Ti60合金热变形过程中的软化机制

采用Thermecmaster-Z型热加工模拟试验机对Ti60合金进行等温恒应变速率压缩实验,通过分析流动应力-应变曲线的流动特征,计算加工硬化率,观察变形微观组织,并结合变形激活能的计算,研究该合金在变形温度为850～950℃、应变速率为0.001～10 s^-1、真应变为0.51热变形条件下的软化机制。结果表明:Ti60合金在低应变速率(0.001～0.1s^-1)和高应变速率(1～10s^-1)区间流动应力-应变曲线分别呈现流动稳态型和流动软化型两种;加工硬化率曲线呈现无拐点特征;变形微观组织为动态回复组织,未出现动态再结晶现象;变形激活能在低应变速率区间和高应变速率区间分别为484.35 kJ/mol和500.76 kJ/mol,两者相差不大。综合这些结果可以判定,Ti60合金的软化机制以动态回复为主。     

Ti8LC合金热变形及其微观组织

采用GLEEBLE-1500热模拟机对Ti8LC合金在温度为850～1000 ℃、变形速率为0.001～0.1 s-1、最大变形程度为60%的条件下,进行恒应变速率高温压缩模拟试验研究,分析合金高温变形时流变应力与应变速率及变形温度之间的关系以及组织变化.结果表明:Ti8LC合金流变应力随应变速率的增大而增大,在恒应变速率条件下,真应力水平随温度的升高而降低;在给定的变形条件下,通过回归计算,建立了一种Ti8LC合金的本构方程;根据试验分析,在850～950 ℃温度时变形,主要发生动态再结晶,随着温度的升高,软化机制主要是动态回复.     

高温变形参数对Ti3Al基合金微观组织的影响

研究了高温变形参数对Ti-24Al-15Nb- 1.5Mo合金显微组织的影响.实验选取的变形温度为980℃,应变速率为10-3～10-1 s-1,变形程度为30％～50％.结果表明:在变形过程中,应变速率对α2相体积分数影响不大,但对α2相晶粒的形态和尺寸有一定影响,较高的应变速率有利于细化晶粒;随着变形程度的提高,α2相晶粒的细化程度增加,晶粒粒径更加细小.     

变形温度对Ti2AlNb/Ti60双合金焊接接头组织性能的影响

研究了近等温锻造温度对Ti2A1Nb/Ti60双合金焊接接头显微组织和力学性能的影响.结果表明:经不同温度近等温变形及相同热处理后,Ti2A1Nb/Ti60双合金试样焊缝组织得到明显细化,强度和塑性得到提高,均高于基体Ti60合金;随着变形温度的升高,Ti60合金热影响区显微组织中初生等轴α相逐渐减少,β转组织增多,片状α相变短变粗.因此,合金的室温拉伸强度逐渐升高,塑性逐渐下降;变形温度为1010℃的试样,其焊缝熔合区显微组织较为均匀,塑性相B2含量较多,焊件室温及600℃高温拉伸均表现出较好的强度与塑性匹配.     

氢对Ti3Al—Nb合金组织和高温变形的影响

研究了氢对一种Ｔｉ３Ａｌ基合金（Ｔｉ－２４Ａｌ－１４Ｎｂ－３Ｖ－０．５Ｍｏ．ａｔ％）组织和高温变形的影响。结果表明,渗氢使所研究合金的Ｏ相中氢化物,这些氧化物在高温下分解,留下一些位错误,渗氮还使Ｏ相的体积发散下降,在高温变形中,氢的存在可促进Ｏ相的动态再结晶和Ｂ２相中的位错运动,并能降低变形过程激活能,同时,对氢降低合金高温变形的流变应国的机制进行了分析。     

变形条件对半固态Al-4Cu-Mg合金微观组织的影响

研究了用应变诱发熔化激活法(SIMA)制备的半固态Al-4Cu-Mg合金在不同变形温度、变形程度和应变速率下半固态压缩变形时的微观组织演变。研究结果表明：在半固态条件下，随变形温度的升高，晶粒平均尺寸增大，分形维数减小；变形程度增大，晶粒平均尺寸减小．分形维数先减小后增大；应变速率增大，晶粒平均尺寸先减小后略有增大，且在小的应变速率下，晶粒平均尺寸随应变速率变化的趋势较大，分形维数随着应变速率的增大而增大。     

热变形参数对Ti53311S合金组织的影响

在Gleeble-1500热模拟机上对Ti53311S合金进行了变形温度为880～1080℃、变形速率为0.001～10s-1的热压缩试验,分析了合金的热变形行为并观察了金相组织.结果表明,该合金流变应力均随应变速率的增加而升高,随温度的升高而降低.在相变点以下变形,随温度增加,合金中β相数量有所增加,但晶粒尺寸变化不大.在高温两相区980℃变形,低应变速率的组织较粗大,中等变形速率0.1s-1可以得到晶粒细小、均匀的组织,而应变速率高于1s-1,则会造成变形组织明显不均匀.在高温β区变形时的变形机理主要为动态回复,而且在该回复区域增加变形量并不能起到细化组织的效果.     

热变形温度对Cu-Sn-P合金微观组织的影响

通过EBSD,TEM等方法对Cu-Sn-P在合金200～500℃的热变形组织进行分析。研究表明:经热变形后的晶粒组织垂直于受力方向被拉长,大部分为变形晶粒,应变硬化效果明显,基体内部存在较大的形变储能。再结晶主要在位错密度较大区域形核,软化作用比较微弱。热变形组织内部亚晶组织及位错聚集区密集分布,发现了刃型位错的交割以及位错列的滑移作用。当变形温度为500℃时,在再结晶晶粒内部会出现台阶状的退火孪晶。     

变形参数对含有少量液相Ti14合金压缩行为的影响(英文)

采用热模拟系统研究了半固态变形温度,应变速率和变形量对Ti14合金压缩行为和组织演变的影响。结果表明:温度和应变对Ti14合金半固态峰值应力影响较大,峰值应力随着温度的增加和应变速率的减小而降低。分析认为:半固态变形中,应变速率的变化会影响产生压缩变形所需的响应时间,而液相的含量受控于变形温度,随着变形温度的升高,组织中出现了网状晶界结构,使得变形机制由固相粒子的塑性变形转变为固液混合流动。此外,变形量对合金半固态变形的应力-应变影响较小,可以认为是液相的润滑作用和协调变形机制缓解了晶粒间的压缩应力和摩擦力,使得应力-应变变化不明显。     

热处理对Ti2AlNb/Ti60双合金接头组织及性能的影响

以连接加变形后的Ti2AlNb/Ti60双合金为对象,研究锻后不同热处理制度对双合金接头显微组织和力学性能的影响.结果表明:热处理制度对Ti60合金侧热影响区的相组成影响较小,但对相的形态、尺寸和数量具有一定的影响;随着固溶温度的升高或固溶时间的延长,双合金试样的强度增加,塑性下降;经过990℃/1h+750℃/4h热处理后的Ti2AlNb/Ti60双合金焊缝组织得到优化,强度和塑性均高于Ti60合金基体,双合金试样在室温及600℃高温均表现出较好的强度与塑性匹配.     

变形参数对Ti40钛合金开裂机制的影响

材料成形过程中,一个备受关注的问题是能否实现在不发生开裂的基础上达到要求的变形。本文基于热压缩实验（变形温度为1123K-1373K,应变速率为0.01-10s-1,变形量为70%）获得的开裂样本,证实了铸态Ti40合金的主要开裂模式为45°剪切开裂、自由表面纵向开裂和内部三叉晶界沿晶开裂。借助SEM重点分析了变形参数对开裂机制的影响规律,发现在低温1123K变形时,主要是穿晶解理脆性断裂,1273K变形时,转变为韧性断裂,高温1373K变形时,大量的小韧窝被观察到;应变速率对铸态Ti40合金的开裂行为也具有重要影响,在低应变速率0.01s-1变形时,样本没有发生开裂,在0.1和1s-1变形时,在开裂表面观察到大量的韧窝,属于韧性开裂,在高应变速率10s-1变形时,开裂表面呈现脆性开裂特征。最后深入探讨了铸态Ti40合金的损伤机制和开裂原因,绘制了铸态Ti40合金的开裂原理图。     

Effect of hot isostatic pressing processing parameters on microstructure and properties of Ti60 high temperature titanium alloy

Hot isostatic pressing parameters are critical to Ti60 high temperature titanium alloy castings which have wide application perspective in aerospace. In order to obtain optimal processing parameters, the effects of hot isostatic pressing parameters on defects, composition uniformity, microstructure and mechanical properties of Ti60 cast high temperature titanium alloy were investigated in detail. Results show that increasing temperature and pressure of hot isostatic pressing can reduce defects, ...     

Influence of deformation parameters on microstructure and mechanical properties of TA 15 titanium alloy

The influence of deformation parameters including deformation temperature, degree and speed on the microstructure and mechanical properties of TA15 titanium alloy was studied. The volume fraction, size and aspect ratio of primary a phase in deformed TAI 5 titanium alloy were quantitatively characterized. With increasing deformation temperature, the volume fraction and size of primary α phase decrease. The aspect ratio of primary a phase decreases with increasing deformation temperature. The tensile strength of TA15 alloy deformed at 0.1 mm/s is higher than that at 0.3 mm/s. After therlnoforming at 960℃, 0.1 mrn/s, the tensile strength is the highest up to 1 035 MPa and the elongation is 13.5%. When the thermoforming temperature is 1 050℃, the strength and elongation are both relative low, because the microstructure is Widmanstaten structure.     

高温变形参量对TC21钛合金组织与性能的影响

在880～950 ℃和不同应变速率0.01～10 s-1条件下,将TC21钛合金高温压缩变形至50%.研究高温变形参量对流动应力及微观组织的影响规律,建立了TC21合金的本构方程.结果表明:流变应力随变形温度的降低及应变速率的增大而升高,变形温度与应变速率对TC21钛合金显微组织的影响显著,应变速率越低,组织球化现象越明显.高温变形过程中,TC21钛合金的流变应力与Zener-Hollomon参数的指数形式呈线性关系.     

Effect of large deformation on microstructure of ZK60 alloy

Microstructure evolution of ZK60 magnesium alloy deformed at 023 hoy cyclic extrusion compression （CEC） large deformation method was investigated. ZK60 alloy was deformed in the range of accumulated true strain of 0.8-17. The microstructure of evolution was investigated by optical microscope （OM） and transmission electron microscopy （TEM）. The results show that microstructure is obviously refined, and homogenous equiaxed microstructure is achieved in the entire range of the examined deformations by subjected to CEC deformation. By increasing the accumulated strain to 17, the grain size decreases into sub-micron regime with about several hundred nanometers. The mechanism of grain refinement in ZK60 alloy by CEC can be attributed to continuous dynamic recovery and recrystallization.     

钛合金针状焊缝组织的超塑性变形机理

钛合金激光焊缝是非理想的针状组织,对其超塑性变形机理的研究可进一步推进钛合金LBW/SPF技术的实际应用,也对材料成形机理的发展具有一定意义.研究结果表明,TC4钛合金激光焊接试样具有良好的超塑性变形能力,在变形过程中,焊缝发生两次重要的组织转变,即针状组织片层化和片层组织等轴化的组织转变.片层组织在应力作用下,通过断裂、解体和等轴化的过程而转变成等轴晶粒.片层断裂的主要机制是动态再结晶和应力挤压作用;片层解体的主要机制是晶界滑动和转动作用,接头组织的塑性流动机理为晶粒滚动和晶界滑动机理.     

Hot deformation behavior and microstructure evolution of titanium alloy Ti-Al-Zr-Sn-Mo-Si-Y

Samples of Ti-Al-Zr-Sn-Mo-Si-Y alloy were compressed on the Gleeble-1500 heat stimulation machine. The compression test was carried out in the temperature range from 800 ℃ to 1 100℃ and strain rate range from 0.001 s^-1 to 10 s^-1. Stress-strain behavior and variation of microstructure of the alloy during hot compression were investigated. The experimental results show that the alloy is sensitive to temperature and strain rate, and the flow softening behavior is more obvious with the decrease of deformation temperature. At higher strain rate, discontinuous yielding is observed in β phase region. When deformed in α＋β phase region, with the increment of deformation temperature, the lamellar a structures globularization is more quick and more uniform. When deformed in β phase region, coarse β grains can be got because of high deformation temperature.