the carboxyl of sodium polyacrylate that interacts with active Al sites on diaspore by chemical absorption, and the hydrogen bond effects between hydroxyl group of macromolecule and surface Al--OH on diaspore to accelerate the sedimentation of diaspore.     

Dissolution of Al2TiO5 inclusions in CaO-SiO2-Al2O3 slags at 1823 K

Al-Ti-O inclusions always clog submerged nozzles in Ti-bearing Al-killed steel.A typical synthesized Al2TiO5 inclusion was immersed in a CaO-SiO2-Al2O3 molten slag for different durations at 1823 K.The Al2TiO5 dissolution paths and mechanism were revealed by scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS).Decreased amounts of Ti and Al and increased amounts of Si and Ca at the dissolution boundary prove that inclusion dissolution and slag penetration simultaneously occur.SiO2 diffuses or penetrates the inclusion more quickly than CaO,as indicated by the w(CaO)/w(SiO2) value in the reaction region.A liquid product (containing 0.7-1.2w(CaO)/w(SiO2),15wt％-20wt％ Al2O3,and 5wt％ -15wt％ TiO2) forms on the inclusion surface when Al2TiO5 is dissolved in the slag.Al2TiO5 initially dissolves faster than the diffusion rate of the liquid product toward the bulk slag.With increasing reaction time,the boundary reaches its largest distance,the Al2TiO5 dissolution rate equals the liquid product diffusion rate,and the dissolution process remains stable until the inclusion is completely dissolved.     

锆英粉涂料涂层结构研究

通过研究锆英粉(其中有少量铝矾土)涂料层的断面结构,发现在高温条件下,锆英粉能分解出少量ZrO2微粉和SiO2;钢液表面的FeO能渗透到涂层中,与SiO2和水玻璃等形成铁橄榄石相;锆英粉能被水玻璃缓慢溶解,但其颗粒仍然能保持完整状态;SiO2、FeO、Al2O3、Na2O等生成了大量低熔点的玻璃相,填充其颗粒间空隙,形成致密层,能防止钢液渗透;涂层中的铝矾土在水玻璃的作用下,其颗粒状态消失,形成铝酸铁钠新相.     

低硅烧结矿的矿物组成分析

为研究二氧化硅对烧结矿的矿物组成的影响,采用EPMA面分析的方法对两种低硅烧结矿进行了分析。结果表明,与传统烧结矿相比,低硅烧结矿里的氧化铁量增加,铁酸钙量减少。在低硅烧结矿里没有氧化铝集中于铁酸钙里的趋势,各矿物组成里,随着二氧化硅含量的增加,MgO含量减少,而CaO含量却增加。     

广西某赤褐铁矿选矿试验研究

对广西某含铁品位为52．07％、磁性率（FeO／TFe）为2．11％的难选赤褐铁矿矿石进行理化性能分析和矿物工艺学研究,并进行了强磁选、还原焙烧－磁选选矿试验,确定还原焙烧磁选可以获得较好的选别指标为：精矿铁品位达63．27％,产率达82．7％,铁回收率95．99％,有害元素硫,磷都较低,Si02、Al2O3、CaO、MgO的含量都能满足高炉冶炼的要求,属于优质铁精矿．     

Separation of hematite from banded hematite jasper(BHJ) by magnetic coating

The separation of iron oxide from banded hematite jasper(BHJ) assaying 47.8% Fe, 25.6% Si O2 and 2.30%Al2O3 using selective magnetic coating was studied. Characterization studies of the low grade ore indicate that besides hematite and goethite,jasper, a microcrystalline form of quartzite, is the major impurity associated with this ore. Beneficiation by conventional magnetic separation technique could yield a magnetic concentrate containing 60.8% Fe with 51% Fe recovery. In order to enhance the recovery of the iron oxide minerals, fine magnetite, colloidal magnetite and oleate colloidal magnetite were used as the coating material. When subjected to magnetic separation, the coated ore produces an iron concentrate containing 60.2% Fe with an enhanced recovery of56%. The AFM studies indicate that the coagulation of hematite particles with the oleate colloidal magnetite facilitates the higher recovery of iron particles from the low grade BHJ iron ore under appropriate conditions.     

磁性聚硅酸铝锌-壳聚糖复合絮凝剂的制备及其絮凝性能研究

絮凝是常用的污水处理方法,将磁性粒子引入到絮凝剂中可以提高污水处理的性能和沉淀物的分离效率。以Fe3O4纳米粒子、硅酸钠、硫酸铝、硫酸锌、壳聚糖为原料制备出无机高分子磁性聚硅酸铝锌-壳聚糖（Fe3O4-PSAZn-CTS）复合絮凝剂,应用于以高岭土为原料制备的模拟水样。通过单因素试验优化了制备pH,Fe3O4投加量,铝和锌与硅的摩尔比,铝与锌的摩尔比,铝和锌与壳聚糖的质量比,确定了Fe3O4-PSAZn-CTS絮凝剂的最佳制备条件。通过对Fe3O4-PSAZn-CTS进行FTIR、XRD、TGA以及SEM分析测试,证明了Fe3O4-PSAZn-CTS是一种Fe3O4与PSAZn-CTS紧密结合,并且表面呈无定形化的新型磁性复合聚合物。接着,通过单因素实验优化了絮凝剂投加量,模拟水样的pH,絮凝后沉降时间,得到Fe3O4-PSAZn-CTS絮凝剂的最佳絮凝条件。最后,以最优条件处理吉林段松花江原水样,将其产生的絮凝物分离出来并进行烘干处理。向松花江原水样中投加50%烘干后的絮凝物和50%最佳投加量的初始絮凝剂进行磁性絮体重复利用实验,浊度去除率仍可达到95%以上。     

Magnetic and flotation studies of banded hematite quartzite （BHQ） ore for the production of pellet grade concentrate

To identify and establish beneficiation techniques for banded hematite quartzite (BHQ) iron ore, a comprehensive research on BHQ ore treatment was carried out. The BHQ ore was assayed as 38.9wt% Fe, 42.5wt% SiO2, and 1.0wt% Al2O3. In this ore, hematite and quartz are present as the major mineral phases where goethite, martite, and magnetite are present in small amounts. The liberation of hematite particles can be enhanced to about 82% by reducing the particle size to below 63 μm. The rejection of silica par...     

方铅精矿中脉石成分在Na2CO3熔盐中的 反应行为研究

为探究方铅精矿低温熔盐清洁冶金方法,在热力学分析的基础上,采用XRD分析技术,研究了方铅精矿中主要脉石成分SiO2、CaCO3、MgCO3、Al2O3等与Na2CO3熔盐的反应行为。研究结果表明:SiO2在温度高于1 173 K时会和Na2CO3反应生成Na2SiO3;CaCO3在温度高于923 K时会和Na2CO3结合成Na2Ca(CO3)2,但是其在温度高于1 123 K时又会发生分解;MgCO3在温度为873～1 123 K时会分解为MgO,但MgO不会和Na2CO3发生反应;Al2O3与Na2CO3在温度高于973 K时会发生反应,生成铝酸钠。为降低Na2CO3熔盐的消耗量,低温熔盐炼铅温度宜控制为1 073～1 173 K。     

MoP/TiO_2-SiO_2-Al_2O_3的制备及加氢脱芳性能研究

采用溶胶—凝胶法及共浸渍法制备了TiO2-SiO2-Al2O3复合载体,并用共浸渍法制备负载型MoP/TiO2-SiO2-Al2O3催化剂。XRD结果表明,TiO2的晶相衍射峰呈锐钛矿,SiO2则大多以无定型态分散于γ-Al2O3晶体表面。通过原位还原技术对催化剂进行还原处理,在连续固定床反应器上进行活性评价,结果表明,钛硅铝物质的量比对催化剂的活性有很大的影响,在温度为360℃,压力为3MPa,液时空速为1h-1,氢油体积比为500∶1的反应条件下,n（Ti）∶n（Si）∶n（Al）为1∶1∶4,Mo负载量为20%时,MoP/TiO2-SiO2-Al2O3催化剂的加氢脱芳活性最高,达到65.6%。并且TiO2-SiO2-Al2O3三元复合载体比传统的γ-Al2O3和SiO2-Al2O3二元复合载体的活性分别提高了19.6%和13.6%。     

丁二烯聚合铁催化体系FeCl_3-phen-Al(i-Bu)_3的紫外可见光谱

紫外可见光谱表明,phen能与Fe(Ⅲ)、Fe(Ⅱ)、Al(Ⅲ)形成稳定络合物,其电荷转移跃迁吸收峰分别在355、515和260mm处;在FeCl_3~-phen-Al(i-Bu)_3体系中,随Al/Fe摩尔比由小到大,Fe(Ⅲ)-phen络合物逐渐减少,而Fe(Ⅱ)-phen络合物逐渐增多;Al(Ⅲ)、Fe(Ⅲ)、Fe(n)之间有竞争phen配体的现象存在。     

微波辐射条件下SAPO-5分子筛的合成与表征

以异丙醇铝、磷酸、正硅酸乙酯为反应原料,三乙胺作为模版剂,功率800 W、180℃微波辐射30min合成了粒径均一、具有AFI拓扑结构的SAPO-5分子筛,系统研究了Al2O3与SiO2摩尔比和HF添加量等因素对产物长径比和晶体形貌的影响。采用XRD、SEM等分析手段对产物进行表征。结果表明,n(Al2O3)/n(SiO2)可以控制晶体尺寸的大小以及长径比,HF的存在影响晶体的成核及分散性。     

新型无机高分子絮凝剂—聚合硅酸铝的研制及应用

聚合硅酸铝是一类性能优良的无机高分子絮凝剂。以水玻璃,硫酸铝,硫酸为原料,通过考察不同ＰＨ值条件下硅酸溶液的胶凝时间,Ａｌ＾３＋与ＳｉＯ２摩尔比等因素对ＰＳＡＡ产品应用性能的影响,确定了ＰＳＡＡ的最佳合成条件为ＰＨ３－４,Ａｌ＾３＋与ＳｉＯ２摩尔比０．８－１．２,活化时间３０－５０ｍｉｎ。     

硅酸钠催化合成生物柴油

以硅酸钠(Na2SiO3)为催化剂,以餐饮废油和甲醇为原料合成生物柴油脂肪酸甲酯.通过实验考察了原料配比、催化剂用量、反应时间等因素对反应过程的影响.得到了较佳反应工艺条件:n(甲醇):n(废油酯)=6:1,Na2SiO3催化剂用量为餐饮废油和甲醇总质量的5%,反应温度<90℃,反应时间为6.0h,在该条件下餐饮废油的转化率达到97.8%.     

聚硅硫酸铁絮凝剂的研制

以Na2SiO2、H2SO4和Fe2(SO4)3为主要原料，采用复合共聚生产工艺，制备了聚硅硫酸铁絮凝剂（PFSS）。研究了pH值，SiO2含量，温度对硅酸聚合过程的影响，并考察了Fe^3 /SiO2摩尔比对PFSS稳定性和CODcr去除率的影响，结果表明，在最佳条件下合成的PFSS在脱色、CODcr去创造率方面比PFS和PAC效果更显，具有广阔的应用前景。     

聚硅硫酸铁混凝性能的试验研究

采用复合共聚生产工艺,以Ｆｅ２（ＳＯ４）３、Ｈ２ＳＯ４和Ｎａ２ＳｉＯ３为原料,制备聚合硅酸硫酸铁（ＰＦＳＳ）混凝剂。采用正交试验方法,研究了Ｆｅ＾３＋／ＳｉＯ２摩尔比、ｐＨ、加药量对混凝效果的影响,与聚合氯化铝（ＰＡＣ）对比试验结果表明：ＰＦＳＳ和ＰＡＣ具有更好的去浊的效果。     

化学沉淀-磁絮凝深度快速除磷的研究

采用化学沉淀法研究Al2（SO4）3、FeCl3、CaCl2的药剂用量和pH值对除磷效果的影响,探讨非磁性悬浮物磁性接种的机理,并分析了铝、铁、钙的磷酸盐沉淀物由于加入磁种而变得易于沉降,特别是在磁场力作用下沉降速度加快的原因。结果表明,Al2（SO4）3、FeCl3、CaCl2是磷酸根离子的有效沉淀剂,在适当的药剂投加量和pH值条件下,废水经过处理后,剩余磷的浓度小于0．5mg／L;生成的铝、铁、钙的磷酸盐沉淀物颗粒与Fe3O4颗粒在某一pH值下表面电性相反,易发生相互凝聚;磁性接种的铝、铁、钙的磷酸盐沉淀物不仅变得更重,而且在磁场中还受到与重力方向相同的磁场力作用。     

胶磷矿浮选中碱性联合调整剂

为了降低胶磷矿正浮选pH值调整剂碳酸钠的用量,同时又能有效调整矿浆的性质,改善浮选性能,以某磷矿为试验样品进行了氢氧化钠或氧化钙联合碳酸钠调整矿浆性质的浮选试验.结果表明,氢氧化钠与氧化钙单独作为调整剂时的浮选效果较差,配合碳酸钠作为调整剂,可以改善浮选效果;当使用氢氧化钠与碳酸钠比例1∶3用量4.0kg/t作为pH调整剂时的选矿指标精矿品位18.58%、回收率91.64%、选矿效率18.18%优于单独使用碳酸钠6~7.0kg/t时选矿指标,前者的药剂用量低,因此选矿过程中的药剂成本会有所降低.在工业生产中,可以使用碳酸钠配合氢氧化钠作为矿浆pH调整剂.     

赤泥-粉煤灰-矿渣碱激发胶凝材料性质的研究

以赤泥、粉煤灰、矿渣等工业废渣为主要原料制备碱激发胶凝材料,通过正交实验找出了赤泥、矿渣和粉煤灰的最佳配比。当赤泥与粉煤灰比例为3∶1、矿渣的掺量为40%、12%硅酸钠促硬剂为0.12A、减水剂为0.7%时,所制备的碱激发胶凝材料力学性能较好。用蒸压养护制度可得出性能最优的碱激发胶凝材料。赤泥-粉煤灰-矿渣碱激发胶凝材料具有一定的耐酸碱盐腐蚀性、耐高温性能和良好的抗冻性能;吸水率由高到低依次为:水泥、净浆试体、胶砂试体Ⅰ(灰砂比为2∶1)、胶砂试体Ⅱ(灰砂比为1∶1)。X-射线衍射分析表明:在碱激发胶凝材料中生成了大量的铝硅酸盐和钙硅酸盐的复合反应产物,如:莫来石(K2O.Na2O.H2O、Al6Si2O13)、托勃莫来石和C-S-H、C2-S-H凝胶产物等。该类材料不仅具有类似有机聚合物的完整岛状结构及链状结构,还能与矿物颗粒表面的[SiO4]4-和[AlO4]4-四面体通过脱烃基作用形成化学键;来源于原料中Ca(OH)2的C-S-H凝胶多生成于水泥水化的C-S-H凝胶孔隙之中,从而大大提高了结构密实度,是其获得高强度的直接原因。     

Al_2O_3对水玻璃砂高温溃散性作用机理的探讨

本文通过x光粉末衍射、扫描电子显微镜及差热分析对水玻璃砂不同温度下的反应、相变、结构、形貌进行研究。观察了随温度升高Al_2O_3在水玻璃砂中的行为。最终探讨了Al_2O_3对水玻璃砂高温溃散性的作用机理。