热处理温度对Ni-W-P化学镀层结构和性能的影响

为了改善Ni-W-P化学镀层的耐蚀性,提高镀层硬度,将其在不同温度下进行热处理,通过扫描电镜、能谱分析、X射线衍射等技术研究了热处理温度对镀层结构、耐蚀性、硬度及表面形貌的影响.结果表明:热处理后,镀层具有较高的硬度,400℃时高达1 120 HV;镀态镀层为非晶态,随着热处理温度的升高,镀层经历了非晶态、混晶态、晶态过程,且热处理后镀层晶粒长大.     

镍钨磷合金电镀层的性能研究

通过对Ni-W-P合金电镀层在200 ℃、0.5 h热处理后的XRD和SEM分析发现,不论镀态还是热处理态,镀层结构均为非晶态,且晶粒均匀,晶界清楚,热处理后晶粒略长大.在盐酸和硫酸介质中的耐蚀性测试结果表明,热处理后镀层的耐蚀性略高于镀态的耐蚀性;通过析氢性能测得镍基合金的电催化活性依次为:Ni-W-P＞Ni-P＞Ni-W＞Ni.     

化学镀Ni-W-P-SiC复合镀层的性能研究

研究了化学镀Ni W P SiC复合镀层的性能。结果表明,该化学复合镀层在HCl、H2SO4、H3PO4和FeCl34种腐蚀介质中的耐蚀性优于1Cr18Ni9Ti不锈钢的,经600℃以下热处理的镀层的耐蚀性优于镀态镀层的,其中400℃热处理后镀层的耐蚀性最好。镀层硬度和耐磨性随温度的升高而升高,在400～600℃之间硬度和耐磨性都较高,加热温度继续升高,镀层硬度和耐磨性下降较快。在400℃热处理条件下,随着热处理时间的延长,镀层的硬度和耐磨性提高,当热处理时间达到3h时,镀层硬度和耐磨性最高,若继续延长时间,镀层的硬度和耐磨性又降低。     

氢气气氛中热处理对Ni-W合金镀层组织和性能的影响

研究了在氢气气氛中,不同的热处理温度对Ni-W合金镀层表面状态、相结构及显微硬度和耐蚀性的影响。结果表明,镀态的Ni-W合金镀层存在一种未知相(2θ≈41.4°),热处理过程中这一未知相消失,同时镀层中析出NiW、Ni_4W等沉淀相。随着热处理温度的升高,镀层的晶粒度逐渐增大,镀层在热处理过程中形成的孔隙逐渐增多。当热处理温度达到1 000℃后,镀层表面出现明显的裂纹,同时镀层中可还原形成单质W。Ni-W合金镀层的显微硬度经热处理后显著增大,热处理温度为500℃时镀层的显微硬度最大,同时镀层具有与镀态Ni-W合金相近的耐蚀性,热处理温度进一步升高后镀层的耐蚀性降低。     

热处理对化学沉积Ni-Zn(Fe)-P合金结构和性质的影响

通过差示扫描量热(DSC)、X射线衍射(XRD)、扫描电镜(SEM)、电化学买验和失重买验研究了热处理对化学沉积Ni-Zn(Fe)-P合金结构、显微硬度、表面形貌和耐蚀性的影响。镀态镀层由非晶相和立方镍相组成(多晶态结构),在384．8℃晶化为四方Ni3P和Ni5Zn12相。镀层显微硬度随热处理温度升高而升高,相反地,500℃后随热处理温度升高而下降。在3．5％(质量分数)NaCl溶液中(pH7．0)镀态镀层的耐蚀性比经热处理过的镀层好。     

铝材化学镀Ni-W-P溶液中硝酸镧含量对镀层性能的影响

为了提高铝材Ni-W-P镀层的耐腐蚀性,在镀液中加入La(NO3)3,在1060铝表面化学镀Ni-W-P合金层.采用电化学法和失重法分析了合金镀层的耐蚀性,采用扫描电镜观察合金镀层的形貌,采用X射线衍射仪分析了镀层的结构;研究了La(NO3)3含量对Ni-W-P镀层沉积速率、孔隙率、腐蚀速率、腐蚀电位、腐蚀电流、交流阻抗、维氏硬度等性能的影响;对镀层进行热处理,研究了热处理对合金镀层性能的影响.结果表明:当镀液中La(NO3)3质量分数为1.0％时,所得镀层的沉积速率最大,为65.7 g/(m2·h),维氏硬度最高,为80.3 HV,孔隙率最低,镀层的耐蚀性能最好,镀层包状物颗粒大小均匀、紧密、无缺陷;经100～500℃热处理后,镀层硬度有所提高,但耐蚀性有不同程度下降,经300℃热处理后,合金维氏硬度高达136 HV,是未热处理的1.7倍.     

脉冲电沉积Ni-W-P合金工艺的研究

为了研究Ni-W-P合金脉冲电沉积中脉冲参数对镀速和镀层中钨、磷含量的影响以及对镀层耐蚀性和硬度的影响,采用称重法、硫酸浸泡法、日本岛津EPMA-1600型电子探针以及HX-1型显微硬度计对Ni-W-P合金工艺进行了研究.结果表明,镀层的沉积速率、镀层成分及镀层的性能都随脉冲频率和占空比的变化而变化;Ni-W-P镀层的脉冲电沉积速率比直流电沉积大,脉冲镀层的耐蚀性和硬度都优于直流镀层,其耐蚀性还优于1Cr18Ni9Ti不锈钢.本工艺操作方便,镀层性能稳定.     

非晶态Ni-Cu-P合金镀层的结构及性能研究

研究了化学镀Ni-Cu-P非晶态合金镀层的成分，结构、硬度及形貌等性能．研究结果表明：镀层中铜含量随着镀液中硫酸铜浓度的增加而提高，镍、磷含量随着镀液中硫酸铜浓度的增加而降低。由于铜具有优先析出的特征，导致合金镀层中Cu／Ni质量比远高于镀液中Cu^2＋／Ni^2＋质量比．在镀态下，Ni-Cu-P合金镀层为含铜、磷原子的镍基饱合固溶体．X-ray衍射表明：在镀态下及300℃以下热处理时，Ni-7．929％Cu-8．227％P（质量分数）合金镀层为非晶态结构，经400℃热处理后，开始有热力学平衡相Ni3P和Cu3P析出，合金镀层已转为晶态结构．Ni-7．929％Cu-8．227％P合金镀层的硬度随热处理温度的升高而增加，在400℃时，硬度达到最大值（845HV），热处理温度继续升高，合金镀层的硬度反而下降．     

化学镀Ni-W-P合金层的组织结构与耐蚀性能的研究

本文采用x射线衍射、电子衍射、扫描及透射电子显微镜和阳极极化曲线测定等方法研究化学镀Ni-W-P合金层的组织结构和耐蚀性能。结果表明,随含磷量的增加,Ni-W-P的结构由晶态转变为非晶态。在250～500℃热处理时,Ni-W-P镀层的抗蚀性降低,但是600℃以上热处理,抗蚀性又明显增加。     

回火温度对Ni-P基化学镀层显微硬度和耐蚀性的影响

研究了回火温度对Ni P基化学镀层显微硬度和耐蚀性的影响。结果表明 ,Ni P、Ni Co P、Ni Co P SiC 3种镀层的硬度随着回火温度的升高总体上呈上升趋势 ,并在一定温度范围内出现了硬度峰值 ;3种镀层的腐蚀率随回火温度的升高而增大 ,在 40 0℃时达到最大值     

Estimation of Parameters of Universal Distribution of Moments of Failure of Products

A method is proposed for estimating the parameters of a mixture of exponential and Weibull distributions for which the accuracy of preliminary estimates obtained by graphical analysis is refined in accordance with the criterion of maximum likelihood. The efficiency of the proposed method is supported by the results of statistical modeling.     

Analysis of the rate of propagation of the wave of change of boiling modes

An approximate analytical expression is derived for the velocity of the front of the wave of change of boiling modes on a rod and on a plate. The impact of the Thomson effect and of the heater orientation in the gravity field is included. Adequate agreement is demonstrated between the derived relations and experimental data.     

Evaluation of optical properties of highly scattering media by moments of distributions of times of flight of photons

A novel method for the determination of the optical properties of tissue from time-domain measurements is presented. The data analysis is based on the evaluation of the first moment and the second centralized moment, i.e., the mean time of flight and the variance of the measured distribution of times of flight (DTOF) of photons injected by short (picosecond) laser pulses. Analytical expressions are derived for calculation of absorption and of reduced scattering coefficients from these moments by application of diffusion theory for infinite and semi-infinite homogeneous media. The proposed method was tested on experimental data obtained with phantoms, and results for absorption and reduced scattering coefficients obtained by the proposed method are compared with those obtained by fitting of the same data with analytical solutions of the diffusion equation. Furthermore, the accuracy of the moment analysis was investigated for a range of integration limits of the DTOF. The moment analysis may serve as a comparatively fast method for evaluating optical properties with sufficient accuracy and can be used, e.g., for on-line monitoring of optical properties of biological tissue.     

可燃气体检测报警器测量结果的不确定度评定

本文详细介绍了可燃气体检测报警器示值误差测量结果的不确定度评定方法。     

水三相点复现的不确定度评定

水三相点是开尔文热力学温度的唯一基准点，也是ITS-90国际温标重要的定义固定点。因此，水三相点不确定度分析对整个温标的建立、温度量值传递起着至关重要的作用。近3年来，中国计量科学研究院研制出一系列高质量的水三相点容器，加强了水三相点的研究，为不确定度的分析提供了更为可靠的实验依据。同时，不确定度的分析也是客观评价新研制容器性能的一个重要指标。因此，根据实验结果对新研制容器所复现的水三相点进行了不确定度评定。评定结果表明，其扩展不确定度为0．16mK(k=2．69，P=0．99)。     

心电图机电压测量示值误差测量值的不确定度评定

本文介绍了心电图机电压测量示值误差测量值的不确定度评定与表示方法。     

Estimation of potentialities of methods of summation of direct measurement errors

Conventional methods for summation of direct measurement errors are considered. Conditions under which these methods provide consistent results are stated. It is proposed to utilize for characteristic of the total error, its interval estimator or the half-sum of the value obtained by adding up its arithmetic and geometric random errors.Translated from Izmeritel'naya Tekhnika, No. 4, pp. 10–12, April, 1995.