自蔓延高温合成法制备MgSiN2粉体

以自蔓延高温合成法制备了高纯MgSiN2粉体。通过绝热燃烧温度的理论计算,提出3种可能的反应体系——Mg粉／Si粉、Mg2Si粉或者Mg粉／Si3N4粉。对3种体系的研究结果表明：Mg粉／Si粉体系很难得到纯相的MgSiN2粉体,Mg2Si粉或者Mg粉／Si3N4粉燃烧可得纯MgSiN2粉体,其氧含量最低可达到0．377％,并具有良好的抗水化性能。     

自蔓延高温合成镍铜锌铁氧体粉体研究

为了研究低成本大批量生产制备NiCuZn铁氧体的方法,采用自蔓延高温合成(SHS)工艺制备了Ni0.25Cu0.25zn0.5Fe1.96O3.94粉体,将铁氧体粉体分别在800℃、850℃、900℃进行热处理.以XRD、SEM、TG-DSc、振动样品磁强计(VSM)等手段分别对产物的物相、微观结构和磁性能进行研究.结果表明,SHS制备的NiCuZn铁氧体粉体经900℃热处理后可以转变成单一的尖晶石相,所得铁氧体粉体结构完整,矫顽力达到最小值,Hc=72.3Oe,同时饱和磁化强度达到最大值,Ms=68.34emu/g.     

Comparative study of β-Si3N4 powders prepared by SHS sintered by spark plasma sintering and hot pressing

β-Si3N4 powders prepared by self-propagating high-temperature synthesis (SHS) with additions of Y2O3 and Al2O3 were sintered by spark plasma sintering (SPS). The densification, microstructure, and mechanical properties of Si3N4 ceramics prepared using this method were compared with those obtained by hot pressing process. Well densified Si3N4 ceramics with finer and homogeneous microstructure and better mechanical properties were obtained in the case of the SPS technique at 200℃ lower than that of hot pressing. The microhardness is 15.72 GPa, the bending strength is 716.46 MPa, and the fracture toughness is 7.03 MPa.m1/2.     

Comparative study of β-Si3N4 powders prepared by SHS sintered by spark plasma sintering and hot pressing

β-Si3N4 powders prepared by self-propagating high-temperature synthesis (SHS) with additions of Y2O3 and Al2O3 were sintered by spark plasma sintering (SPS). The densification, microstructure, and mechanical properties of Si3N4 ceramics prepared using this method were compared with those obtained by hot pressing process. Well densified Si3N4 ceramics with finer and homo- geneous microstructure and better mechanical properties were obtained in the case of the SPS technique at 200°C lower than that of hot pressing. The microhardness is 15.72 GPa, the bending strength is 716.46 MPa, and the fracture toughness is 7.03 MPa?m1/2.     

自蔓延高温合成（SHS）技术简介

自蔓延高温合成广泛用于制备难熔高温材料及其它先进材料,本文综述了自蔓延高温合成的发展概况、理论基础及技术应用,对目前SHS研究中存在的问题及未来SHS的研究发展方向作了简要论述。     

磨球直径对机械合金化合成TiC反应过程的影响

使用机械合金化方法在卧式行星式球磨机上制备了TiC。利用X射线衍射、扫描电子显微镜对粉末的微观结构和形貌的变化进行了分析。讨论了在机械合金化制备TiC过程中磨球直径对于球磨效率、球磨能量的传递以及Ti+C→TiC发生机理的影响,对于TiC的不同形成机理作出了解释。结果表明:在机械合金化制备TiC的过程中,磨球直径对于反应发生的速率和反应机理有着明显的影响,即当磨球直径较小时,Ti+C→TiC反应是以机械诱发扩散反应(MRD)的形式逐步进行的;当磨球直径较大时,反应是以自蔓燃反应(SHS)的形式快速进行的。     

Ba1-xSrxTiO3固溶体粉体的均相直接合成与表征

以钛、钡和锶的可溶性盐分别作为钛、钡和锶的前驱体，以MOH（M=Na、K）为沉淀剂，温度在100℃以下，反应时间为4～5h，采用均相直接合成法获得Ba1-xSrxTiO3一系列的固溶体粉体，经SEM和XRD分析发现，Ba1-xSrxTiO3粉体的形貌为球形，粉体晶相均为立方相；该固溶体为完全互溶体，而且它的晶胞参数随着Sr的含量的增加而减小。     

溶胶低温燃烧法制备Ba0.7Sr0.3TiO3纳米粉体

以Ba(NO3)2Sr(NO3)2TiO(NO3)2C6H8O7.H2O为反应体系,采用溶胶低温燃烧合成法制备了Ba0.7Sr0.3TiO3超细粉末。以正交试验考察了柠檬酸与金属离子物质的量比、溶胶pH值、燃烧及热处理温度对合成粉体粒径的影响,得到的工艺参数最优组合为:n(柠檬酸)∶n(金属离子)=1.5∶1,pH=7,燃烧及热处理温度为650℃。对比了溶胶燃烧法与凝胶燃烧法对BST粉末粒度和相结构的影响。应用X射线衍射和透射电镜等对粉体的相结构、粒径、形貌进行了分析和观察。     

SHS法复合引风机金属陶瓷覆层叶片研究

发电厂引风机普遍存在叶片磨蚀问题,此类问题造成较大的经济损失,而精细结构陶瓷具有一一般金属难以比拟的耐磨性能,研究开发耐磨瓷覆层风机叶片是一项有效的新型防磨技术,提出了一种自蔓延高温合成风机叶片耐磨陶瓷覆层新技术。     

SHS法合成Ni_3Al有序度和有序畴尺寸的测定

用Ｘ射线衍射法测定自蔓延高温合成（简称ＳＨＳ）Ｎｉ３Ａｌ固溶体有序度和有序畴尺寸，结果指出：待反应混合物成形压力越大，有序度越高，有序畴尺寸越大。     

Preparation of ZrB_2 Ceramics by Self-propagating High-temperature Synthesis and Hot Pressing Sintering

1Introduction Self propagatinghigh temperaturesynthesis(SHS)isanattractivetechniquethatutilizesthehighheatofexother micreactionsbetweentherawmaterialstoproduceavariety ofceramicmaterials.Oncetheexothermicreactionswereinitiated,asufficientheatisreleasedtha…     

自蔓延高温合成La0.67Sr0.33MnO3-δ粉体的研究

采用自蔓延高温合成(SHS)技术合成了La0．67Sr0．33MnO3-δ粉体。研究了KMnO4含量、压坯密度对燃烧反应及退火温度对粉体性能的影响，并用XRD、SEM对粉体的性能进行了表征，结果表明：KMnO4用量为0．3时，反应完全且晶粒大小均匀；反应的原料混合物压坯密实度的降低可使燃烧温度有所增大；最佳退火温度为1100℃。     

A New Process for Preparing Fine-ceramic-containing Composite Coatings--Flame Spray Synthesis

Flame spray synthesis (FSS), a combination of the flame spray technology and Self-propagation High-temperature Synthesis (SHS) was developed for preparing fine-ceramic-containing composite coatings. It can simplify the preparations of powder to synthesize and deposit the desired materials in one step. The preliminary results obtained from TiC-Fe cermet coatings by FSS process are reported. The peculiar microstructure of the composite coatings, which contains very fine (<1m) and round TiC and alternate TiC-rich (Hv=11?13GPa) and TiC-poor layers (Hv=3.0 -6.0GPa), is expected to play an important role in their tribological properties.     

封闭式电子回旋共振等离子体低温沉积SrTiO3膜

在室温条件下，用封闭式电子回旋共振(MCECR)等离子体溅射方法沉积了SrTiO3(STO)膜．用Ar等离子体在Si基片上溅射的STO膜是非晶的，然而用Ar／O2等离子体在Pt／Ti／SiO2／Si上溅射的是充分结晶的STO膜．为了使非晶薄膜结晶，用电炉加热或28GHz微波辐射对非晶STO膜进行退火处理．采用微波辐射，使基片温度为573K时，在Si上的STO膜退火后的介电常数大约为260，这值近似等于块状STO材料的介电常数．由于微波辐射能够降低薄膜的退火温度和提高薄膜的电特性，因而被认为是非常有用的．     

钛酸四丁酯催化合成柠檬酸三丁酯的反应动力学

以钛酸四丁酯为催化剂合成柠檬酸三丁酯。研究了其反应机理 ,建立了反应动力学模型 ,并根据实验数据 ,确定了模型中的有关参数。在本实验反应体系下 ,测出了反应的表观活化能为 61 89kJ·mol- 1 ,指前因子为 8 390× 1 0 5 min- 1 。     

SO_3磺化法合成PNTS新工艺的研究

本文采用正交设计及方差分析法,确定了 SO_3磺化法合成 PNTS 新工艺的最佳工艺条件;并从技术及经济方面将新工艺同国内现有的生产老工艺进行了分析对比。     

水热法制备正交相铌酸钠纳米粉体

铌酸钠作为反铁电体,能与多种结构的铁电体形成不同特性的固溶体陶瓷,制备纳米尺寸的NaNbO3不仅有利于降低烧结温度,而且有利于与LiNbO3等形成均匀固溶体。该文利用水热法制备纳米铌酸钠(NaNbO3)。实验表明,利用五氧化二铌(Nb2O5)和以氢氧化钠(NaOH)为原料,当NaOH浓度不低于3 mol/L,水热温度160~180℃条件下制备出了纯正交相铌酸钠纳米粉体。并对其进行了X-ray衍射结构分析及SEM、TEM形貌分析。X-ray衍射结构分析表明:合成的NaNbO3粉体为正交相结构,晶胞参数为a=9.559 7,α=β=γ=90°,c=5.787 3。透射电镜(TEM)分析表明,合成的NaNbO3粉体主要有片状和柱状2种形状,片状尺寸一般为0.02~0.05μm,柱状长度一般在0.1μm左右。     

非光气法合成吡嘧黄隆

研究了利用二（三氯甲基）碳酸酯代替光气与吡唑磺酰胺反应,然后再与２－氨基－４,６－ 二甲氧基嘧啶反应合成吡嘧黄隆的方法．反应安全、条件温和,从根本上消除了光气的危险性。     

空气中合成LiNi1-xAlxO2的条件及其对结构的影响

以Ni(OH)2,Al(OH)3和LiOH·H2O为原料,采用高温固相反应法在空气中合成了锂离子电池正极材料LiNi1-xAlxO2(x=0.025～0.30),用XRD研究了合成材料的物相和结构.研究了合成温度、合成时间、补锂量以及掺铝量对合成产物结构的影响.实验表明,掺铝有利于形成和稳定α-NaFeO2型层状有序结构.随着掺铝量的增加,晶胞参数a0逐渐减小,而c0则逐渐增大.在空气中合成LiNi1-xAlxO2的最佳温度为750 ℃,合成时间以18～24 h为宜,补锂量为10%(摩尔分数)效果较好.     

空气中合成锂离子电池正极材料LiNi1-xTixO2

以N i(OH)2、TiO2和LiOH.H2O为原料,采用固相反应法在空气中合成了LiN i1-xTixO2(x=0.025、0.050、0.100),用XRD研究了合成材料的物相和结构,用SEM研究了合成材料的形貌,用电池性能测试仪研究了合成材料的电化学性能.结果表明,原料中的n(Ti)/n(N i Ti)值对合成材料的结构和电化学性能影响很大.少量的钛可以进入LiN iO2的晶格形成LiN i1-xTixO2固溶体,而钛含量过大则会出现杂相.n(Ti)/n(N i Ti)值为0.050的样品结构有序度最高,充放电容量最大.