研究了聚乙烯醇、塑化剂等主要原料及无机填料CaCO3的含量对降解材料性能的影响.结果表明:随着聚乙烯醇、塑化剂含量增加,材料的机械性能有较大提高,尤其是断裂伸长率变化显著;加入碳酸钙可以提高制品的刚度、尺寸稳定性等,但强度、断裂伸长率有所下降.     

聚乙烯醇/纳米氧化锌复合材料的性能

为了改善聚乙烯醇的性能,通过熔融挤出的方法制备了聚乙烯醇/纳米氧化锌复合材料.采用力学性能测试、热分析、X射线衍射和紫外光谱研究了纳米氧化锌对聚乙烯醇力学性能、热稳定性、结晶性能和紫外屏蔽性能的影响.结果表明:复合材料的拉伸强度和断裂伸长率分别在纳米氧化锌含量为1.0wt%和0.5wt%时达到最大值,拉伸强度比纯聚乙烯醇提高了20.27%,断裂伸长率略高于纯聚乙烯醇;当纳米氧化锌含量为2.0wt%时,复合材料失重10%的温度比纯聚乙烯醇提高20℃;纳米氧化锌显著提高了聚乙烯醇的耐光老化性能,同时使聚乙烯醇中产生了新的晶相.纳米氧化锌的加入有助于多种性能的改善.     

淀粉基/聚乙烯醇复合薄膜的制备及性能研究

以淀粉和聚乙烯醇为主要原料,丙三醇为增塑剂,通过流延成膜法制备淀粉基/聚乙烯醇生物薄膜.考察了料液浓度、原料配比及增塑剂含量对复合薄膜力学性能、耐油性能以及结晶性能的影响.研究结果表明:复合薄膜的最佳料液浓度为7.5%;聚乙烯醇的含量越高,共混膜的综合性能越好;当淀粉、聚乙烯醇与增塑剂的质量比为6∶6∶4时,制备的淀粉基/聚乙烯醇复合薄膜的力学性能最好,其拉伸强度和断裂伸长率分别达到13.3MPa和160%;偏光显微镜测试结果表明其相应材料的结晶性能最佳.     

PVC/SBS共混材料力学性能研究

以通用型PVC树脂为基体,使用SBS-g-MAH通过双螺杆挤出机对其进行共混改性,研究了SBS-g-MAH的含量对PVC/SBS-g-MAH共混材料的力学性能影响.结果表明,SBS-g-MAH的引入可以提高PVC树脂的断裂伸长率、冲击强度,而材料的拉伸强度则降低.当SBS-g-MAH含量为5%时,断裂伸长率出现极大值;SBS-g-MAH含量为20%时,冲击强度出现极大值.     

聚乙烯醇对SiC泥坯料性能的影响

以聚乙烯醇为塑性剂,讨论了陈腐时间、塑性剂含量和水含量对SiC泥料的塑性、伸长率、密度、气孔率等性能的影响.实验结果表明:在聚乙烯醇含量3%、水含量30%、陈腐时间24h的条件下,可获得以上性能参数的最佳值.     

玻纤、木粉组合增强PP复合材料的制备及性能研究

制备玻纤与木粉组合增强聚丙烯（PP）复合材料,并研究材料的湿热性能、力学性能、表面性能及其影响因素．结果表明：随木粉含量的增加,复合材料的吸湿率增大,密度降低,拉伸强度和断裂伸长率减小,但对冲击强度影响不大,且木粉可以有效改善材料表面的亲水性,提高表面张力;而随玻纤含量的增加,材料的吸湿率减小,密度增加：适当的玻璃纤维含量能提高材料的拉伸强度和冲击强度,但玻纤含量超过一定值时,PP复合材料的断裂伸长率反而会降低;用KH-550偶联剂处理、木粉质量分数〈10％、玻纤质量分数〈15％的玻纤木粉组合增强PP复合材料的综合性能较好．     

生物质微粉塑化及表面塑化工艺

为了改善生物质的亲水特性,提高生物质对树脂挤出工艺的适应性,本文分别使用硫酸、醋酸、甘油和乳酸作为主要的塑化剂,对生物质微粉进行塑化处理。通过激光粒径分析、DSC-TGA、红外光谱和SEM分析,初步判断生物质的塑化效果。将塑化后的生物质与PLA共混挤出制备成生物质/PLA树脂颗粒,测量其拉伸强度、断裂伸长率和熔融指数。实验结果表明:甘油作为塑化剂,塑化效果较差;硫酸作为塑化剂,塑化效果较好,但不会改善生物质表面的亲水特性;醋酸和乳酸作为塑化剂,不仅可以起到塑化的作用,同时也能够改善生物质与树脂间的相容性,具有良好的实用效果。     

复配增塑剂对聚乙烯醇薄膜性能的影响

以甘油和乙二醇为复配增塑剂,研究了复配增塑剂对聚乙烯醇的熔融和结晶行为的影响;采用熔融共混法制备聚乙烯醇薄膜,考察了复合增塑剂对薄膜力学性能、水溶性能的影响.结果表明:复配增塑剂质量百分含量在10%~30%时可有效降低聚乙烯醇的熔融温度和结晶温度;当其在30%时,薄膜的力学性能达到最优,拉伸强度为24.9 MPa,断裂伸长率为380%;薄膜的溶解失重率与时间呈良好的线性关系.     

生物酶处理对制备秸秆聚乙烯醇复合膜的影响

为了提高秸秆的高值化利用率,对秸秆进行酶改性处理,并与聚乙烯醇进行复配得到秸秆聚乙烯醇复合膜。结果表明,经漆酶木聚糖酶复配处理秸秆得到的复合膜力学强度最高,达到2.9 MPa,断裂伸长率由未改性的12.4%降至7.7%。复合膜的表面疏水性以及结晶度均有一定程度的提高。经过对复合膜官能团的检测,发现复合膜无新增官能团,表明秸秆与聚乙烯醇为物理的氢键连接能力增强。经过酶改性处理后的秸秆聚乙烯醇复合膜在包装领域具有极大的应用价值。     

纸质基材抗菌包装及性能研究

以纳米银为抗菌剂、聚乙烯醇为黏结剂处理普通成纸,制备了包装用抗菌纸。采用抑菌圈法评价了该抗菌纸对大肠杆菌的抑制效果,研究了聚乙烯醇和纳米银的含量对抗菌纸抗菌性能、抗张强度和伸长率的影响。结果表明:抗菌纸的抗张强度及伸长率均能满足包装需求,且具有良好的抗菌性能,其抗菌效果随纳米银和聚乙烯醇含量的增加而增强。     

Effect of Microfibrillated Cellulose Loading on Physical Properties of Starch/Polyvinyl Alcohol Composite Films

The starch/polyvinyl alcohol (PVA)/ microfibrillated cellulose (MFC) composite films were prepared using solution casting method after adding MFC into starch/PVA blend matrix.The effects of MFC content on the mechanical properties of starch/PVA composite films were investigated.As MFC content increases,the elongation at break and tensile strength increase firstly and then decrease.When the content of MFC is 2wt%,the tensile strength is 26.6 MPa and reaches the maximum.Through Fourier transform infrared (FTIR),scanning electron microscopy (SEM),X-ray diffraction (XRD) and thermogravimetric analysis (TGA),good dispersion of MFC in starch/PVA matrix at the loading of 2wt%,lower crystallinity of the starch/PVA/MFC films in comparison with starch/PVA blend and the effect of glass transition temperature increasing with MFC content from 0.5wt% to 4wt% can be found observed.And,incorporating MFC does not change the composition and crystal structure of the starch/PVA composite films.Thus,the reinforcing mechanism for the improvement of mechanical properties is attributed to the homogeneous dispersion of MFC with large aspect ratio,good compatibility and interfacial interactions between starch/PVA blend matrix and MFC.     

Preparation of Triethylene Glycol Maleate and Its Effect on Plasticization of Oxidized Starch

A plasticizer triethylene glycol maleate(TEG-MA) was synthesized. The dominated monoester of moderate hydrophobicity with apparent oil-water partition coefficient of 0.042 in the product was confirmed by acid value determination, HPLC and FTIR. Its plasticizing effect on oxidized starch was manifested by crystallization, aging behaviour, moisture absorption, and mechanical performance. X-ray diffraction data showed that the relative crystallinity of the plasticized starch decreased. Both the crystal and the crystallinity of starch films were rarely changed in aging. Moisture absorption relied on the ester content and relative humidity. The elongation at break increased significantly with plasticizer content more than 10% in the matrix.     

醋酸纤维素水分散体游离膜性质的分析

以醋酸纤维素（CA）为主要原料,采用相转变法制备醋酸纤维素水分散体（CAD）.利用铸膜法制备水分散体游离膜,考察了增塑剂添加量、膜厚度对固化速率、游离膜表面特性、玻璃化转变温度Tg、力学性能、透湿性及洗脱率的影响.结果表明：由CA到醋酸纤维素水分散体游离膜的制备为物理过程,膜的厚度增加,透湿性减小.增塑剂添加量增大,固化速率和Tg均减小,透湿性、洗脱率和断裂伸长率均增大,弹性模量和拉伸强度先增大后减小,游离膜的表面越平整.     

Compatibility and Properties of Biodegradable Blend Films with Gelatin and Poly（vinyl alcohol）

The blend films with gelatin and poly（vinyl alcohol） （PVA） were prepared by a solution casting method. The compatibility between gelatin and PVA in the blend films was investigated. The transmittance, Fourier-transform infrared spectroscopy （FTIR）, x-ray diffraction （XRD）, thermogravimetry analysis （TG）, and differential scanning calorimetry （DSC） were employed to characterize the resultant blend films. According to optic result, the opacity of the blend film at the ratio of 20/80 （w/w, Gel to PVA） was the lowest, indicating the best compatibility between Gel and PVA at the ratio. The results oflR, XRD, DSC, and TG revealed an intensive interaction and good compatibility between them in the blend film at the ratio. The mechanical properties and solubility showed that PVA content in the blend films obviously affected the elongation at break and solubility. The mechanical properties and water resistance of gelatin film may be improved by the introduetion of PVA.     

膨松型转杯纺棉／PVA长丝复合材料的性能

对转杯纺棉/PVA长丝复合材料及传统的转杯纺织材料等3种材料进行性能测试,涉及到的纺织材料性能指标有强伸性能、条干均匀度、毛羽、膨松度等,侧重于对材料物理性能的研究。研究表明,经溶解的复合材料的膨松度明显上升,断裂强力下降,断裂伸长增加,毛羽增加明显,条干均匀度明显下降。     

纳米CaCO3／SiO2复合粒子对硅橡胶性能的影响

硅橡胶力学性能差．需要补强．这是硅橡胶产品开发的关键。本文报道用溶胶沉淀法制备具有核一壳结构的纳米CaCO3／SiO2复合粒子．将该复合粒子替代部分二氧化硅作为硅橡胶的补强材料。通过实验确定它对硅橡胶的力学性能和热稳定性能的影响。比较用纳米CaCO3／SIO2复合粒子以及用CaCO3补强的硅橡胶。前者不仅物理力学性能较佳，而且能降低材料的成本。但后者耐热性能较好。     

纳米CaCO_3/SiO_2复合粒子对硅橡胶性能的影响

硅橡胶力学性能差,需要补强,这是硅橡胶产品开发的关键。本文报道用溶胶沉淀法制备具有核-壳结构的纳米CaCO3/SiO2复合粒子,将该复合粒子替代部分二氧化硅作为硅橡胶的补强材料。通过实验确定它对硅橡胶的力学性能和热稳定性能的影响。比较用纳米CaCO3/SiO2复合粒子以及用CaCO3补强的硅橡胶,前者不仅物理力学性能较佳,而且能降低材料的成本。但后者耐热性能较好。