Microwave dielectric properties and its compatibility with silver electrode of Li2MgTi3O8 ceramics

The effects of BaCu(B₂O₅) (BCB) additions on the sintering temperature and microwave dielectric properties of Li₂MgTi₃O₈ ceramic have been investigated. The pure Li₂MgTi₃O₈ ceramic shows a relative high sintering temperature (∼1000 °C) and good microwave dielectric properties as Q × f of 40,000 GHz, ?_r of 27.2, τ_f of 2.6 ppm/°C. It was found that the addition of a small amount of BCB can effectively lower the sintering temperature of Li₂MgTi₃O₈ ceramics from 1025 to 900 °C and induce no obvious degradation of the microwave dielectric properties. Typically, the 0.5 wt% BCB added Li₂MgTi₃O₈ ceramic sintered at 900 °C for 2 h exhibited good microwave dielectric properties of Q × f = 36,200 GHz (f = 7.31 GHz), ?_r = 26 and τ_f = −2 ppm/°C. Compatibility with Ag electrode indicates this material can be applied to low temperature-cofired ceramics (LTCC) devices.     

Low-loss microwave dielectrics using rock salt oxide Li2MgTiO4

Rock-salt-structured Li₂MgTiO₄ ceramic was prepared by the conventional mixed oxide route and its microwave dielectric properties were investigated. The microstructures of the ceramics were characterized by SEM. The dielectric properties of the ceramics exhibited a significant dependence on the sintering condition and crystal structure. A new microwave dielectric material, Li₂MgTiO₄ sintered at 1360 °C has a dielectric constant (?_r) of ∼17.25, a Q × f of ∼97,300 GHz (where f = 9.86 GHz, is the resonant frequency) and a τ_f of ∼-27.2 ppm/°C. The microwave dielectric properties of the ceramic are reported for the first time.     

Microwave dielectric properties of temperature stable Li2ZnxCo1−xTi3O8 ceramics

The Li₂Zn_xCo_1−xTi₃O₈ (x = 0.2-0.8) solid solution system has been synthesized by the conventional solid-state ceramic route and the effect of Zn substitution for Co on microwave dielectric properties of Li₂CoTi₃O₈ ceramics has also been investigated. The microwave dielectric properties of these ceramics show a linear variation between the end members for all compositions. The optimized sintering temperatures of Li₂Zn_xCo_1−xTi₃O₈ ceramics increase with increasing content of Zn. The specimen with x = 0.4 sintered at 1050 °C/2 h exhibits an excellent combination of microwave dielectric properties with ?_r = 27.7, Q_u × f = 57,100 GHz and τ_f = −1.0 ppm/°C.     

A new temperature stable microwave dielectric ceramics: ZnTiNb2O8 sintered at low temperatures

The phases, microstructure and microwave dielectric properties of ZnTiNb₂O₈-xTiO₂ composite ceramics with different weight percentages of BaCu(B₂O₅) additive prepared by solid-state reaction method have been investigated using the X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy-dispersive spectroscopy (EDS). The results showed that the microwave dielectric properties were strongly dependent on densification, grain sizes and crystalline phases. The sintering temperature of ZnTiNb₂O₈ ceramics was reduced from 1250 °C to 950 °C by doping BaCu(B₂O₅) additive and the temperature coefficient of resonant frequency (τ_f) was adjusted from negative value of −52 ppm/°C to 0 ppm/°C by incorporating TiO₂. Addition of 2 wt% BaCu(B₂O₅) in ZnTiNb₂O₈-xTiO₂ (x = 0.8) ceramics sintered at 950 °C showed excellent dielectric properties of ?_r = 38.89, Q × f = 14,500 GHz (f = 4.715 GHz) and τ_f = 0 ppm/°C, which represented very promising candidates as LTCC dielectrics for LTCC applications.     

Phase structure and electrical properties of (0.8 − x) BaTiO3-0.2Bi0.5Na0.5TiO3-xBaZrO3 lead-free piezoceramics

Lead-free piezoelectric ceramics (0.8 − x)BaTiO₃-0.2Bi_0.5Na_0.5TiO₃-xBaZrO₃ (BT-BNT-xBZ, 0 ≤ x ≤ 0.08) doped with 0.3 wt% Li₂CO₃ were prepared by conventional solid-state reaction method. With the Li₂CO₃ doping, all the ceramics can be well sintered at 1170-1210 °C. The phase structure, dielectric, ferroelectric and piezoelectric properties of the ceramics were investigated. Results show that a morphotropic phase boundary (MPB) between tetragonal and pseudocubic phases exists at x = 0.03-0.04. The addition of Zr can improve the piezoelectric properties of BT-BNT ceramics. Furthermore, a relaxor behavior is induced and the tetragonal-cubic phase transition shifts towards lower temperatures after the addition of Zr. The ceramics with x = 0.03 possess the optimum electrical properties: d₃₃ = 72 pC/N, k_p = 15.4%, ?_r = 661, P_r = 18.5 μC/cm², E_c = 34.1 kV/cm, T_c = 150 °C.     

High-dielectric-constant and low-loss microwave dielectric in the (1 − x)La(Mg0.5Ti0.5)O3-x(Ca0.8Sr0.2)TiO3 solid solution system

The microwave dielectric properties and microstructures of (1 − x)La(Mg_0.5Ti_0.5)O₃-x(Ca_0.8Sr_0.2)TiO₃ ceramics, prepared by a mixed oxide route, have been investigated. The forming of solid solutions was confirmed by the XRD patterns and the measured lattice parameters for all compositions. A near zero τ_f was achieved for samples with x = 0.5, although the dielectric properties varied with sintering temperature. The Q × f value of 0.5La(Mg_0.5Ti_0.5)O₃-0.5(Ca_0.8Sr_0.2)TiO₃ increased up to 1475 °C, after which it decreased. The decrease in dielectric properties was coincident with the onset of rapid grain growth. The optimum combination of microwave dielectric properties was achieved at 1475 °C for samples where x = 0.5 with a dielectric constant ?_r of 47.12, a Q × f value of 35,000 GHz (measured at 6.2 GHz) and a τ_f value of −4.7 ppm/°C.     

Enhancement microwave dielectric properties of La(Mg0.5Sn0.5)O3 ceramics by substituting Mg with Ni

The microwave dielectric properties of La(Mg_0.5−xNi_xSn_0.5)O₃ ceramics were examined with a view to their exploitation for mobile communication. The La(Mg_0.5−xNi_xSn_0.5)O₃ ceramics were prepared by the conventional solid-state method at various sintering temperatures. The X-ray diffraction patterns of the La(Mg_0.4Ni_0.1Sn_0.5)O₃ ceramics revealed no significant variation of phase with sintering temperatures. Apparent density of 6.71 g/cm³, dielectric constant (?_r) of 20.19, quality factor (Q × f) of 74,600 GHz, and temperature coefficient of resonant frequency (τ_f) of −85 ppm/°C were obtained for La(Mg_0.4Ni_0.1Sn_0.5)O₃ ceramics that were sintered at 1550 °C for 4 h.     

Microwave dielectric properties of (1 − x)ZnMoO4-xTiO2 composite ceramics

(1 − x)ZnMoO₄-xTiO₂ (x = 0.0, 0.05, 0.158, 0.25, and 0.35) composite ceramics were synthesized by the conventional solid state reaction process. The sintering behavior, phase composition, chemical compatibility with silver, and microwave dielectric properties were investigated. All the specimens can be well densified below 950 °C. From the X-ray diffraction analysis, it indicates that the triclinic wolframite ZnMoO₄ phase coexists with the tetragonal rutile TiO₂ phase, and it is easy for silver to react with ZnMoO₄ to form Ag₂Zn₂(MoO₄)₃ phase and hard to react with TiO₂. When the volume fraction of TiO₂ (x value) increasing from 0 to 0.35, the microwave dielectric permittivity of the (1 − x)ZnMoO₄-xTiO₂ composite ceramics increases from 8.0 to 25.2, the Q_f value changes in the range of 32,300-43,300 GHz, and the temperature coefficient τ_f value varies from −128.9 to 157.4 ppm/°C. At x = 0.158, the mixture exhibits good microwave dielectric properties with a ?_r = 13.9, a Q_f = 40,400 GHz, and a τ_f = +2.0 ppm/°C.     

Elucidating the dielectric properties of Mg2SnO4 ceramics at microwave frequency

This study investigated the potential applications of microwave dielectric properties of Mg₂SnO₄ ceramics in mobile communication. Mg₂SnO₄ ceramics were prepared using a conventional solid-state method. The X-ray diffraction patterns of the Mg₂SnO₄ ceramics revealed no significant variation of phase with sintering temperature. A maximum density of 4.62 g/cm³, a dielectric constant (?_r) of 8.41, a quality factor (Q × f) of 55,100 GHz, and a temperature coefficient of resonant frequency (τ_f) of −62 ppm/ °C were obtained when Mg₂SnO₄ ceramics were sintered at 1550 °C for 4 h.     

Effect of addition of Ba(W0.5Cu0.5)O3 in Pb(Mg1/3Nb2/3)O3-Pb(Zn1/3Nb2/3)O3-Pb(Zr0.52Ti0.48)O3 ceramics on the sintering temperature, electrical properties and phase transition

In this work, we report on the Pb(Mg_1/3Nb_2/3)O₃-Pb(Zn_1/3Nb_2/3)O₃-Pb(Zr_0.52Ti_0.48)O₃ (PMN-PZN-PZT) ceramics with Ba(W_0.5Cu_0.5)O₃ as the sintering aid that was manufactured in order to develop the low-temperature sintering materials for piezoelectric device applications. The phase transition, microstructure, dielectric, piezoelectric properties, and the temperature stability of the ceramics were investigated. The results showed that the addition of Ba(W_0.5Cu_0.5)O₃ significantly improved the sintering temperature of PMN-PZN-PZT ceramics and could lower the sintering temperature from 1005 to 920 °C. Besides, the obtained Ba(W_0.5Cu_0.5)O₃-doped ceramics sintered at 920 °C have optimized electrical properties, which are listed as follows: (K_p = 0.63, Q_m = 1415 and d₃₃ = 351 pC/N), and high depolarization temperature above 320 °C. These results indicated that this material was a promising candidate for high-power multilayer piezoelectric device applications.     

Low temperature sintering and microwave dielectric properties of (Mg0.7Zn0.3)0.95Co0.05TiO3 ceramics with BaCu(B2O5) additions

The effects of BaCu(B₂O₅) additives on the sintering temperature and microwave dielectric properties of (Mg_0.7Zn_0.3)_0.95Co_0.05TiO₃ ceramics were investigated. The (Mg_0.7Zn_0.3)_0.95Co_0.05TiO₃ ceramics were not able to be sintered below 1000 °C. However, when BaCu(B₂O₅) were added, they were sintered below 1000 °C and had the good microwave dielectric properties. It was suggested that a liquid phase with the composition of BaCu(B₂O₅) was formed during the sintering and assisted the densification of the (Mg_0.7Zn_0.3)_0.95Co_0.05TiO₃ ceramics at low temperature. BaCu(B₂O₅) powders were produced and used to reduce the sintering temperature of the (Mg_0.7Zn_0.3)_0.95Co_0.05TiO₃ ceramics. Good microwave dielectric properties of Q × f = 35,000 GHz, ?_r = 18.5.0 and τ_f = −51 ppm/°C were obtained for the (Mg_0.7Zn_0.3)_0.95Co_0.05TiO₃ ceramics containing 7 wt.% mol% BaCu(B₂O₅) sintered at 950 °C for 4 h.     

Low-firable high-K dielectric in the Zrx(Zn1/3Nb2/3)1−xTiO4 ceramic system

Composite ceramics in the solid solution of Zr_x(Zn_1/3Nb_2/3)_1−xTiO₄ (x = 0.1-0.4) have been prepared by the mixed oxide route. Formation of solid solution was confirmed by the X-ray diffraction patterns. The microwave dielectric properties, such as dielectric constant (?_r), Q × f value and temperature coefficient of resonant frequency (τ_f) have been investigated as a function of composition and sintering temperature. With x increasing from 0.1 to 0.4, the dielectric constant decreases from 70.9 to 43.2, and the τ_f decreases from 105 to 55 ppm/°C. The Q × f value, however, increases with increasing x value to a maximum 26,600 GHz (at 6 GHz) at x = 0.3, and then decreases thereafter. For low-loss microwave applications, a new microwave dielectric material Zr_0.3(Zn_1/3Nb_2/3)_0.7TiO₄, possessing a fine combination of microwave dielectric properties with a high ?_r of 51, a high Q × f of 26,600 GHz (at 6 GHz) and a τ_f of 70 ppm/°C, is suggested.     

Structure and dielectric characterization of xNd(Mg1/2Ti1/2)O3-(1 − x)Ca0.6La0.8/3TiO3 in the microwave frequency range

The crystal structures, phase compositions and the microwave dielectric properties of the xLa(Mg_1/2Ti_1/2)O₃-(1 − x)Ca_0.8Sr_0.2TiO₃ composites prepared by the conventional solid state route have been investigated. The formation of solid solution is confirmed by the XRD patterns. Doping with B₂O₃ (0.5 wt.%) can effectively promote the densification and the dielectric properties of xNd(Mg_1/2Ti_1/2)O₃-(1 − x)Ca_0.6La_0.8/3TiO₃ ceramics. It is found that xNd(Mg_1/2Ti_1/2)O₃-(1 − x)Ca_0.6La_0.8/3TiO₃ ceramics can be sintered at 1375 °C, due to the liquid phase effect of B₂O₃ addition observed by Scanning Electronic Microscopy. At 1375 °C, 0.4Nd(Mg_1/2Ti_1/2)O₃-0.6Ca_0.6La_0.8/3TiO₃ ceramics with 1 wt.% B₂O₃ addition possesses a dielectric constant (?_r) of 49, a Q × f value of 13,000 (at 8 GHz) and a temperature coefficients of resonant frequency (τ_f) of 1 ppm/°C. As the content of Nd(Mg_1/2Ti_1/2)O₃ increases, the highest Q × f value of 20,000 GHz for x = 0.9 is achieved at the sintering temperature 1400 °C.     

Crystal structure and dielectric properties of La(Mg0.5Ti0.5)O3-Ca0.8Sm0.4/3TiO3 solid solution system at microwave frequencies

The crystal structure and the dielectric properties of (1 − x)La(Mg_0.5Ti_0.5)O₃-xCa_0.8Sm_0.4/3TiO₃ ceramics have been investigated. Ca_0.8Sm_0.4/3TiO₃ was employed as a τ_f compensator and was added to La(Mg_0.5Ti_0.5)O₃ to achieve a temperature-stable material. The formation of (1 − x)La(Mg_0.5Ti_0.5)O₃-xCa_0.8Sm_0.4/3TiO₃ solid solutions were confirmed by the XRD results and the measured lattice parameters for all compositions. The dielectric properties are strongly correlated to the sintering temperature and the compositional ratio of the specimens. Although the ?_r of the specimen could be boosted by increasing the amount of Ca_0.8Sm_0.4/3TiO₃, it would instead render a decrease in the Q × f. The τ_f value is strongly correlated to the compositions and can be controlled by the existing phases. A new microwave dielectric material 0.45La(Mg_0.5Ti_0.5)O₃-0.55Ca_0.8Sm_0.4/3TiO₃, possessing a fine combination of microwave dielectric properties with an ?_r of 47.83, a Q × f of 26,500 GHz (at 6.2 GHz) and a τ_f of −1.7 ppm/°C, is proposed as a very promising candidate material for today's 3G applications.     

Phase evolution and microwave dielectric properties of TiO2-modified (Mg0.95Co0.05)2TiO4 ceramics

Phase evolution and microwave dielectric properties of (1 − x)(Mg_0.95Co_0.05)₂TiO₄-xTiO₂ (x = 0-1) ceramics prepared by the conventional mixed oxide route have been investigated. Increasing the TiO₂ content would lead to a main phase transformation from (Mg_0.95Co_0.05)₂TiO₄ to (Mg_0.95Co_0.05)TiO₃, (Mg_0.95Co_0.05)Ti₂O₅ and then TiO₂. Not only did the TiO₂ addition compensate the τ_f, it also lowered the sintering temperature of specimen. A huge drop of Q × f occurs at a 40-60 mol% TiO₂ addition was attributed to the formation of (Mg_0.95Co_0.05)Ti₂O₅ phase. Specimen with x = 0.78 can possess an excellent combination of microwave dielectric properties: ?_r ∼ 24.77, Q × f ∼ 38,500 GHz and τ_f ∼ −1.3 ppm/°C.     

Mg-substituted ZnNb2O6-TiO2 composite ceramics for RF/microwaves ceramic capacitors

Microstructure and microwave dielectric properties of Mg-substituted ZnNb₂O₆-TiO₂ microwave ceramics were investigated. Mg acted as a grain refining reagent and columbite phase stabilization reagent. With an increasing Mg content, the amount of ixiolite (Zn, Mg) TiNb₂O₈ decreased, and the amount of (Zn_0.9Mg_0.1)_0.17Nb_0.33Ti_0.5O₂ and columbite increased. ZnO-Nb₂O₅-1.75TiO₂-5 mol.%MgO exhibited excellent dielectric properties (at 950 °C): ?_r = 35.6, Q × f = 16,000 GHz (at 5.6 GHz) and τ_f = −10 ppm/°C. The material was applied successfully to make RF/microwaves ceramic capacitor, whose self-resonance frequency was 19 GHz at low capacitance of 0.13 pF.     

Dielectric properties and crystal structure of La(Mg1/2Ti1/2)O3 ceramics with Mg substituted by Co

Solid solutions of (1 − x)La(Co_1/2Ti_1/2)O₃-xLa(Mg_1/2Ti_1/2)O₃ were used to prepare La(Mg_1−xCo_x)_1/2Ti_1/2O₃ using solid-state synthesis. X-ray diffraction patterns of the sintered samples revealed single phase formation. A maximum density of 6.01 g/cm³ was obtained for La(Mg_1−xCo_x)_1/2Ti_1/2O₃ (x = 1) ceramics sintered at 1375 °C for 4 h. The maximum values of the dielectric constant (?_r = 29.13) and the quality factor (Q × f = 80,000 GHz) were obtained for La(Mg_1−xCo_x)_1/2Ti_1/2O₃ with 1 wt% ZnO additive sintered at 1375 °C for 4 h. The temperature coefficient of resonant frequency τ_f was −59 ppm/°C for x = 0.3.     

Synthesis, structure, and properties of Li2Pb2CuB4O10 with isolated [CuB4O10] units

The copper borate Li₂Pb₂CuB₄O₁₀ has been synthesized in air by the standard solid-state reaction at temperature in the range 550-650 °C and the structure of Li₂Pb₂CuB₄O₁₀ was determined by single-crystal X-ray diffraction. Li₂Pb₂CuB₄O₁₀ crystallizes in the monoclinic space group C2/c (no. 15) with a = 16.8419(12), b = 4.7895(4), c = 13.8976(10) Å, and β = 125.3620(10)°, V = 914.22(12) Å³, and Z = 4, as determined by single-crystal X-ray diffraction. The Li₂Pb₂CuB₄O₁₀ structure exhibits isolated units of stoichiometry [CuB₄O₁₀]⁶⁻ that are built from CuO₄ distorted square planes and triangular BO₃ groups. The IR spectroscopy and thermal analysis investigations of Li₂Pb₂CuB₄O₁₀ are also presented.     

Fabrication of Nd:YAG transparent ceramics with both TEOS and MgO additives

Neodymium doped YAG transparent ceramics were fabricated by vacuum reactive sintering method using commercial α-Al₂O₃, Y₂O₃ and Nd₂O₃ powders as the starting materials with both tetraethyl orthosilicate (TEOS) and MgO as sintering aids. The morphologies and microstructure of the powders and Nd:YAG transparent ceramics were investigated. Fully dense Nd:YAG ceramics with average grain size of ∼10 μm were obtained by vacuum sintering at 1780 °C for 8 h. No pores and grain-boundary phases were observed. The in-line transmittance of the ceramic was 83.8% at 1064 nm.