三电极高速CO2双边角焊工艺参数对焊缝成形影响

在传统双电极角焊焊接工艺基础上,为了进一步提高焊接效率,采用三电极高速CO2双边角焊工艺,分析不同焊接工艺参数对焊缝成形参数的影响.结果表明,采用不同极性组合的焊缝成形参数差别不大;随着速度的减慢和焊接工艺参数的增大,脚长、熔深和熔宽均呈增大趋势,但焊脚长度有一个最大值限制.下脚长、上脚长受中间焊枪的指向位置影响更为明显,当左右两侧焊枪对中时,脚长最小.另外,随着焊丝之间距离的增大,脚长和熔宽逐渐减小,余高随焊丝距离增大而增大,但差别不大.     

三丝CO2双边角焊全因子试验设计

影响三丝高速CO2双边角焊焊缝成形参数的因素众多,在试验中应集中在影响较大的焊接参数研究.文中以影响其主要的两个焊接参数,即焊接功率和焊接速度为研究对象,建立两因素三水平的全因子工艺试验设计,分析焊接参数对焊缝成形参数的影响.结果表明,下脚长、上脚长和焊缝凸度均受焊接功率和焊接速度的主效应影响,而与交叉效应无关.上脚长的预测范围大约为4mm,下脚长的预测范围大约为2.5mm,而焊缝凸度的预测范围大约为2.5 mm.     

三电极高速CO2双边角焊质量及稳定性分析

对三电极高速CO2双边角焊焊接工艺进行研究,通过LabVIEW电信号采集与高速摄影分析了焊接质量及过程稳定性.结果表明,焊接中引导电流应为最大,且引导焊枪与中间焊枪之间电流差距100A左右可获得理想的焊缝成形,中间焊枪与跟随焊枪的电流差距大小对焊接质量无明显影响,且焊枪指向位置在底板为宜.在同一工艺时,随着焊接速度增大,焊接过程变得不稳定,同一焊接速度时,试验电流400/300/300A组合时焊接过程最稳定.大电流组合时,应增大焊丝之间距离以减小电弧之间的干扰.     

三电极高速CO_2焊焊接速度和焊接电流对焊缝成形影响

MAG角焊焊接在大型船舶制造中占有重要地位,目前应用最为广泛的是双电极角焊工艺,最大焊接速度为1.2m/min.为了提高焊接速度,进而提高焊接效率,研究了焊接速度可达1.8m/min的三电极高速CO2气保护角焊工艺.实验表明:采用DCEP/DCEN/DCEP极性组合的三电极CO2气保护角焊焊接过程稳定,成形良好,角焊焊缝上脚长、下脚长以及熔深均随着焊接速度的增大而减小,随着三电极焊接电流规范组合的增大而增大.在试验基础上,给出了焊接速度和三电极电流规范组合影响下的角焊缝脚长范围预测.     

高速CO2焊接中的熔池稳定性及焊缝成形

应用具有自由表面的流体稳定性理论,解释了高焊接时地道的产生机理,并通过对熔池形成过程的产时图像采集对该理论进行了验证。理论分析和试验结果均表明,采用自由过渡的熔滴过渡形式进行焊接,工件始终处于焊接电弧的加热下,在高速焊接时,熔池不能及时却,熔池明显拉长,由扰动引起的振动波长大,当熔池的拉长达到一定程度时,会发生液体金属的失稳和颈缩的现象,造成它峰焊道。在此基础上提出,可以采用短路过渡代替高电压下的     

摆焊参数对焊缝成形的影响分析

采用摆焊工艺对3 mm厚的普通低碳钢进行了焊接,并对摆焊参数的改变对焊缝成形的影响进行了研究,在此基础上设计并实施了3组不同焊缝宽度的宽焊缝焊接试验。 结果表明,摆动模式对焊缝形状的影响不明显,随着周期摆动长度的增大,焊缝在水平方向上的间隙逐渐增大,适当增大周期摆动宽度可增大焊缝宽度,摆动停顿距离应控制在4 mm以内,否则会出现焊缝塌陷现象。所设计的3组宽焊缝焊接参数,其焊缝成形良好,未见焊缝塌陷、层间未熔合和咬边现象发生,满足宽焊缝焊接要求。     

旋转电弧CO2焊接焊缝成形的敏感度分析

在焊接生产中经常遇到需要进行全位置焊接的场合,采用旋转电弧焊接可获得美观的焊缝成形。旋转电弧CO2焊接的参数众多,而且参数组合对焊缝成形的影响很大。在此对旋转电弧实心焊丝CO2仰焊的焊缝成形与焊接参数的关系进行研究,采用敏感度分析技术,研究焊接参数对熔深和熔宽的影响。研究结果表明,旋转直径和焊接速度对熔宽的敏感度的绝对值最大,说明可以通过调节旋转直径和焊接速度来改变熔宽;增大旋转直径和减小焊接速度,熔宽明显增加。旋转频率越高,导电嘴至工件距离(CTWD)越大,则焊缝熔宽越窄。本研究结果对旋转电弧仰焊工艺参数的制定有指导作用。     

基于图像过渡区的CO2气体保护焊焊缝识别算法

利用过渡区图像分割技术实现CO2气体保护焊焊缝的识别.采集到的焊缝图像在目标区和背景区存在过渡区域,在直方图上表现为双峰之间的谷比较宽广且平坦.通过对原始图像进行高端剪切和低端剪切变换,利用不同灰度像素的梯度信息来确定过渡区,进而利用过渡区来确定图像分割的阈值.克服了图像中非目标区域的影响,可以抗噪声和干扰.算法简单,实时跟踪性也较好.结果表明,该方法边缘检测效果良好,是一种比较适合CO2气体保护焊焊缝识别的方法.     

工艺参数对机器人TIG焊焊缝成形与组织的影响

在Q235钢平板上进行机器人TIG焊试验,研究焊接电流、电弧电压和焊接速度3个焊接工艺参数对焊缝成形与微观组织的影响。研究结果表明,当其中两个焊接工艺参数恒定时,熔深、熔宽和深宽比均随着焊接电流的增大而明显增大;焊缝的熔深和深宽比随着电弧电压的增大而减小,熔宽随着电弧电压的增大而增大;熔深、熔宽和深宽比均随着焊接速度的增大而减小。随着焊接速度的增大,焊缝区与热影响区的珠光体组织减少,铁素体组织增加,组织细化。     

激光焊工艺参数对马氏体不锈钢焊缝成形与组织的影响

以0Cr13Ni5Mo钢作为母材,研究激光功率、焊接速度和离焦量等激光焊工艺参数对焊缝成形与组织的影响。研究结果表明,当其中2个焊接工艺参数恒定时,熔深、熔宽和深宽比均随着激光功率的增大而明显增大,焊缝的熔深、熔宽和深宽比分别增加了约8倍、2倍、2倍;焊缝的熔深和熔宽随着焊接速度的增大而降低;熔深和深宽比均随着离焦量的适当降低而增加。随着激光功率的增大,焊缝的板条马氏体变得粗大。     

Evaluation model for arc fluctuations of triple-electrode high speed fillet welding

To improve the welding efficiency of conventional arc welding, triple-electrode fillet welding was proposed and developed. Stability of triple-electrode fillet welding process is the assurance for ideal joint. The evaluation model for arc fluctuations of triple-electrode fillet welding was established based on the characteristic parameters and their variation coefficients. This model indicated that variation coefficients could reflect arc voltage flnctuations of welding process, and its analysis result was consistent with the actual welding process.     

Analysis on the stability of the single weld pool formed during the triple-electrode high speed CO2 welding

The pinch instability theory with free surface and wave superposition principle was applied to understanding the critical disturbance wavelength and the theoretical bead width for the single weld pool formed during the triple-electrode high speed CO2 welding.In addition,the reason for higher stability in the single weld pool was analyzed.Then single-,twin-,and triple-electrode overlaying experiments were conducted,it was found that triple-electrode CO2 welding can improve welding efficiency greatly without reducing the weld quality.The results indicated that the oscillation frequency of the weld pool increased,oscillation wavelength decreased,and bead width increased with the increase of welding electrodes under the same disturbance circumstances.     

工艺参数对304不锈钢脉冲Nd∶YAG激光/TIG电弧复合焊焊缝成形的影响

研究了304不锈钢脉冲Nd:YAG激光TIG电弧复合热源焊接工艺参数对焊缝成形的影响.结果表明,脉冲Nd:YAG激光/TIG电弧复合焊焊缝横截面面积大于单一激光焊焊缝横截面面积与单一TIG焊焊缝横截面面积之和,具有协同效应;激光功率增大时,复合焊焊缝熔深和熔宽均增大,复合焊焊缝横截面面积增大,复合热源热效率也增大;离焦...     

焊接工艺对压铸镁合金CO2激光焊缝气孔率的影响

研究了激光功率和焊接速度等焊接工艺参数对两种不同含气量的压铸镁合金激光焊气孔倾向(以气孔率为表征)的影响规律,并对气孔的防止措施进行了探索.结果表明,含气量较高的2 mm厚压铸镁合金激光焊气孔倾向大于含气量较低的5 mm厚压铸镁合金.两种厚度的压铸镁合金激光焊缝气孔率总体上均随着激光功率的升高及焊接速度的降低而升高.对...     

焊接工艺参数对镁合金CO2激光焊焊缝表面成形的影响

探讨了焊接工艺参数包括激光功率、焊接速度、正面和背面的保护气体流量对焊接工艺效果和接头成形的影响.结果表明,对AZ61和AZ31两种镁合金,激光功率的增大,焊缝正面和背面的熔宽都明显增大;而焊接速度的增大,焊缝正面和背面的熔宽明显减小.在同样的工艺参数情况下,AZ61的熔化效率比AZ31更高,获得的焊缝正面和背面熔宽更大.正面的保护气体流量大小对焊缝熔宽的影响较小,而背面保护气体流量对焊缝熔宽基本没有影响,但正面和背面气体流量主要影响到焊缝正反面的保护效果,影响到焊缝的表观.试验结果表明,在适当的工艺参数下,采用CO2激光焊接方法可以较好地实现不同厚度的AZ61和AZ31镁合金的焊接,而且焊缝成形良好,接头的力学性能优良.     

CO_2激光-MAG电弧复合焊接工艺参数的优化

采用汉诺威分析仪和高速摄像机采集了CO2激光-MAG电弧复合焊接过程中的电信号和熔滴过渡图像,研究了焊接电流、电弧电压、激光功率等参数对复合焊接瞬时电压和电流信号、电压和电流概率密度分布、熔滴过渡特征和工艺稳定性的影响.结果表明,将汉诺威分析仪和高速相机相结合能提供丰富的焊接电弧物理指数和熔滴过渡形态信息,可为复合焊接...     

铝合金激光-电弧双面焊接头特征分析

采用激光-电弧双面焊工艺进行铝合金焊接试验,发现该工艺不仅可以获得稳定可靠的焊接过程与美观的焊缝成形,还可以有效地增加接头熔深和降低焊接成本。主要研究了焊接参数对双面焊接头特征的影响。结果表明,激光功率增加时,双面焊两侧的熔宽都以同样的趋势增大;焊接电流增大时,电弧侧熔宽的增加趋势明显大于激光侧;增加激光功率或提高焊接电流都会引起焊缝最小熔宽的增大,且焊缝最小熔宽的深度也发生一定的变化。随焊接速度的提高,激光侧的深宽比增加,而电弧侧的深宽比减小。