Corrosion of Glassy (Ni8Nb5)99.5Sb0.5 Alloy and Stability of Passive Film

通过浸泡法和电化学腐蚀法研究了(Ni8Nb5)99.5Sb0.5非晶在1,6mol/LHCl,1mol/LH2SO4和3%NaCl(质量分数)溶液中的腐蚀行为,对相应的组分金属Ni,Nb和Sb的腐蚀行为进行了比较。钝化膜的稳定性使用恒电位法和XPS深度剖析进行了研究,电化学极化测试后用扫描电镜观察了合金的表面形貌。结果表明,Ni-Nb-Sb合金在1mol/LHCl,1mol/LH2SO4和3%NaCl(质量分数)溶液中具有良好的抗腐蚀性,在6mol/LHCl溶液中,非晶合金的抗腐蚀性较差。在含有氯的介质中,电化学腐蚀后非晶合金表面被晶化,且有过钝化溶解。对钝化膜的稳定性研究表明,在低电压下,钝化膜的生长是由扩散控制的,而在高电压下,则主要呈活化腐蚀。     

Fe41Co7Cr15Mo14C15B6Y2块体非晶合金在HCl溶液中的腐蚀行为

采用电化学极化曲线和电化学阻抗(EIS)测试方法研究Fe_(41)Co_7Cr_(15)Mo_(14)C_(15)B_6Y_2块体非晶合金在0.5,1,2以及4 mol/L HCl溶液中的腐蚀行为,并比较了1 mol/L HCl溶液中非晶合金和不锈钢的腐蚀行为.极化曲线测试结果表明,Fe_(41)Co_7Cr_(15)Mo_(14)C_(15)B_6Y_2块体非晶合金在各种浓度的HCl溶液中都具有很好的耐蚀性,阳极极化曲线表现出明显的钝化特征.随着HCl溶液浓度的增大,其耐蚀性能逐渐下降.在1 mol/L HCl溶液中,非晶合金的自腐蚀电位高于不锈钢,自腐蚀电流密度比不锈钢小1个数量级.EIS结果显示,在开路电位下,Fe_(41)Co_7Cr_(15)Mo_(14)C_(15)B_6Y_2非晶合金和不锈钢的Nyquist图均由单一的容抗弧构成,但非晶合金的电化学转移电阻Rt比不锈钢的大2个数量级,这一结果与极化曲线结果一致,说明非晶合金在HCl溶液中的耐蚀性能优于不锈钢.     

Fe基非晶及纳米晶合金的制备和电化学腐蚀行为

分别采用单辊甩带法和非晶晶化退火法制备出非晶及纳米晶合金Fe73.5Si13.5B9Nb3Cu1;利用DSC、XRD和TEM对该非晶合金的晶化行为进行了分析;并用电化学极化曲线的方法和电化学阻抗技术研究了该非晶合金经不同温度退火后在1mol/LHCl溶液里的电化学腐蚀行为。结果表明,该非晶合金的晶化过程出现2个阶段。当退火温度为500℃时,合金尚未晶化,仍保持非晶态;当温度达到550℃时,出现了晶化衍射峰,晶粒平均直径约13nm;当温度达到600℃时,晶粒平均直径约为15nm。经过退火得到的纳米晶合金的腐蚀电位大于未退火的非晶,且阳极电流密度变得更低,表明纳米晶状态时的耐腐蚀性能比非晶状态的更好。该非晶合金未退火、550℃退火和600℃退火时的EIS均由单一容抗弧构成,具有一时间常数;且随着退火温度升高,电化学反应电荷转移电阻在增大。     

铁基非晶基涂层的HVOF制备及耐腐蚀性能(英文)

以工业原材料制备的铁基非晶合金、镍铬合金、碳化钨颗粒的混合粉末为原材料,采用高速火焰喷涂技术制备铁基非晶基涂层。通过分析铁基非晶基涂层分别在1 mol/L盐酸、氯化钠、硫酸和氢氧化钠溶液中的动态极化特性,研究其腐蚀阻抗。采用扫描电子显微镜(SEM)分析涂层的腐蚀形貌。结果表明:铁基非晶基涂层具有优良的耐蚀性能,而且在含氯离子溶液中,表现出比304L奥氏体不锈钢更高的腐蚀阻抗。在1 mol/L盐酸溶液中,铁基非晶基涂层的腐蚀电流密度和钝化电流密度分别为132.0μA/cm2和9.0 mA/cm2,在1 mol/L氯化钠溶液中分别为2.5μA/cm2和2.3 mA/cm2,且表现出一个宽的自钝化区间。其优异的耐蚀性能表明铁基非晶基粉末可以作为一种耐腐蚀、耐磨损的工程材料。     

Zr基和Ti基块体非晶合金的电化学腐蚀性能(英文)

用电化学方法研究Ti基和Zr基非晶合金及与非晶成分相同的Zr基晶态合金在1mol/LH2SO4和3.5%NaCl溶液中的腐蚀行为。极化曲线测试结果表明:在H2SO4溶液中,Zr基非晶和晶态合金自腐蚀电位比Ti基非晶合金的低;在NaCl溶液中,Zr基晶态合金的自腐蚀电位最低,而且在腐蚀过程中没有发生钝化,然而非晶合金都表现出钝化特性。交流阻抗测试结果表明:在NaCl溶液中非晶合金比晶态合金表现出更好的耐腐蚀性能,但是在H2SO4溶液中并没看到它们之间有明显的区别。表面形貌分析表明:在NaCl溶液中,这2种非晶合金都发生点蚀,而在H2SO4溶液中所有试验合金都表现出类似的特征,试样表面基本保持平整,只是在腐蚀表面的局部区域有一些裂纹出现。     

(FeCoNiCr)100-xMnx高熵合金在NaCl和NaOH溶液中的抗腐蚀性能

研究了放电等离子烧结(FeCoNiCr)_100-xMn_x(x=4,8,12,20)高熵合金的组织结构及在NaCl和NaOH溶液中的耐腐蚀性能。结果表明,(FeCoNiCr)_100-xMn_x合金主要由FCC单相组织和少量BCC相组成。(FeCoNiCr)₈₈Mn₁₂合金在3.5wt%NaCl 溶液中具有最好的耐腐蚀性能。Mn的添加使合金在1 mol NaOH 溶液中耐腐蚀性增强。退火对合金在1 mol NaOH 溶液中抗腐蚀性能影响不大。(FeCoNiCr)_100-xMn_x合金在3.5wt%NaCl溶液和1 mol NaOH溶液中的抗腐蚀性能均优于304S不锈钢。     

化学镀Ni-Fe-P和Ni-Fe-P-B合金的耐蚀性研究

利用失重法和电化学测试法,对比研究以铝合金为基体化学镀Ni-Fe-P和Ni-Fe-P-B合金的耐蚀性.结果表明:这两种镀层浸泡在3.5%NaCl和10%NaOH溶液中均比浸泡在0.1mol/L H2SO4和1mol/L HCl中有更好的耐蚀性.另外,在3.5%NaCl和10%NaOH溶液中,Ni-Fe-P-B镀层合金比Ni-Fe-P有更好的耐蚀性;但是在0.1mol/L H2SO4和1mol/L HCl溶液中,Ni-Fe-P镀层合金却比Ni-Fe-P-B有更好的耐蚀性;     

铁基非晶及纳米晶合金在NaOH溶液中的耐蚀性比较

冶炼制备了纳米晶Fe73.5Si13.5B9Nb3Cu1和非晶带材Fe78Si13B9。在电化学工作站上测试了两种合金在不同浓度的NaOH碱溶液里的极化曲线。随着NaOH溶液浓度的不同,非晶Fe78Si13B9和纳米晶Fe73.5Si13.5B9Nb3Cu1合金极化曲线具有相似的变化规律,且纳米晶合金比非晶合金的腐蚀电位要高,耐腐蚀性要好。     

超音速火焰喷涂FeCrSiB涂层的腐蚀行为

采用超音速火焰(high velocity oxygen fuel,HVOF)喷涂技术在Q235钢基体上制备了FeCrSiB合金涂层.利用X射线衍射仪、扫描电子显微镜、电化学工作站等设备对涂层的显微组织结构和耐腐蚀性进行了研究.结果表明,采用HVOF喷涂技术制备的FeCrSiB涂层结构致密,孔隙率为0.65%,与基体结合良好.FeCrSiB涂层在3.5%NaCl溶液、1 mol/L HCl溶液和1 mol/L NaOH溶液中都经历了活性溶解-钝化-过钝化的过程,且该涂层在3.5%NaCl溶液和1 mol/L HCl溶液中的耐腐蚀性能要优于镀铬层,在1 mol/L NaOH溶液中的耐腐蚀性能低于镀铬层.     

电沉积非晶态Ni-P合金的腐蚀行为

<正> 电沉积Ni-P合金时,只要沉积层中的磷含量大于8at％就能得到非晶态。 尽管化学镀Ni-P已作为防护工程的一种标准镀层,而电镀Ni-P台金的研究还相当有限。本工作就电镀非晶态Ni-P合金在若干酸中的腐蚀行为进行了研究。     

Nd对Zr基非晶合金形成能力、热稳定性及耐腐蚀性的影响

利用铜模吸铸法在水冷坩埚中制备了4种(Zr0.55Al0.1Ni0.05Cu0.3)100-xNdx(x=0,1,2,3)块体非晶合金。采用XRD和DSC检测了所获合金相组成、非晶形成能力及热稳定性,并采用盐酸溶液浸泡腐蚀试验评价了不同合金的腐蚀速率。结果表明,适量添加Nd可提高Zr0.55Al0.1Ni0.05Cu0.3非晶合金的形成能力和热稳定性,但非晶合金在2mol/L HCl溶液中的耐蚀性随Nd含量的增加而降低。该结果对进一步改善和提高非晶合金的性能具有重要的参考价值。     

Al86Fe10Zr4非晶合金的晶化与腐蚀行为研究

利用甩带法制备出Al86Fe10Zr4非晶薄带,用X射线衍射仪和差示扫描量热计对该非晶的非晶特性及晶化过程进行了研究.结果表明,Al86Fe10Zr4非晶薄带的晶化过程为两步晶化,其晶化温度分别约为603和718 K.用Kissinger 法得到了合金两步晶化过程的激活能分别为273和239 kJ/mol.对该非晶薄带...     

Al86Fe10Zr4非晶合金的晶化与腐蚀行为研究

利用甩带法制备出Al86Fe10Zr4非晶薄带,用X射线衍射仪和差示扫描量热计对该非晶的非晶特性及晶化过程进行了研究。结果表明,Al86Fe10Zr4非晶薄带的晶化过程为两步晶化,其晶化温度分别约为603和718 K。用Kissinger法得到了合金两步晶化过程的激活能分别为273和239 kJ/mol。对该非晶薄带及其不同晶化程度的试样在0.01 mol·L-1 NaCl,pH=12碱性溶液中的室温电化学腐蚀性能的研究结果表明,部分晶化态试样表现出比非晶态试样更佳的耐蚀性能,而完全晶化态试样的耐蚀性能明显降低。     

Microstructure and Electrochemical Behavior of Fe-Based Amorphous Metallic Coatings Fabricated by Atmospheric Plasma Spraying

A Fe₄₈Cr₁₅Mo₁₄C₁₅B₆Y₂ alloy with high glass forming ability (GFA) was selected to prepare amorphous metallic coatings by atmospheric plasma spraying (APS). The as-deposited coatings present a dense layered structure and low porosity. Microstructural studies show that some nanocrystals and a fraction of yttrium oxides formed during spraying, which induced the amorphous fraction of the coatings decreasing to 69% compared with amorphous alloy ribbons of the same component. High thermal stability enables the amorphous coatings to work below 910 K without crystallization. The results of electrochemical measurement show that the coatings exhibit extremely wide passive region and relatively low passive current density in 3.5% NaCl and 1 mol/L HCl solutions, which illustrate their superior ability to resist localized corrosion. Moreover, the corrosion behavior of the amorphous coatings in 1 mol/L H₂SO₄ solution is similar to their performance under conditions containing chloride ions, which manifests their flexible and extensive ability to withstand aggressive environments.     

FeCo基大块非晶合金盐雾与电化学腐蚀研究

通过电化学测试方法与中性盐雾腐蚀实验研究Fe24 xCo24-xCr15Mo14C15B6Y2 (X=0, 2, 4, 6, 17)块体非晶合金的耐蚀性。合金在1 mol/L HCl中出现了宽的钝化区,其EIS图谱均由单一容抗弧组成,显示出良好耐蚀性;结合极化曲线与交流阻抗结果分析可得合金耐蚀性随着Co含量的增加先增大后减小,当Co含量为20%时合金耐蚀性最好。利用能谱分析(EDS)与原子力显微镜(AFM)对合金的中性盐雾腐蚀结果进行分析,可知它们的腐蚀产物主要由铁和钴的氧化物以及它们的氯化物组成。同时FeCo基大块非晶合金腐蚀程度随着Co含量的变化而变化,其盐雾腐蚀耐蚀性规律与电化学腐蚀耐蚀性规律一致。     

Mg65Cu25Gd10非晶合金的腐蚀行为

采用电化学方法研究了块体Mg65Cu25Gd10非晶合金在0.01 mol/L,pH=13的NaCl溶液及0.1 mol/L,pH=13的NaOH溶液中的腐蚀行为.在2种电解质溶液中,非晶合金样品的极化曲线具有明显的钝化区和较低的钝化电流密度.浸蚀样品的表面形貌和腐蚀产物采用SEM和EDS来表征.恒电位钝化后样品表面层化学信息运用DP-XPS来考察.结果表明,样品在NaOH溶液中形成致密少孔的钝化膜,而在含Cl离子的溶液中,样品表面钝化膜疏松且多孔,导致合金在含Cl离子的溶液中具有较低的耐蚀性.     

闭合场非平衡磁控溅射镀Cr-C层的耐蚀性研究

    利用闭合场非平衡磁控溅射离子镀技术在高速钢表面制备Cr-C镀层。采用电化学腐蚀法研究了Cr-C镀层、电镀Cr层及高速钢基体的腐蚀行为.结果表明,在1 mol/L NaCl、1 mol/L HCl及7.5 mol/L NaOH溶液中,闭合场非平衡磁控溅射离子镀制备的Cr-C镀层的耐蚀性优于电镀Cr镀层,并且其Cr含量越高耐腐蚀性越好.     

Electrochemical response of amorphous and devitrified Al‐Ni‐La‐X (X = Ag,Cu) alloys

The electrochemical response of melt‐spun Al‐Ni‐La alloys with partial substitution of Ni after different stages of devitrification was studied. The base alloy was found to have the best corrosion resistance. It was observed that primary crystallization caused minimal deterioration in the corrosion resistance of the base alloy as compared to its amorphous state. The substitute alloys had different corrosion resistance dependent on the substituting element with the Ag containing alloy having the least resistance. This could be attributed to the operation of local galvanic cells, enhanced by chemical heterogeneities in the alloys. Secondary crystallization caused a reduction in the corrosion resistance of all the alloys due to the creation of intermetallic phases that increased the galvanic activity.     

Effects of Zr on crystallization kinetics of Pr—Fe—B amorphous alloys

The effects of Zr on crystallization kinetics of Pr-Fe-B amorphous alloys have been investigated by DTA and XRD methods.It was found that for Pr8Fe86-xZrxB6(x=0,1,2)amorphous alloys,the final crystallized mixture is α-Fe and Pr2Fe14B,and the metastable Pr2Fe23B3 phase occurs during crystallization of Pr8Fe86B6 amorphous alloy,not during crystallization of Pr8Fe86-xZrxB6(x=1,2)amorphous alloys,By analyzing the activation energy of crystallization,the formation of an α-Fe/Pr2Fe14B composite microstructure with a coarse grain size in annealed Pr8Fe86B6 alloy,is attributed to a difficult nucleation and an easy growth for both the α-Fe and Pr2Fe14B in the alloy.The addition of Zr can be used to change the crystallization behavior of the α-Fe phase in Pr-Fe-B amorphous alloy,which is helpful to reduce the grain size for the α-Fe phase.     

Al-Mg-Sn-Si-In铝合金在不同溶液中的腐蚀与电化学性能研究

研究了Al-0.5Mg-0.1Sn-0.1Si-0.02In合金作为铝空气电池的阳极材料,在2 mol/L NaCl,4 mol/L NaOH乙醇-10%水,4 mol/L NaOH溶液中的腐蚀行为及电化学性能。结果表明,该合金在4 mol/L NaOH乙醇-10%水溶液中性能优良,具有较高的阳极利用率及较低的自腐蚀速率。腐蚀形貌及电化学阻抗谱测试结果与合金腐蚀特性一致。通过对比Zn在4 mol/L NaOH溶液中的电化学性能,Al-0.5Mg-0.1Sn-0.1Si-0.02In合金在4 mol/L NaOH乙醇-10%水介质中作为铝空气电池的阳极材料具有可行性。