Rheology,crystallization behaviors,and thermal stabilities of poly(butylene succinate)/pristine multiwalled carbon nanotube composites obtained by melt compounding

Poly(butylene succinate) (PBS)/pristine raw multiwalled carbon nanotube (MWCNT) composites were prepared in this work via simple melt compounding. Morphological observations indicated that the MWCNTs were well dispersed in the PBS matrix. Moreover, the incorporation of MWCNTs did not affect the crystal form of PBS as measured by wide‐angle X‐ray diffraction. The rheology, crystallization behaviors, and thermal stabilities of PBS/MWCNT composites were studied in detail. Compared with neat PBS, the incorporation of MWCNTs into the matrix led to higher complex viscosities (|η*|), storage modulus (G′), loss modulus (G″), shear thinning behaviors, and lower damping factor (tan δ) at low frequency range, and shifted the PBS/MWCNT composites from liquid‐like to solid‐like, which affected the crystallization behaviors and thermal stabilities of PBS. The presence of a very small quantity of MWCNTs had a significant heterogeneous‐nucleation effect on the crystallization of PBS, resulting in the enhancement of crystallization temperature, i.e., with the addition of 0.5 wt % MWCNTs, the values of T_c of PBS/MWCNT composites could attain to 90°C, about 6°C higher than that of neat PBS, whereas the values of T_c increased slightly with further increasing the MWCNTs content. The thermogravimetric analysis illustrated that the thermal stability of PBS was improved with the addition of MWCNTs compared with that of neat PBS. © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2011     

Multiwalled carbon nanotubes‐based polypropylene composites: Influence of interfacial interaction on the crystallization behavior of polypropylene

Composites of polypropylene (PP) and multi‐walled carbon nanotubes (MWCNTs) were prepared via melt‐mixing utilizing Li‐salt of 6‐amino heaxanoic acid (Li‐AHA) modified MWCNTs in the presence of a compatibilizer (polypropylene‐g‐maleic anhydride; PP‐g‐MA). Improved interaction between the anhydride group of PP‐g‐MA and the amine functionality of Li‐AHA was confirmed via FTIR and Raman spectroscopic analysis. A higher glass transition temperature (T_g) of the PP phase has been observed in these composites as compared to pristine MWCNTs‐based composites. The crystallization temperature (T_c) of the PP phase was increased as a function of pristine MWCNTs concentration in PP/MWCNTs composites indicating hetero‐nucleating action of MWCNTs. However, T_c value was decreased in the presence of Li‐AHA modified MWCNTs indicating the adsorbed Li‐AHA on the MWCNTs surface. Moreover, T_c value was higher in the presence of Li‐AHA modified MWCNTs with PP‐g‐MA as compared to that of without PP‐g‐MA, suggesting the desorbed Li‐AHA from the MWCNTs surface due to melt‐interfacial reaction. Further, MWCNTs were extracted by hot vacuum filtration technique from PP/MWCNTs composites containing Li‐AHA and PP‐g‐MA. The isothermal crystallization kinetics showed a variation in crystallization behavior of the PP phase in the corresponding composites as compared to the “extracted MWCNTs.” POLYM. ENG. SCI., 57:183–196, 2017. © 2016 Society of Plastics Engineers     

Hybrid composites of ABS with carbonaceous fillers for electromagnetic shielding applications

This work evaluates the influence of two types of carbonaceous fillers, carbon black (CB) and carbon nanotubes (CNTs), on the electrical, electromagnetic, and rheological properties of composites based on poly(acrylonitrile‐co‐butadiene‐co‐styrene) (ABS) prepared by the melt mixing. Electrical conductivity, electromagnetic shielding efficiency (EMI SE) in the X‐band frequency range (8–12.4 GHz), and melt flow index (MFI) results showed that ABS/CNT composites exhibit higher electrical conductivity and EMI SE, but lower MFI when compared to ABS/CB composites. The electrical conductivity of the binary composites showed an increase of around 16 orders of magnitude, when compared to neat ABS, for both fillers. Binary composites with 5 and 15 wt % of filler showed an EMI SE of, respectively, ?44 and ?83 dB for ABS/CNT, and ?9 and ?34 dB for ABS/CB. MFI for binary composites with 5 wt % were 15.45 and 0.55 g/10 min for CB and CNT, respectively. Hybrid composites ABS/CNT.CB with 3 wt % total filler and fraction 50:50 and 75:25 showed good correlation between EMI SE and MFI. © 2018 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2018 , 135, 46546.     

Effect of carbon nanotube on PA6/ECO composites: Morphology development,rheological, and thermal properties

Thermoplastic elastomer (TPE) nanocomposites based on polyamide‐6 (PA6)/poly(epichlorohydrin‐co‐ethylene oxide) (ECO)/multiwall carbon nanotube (MWCNTs) were prepared by melt compounding process. Different weight ratios of ECO (20, 40, and 60 wt %) and two kinds of functionalized and non‐functionalized MWCNTs were employed to fabricate the nanocomposites. The morphological, rheological, and mechanical properties of MWCNTs‐filled PA6/ECO blends were studied. The scanning electron microscopy of PA6/ECO blends showed that the elastomer particles, ECO, are well‐dispersed within the PA6 matrix. The significant improvement in the dispersibility of the carboxylated carbon nanotubes (COOH‐MWCNTs) compared to that of non‐functionalized MWCNTs (non‐MWCNTs) was confirmed by transmission electron microscopy images. The tensile modulus of samples improved with the addition of both types of MWCNTs. However, the effect of COOH‐MWCNTs was much more pronounced in improving mechanical properties of PA6/ECO TPE nanocomposites. Crystallization results demonstrated that the MWCNTs act as a nucleation agent of the crystallization process resulted in increased crystallization temperature (T_c) in nanocomposites. Rheological characterization in the linear viscoelastic region showed that complex viscosity and a non‐terminal storage modulus significantly increased with incorporation of both types of MWCNTs particularly at low frequency region. The increase of rheological properties was more pronounced in the presence of carboxylic (COOH) functional groups, in the other words by addition of COOH‐MWCNTs. © 2017 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2018 , 135, 45977.     

Effects of silica on the morphology,structure, and properties of thermoplastic cassava starch/poly(vinyl alcohol) blends

Thermoplastic cassava starch (TPS)/poly(vinyl alcohol) (PVA)/silica (SiO₂) composites were prepared by a melt‐mixing method. The effects of the content and surface properties of SiO₂ on the processing, mechanical properties, thermal stability, morphology, and structure of the TPS/PVA/SiO₂ composites were investigated. With increasing SiO₂ content, the plasticizing times of the TPS/PVA/SiO₂ composites were shortened. After the SiO₂ surface was treated with a silane coupling agent (KH550), the plasticizing times of the TPS/PVA/SiO₂ composites decreased significantly. The tensile strength, elongation at break, and Young's modulus of the TPS/PVA/SiO₂ composites increased. The mechanical properties of the TPS/PVA/SiO₂ composites containing treated SiO₂ were higher than those with untreated SiO_2. The thermal decomposition temperatures of the TPS/PVA/SiO₂ composites were improved with the addition of SiO₂. The presence of inorganic fillers was beneficial to the improvement of the thermal stability of the polymers. The reaction between the treated SiO₂ and the starch molecules was beneficial to the formation of more stable structures. The treated SiO₂ indicated good interfacial adhesion and uniform dispersion in the matrix. © 2016 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2016 , 133, 44020.     

Graphene nanoplate and multiwall carbon nanotube–embedded polycarbonate hybrid composites: High electromagnetic interference shielding with low percolation threshold

This study has reported the preparation of polycarbonate (PC)/graphene nanoplate (GNP)/multiwall carbon nanotube (MWCNT) hybrid composite by simple melt mixing method of PC with GNP and MWCNT at 330°C above the processing temperature of the PC (processing temperature is 280°C) followed by compression molding. Through optimizing the ratio of (GNP/MWCNT) in the composites, high electromagnetic interference shielding effectiveness (EMI SE) value (∼21.6 dB) was achieved at low (4 wt%) loading of (GNP/MWCNT) and electrical conductivity of ≈6.84 × 10⁻⁵ S.cm⁻¹ was achieved at 0.3 wt% (GNP/MWCNT) loading with low percolation threshold (≈0.072 wt%). The high temperature melt mixing of PC with nanofillers lowers the melt viscosity of the PC that has helped for better dispersion of the GNPs and MWCNTs in the PC matrix and plays a key factor for achieving high EMI shielding value and high electrical conductivity with low percolation threshold than ever reported in PC/MWCNT or PC/graphene composites. With this method, the formation of continuous conducting interconnected GNP‐CNT‐GNP or CNT‐GNP‐CNT network structure in the matrix polymer and strong π–π interaction between the electron rich phenyl rings and oxygen atom of PC chain, GNP, and MWCNT could be possible throughout the composites. POLYM. COMPOS., 37:2058–2069, 2016. © 2015 Society of Plastics Engineers     

Electromagnetic interference shielding properties of graphene quantum-dots reinforced poly(vinyl alcohol)/polypyrrole blend nanocomposites

Graphene quantum dots (GQDs) reinforced poly(vinyl alcohol) (PVA)/polypyrrole (WPPy) nanocomposite films with various GQDs loadings were synthesized using the versatile solvent casting method. The structural and morphological properties of PVA/WPPy/GQDs nanocomposite films were investigated by employing Fourier transform infrared spectroscopy, X-ray diffraction, and scanning electron microscopy. The thermogravimetric analysis revealed enhanced thermal stability of synthesized nanocomposites while enhanced dielectric properties were also observed. The maximum dielectric constant value for PVA/WPPy/GQDs nanocomposite films was observed to be ε = 6,311.85 (50 Hz, 150°C). The electromagnetic interference (EMI) shielding effectiveness (SE) of nanocomposite films was determined in the X-band (8–12 GHz) and Ku-band (12–18 GHz) frequency region. The EMI SE was found to be increased from 0.8 dB for the pure PVA film to 9.8 dB for the PVA/WPPy/GQDs nanocomposite film containing 10 wt% GQDs loading. The enhanced EMI shielding efficiency of nanocomposite films has resulted from the homogenous dispersion of GQDs in PVA/WPPy blend nanocomposites. Thus, the prepared nanocomposites are envisioned to utilize as a lightweight, flexible, and low-cost material for EMI shielding applications.     

5‐Sulfoisophthalic acid monolithium salt doped polypyrrole/multiwalled carbon nanotubes composites for EMI shielding application in X‐band (8.2–12.4 GHz)

This article describes the synthesis and characterization of highly conductive polypyrrole (PPy)/multiwalled carbon nanotube (MWCNT) composites prepared by in situ polymerization of pyrrole using 5‐sulfoisophthalic acid monolithium salt [lithio sulfoisophthalic acid (LiSiPA)] as dopant and ferric chloride as oxidant. Several samples were prepared by varying the amounts of MWCNTs ranging from 1 to 5 wt %. Scanning electron microscope and transmission electron microscope images clearly show a thick coating of PPy on surface of MWCNTs. The electrical conductivity of PPy increased with increasing amount of MWCNTs and maximum conductivity observed was 52 S/cm at a loading of 5 wt % of MWCNTs. Pure PPy prepared under similar conditions had a conductivity of 25 S/cm. Electromagnetic interference (EMI) shielding effectiveness (SE) also showed a similar trend and average EMI shielding of ?108 dB (3 mm) was observed for sample having 5 wt % MWCNT in the frequency range of 8.2–12.4 GHz (X‐band). The light weight and absorption dominated total SE of ?93 to ?108 dB of these composites indicate the usefulness of these materials for microwave shielding. © 2017 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2017 , 134 , 45370.     

Nonisothermal crystallization kinetics and thermomechanical properties of multiwalled carbon nanotube‐reinforced poly(ε‐caprolactone) composites

BACKGROUND: The technological development of poly(ε‐caprolactone) (PCL) is limited by its short useful lifespan, low modulus and high crystallinity. There are a few papers dealing with the crystallization behavior of carbon nanotube‐reinforced PCL composites. However, little work has been done on the crystallization kinetics of melt‐compounded PCL/multiwalled carbon nanotube (MWNT) nanocomposites. In this study, PCL/MWNT nanocomposites were successfully prepared by a simple melt‐compounding method, and their morphology and mechanical properties as well as their crystallization kinetics were studied. RESULTS: The MWNTs were observed to be homogeneously dispersed throughout the PCL matrix. The incorporation of a very small quantity of MWNTs significantly improved the storage modulus and loss modulus of the PCL/MWNT nanocomposites. The nonisothermal crystallization behavior of the PCL/MWNT nanocomposites exhibits strong dependencies of the degree of crystallinity (X_c), peak crystallization temperature (T_p), half‐time of crystallization (t_1/2) and Avrami exponent (n) on the MWNT content and cooling rate. The MWNTs in the PCL/MWNT nanocomposites exhibit a higher nucleation activity. The crystallization activation energy (E_a) calculated with the Kissinger model is higher when a small amount of MWNTs is added, then gradually decreases; all the E_a values are higher than that of pure PCL. CONCLUSION: This paper reports for the first time the preparation of high‐performance biopolymer PCL/MWNT nanocomposites prepared by a simple melt‐compounding method. The results show that the PCL/MWNT nanocomposites can broaden the applications of PCL. Copyright © 2008 Society of Chemical Industry     

Influence of nanoclay on properties of HDPE/wood composites

Composites based on high density polyethylene (HDPE), pine flour, and organic clay were made by melt compounding and then injection molding. The influence of clay on crystallization behavior, mechanical properties, water absorption, and thermal stability of HDPE/pine composites was investigated. The HDPE/pine composites containing exfoliated clay were made by a two‐step melt compounding procedure with the aid of a maleated polyethylene (MAPE). The use of 2% clay decreased the crystallization temperature (T_c), crystallization rate, and the crystallinity level of the HDPE/pine composites, but did not change the crystalline thickness. When 2% MAPE was added, the crystallization rate increased, but the crystallinity level was further lowered. The flexural and tensile strength of HDPE/pine composites increased about 20 and 24%, respectively, with addition of 1% clay, but then decreased slightly as the clay content increased to 3%. The tensile modulus and tensile elongation were also increased with the addition of 1% clay. The impact strength was lowered about 7% by 1% clay, but did not decrease further as more clay was added. The MAPE improved the state of dispersion in the composites. Moisture content and thickness swelling of the HDPE/pine composites was reduced by the clay, but the clay did not improve the composite thermal stability. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 2007     

Synergistic effect of multiwalled carbon nanotubes and an intumescent flame retardant: Toward an ideal electromagnetic interference shielding material with excellent flame retardancy

To shield undesirable electromagnetic waves caused by electronic devices and simultaneously resolve the flame safety of the electronic components, an electromagnetic interference (EMI) shielding material with excellent flame‐retardant properties is urgently needed. The synergistic effect of the intumescent flame retardant (IFR) and multiwalled carbon nanotubes (MWCNTs) for polystyrene (PS) nanocomposites prepared by melt blending was investigated. The results show that addition of certain amounts of IFRs facilitated the dispersion of MWCNTs in the PS matrix, and the percolation threshold of the MWCNTs in the PS matrix also decreased from 1.67 ± 0.05 to 1.29 ± 0.04 wt %. Moreover, the EMI shielding efficiencies (SEs) of the PS–MWCNT–IFR composites were consistently higher than those of the PS–MWCNT composites without the addition of the IFRs at the same MWCNT content; this indicated that the synergistic effect of the MWCNTs and IFRs effectively improved the EMI SE of the PS–MWCNT–IFR composites. Furthermore, the limiting oxygen index (LOI) testing results show that the LOI values of the PS–MWCNT composites were consistently higher than 27%; this indicated that the PS–MWCNT composites effectively met the needs of flame safety; this indicated that the PS–MWCNT–IFR composite is a novel and promising candidate for an ideal EMI shielding material with excellent flame‐retardant properties for today's electronic devices. © 2017 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2017 , 134, 45088.     

Dynamic mechanical analysis and broadband electromagnetic interference shielding characteristics of poly (vinyl alcohol)-poly (4-styrenesulfonic acid)-titanium dioxide nanoparticles based tertiary nanocomposites

ABSTRACT

Novel tertiary nanocomposite films comprising of poly (vinyl alcohol) (PVA), poly (4-styrenesulfonic acid) (PSSA) and titanium dioxide (TiO₂) nanoparticles (NP_S) were prepared using simple solvent casting method. The structural, thermal, morphological, thermo-mechanical and electromagnetic interference (EMI) shielding properties of PVA/PSSA/TiO₂ nanocomposite films were investigated. The EMI shielding effectiveness (SE) of PVA/PSSA/TiO₂ nanocomposite films in the X and Ku band was found to be 12 dB and 13 dB respectively at 25 wt% TiO₂ NPs loading. These results demonstrate the possible applications of PVA/PSSA/TiO₂ nanocomposite films as low cost, lightweight and flexible material for EMI shielding.     

Structure,mechanical, and electrical properties of high‐density polyethylene/multi‐walled carbon nanotube composites processed by compression molding and blown film extrusion

The structure and properties of melt mixed high‐density polyethylene/multi‐walled carbon nanotube (HDPE/MWCNT) composites processed by compression molding and blown film extrusion were investigated to assess the influence of processing route on properties. The addition of MWCNTs leads to a more elastic response during deformations that result in a more uniform thickness distribution in the blown films. Blown film composites exhibit better mechanical properties due to the enhanced orientation and disentanglement of MWCNTs. At a blow up ratio (BUR) of 3 the breaking strength and elongation in the machine direction of the film with 4 wt % MWCNTs are 239% and 1054% higher than those of compression molded (CM) samples. Resistivity of the composite films increases significantly with increasing BURs due to the destruction of conductive pathways. These pathways can be recovered partially using an appropriate annealing process. At 8 wt % MWCNTs, there is a sufficient density of nanotubes to maintain a robust network even at high BURs. © 2015 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015 , 132, 42665.     

Miscibility,UV resistance,thermal degradation,and mechanical properties of PMMA/SAN blends and their composites with MWCNTs

Poly(methyl methacrylate)/poly(styrene‐co‐acrylonitrile) (PMMA/SAN) blends, with varying concentrations, were prepared by melt‐mixing technique. The miscibility is ensured by fixing the acrylonitrile (AN) content of styrene acrylonitrile (SAN) as 25% by weight. The blends were transparent as well. The Fourier transform infrared spectroscopic (FTIR) studies did not reveal any specific interactions, supporting the well accepted ‘copolymer repulsion effect’ as the driving mechanism for miscibility. Addition of SAN increased the stability of PMMA towards ultraviolet (UV) radiations and thermal degradation. Incorporation of even 0.05% by weight of multi‐walled carbon nanotubes (MWCNTs) significantly improved the UV absorbance and thermal stability. Moreover, the composites exhibited good strength and modulus. However, at higher concentrations of MWCNTs (0.5 and 1% by weight) the thermo‐mechanical properties experienced deterioration, mainly due to the agglomeration of MWCNTs. It was observed that composites with 0.05% by weight of finely dispersed and well distributed MWCNTs provided excellent protection in most extreme climatic conditions. Thus, PMMA/SAN/MWCNTs composites can act as excellent light screens and may be useful, as cost‐effective UV absorbers, in the outdoor applications. © 2016 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2016 , 133, 43628.     

Isothermal crystallization kinetics of polypropylene in melt‐mixed composites of polypropylene and multi‐walled carbon nanotubes

The isothermal crystallization behaviour of the polypropylene (PP) phase in PP/multi‐walled carbon nanotubes (MWCNTs) composites has been investigated via differential scanning calorimetric analysis, which showed the influence of the varying dispersion level of MWCNTs in the respective PP matrix. PP/MWCNTs composites were prepared via melt‐blending technique, wherein two different grades of MWCNTs of varying average “agglomerate” size and varying entanglements (N‐MWCNTs and D‐MWCNTs) were utilized. Furthermore, the influence of melt‐viscosity of the PP phase was investigated on the crystallization kinetics of the PP/MWCNTs composites. Heterogeneous nucleation ability of MWCNTs has resulted in a decrease in half time of crystallization (t _1/2) from ～14 min for pure PP to ～6 min for PP/N‐MWCNTs and ～11 min for PP/D‐MWCNTs composites at 1 wt% of MWCNTs at 132 °C. Overall rate of crystallization (k) has significantly increased to 4.9 × 10^?2 min^?1 for PP/N‐MWCNTs composite as compared with 6.2 × 10^?3 min^?1 for PP/D‐MWCNTs composite at 0.5 wt% of MWCNTs at 132 °C. Moreover, the effect of a novel organic modifier, Li‐salt of 6‐amino hexanoic acid along with a compatibilizer (PP‐g‐MA) has also been investigated on the crystallization kinetics of the PP phase in PP/MWCNTs composites. POLYM. ENG. SCI., 57:1136–1146, 2017. © 2017 Society of Plastics Engineers     

Multiwalled carbon nanotubes–BaTiO3/silica composites with high complex permittivity and improved electromagnetic interference shielding at elevated temperature

Composites with silica matrix and mixed filler of multiwalled carbon nanotubes (MWCNTs) and BaTiO₃ powder were fabricated. Excellent uniform dispersion of MWCNTs can be obtained using a two-step mixing method. Both of the real and imaginary parts of complex permittivity increased with increasing MWCNT content and measured temperature. The electromagnetic interference (EMI) shielding results showed that the absorption mechanism is the main contribution to the total EMI shielding effectiveness (SE). Compared with the EMI SE resulting from reflection, the absorption showed more dependence on the MWCNT content, measured temperature and frequency. The total EMI SE is greater than 20 dB at 25 °C and 50 dB at 600 °C in the whole frequency range of 12.4–18 GHz with a 1.5 mm composite thickness, which suggests that the MWCNT–BaTiO₃/silica composites could be good candidates for the EMI shielding materials in the measured frequency and temperature region.     

Preparation and thermal,electrical, and morphological properties of multiwalled carbon nanotubeand epoxy composites

Multiwalled carbon nanotube (MWCNT)/epoxy composites are prepared, and the characteristics and morphological properties are studied. Scanning electron microscopy microphotographs show that MWCNTs are dispersed on the nanoscale in the epoxy resin. The glass‐transition temperature (T_g) of MWCNT/epoxy composites is dramatically increased with the addition of 0.5 wt % MWCNT. The T_g increases from 167°C for neat epoxy to 189°C for 0.5 wt % CNT/epoxy. The surface resistivity and bulk resistivity are decreased when MWCNT is added to the epoxy resins. The surface resistivity of CNT/epoxy composites decreases from 4.92 × 10¹² Ω for neat epoxy to 3.03 × 10⁹ Ω for 1 wt % MWCNT/epoxy. The bulk resistivity decreases from 8.21 × 10¹⁶ Ω cm for neat epoxy to 6.72 × 10⁸ Ω cm for 1 wt % MWCNT/epoxy. The dielectric constant increases from 3.5 for neat epoxy to 5.5 for 1 wt % MWCNT/epoxy. However, the coefficient of thermal expansion is not affected when the MWCNT content is less than 0.5 wt %. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 103: 1272–1278, 2007     

Enhanced Dielectric Constant for Efficient Electromagnetic Shielding Based on Carbon-Nanotube-Added Styrene Acrylic Emulsion Based Composite

An efficient electromagnetic shielding composite based on multiwalled carbon nanotubes (MWCNTs)-filled styrene acrylic emulsion-based polymer has been prepared in a water-based system. The MWCNTs were demonstrated to have an effect on the dielectric constants, which effectively enhance electromagnetic shielding efficiency (SE) of the composites. A low conductivity threshold of 0.23 wt% can be obtained. An EMI SE of ~28 dB was achieved for 20 wt% MWCNTs. The AC conductivity (σ _ac) of the composites, deduced from imaginary permittivity, was used to estimate the SE of the composites in X band (8.2–12.4 GHz), showing a good agreement with the measured results.     

Preparation,characterization, electrical and antibacterial properties of sericin/poly(vinyl alcohol)/poly(vinyl pyrrolidone) composites

In this study, we focused on the fabrication of poly(vinyl alcohol) (PVA)/poly(vinyl pyrrolidone) (PVP)/sericin composites via a simple solution‐blending method. The composites were characterized by Fourier transform infrared (FTIR) spectroscopy, UV spectroscopy, X‐ray diffraction (XRD), scanning electron microscopy (SEM), differential scanning calorimetry, thermogravimetric analysis (TGA), and measurements of the conductivity, tensile strength, and antibacterial activity against Staphylococcus aureus. The results of FTIR and UV spectroscopy implied the occurrence of hydrogen bonding between sericin and the PVA/PVP blend. The structure and morphology, studied by XRD and SEM, revealed that the sericin particles were well dispersed and arranged in an orderly fashion in the blend. The glass‐transition temperature (T_g) of the composite was higher than that of the pure blend, and the T_g value shifted toward higher temperatures when the volume fraction of sericin increased. TGA indicated that sericin retarded the thermal degradation; this depended on the filler concentration. The mechanical and electrical properties, such as the tensile strength, alternating‐current electrical conductivity, dielectric constant, and dielectric loss of the composites, were higher than those of the pure blend, and these properties were enhanced when the concentration of sericin was increased up to 10 wt % filler content, whereas the elongation at break of the composite decreased with the addition of sericin particles. The antibacterial properties of the composite showed that sericin had a significant inhibitory effect against S. aureus. © 2016 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2016 , 133, 43535.     

Thermal,mechanical, and rheological properties of biodegradable polybutylene succinate/carbon nanotubes nanocomposites

Biodegradable poly(butylene succinate)/carbon nanotubes nanocomposites were prepared by melt mixing process, and the influence of carbon nanotubes on the properties of the nanocomposites was investigated. Differential scanning calorimetry showed that crystallization temperature (T_c) increase with increasing carbon nanotube content. Improvement of tensile modulus was observed by the addition of carbon nanotubes compared with pure poly(butylene succinate). Electrical conductivity showed that conductivity of polybutylene succinate/carbon nanotube composites increased with addition of carbon nanotube content. The storage moduli of polybutylene succinate/carbon nanotube composites are higher than the neat polybutylene succinate. The processability of polybutylene succinate/carbon nanotubes composites was improved and more pronounced in higher content of carbon nanotubes. POLYM. COMPOS., 31:1309–1314, 2010. © 2009 Society of Plastics Engineers