降解淀粉与乙烯基类单体接枝聚合物的合成及应用

适当降解的玉米淀粉与乙烯基类单体在引发剂作用下通过接枝聚合得到了改性淀粉鞣剂。当体系中w (降解淀粉 ) =10 %、w (乙烯基类单体 ) =2 0 %、引发剂质量为反应物质量的2 .0 %、反应温度为 5 0℃、反应时间为 1 5h时所得聚合物的接枝百分率为 87%、接枝效率为94%及接枝频率为 43。用其预鞣时可减少铬鞣剂用量 30 %～ 5 0 % ,铬鞣废液中铬含量降低到 ρ(Cr2 O3) =0 .2 6g/L ,用其复鞣时所得成革的选择填充性显著。成品革丰满柔软 ,粒面细腻。     

Fe_3O_4/P(St-CBA)核壳磁性复合微球的制备及性质

运用分散聚合法制备出Fe3O4 /P(St -CBA)核壳磁性复合微球。该微球粒径为 0 .0 75～0 .70 0 μm、w(Fe3O4 ) =0 .0 5 %～ 0 .90 % ,呈规整球型 ,表面光滑 ,在 0 .0 5T磁场中的磁响应性为3.0cm/min。制备微球的最佳条件为 :w(磁流体 ) =0 .5 %～ 3 .0 %、w(马来酸酐 ) =0 .0 %～2 .0 %、w(无水乙醇 ) =30 .0 %～ 70 .0 %。     

添加Fe2O3、Al2O3和SiO2纳米粉对MgO烧结性能的影响

以烧结镁砂为主原料,分别以粒度20～60 nm的SiO2纳米粉、粒度20～40 nm的Fe2O3纳米粉和粒度50 nm的Al2O3纳米粉(纯度(w)均为99.9%)为添加剂,设计了添加剂加入量(w)分别为1%、3%、5%(其余为烧结镁砂)的9种试样。配料后,外加10%(w)的分散剂和5%(w)的丙酮,研磨10min后,以100 MPa压力制成2.54 mm×2.54 mm的试样,在电炉中以5℃.min-1的升温速度分别升温至1 300、1 500和1 620℃保温4 h,冷却后分析试样的体积密度、显气孔率、相     

用玉米秸秆制备羧甲基纤维素

玉米秸秆为原料制备羧甲基纤维素 (CMC) ,最佳条件为 :m (纤维素 )∶m (NaOH)∶m(ClCH2 COOH) =1 0∶1 0∶1 2 ,以w (C2 H5OH) =85 %的酒精为溶剂 ,碱化温度 30℃ ,时间 6 0min ,醚化温度 70℃ ,时间 15 0min ,产品黏度 40 0～ 6 0 0mPa·s,取代度 0 6～ 0 7,有效成分质量分数 >80 %     

抗高温抑制型钻井液降滤失剂的合成与评价

以甲基丙烯酰氧乙基三甲基氯化铵(DMC)、对苯乙烯磺酸钠(SSS)、丙烯酰胺(AM)和2-丙烯酰胺基-2-甲基丙磺酸(AMPS)为单体,(NH_4)_2S_2O_8-Na HSO_3为引发剂,采用自由基水溶液聚合方式合成了一种抗高温钻井液降滤失剂。通过合成条件的单因素实验评价了聚合物的降滤失性能,用红外光谱法对共聚物的结构进行了表征。实验结果表明,聚合物质量分数为2%时,淡水、饱和盐水以及复合盐水钻井液的FL_(API)分别为5.2、7.4 m L和6.8 m L,淡水钻井液经200℃老化16 h后的FL_(API)为10.6 m L,饱和盐水钻井液经180℃老化16 h后的FL_(API)为16.4 m L。聚合物质量分数为1%的淡水钻井液经100℃老化16 h后的页岩相对回收率为97.1%。     

稳定煤岩地层的钻井液体系研究

当下我国石油行业急需多种技术,尤其是具有较优的常规性能(如流变性、滤失性)的钻井液。本文通过综合考虑成本和环境保护因素,采用水基钻井液体系,初步确立了实验所用钻井液体系:4%～5%膨润土+0. 2%中分子降失水剂JNP(聚合物)+0. 5%～1. 5%LV-CMC+2%～3%磺化酚醛树脂+1%～1. 5%降粘降滤失剂Redu~(2+)2%～3%干粉/磺化沥青+1%乳化沥青,通过钻井液流变性、滤失量以及抑制性和封堵性实验等,对钻井液体系性能进行表征,优选出这种适用于煤岩地层的稳定井壁钻井液体系。     

异形截面POY生产工艺探讨

研究五叶形POY的开发生产。干燥后切片的w(H2 O)为 (2 4～ 3 0 )× 10 - 6 ,[η]为 0 .64 5～ 0 .65 1dL/g ,80～ 10 0目金属砂作过滤介质 ,纺丝温度在 2 97～ 3 0 0℃ ,在喷丝板附近设置纺丝隔板延缓冷却 ,侧吹风速 0 .3 0～ 0 .40m/s ,纺丝速度 270 0～ 3 0 0 0m/min ,超喂率 1.0 %～ 1.5 %进行卷绕产品优良 ,使后加工产品DTY的一等品率达到 90 %。     

一种新型聚丁二烯

MoCI_4OR与适当烷基铝组成的催化体系,对丁二烯聚合有很高的催化活性.在聚合温度为70℃、催化剂用量Mo/Bd比为5×10~(-5)时,转化率可达80%以上.聚合温度为30—70℃范围内所得聚合物分子量分布宽度指数为1.5—2.0.烯丙基卤等极性添加剂可以调节聚合物分子量和链结构,以烯丙基碘效果最好;随着烯丙基碘用量的增加,聚合物分子量降低,1,2-链节增多,链结构规整性增加.聚合物基本性能是:1,2-链节含量,88-97%;特性粘数,1.8—6.2(dl/g)玻璃化温度,-10—-27℃;屈服强度,6.5—8.5(kg/cm~2);断裂强度,12—25(kg/cm~2)断裂伸长,1700—2900%.     

3,3′-二氯联苯胺的合成

以邻硝基氯苯 (Ⅰ)为起始原料 ,经过三步化学反应合成 3,3′ 二氯联苯胺 (Ⅳ ) :Ⅰ在 0 .2g 1,4 萘醌催化下与CH2 O NaOH[m(NaOH)∶m(CH2 O) =0 .95∶1 0 0 ]在 5 6～ 5 7℃反应 7h ,得到 2 ,2′ 二氯氧化偶氮苯 (Ⅱ) ,产率 91.0 % ;Ⅱ在 0 .5gAl-Ni合金及 0 .3g 1,4 萘醌催化下与水合肼在 5 6～ 5 7℃反应 7.5h ,得到 2 ,2′ 二氯氢化偶氮苯 (Ⅲ) ,产率 97.0 % ;Ⅲ在盐酸中分别于 5℃反应 2h、于 10℃反应 11h、于 2 3～2 4℃反应 11h ,得到Ⅳ ,产率 96 .9%。Ⅳ的总产率可达 85 .5 % ,纯度w (Ⅳ) =97.7%     

已公开的部分化工专利

低砷黄磷的制造方法该方法在ω(ＨＮＯ3 )为 5 %～ 15 %的稀硝酸中加入工业粗黄磷和 0 .1%～ 5 .0 %的含卤素元素化合物添加剂 ,加热至 5 5～ 6 5℃ ,在 2 0 0～ 6 0 0ｒ/ｍｉｎ下搅拌 ,反应 1～ 3ｈ ,冷却后再分离出磷。具有磷回收率高、脱砷率高、工艺流程简单、反应时间短、反应过程危险性小等优点。 (公开号ＣＮ12 5 70 40Ａ ,申请人云南工业大学 )●　用磷渣生产水泥的方法其配比 (质量分数 )为 6 0 %～ 70 %的熟料 ,30 %～ 40 %磷渣、2 %～ 3%的石膏及 2 %～ 10 %的烧矾土 ,按常规的生产方法制得。由于磷渣渗入量高于 30 % ,每吨水泥…     

抗高温耐盐型钻井液用降滤失剂的合成与性能评价

选用对苯乙烯磺酸钠(SSS)、2-丙烯酰胺基-2-甲基丙磺酸(AMPS)、丙烯酰胺(AM)单体为原料,利用自由基聚合的方式,得到一种抗高温耐盐聚合物降滤失剂.通过傅里叶红外光谱分析(FT-IR)表明合成产物结构与设计结构相符.当降滤失剂加量为1.8%时,室温下和210℃下淡水基浆的滤失量分别为7.9mL和13.5mL;在25%NaCl和3%CaCl₂的盐水泥浆中,钻井液的滤失量分别为14.8mL和11.0mL.通过扫描电镜(SEM)可以分析钻井液形成的滤饼的微观结构,由此得到降滤失剂作用的机理是:当降滤失剂吸附在黏土表面时,降滤失剂可以使黏土颗粒在钻井液中分散,从而形成致密的滤饼来减少滤失量.     

国内外黏土水化抑制剂研究现状与发展趋势

黏土水化抑制剂在钻井液中的添加可有效降低钻井事故发生,但存在效果不明显、抗温性能尚待提高等缺点。本文简述了国内外黏土水化抑制剂研究现状并分析了其发展趋势。从研究历程来看,黏土水化抑制剂大体上经过了从无机离子型向有机铵（胺）型过渡并逐步成熟于聚合物型的过程。从最新研究结果来看,聚醚胺型抑制剂为主流研究对象,由此形成的高性能水基钻井液在国内外广泛应用;超支化聚合物型抑制剂因具有体型结构而具有较好抗温、抗盐性能而颇具发展优势;传统共聚物型抑制剂分子量大,在高温高密度钻井液中难以适用,仍有改进空间。指出了今后发展趋势是充分利用生物质资源,开发绿色、环保高效的黏土水化抑制剂;研究低聚物抑制剂,提高抑制剂的抗温性、普适性和一剂多效性;摆脱传统钻井液处理剂之间化学作用力观念束缚,探索超支化抑制剂的开发,积极有效结合纳米技术与钻井流体之互补点,以促进钻井液及相关技术发展。     

新型聚合物钾盐抑制泥页岩水化的性能与机理

泥页岩水化膨胀是井壁失稳的重要原因。本文通过膨润土压片浸泡与线性膨胀实验、页岩钻屑滚动回收实验以及流变性、滤失性测试,评价了一种新型聚合物钾盐抑制剂聚阴离子纤维素钾（K-PAC）的抑制性能及其对水基钻井液流变性和滤失性的影响。评价结果表明,0.5% K-PAC的抑制泥页岩水化膨胀的性能明显优于5% KCl、2%聚醚胺-D230（PEA-D230）,与0.5%聚丙烯酰胺钾盐（K-PAM）相近;0.5% K-PAC的增黏提切、降滤失性能要优于0.5% K-PAM。通过扫描电镜和X射线衍射分析了K-PAC的抑制机理,结果表明,K-PAC的阳离子部分（K⁺）能够进入膨润土晶层中并置换出水化钠离子,从而起到抑制黏土晶层膨胀的作用;K-PAC的阴离子部分吸附在黏土颗粒上起到护胶、降滤失的作用,二者协同增效,从而起到强抑制作用。由于K-PAC由聚阴离子纤维素和K⁺构成,对环境友好、成本低廉。因此,K-PAC具有成为低成本、环保型、强抑制性的水基钻井液抑制剂的巨大潜力。     

Hydrotalcite synthesis via co-precipitation reactions using MgO and Al(OH)3 precursors

Hydrotalcite (Mg₆Al₂(OH)₁₆(CO₃)·4H₂O), also known as aluminum-magnesium layered double hydroxide (LDH) or anionic clay, is a synthetic compound that was broadly investigated in the past decade due to its many potential applications, such as clinic anti-acid, catalyst support, adsorptive flotation, flame retardant, acid scavengers in polymer composites and as a raw material for high temperature insulating porous ceramics. This compound is usually produced by controlled chemical equilibrium shifting processes (such as co-precipitation) that requires various other purification steps (centrifugation, for example) and careful drying (freeze drying or ultrafiltration). In this paper, a novel route to synthesize hydrotalcite is presented, based on the hydration, dissolution and co-precipitation reactions carried out almost simultaneously in aqueous suspension containing reactive magnesium oxide and aluminum hydroxide. Compared to other methods (the regular co-precipitation, particularly), it presents various technological advantages such as low time-energy consumption, no further purification step requirement, high output and competitive production costs.     

纳米材料在抗高温钻井液中的应用进展

纳米材料具有尺寸较小、热稳定性强等性质,使其可作为钻井液处理剂来提高钻井液的抗高温性能。抗高温钻井液用纳米材料一般采用将材料纳米化或将纳米材料与聚合物复合制得,大致可分为无机纳米材料、聚合物纳米球和纳米复合材料三类。此外,对纳米材料进行结构优化可提高其热稳定性和分散性,用于封堵岩层中纳米孔隙、降低钻井液滤失量、改善钻井液流变性和提高钻井液抗温能力。本文简要阐述高温对钻井液性能的影响,分析纳米材料在钻井液中的作用,重点介绍不同类型纳米材料在抗高温（≥150℃）钻井液中的应用,尤其是对钻井液流变性能和降滤失效果的影响。最后指出纳米材料作为钻井液处理剂未来发展应向着环保、合成工艺简化和室内与现场研究相结合等方向突破。     

Hyperbranched polyglycerols,obtained from environmentally benign monomer,as reactive clays inhibitors for water‐based drilling fluids

To prevent the degradation of the borehole and also the disintegration and dispersion of drilled cuttings, different shale stabilizing additives are used in water‐based drilling fluids (WBFs). Glycols, poly(ethylene glycol), glycerols, and polyglycerol derivatives, also called polyols, have been used to inhibit shales containing reactive clays in WBF. These additives are normally used in conjunction with KCl to reduce clay swelling and dispersion of drilled cuttings. Highly branched polymers have become an important field in current polymer science. Such materials typically exhibit compact, globular structures in combination with an exceptionally high number of sites with functional groups. They have unique properties that differ significantly from their linear counterparts, and the hyperbranched polyglycerol (hPG) is an important hyperbranched polymer that can be produced from an environmentally benign monomer, the glycerol carbonate. In this article, the clay inhibitive properties of hPG were evaluated by different test methods including bentonite inhibition test, cuttings recovery, and X‐ray diffraction measurements. The results show that the hPG has a great potential to be used as an environmental friendly inhibitor additive in WBFs. © 2014 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2014 , 131, 40384.     

一种深水用白油基恒流变钻井液体系的建立与评价

主要针对深海钻井作业设计了一种白油基恒流变钻井液。我们主要通过添加有机土和高分子聚合物来达到钻井液恒流变的目的。还评价了有机土的种类与含量、高分子聚合物的含量、油水比和钻井液密度对白油基钻井液流变性(动切力YP)的影响。     

智能钻井液的化学体系及辅助系统研究进展

智能钻井液是石油钻井行业的全新研究方向,与传统钻井液的指向性不足、自适应能力弱、监测困难以及人工操作过于繁琐等问题相比,智能钻井液拥有更好的针对性、钻井液性能也更加突出,同时能够大幅缩减人工干预程度,因此对钻井液智能化的研究具有重要意义。本文对智能化钻井液化学体系的合成研发、钻井液智能辅助系统的功能强化、开发应用以及当前主要研究现状进行综述,指出了当前智能钻井液技术虽在化学体系、智能传送及监测装置、智能平台等研究方向都有所发展,但在智能化学体系方面尚不能实现对钻井液性能参数的精准控制,在智能钻井液的研制、智能钻井液平台建设方面智能方向过于单一,不能满足当前钻井现场需要,建议未来的钻井液智能化应多向综合性多元化方向发展。     

Removal of copper by modified chitosan adsorptive membrane

In this study, a novel adsorptive membrane was prepared from chitosan as the functional polymer and some additive blend solutions by solution casting method. The modified chitosan membrane was characterized by FTIR and its Water Swelling Ratio (WSR). The adsorption of copper ions on the adsorptive membrane was investigated in batch experiments. The results obtained from the experiments indicated that the membrane had a good adsorption capacity for copper ions, the optimal ionic strength and pH were 0.1 and 5–6, respectively. Compared with the Langmuir isotherm model, the experimental data were found to be following the Freundlich model.     

智能钻井液的化学体系及辅助系统研究进展

传统钻井液的指向性不足、自适应能力弱、监测困难且人工操作过于繁琐,智能钻井液具有更强的针对性,钻井液性能也更加突出,同时能够大幅缩减人工干预程度。该文对智能钻井液化学体系的研发、钻井液智能辅助系统的功能强化及开发应用进行了综述,指出了当前智能钻井液技术虽在化学体系、智能传送及监测装置、智能平台等方面都有所发展,但在智能化学体系方面尚不能实现对钻井液性能参数的精准控制,智能钻井液的研制及其平台建设智能方向过于单一,不能满足当前钻井现场需要,建议未来的钻井液智能化应向综合性多元化方向发展。