为探究水泥、石英砂、重质硅酸钙的用量对聚合物水泥防水涂料力学性能的影响,分别制备了不同水泥用量、不同石英砂用量、不同重质硅酸钙用量聚合物水泥防水涂料,将其成型为涂膜,测定了涂膜的拉伸性能。随着水泥、重质硅酸钙用量的增加,涂膜的拉伸强度逐渐增加,断裂伸长率逐渐降低;随着石英砂用量的增加,涂膜的拉伸强度逐渐降低,断裂伸长率逐渐升高。结果表明,当液料配比为m(丙烯酸乳液)∶m(消泡剂)∶m(杀菌剂)=100∶0.5∶0.5时,液料、水泥、石英砂、重质硅酸钙的用量分别为100份、40份、25份、30份时,制备的聚合物水泥防水涂料拉伸性能最佳。     

JS防水涂料拉伸性能检测的主要影响因素

为研究涂覆次数、养护时间对聚合物水泥防水涂料检测结果的影响,分别制备了1次涂覆、2次涂覆、3次涂覆、4次涂覆和养护时间7 d、养护时间14 d、养护时间21 d的聚合物水泥防水涂膜,并分别对其进行拉伸性能测试。随着涂覆次数的增加,拉伸强度和断裂伸长率逐渐升高,当达到4次涂覆时升高趋势开始缓和;随着养护天数从7 d增加到14 d,拉伸强度显著升高,断裂伸长率显著降低,养护天数从14 d增加到21 d,拉伸强度和断裂伸长率则无明显变化。结果表明,聚合物水泥防水涂料检测时涂覆3次,养护14 d最能体现材料的拉伸性能。     

金属屋面丙烯酸高弹防水涂料的性能研究

探讨了丙烯酸乳液用量、粉体填料粒径以及氧化锌用量对金属屋面丙烯酸防水涂料涂膜断裂伸长率、拉伸强度及撕裂强度的影响,结果表明,乳液含量的增加有利于提高涂膜拉伸强度、断裂伸长率以及撕裂强度;随着填料粒径越小,涂膜的断裂伸长率和撕裂强度越大;氧化锌的用量增加,涂膜的撕裂强度也增大。     

添加剂对聚合物水泥防水涂料性能的影响

聚合物水泥防水涂料是一种以水为溶剂的环境友好型防水涂料,主要探讨各种添加剂对聚合物水泥防水涂料涂膜拉伸强度和断裂伸长率的影响。结果表明:在聚合物水泥防水涂料中添加占乳液质量4.5%成膜助剂、0.25%分散剂A、0.3%分散剂B、1.0%防水剂和2.5%增塑剂制得的防水涂料涂膜拉伸强度为1.96 MPa,断裂伸长率为271.22%。     

填料对聚合物水泥防水涂料力学性能的影响

简要介绍了JS防水涂料的成膜机理,并详细讨论了填料种类、目数、水泥用量等因素对JS防水涂膜拉伸强度和断裂伸长率的影响.指出在本研究范围内,在选用丙烯酸乳液A的情况下,白水泥用量为35％,400目重质碳酸钙用量为35％,200目石英粉用量为30％,制得的JS防水涂膜的力学性能及耐水性能最优.     

聚合物水泥防水涂料的研制及液粉比对其性能的影响研究

以苯乙烯-丙烯酸酯共聚物胶乳为聚合物基体液料,以硫铝水泥、高铝水泥及其他惰性填料为粉料制备了JS防水涂料,并探究了液粉比对JS防水涂料凝结时间、力学性能、粘结强度及防水性能的影响。结果表明:对于JS防水涂料,粉料的增加大幅度缩短了涂料的表干时间与实干时间,涂膜的拉伸强度得到不同程度的增强,断裂伸长率呈现降低趋势,涂膜的粘结强度和抗渗性能均得到提高,而防水性能逐步降低。     

聚合物水泥防水涂料耐水性能影响因素研究

研究了聚合物乳液种类、聚合物乳液T_g值、水泥用量、填料种类和硅烷偶联剂用量对Ⅱ型JS防水涂料浸水后拉伸强度保持率、断裂伸长率和吸水率等指标的影响,结果表明,随着浸水时间的延长,JS防水涂料的拉伸强度、断裂伸长率都有不同程度的下降;选用T_g值为-15.3℃的丁苯乳液,水泥用量为50%,填料选用重钙,适量添加硅烷偶联剂制得的JS防水涂料耐水性能较佳。     

聚合物水泥防水涂料拉伸性能影响因素的探讨

探讨了不同的聚合物乳液、乳液用量、液粉比、水泥种类、水泥用量以及不同级配填料等因素对聚合物水泥防水涂料拉伸性能的影响。结果表明,按照m(乳液)∶m(消泡剂)∶m(杀菌剂)∶m(水)=80∶0.5∶0.5∶20的配比制备液料,m(水泥)∶m(石英砂)∶m(增稠剂)=100∶100∶0.2的配比制备粉料,按液粉比为1∶2制备的聚合物水泥防水涂料拉伸强度和断裂伸长率满足GB 23445—2009中Ⅱ型产品的要求。     

聚碳酸酯二醇型高强聚氨酯防水涂料的制备

以聚碳酸酯二醇和聚醚多元醇为主要原料,一步法合成单组份高强聚氨酯防水涂料。研究表明,随着聚碳酸酯二醇用量的增加,其拉伸强度、撕裂强度、耐磨性、耐紫外老化性能以及与水泥块的粘接性能均得到不同程度的提高,但断裂伸长率降低。涂膜经检测,其拉伸强度为4~12 MPa,断裂伸长率200%~800%,撕裂强度14~60 N/mm,粘接强度1.0~4.0 MPa。     

重质碳酸钙对丙烯酸酯乳液改性乳化沥青防水涂料性能的影响

研究探讨了重质碳酸钙的掺入对丙烯酸酯乳液改性乳化沥青防水涂料性能的影响。结果表明,当重质碳酸钙的含量不超过临界填料体积浓度(CPVC)时,涂料的拉伸强度、断裂伸长率、黏度及施工应用性能均明显增加,但低温性能受其影响较小;当重质碳酸钙的含量超过CPVC时,涂料的拉伸强度与断裂伸长率骤降,黏度剧增,低温柔性也会出现较大幅度的衰减。     

Effects of the law reforming public works contracts on the Italian building process

The Italian construction industry was rocked by the scandals regarding procurement by the public sector during the early 1990s. Although not confined to construction, the role of the state in construction demand meant that it was one of the most heavily implicated sectors. Known as 'tangentopoli', the scandals have prompted a major reform of public sector procurement in the Italian industry which, combined with changes required to conform with EU directives, is leading to a profound cultural change in the industry. This paper provides an authoritative review of the changes in the procurement codes and the roles and relationships within the construction industry. It shows how the project management of public sector programmes is being strengthened, and how the procurement of the design and construction processes is being separated to provide greater transparency in the process. Although it is too soon to tell what the actual impact of these changes will be upon construction industry practice, some suggestions are made in the concluding comments. En Italie, le secteur de la construction a ete secoue par les scandales concernant les approvisionnements par le secteur public au debut des annees 1990. Bien que n'etant pas limitee a la construction, la part de l'Etat dans la demande pour les travaux de construction temoignait que c'etait bien l'un des secteurs les plus impliques. Connus sous l'appellation de 'tangentopoli', ces scandales ont declenche une vague de reformes qui a touche les approvisionnements par le secteur public qui, combines aux changements necessaires pour se conformer aux directives de l'UE, conduisent a un profond changement culturel de cette industrie. La presente communication constitue une etude documentee des changements qui affectent les codes d'approvisionnement ainsi que les roles et les relations qui s'etablissent au sein de l'industrie de la construction. Elle montre comment la gestion de projets, lorsqu'il s'agit de programmes du secteur public, se trouve renforcee et comment la fourniture de prestations d'etudes et de travaux de construction joue en faveur d'une plus grande transparence du procede. Bien qu'il soit trop tot pour dire quel impact auront ces changements sur les pratiques dans le secteur de la construction, l'auteur conclut en faisant certaines recommandations.