硅酸盐水泥—阳离子乳化沥青浆体的流变模型

硅酸盐水泥--乳化沥青浆体的流变性决定了水泥乳化沥青砂浆的施工性能,并影响高速铁路板式无砟轨道砂浆充填层的施工质量和耐久性。采用P·II52.5R硅酸盐水泥和阳离子乳化沥青制备了不同配合比的硅酸盐水泥--阳离子乳化沥青(PC-CEA)浆体。在25℃用同轴旋转流变仪测量各种PC-CEA浆体的流变曲线。用不同流变模型拟合实测的PC-CEA浆体的剪切应力和剪切应变数据,分析了其流变行为和组成配比的关系。结果表明:PC-CEA浆体具有屈服应力和触变性,并主要呈剪切变稀行为;依据拟合良好性,Herschel-Bulkley模型最适合表征PC-CEA浆体流变性;由该模型拟合获得的PC-CEA浆体的屈服应力和稠度系数随浆体中水泥占浆体总体积分数(水泥体积分数)增加而增加,随着浆体中水泥和沥青颗粒的体积分数(固体体积分数)的减小而减小;当固体体积分数≤40%时,PC-CEA浆体出现剪切增稠行为。     

可再分散乳化沥青粉末改性水泥砂浆的力学性能和微观形貌

为解决水泥基材料脆性大、韧性差问题,本文提出了掺加可再分散乳化沥青粉末（REAP）以改善水泥基材料韧性的方法。试验制备了REAP 掺量为胶凝材料用量0、10%、20%、30%的可再分散乳化沥青颗粒改性水泥砂浆（REAPMCM）,研究了REAP对REAPMCM抗压、抗折强度、折压比、弹性模量等力学性能影响,分析了其对水泥水化产物微观形貌影响,对比了其与采用乳化沥青制备水泥乳化沥青砂浆微观形貌。结果表明,随着REAP掺量增加,REAPMCM抗压、抗折强度与弹性模量均有所降低,折压比有所提高,REAP掺量30%的REAPMCM折压比为28.5%,其相比未掺加REAP砂浆的折压比提高了46.6%;掺入REAP改善了水泥基材料的韧性,但其改善效果随着水泥水化龄期增长而有所降低;随着REAP掺量增加,一方面浆体总孔隙率含量有所增大,另一方面水泥水化产物间填充覆盖的沥青膜面积增大,且其断面显微形貌与相同沥青固含量掺量的乳化沥青砂浆断面基本类似,证实了REAP亦可较好分散、成膜分布于水泥水化产物间,达到了其与乳化沥青乳浊液对水泥基材料改性相类似的使用效果。     

水泥沥青砂浆力学性能的温度敏感性

研究了不同温度条件下不同沥青含量的水泥沥青砂浆的抗压性能,以揭示该类有机–无机复合材料力学性能的温度敏感性规律。在–40～80℃范围内选择不同环境温度,采用电液伺服控制材料万能试验机测试了水泥沥青砂浆静态单轴抗压荷载下的应力–应变全曲线,获得了峰值应力和弹性模量随温度变化的基本规律。结果表明:随温度的降低,应力–应变曲线的上升段斜率增大,峰后下降段逐渐变陡,力学特性逐渐出现韧–脆转换。一般而言,水泥沥青砂浆的弹性模量和峰值应力随温度的升高和沥青含量的增大而降低,其温度敏感性随沥青含量的增大而增大。沥青含量较大的水泥沥青砂浆,其弹性模量和峰值应力随沥青含量变化幅度不大。建立的经验关系式成功描述了不同沥青含量的水泥沥青砂浆力学性能随温度变化的定量关系,且拟合结果表明以温感因子表征其力学性能对温度的敏感性具有一定的合理性。温感因子随着沥青含量的增大而增大,峰值应力的温感因子大于弹性模量的。     

预水化对水泥性能及水泥-聚羧酸系减水剂相互作用的影响（英文）

将新鲜的硅酸盐水泥暴露于(20±2)℃,相对湿度为85%~90%的环境中,研究了硅酸盐水泥因暴露于湿空气中产生预水化而对水泥标准稠度用水量、水泥水化行为、水泥胶砂强度以及水泥与聚羧酸系减水剂(PCE)间相互作用的影响。结果表明:随着暴露时间的增长,水泥预水化速率不断降低,标准稠度用水量则先轻微减小后显著增加,预水化4 d的水泥具有最小的标准稠度用水量;预水化作用总体上降低了水泥水化温峰值及水泥水化放热速率,但对于预水化作用不超过10 d的水泥。在其水化200~500 min期间,预水化水泥的水化放热速率随预水化时间的延长而增大,对于预水化10 d的水泥,其水化放热速率甚至一度高于新鲜水泥,这可能会导致预水化水泥的异常凝结。此外,预水化作用不利于胶砂强度的发展,且对抗折强度的不利影响尤为显著。预水化作用还会影响PCE的分散效果,随着预水化时间的延长,PCE的分散性及其分散保持性先增大后减小,对预水化4 d的水泥分散效果最佳,其初始流动度达到新鲜水泥的136%,且120 min后的浆体流动度仍高达235 mm。PCE对预水化20 d和30 d的水泥无分散效果。     

养生条件对乳化沥青冷再生混合料路用性能的影响

为探究养生条件对乳化沥青冷再生混合料路用性能的影响与其强度形成机理,研究了养生时间、养生温度、表面风速对乳化沥青冷再生混合料路用性能影响规律。研究结果显示：乳化沥青冷再生混合料的路用性能随着养生时间延长而提升,且在前6d提升较快;养生温度低于50℃时,随着养生温度升高,乳化沥青冷再生混合料的路用性能逐渐提高;养生温度超过50℃时,冷再生混合料路用性能有所降低;在相同养生温度及养生时间下,增大表面风速可以加快混合料上表面乳化沥青的破乳速率,小幅度提高混合料的路用性能;在乳化沥青破乳结束后,由于沥青对集料的粘结作用与水泥水化产物强度的形成,乳化沥青冷再生混合料的强度也逐渐形成。     

锂渣掺量对水泥-减水剂浆体流变特性和混凝土性能的影响

本文研究了锂渣掺量对水泥-减水剂浆体流变特性、新拌混凝土工作性及硬化混凝土强度的影响。从紧密堆积理论和固体颗粒体积分数角度解释了锂渣掺量对水泥-减水剂浆体流变性能的影响。结果表明：锂渣水化初始的屈服应力和塑性黏度均随锂渣掺量的增加而增大，流变性能劣化。新拌混凝土的工作性与锂渣掺量呈负相关；随锂渣掺量的增加，7 d抗压强度不断降低，28 d抗压强度呈现出先增后降的趋势。     

速凝剂与石灰石粉对水泥浆体性能的影响

通过不同掺量的速凝剂和石灰石粉对水泥浆体凝结时间、流动度、粘度、胶砂强度和水化进程的影响研究,探讨速凝剂与石灰石粉共同作用下对水泥浆体性能的影响。结果表明:石灰石粉能够提高水泥净浆的流动度和粘度,并且其流动度和粘度损失随着石灰石粉掺量的增加而增大。速凝剂掺量为5%时,石灰石粉掺量为5%,水泥的凝结时间进一步缩短,水泥胶砂3 d、7 d和28 d的抗压强度略有提高,当石灰石粉超过5%时,水泥的凝结时间随着石灰石粉掺量的增加反而延长,水泥的胶砂抗折、抗压强度随着石灰石粉掺量的增加而降低。水泥水化初始期和加速期的水化放热速率随着速凝剂掺量的增加而增加,掺加速凝剂后,水化加速期提前10 h,同时石灰石粉也能够提高水泥水化初始期和加速期的水化放热速率。掺加速凝剂后,水泥水化放热量反而降低了一半,但是加入石灰石粉后,水泥水化放热量增加。     

钢渣粉对MKPC浆体的改性作用试验研究

为了调查钢渣粉对磷酸钾镁水泥浆体的改性作用,测试了含不同量钢渣粉的磷酸钾镁水泥(MKPC)浆体的流动度、抗压强度、干缩率和水化温度,分析了MKPC浆体的物相组成和微观形貌.结果表明:钢渣等量替代MgO粉10％～20％,能使碱组份粉体的颗粒级配更合理,进而改善了新拌MKPC浆体的流动性.含10％～20％钢渣粉的MKPC浆体试件的5 h抗压强度提高5％～17％、1 d抗压强度提高不小于30％.含20％钢渣粉的MKPC试件的收缩变形仅为MKPC试件参考样收缩变形的60％.适量钢渣粉等量替代MgO粉,MKPC浆体中有效碱组份总量降低,造成MKPC浆体的早期水化程度降低.由于钢渣粉中的部分活性元素参与了水化反应,MKPC硬化体中出现了Ca2P2O7·3H2O、Ca2Al2Si2O8·4H2O和Fe3(PO4)2·H2O等新物相,钢渣粉中Ca、Fe、Al和Si元素渗入磷酸盐水化产物中,使水化产物的形貌变化较大,MKPC硬化体结构趋于致密.     

温度对水泥沥青砂浆力学性能影响程度试验研究

为研究不同温度下配比不同的水泥沥青砂浆的力学性能,采用电液伺服万能试验机测试了不同温度下水泥沥青砂浆静态单轴抗压下的应力-应变关系,获得了弹性模量和最大应力随温度的变化规律.试验结果表明:随着温度的降低,应力-应变曲线的上升斜率变大,出现最大值后下降段逐渐变陡;水泥沥青砂浆的弹性模量与最大应力值随沥青含量和温度的增大而降低,其温度敏感性主要由沥青含量决定.联系试验结果,建立了可定量分析水泥沥青砂浆力学性能随温度变化的本构关系,且拟合结果显示用温感因子描述其力学性能的温度敏感性有较高的合理性,随着沥青含量的增高,温感因子数值增大,最大应力所对应的温感因子大于弹性模量的.     

循环流化床粉煤灰对矸石胶结充填材料性能的影响

为充分利用循环流化床粉煤灰(CFA),应用CFA制备矸石胶结充填材料.考察了粉煤灰-水泥体系的净浆流动度、流变特性和自由膨胀率随CFA掺量的变化规律,以及CFA对充填材料工作性和力学性能的影响规律,探讨应用CFA制备充填材料的可行性.结果 表明:粉煤灰-水泥体系复合浆体的流变模型仍为Bingham流体模型,而随着CFA掺量增大,塑性粘度增大,流动度降低,浆体流动性变差.掺加0％ ～ 60％的CFA,能够制备出性能良好的充填材料.在CFA掺量低于60％时,新拌浆体的坍落度、扩展度、含气量降低幅度较小,泌水情况减少,充填材料工作性可完全满足工程设计;新拌浆体硬化后孔隙率更低,力学性能良好.应用CFA制备充填材料具备可行性.     

氢气纯度分析方法准确性的探讨

ONACCURACYOFANALYSISOFOFHYDROGEN1前言我公司目前应用的氢气纯度分析方法有两种,一种是爆炸反应法,另一种是焦性没食子酸吸收法。几年来,人们对两种分析方法的准确性曾有过褒贬不一的评论。这里我们也谈谈自己粗浅的观点。2爆炸法测定氢气纯度一定量的氢气样品与适量的空气之均匀混合物因反应后生成液体水而引起气体体积减少,减少的体积等于参加反应气体体积之和。其中l／3为氧气,2／3为氢气。根据氢气取样量和反应前后混气体体积之差,以及氢气在反应中的体积比例关系,可计算出样品的氢气纯度。计算公式式中：A一混…     

COMPARISON OF METHODS OF ANALYSIS OF GYPSUM1

The different analytical methods proposed for the evaluation of gypsum have been subjected to an experimental test. A combination method, consisting of a fusion with KHCO₃ and determination of CaO by KMnO₄ titration, the SO₃ by Andrews method of titration of BaCrO₄ has been found to give very reliable results with the least consumption of time.     

SEDIMENTATION OF BINARY MIXTURES OF PARTICLES OF UNEQUAL DENSITIES AND OF DIFFERENT SIZES

A model is developed for the sedimentation from a suspension of two particle species of unequal densities and of different sizes. The composition and the thickness of various layers in the sediments are predicted using graphical and analytical methods. The model predictions were in excellent agreement with experimental results, when the particle size ratio was ≥ 108. When size ratio of the particles was 2.60 and 4.31 the agreement occurred in about 50 percent of the cases.     

HEASUREHENT OF INSTANTANEOUS RATES OF LOSS OF VOIATILE COMPOUNDS DURING DRYING OF DROPS

A novel technique serves to monitor instantaneous rates of loss of a volatile solute from a suspended drop during drying. A highly sensitive electron capture detector is used to monitor concentrations of SF6 released into a flowing gas stream from a suspended, drying drop. Simultaneously, the appearance and morphological development of the drop are monitored with a video camera. This provides the wherewithal of relating instantaneous rates of loss of the volatile solute to particular events during the development of particle morphology.

Initial experiments have been carried out with drops of aqueous solutions of glucose, sucrose, maltodextrin and coffee extract. The results clearly display the onset of the volatiles-retentive selective diffusion phenomenon. There is also substantial loss of the volatile component later in the drying process, when the drops undergo repeated ex ansion, bursting and cratering due to the formation of internaf bubbles. These experiments appear to be the first quantitative demonstration of major losses accompanying changes in drop morphology.     

茶多酚提取方法进展

本文综述了国内外现有茶多酚提取方法的现状以及近期的研究进展，并对其优缺点进行了评价。这将有助于中低档茶的综合利用和茶多酚的进一步开发应用。     

ANALYSIS OF RECENT MEASUREMENTS OF THE VISCOSITY OF GLASSES

Viscosity of Simple Soda-Silicate 500° to 1400°C Comparison of the results given by English with those of Washburn, Shelton and Libman, indicates a discrepancy in the absolute values of log₁₀ viscosity amounting to 0.6, those of Washburn et al., being relatively too high. If correction for this is made, the isothermal curves of log₁₀ viscosity as a function of soda content are smooth up to 50% Na₂O, showing no inflection. The observations as a function of temperature T are all represented within accidental error by an equation of the type where all three constants vary regularly with the composition. Change of Viscosity of Glass (6SiO₂, 2Na₂O) due to Molecular Substitution of CaO, MgO and Al₂O₃ for Na₂O The effect is clearly brought out by plotting (from the results of English) the change of log₁₀η due to the substitution as a function of temperature. The curves each show a sharp bend at a temperature between 840° and 1050°C, which is designated the aggregation temperature T_a. If we divide these curves by the corresponding percentage substituted, we get curves for each oxide which are straight and parallel below the aggregation temperatures, the slopes (increase of change of log₁₀η per 100°C) being −0.056 (CaO), −0.055 (MgO), −0.018 (A1₂O₃) per per cent oxide substituted. For substitution of 1/2 molecule the slopes are −0.325 (CaO), −0.23 (MgO) and −0.18 (Al₂O₃) per 100°. At the aggregation temperature the change of log₁₀η per per cent is a minimum, 0.03 to 0.06 for CaO, 0.12 for MgO, 0.07 for Al₂O₃. Evidence of Aggregation in Glasses, from viscosity Measurements The sharp bends in the plots of change of log₁₀η due to substitution of an oxide for Na₂O, suggest the beginning of molecular aggregation at these temperatures. These aggregation temperatures are close to the devitrification temperatures, but the effect on the viscosity curves cannot be due to actual devitrification since it does not change with time. Taking the aggregation temperatures as equal to devitrification temperatures, additional isotherms are roughly sketched into the equilibrium triangle of the system Na₂O-CaO-SiO₂. Change of Viscosity of Glass (4SiO₂, 2Na₂O) due to of Substitution of B₂O₃ for SiO₂ The change of log₁₀η (from the results of English) is plotted as a function of temperature, and also the change of log₁₀η per per cent B₂O₃. The curves are more complex than for the substitution for Na₂O.     

环氧树脂羟基值测定方法的研究

利用乙酸酐、吡啶和浓硫酸混合的乙酰化试剂测定环氧树脂中羟基值含量的方法具有操作简便、滴定终点明显和分析结果误差小等优点。     

骑式摩托车油箱喷涂工艺的改进

面对日益激烈的市场竞争,摩托车油箱外观质量越来越成为影响销售的因素之一。文章介绍了改进工艺后的油箱涂装,该涂装体系提高了油箱外观的丰满度,降低了油箱涂装的生产成本。     

几种针状焦性能对比

针状焦分石油系和煤系两大类,这主要取决于针状焦的原料来源。在同一系列中由于原料不同和工艺条件不同 ,针状焦的各自性能也不相同。针状焦是生产超高功率石墨电极和高功率石墨电极的主要原料 ,针状焦的性能对石墨电极的质量有至关重要的影响。所以对针状焦性能以及其对石墨电极质量影响的研究十分必要的。以下是常用的几种进口针状焦和国产针状焦的性能对比。１原料性能分析对比原料试样包括４种针状焦 ,其中两种为进口针状焦：三菱针状焦和新日化针状焦;另两种为国产针状焦：鞍山针状焦和锦州针状焦。其中除锦州针状焦是石油系针状焦外…     

聚酰亚胺的合成法

本文评述了缩聚型聚酰亚胺的主要合成方法和近年来国际上在合成中所做的探索。