机制砂生态自密实混凝土的工作性研究

传统的自密实混凝土(SCC)集料含量偏低、胶凝材料用量较高,同时制备SCC的细集料一般采用的是河砂,但是河砂作为短期内不可再生资源,且地域性很强。这些因素使得现在SCC造价高昂,而且会造成较大的资源浪费。因此本文用机制砂代替河砂作为细集料,用关键因素法设计配比,通过集料级配优化来提高粗集料的含量,减少胶凝材料的用量,实现生态性。同时研究堆叠率(PR)、砂体积率(VSR)、粗集料级配等因素对自密实混凝土工作性的影响。实验表明关键因素法能成功设计出堆叠率为0.6,砂浆含砂率为0.42的机制砂生态自密实混凝土,胶凝材料用量544kg/m3,水泥用量381kg/m3,扩展度达到655mm,T500测试时间为4.6s,间隙通过性10mm,H2/H1为0.8,减少胶凝材料的同时符合SCC工作性要求。     

机制砂生态自密实混凝土的制备

传统设计法设计出的自密实混凝土集料含量偏低、胶凝材料用量较高,成本高昂,机制砂的应用增加了自密实混凝土配制难度。从集料级配优化、组成设计和流变改性着手制备一种生态机制砂自密实混凝土并研究了堆叠率、砂的体积率,胶凝材料和水粉比对Eco-SCC工作性能、物理性能的影响。研究表明:利用级配合理的机制砂,在堆叠率为0.6及砂的体积率不超过0.44的条件下能制备出性能满意的Eco-SCC;其流动性受堆叠率和砂的体积率影响显著,强度随水粉比、砂的体积率升高而降低,合理的胶凝材料的用量对SCC强度有利。     

集料对自密实混凝土工作性能的影响

根据流变学理论,在试验的基础上,研究了集料的级配、最大颗粒尺寸、砂率和颗粒形态对自密实混凝土流变性的影响.通过在一定范围内降低集料颗粒尺寸、优化配比及砂率、减少针片状颗粒含量,可以改善自密实混凝土的工作性能,对自密实混凝土的设计和应用具有一定的指导意义.     

矿物掺合料对自密实混凝土基本性能的影响

为探讨粉煤灰、硅灰掺量对自密实混凝土工作性能和力学性能的影响,对单掺粉煤灰自密实混凝土和复掺粉煤灰硅灰自密实混凝土进行了工作性能测试、抗压强度和抗折强度试验.结果表明:粉煤灰和硅灰的掺入可以提高水泥浆体的流动性,改善自密实混凝土的填充性、间隙通过能力和抗离析性能;3d龄期时,自密实混凝土的抗压强度和抗折强度随粉煤灰掺量...     

机制砂生态自密实隧道二衬混凝土工作性研究

采用机制砂取代河砂,并通过掺入适量石粉以及粉煤灰调整自密实混凝土工作性以减少水泥用量,制备了一种用于隧道二衬的机制砂生态自密实混凝土,并研究了粗集料级配、砂率、石粉掺量以及粉煤灰掺量对自密实混凝土工作性的影响,最终确定了最优配比。结果表明:当粗细石比例为6∶4、砂率为0.43、石粉掺量为5%、粉煤灰掺量为25%、水胶比为0.32时,混凝土工作性达到最好,同时强度满足工程应用要求。该结果可为机制砂生态自密实在隧道二衬工程中的应用提供理论基础。     

自密实混凝土配合比优化研究

自密实混凝土是一种具有高工作性能的高性能混凝土。本文探讨了自密实混凝土工作性能的评定方法,并对掺加磨细矿渣的自密实混凝土进行了研究。通过分析磨细矿渣含量、胶凝材料总量、砂率、减水剂掺量对自密实混凝土流动性和强度的影响,配制了高工作性能和力学性能的自密实混凝土,为掺加磨细矿渣的高强自密实混凝土配合比设计提供了依据。     

自密实混凝土配合比优化研究

自密实混凝土是一种具有高工作性能的高性能混凝土。本文探讨了自密实混凝土工作性能的评定方法,并对掺加磨细矿渣的自密实混凝土进行了研究。通过分析磨细矿渣含量、胶凝材料总量、砂率、减水剂掺量对自密实混凝土流动性和强度的影响,配制了高工作性能和力学性能的自密实混凝土,为掺加磨细矿渣的高强自密实混凝土配合比设计提供了依据。     

改性再生骨料对自密实混凝土性能的影响

为提高再生骨料的性能,使之适用于自密实混凝土,使用4种强化手段对简单破碎后的两种来源再生骨料进行改性处理,研究其对新配RA-SCC工作性能和硬化后物理力学等性能的影响.结果发现:骨料来源和原生混凝土强度对再生骨料的品质有较大影响,而经过改性处理以后,不同来源的再生骨料品质都有所提升,所制成的RA-SCC性能差异变小;裹浆法以及水玻璃浸泡的方法能够较大程度地改善新拌RA-SCC的自密实性能;高温煅烧法、酸性溶液浸泡法、水玻璃分散技术可使硬化后的RA-SCC内部结构更加致密,从而明显改善了RA-SCC的抗拉强度、抗干燥收缩性能和抗冻性能,但大部分骨料增强技术对RA-SCC的抗压强度和弹性模量的影响较小.     

自密实混凝土配合比设计及相关性能研究

自密实混凝土的配合比设计,既要注重建设工程对混凝土强度的要求,又要考虑施工过程中对混凝土工作性能的要求.通过设计制作不同配合比的混凝土试件并进行相应的实验,分析粉煤灰单掺量、粉煤灰和矿渣复掺量、水胶比和胶结料用量等对混凝土的工作性能和力学性能的影响.结果表明:粉煤灰与矿渣复掺比例为3:2和粉煤灰单掺量达到36％时,新拌...     

PP单丝纤维自密实混凝土强度与抗渗性能

采用力学试验、渗水标号试验、渗水高度试验和氯离子渗透试验研究了聚丙烯(PP)单丝纤维自密实混凝土强度、抗渗性能,通过扫描电镜观察了纤维自密实混凝土的微观结构,从材料的组成结构和断裂力学原理上分析了PP单丝纤维对自密实混凝土强度以及抗渗性能的影响机理。结果表明： 当PP单丝纤维自密实混凝土体积掺量不超过0.15%时,PP纤维自密实混凝土具有较好的抗渗性能,渗水标号大于S 35;PP单丝纤维体积掺量不超过0.1%时,自密实混凝土的强度和抗水渗性能随着纤维体积掺量的增加而提高,电通量有所增加,而当体积掺量超过0.15%后,强度仍然有增长,电通量急剧增加;与普通自密实混凝土相比,0.10%单丝PP纤维自密实混凝土具有较好的强度特性和抗渗性能,28 d弯拉强度提高16.4%,28 d劈裂强度提高13.4%,56 d氯离子渗透电通量为919 C,渗水高度减少57%。     

Effect of Limestone Powder on Microstructure of Concrete

The effect of limestone powder on microstructure of concrete was studied by using mercury intrusion porosimetry (MIP), backscattering scanning electron(BSE), scanning electron mi- croscopy (SEM) and X-ray diffraction (XRD) techniques. The experimental results show that the compressive strength of concrete containing 100 kg/m3 limestone powder can meet the strength re- quirement. Limestone powder has not pozzolanic activity; it is still unhydrated at the age of 28 days. But its filling effect can make the pa...     

自密实防水混凝土收缩特性的研究

运用混凝土收缩仪、X射线衍射及扫描电子显微镜，通过实验研究、测试及相关理论分析，探索了粉煤灰、膨胀剂、纤维3种抗裂组份各自及共同作用对WPSCC收缩性能的影响规律及其机理，确定了配制WPSCC时粉煤灰、膨胀剂及纤维的适宜掺量。     

Influence of Rheological Active Additives on the Properties of Self-compacting Concrete

The effect of rheological-active additives on the properties of cement suspensions and self-compacting concrete mixtures have been studied.In order to increase the rheological matrix and provide high fluidity,stone powders were used during the crushing of local mountain rocks in self-compacting concrete.Taking into account the high dispersion of rheological-active additives,highly effective plasticizers were used to regulate the reotechnological properties of cement-based mixtures.The effect of sulfonaphthalen-formaldehyde oligomer and polycarboxylate-based hyperplasticizer on rheological properties of cement systems as plasticized additive on methodology proposed by V Kalashnikov was evaluated.The flow rate of cement suspension is determined by means of mini-viscosimeter,spreading of cement-sand mortar by means of Hegermann cone,and the slump of concrete mixture by means of Abraham’s cone.On the basis of obtained results,it was determined that limestone powder was more efficient than other stone powders.Thus,when adding 40% limestone powder to the mixture,the compressive strength of the samples taken from self-compacting concrete mixture increases by 15%-30% compared to the control samples.The optimal quantities of rheological-active additives and plasticizers have been identified and the possibility of obtaining high-strength self-compacting concrete based on them has been confirmed.     

石灰石粉与矿物掺合料复掺对混凝土工作性及强度的影响

研究了石灰石超细粉与低品质粉煤灰复掺对混凝土性能的影响,通过对不同比例石灰石超细粉掺加量下新拌混凝土工作性能的试验研究以及混凝土强度发展规律的分析,结果表明,在同坍落度下提高石灰石超细粉的添加量可明显减小混凝土用水量,降低水胶比;在胶凝材料用量相同时,石灰石超细粉替代量提高到一定程度时混凝土强度增长率减小.     

重晶石粉对防辐射超高性能混凝土性能的影响

超高性能混凝土具有高密实度、超高强度和高韧性的特点,是建设超高强射线屏蔽建筑的理想材料,掺入少量重骨料后表观密度较小,且其胶凝材料用量高,水化放热大。因此,采用重晶石粉取代部分胶凝材料(替代粉煤灰微珠体积比例为0%、10%、20%、30%、40%)制备了防辐射超高性能混凝土。结果表明,随着重晶石粉取代粉煤灰微珠量的增加,混凝土工作性能和力学性能逐渐降低,表观密度逐渐增加,水化放热量先增加后逐渐降低,水化放热量在取代量为10%时达到最大,3d的水化热值为139.526J/g。综合考虑,推荐重晶石粉取代粉煤灰微珠量为20%,坍落度/扩展度达到255mm/620mm,表观密度为2 660kg/m~3,28d抗压强度135.4MPa,28d抗折强度25.9MPa,3d的水化放热量为121.650J/g,长期耐久性能良好,~(137) Cs放射源(0.662MeV)线性吸收系数为0.182cm-1,预湿高钛重矿渣砂的内养护作用促进了周围水泥浆体的水化,从而加强了界面过渡区,显著提高了多孔集料制备的UHPC的力学性能和耐久性能。     

钢渣矿粉混凝土的物理力学性能研究

研究了钢渣矿粉细度、掺量对混凝土的工作性能和力学性能的影响，探讨了钢渣矿粉对混凝土性能的作用机理；提出了利用钢渣矿粉作掺舍料制备高强、高性能混凝土的关键技术与方法.     

自密实轻骨料混凝土力学性能试验研究

针对自密实轻骨料混凝土(SCLC)的力学性能与普通混凝土力学性能的差异,采用常规混凝土力学性能的试验方法,对SCLC的力学性能进行研究,得出了SCLC的一般力学性能结论.结果表明表面粗糙的轻骨料有利于SCLC强度的提高和拌合物在改进的L-800流变仪中流动性的增加,SCLC的折压比小于普通混凝土,脆性大于普通混凝土,弹性模量约为同强度等级普通混凝土的67%~78%.为SCLC的力学性能在工程中的应用提供了理论指导.     

养护制度与组分对含石灰石粉水泥基材料力学性能的影响

从胶凝材料组成、硬化水泥石基本物相出发,探讨了标准养护、蒸汽养护和蒸压养护制度下含石灰石粉水泥基胶砂力学性能。结果表明,对于35%石灰石粉+65%硅酸盐水泥体系,标准养护、蒸汽养护对水泥胶砂柔韧性无明显影响,蒸压养护显著增加其脆性;用矿粉等量取代含石灰石粉水泥,蒸压养护显著增加其脆性,明显降低其抗裂性;蒸汽养护也增加其脆性,但增幅低于蒸压养护;用粉煤灰等量取代含石灰石粉水泥,标准养护提高其柔韧性,蒸汽养护对其柔韧性无明显影响,蒸压养护明显降低其柔韧性,但提高其抗裂性;标准养护下,硬化水泥石中出现碳铝酸盐,蒸汽养护和蒸压养护制度下,碳铝酸盐不能稳定存在。     

掺石灰石粉混凝土的性能及其改善途径

采用不同掺量的石灰石粉取代水泥配制混凝土,同时配制复掺6%偏高岭土和20%石灰石粉的混凝土,并采用相同的胶凝材料体系制备水泥净浆,开展Na_2SO_4溶液浸泡试验。测试了混凝土抗压强度,采用RCM法和硫酸盐干湿循环侵蚀试验分别测试混凝土的氯离子扩散系数和抗硫酸盐侵蚀性,采用MIP法测试混凝土孔结构,进一步采用SEM观察浸泡后净浆试件的微观形貌。结果表明,石灰石粉对混凝土抗压强度、抗氯离子渗透性和抗硫酸盐侵蚀性均有一定的不良影响。采用偏高岭土与石灰石粉复掺可以有效提高掺偏高岭土混凝土的强度、抗氯离子渗透性和抗硫酸盐侵蚀性。其机理主要在于优化了混凝土孔结构,降低了有害离子在混凝土中的传输速度,阻止了混凝土在硫酸盐环境中钙钒石、石膏等侵蚀产物的形成。     

自密实混凝土应用研究

区别于普通混凝土,对自密实混凝土的特点进行了分析,并对自密实混凝土的配制方法进行了设计和探讨.