某电厂后水冷壁管角焊缝开裂后疲劳裂纹扩展原因分析

某电厂锅炉后水冷壁上部管子(SA-210C)与耳板焊接角焊缝处发生泄漏现象.通过对失效处样管进行宏观检查、化学成分分析、力学性能检测、金相分析和断口SEM检测并调取炉膛运行曲线.最终确定失效原因为:锅炉运行过程中,曾存在多次较严重炉膛震动现象,同时耳板和管子角焊缝处存在应力集中,在炉膛振动(交变应力)及热应力作用下,裂...     

N06022镍基合金半管夹套的焊接

本文阐述了N06022镍基合金的焊接特性,分析了不开坡口角焊缝,开内坡口全焊透角焊缝、开外坡口全焊透角焊缝的优缺点以及介绍了半管最小间距的要求.产品半管焊接前,对焊工进行了GTAW焊接方法的MOCK-UP试验,对MOCK-UP焊接试板进行无损检测、宏观试验、微观试验、角焊缝有效厚度检测、角焊缝弯曲试验,各试验项目合格....     

脉冲埋弧焊技术在膜式水冷壁管屏拼接中的试验及应用

使用埋弧焊(SAW)进行锅炉水冷壁管屏生产时,如何在保证焊接质量的前提下,提高焊接速度是需要解决的技术难点.上海锅炉厂有限公司采用脉冲埋弧焊[1～2]技术,对水冷壁管屏拼接工艺进行了焊接试验和产品试生产.实践证明,脉冲埋弧焊相比常规的直流埋弧焊能提高焊接速度13%～25%,改善水冷壁管屏生产中因速度提高而产生的咬边等成形不良问题,使焊缝质量更加优良,有效地提高了焊接生产率.     

某电厂锅炉水冷壁管泄漏原因分析

取样对某电厂锅炉水冷壁折烟角泄漏管进行宏观检验、光谱检验、金相组织检验及能谱分析,试验结果表明：泄漏管金相组织未见异常,泄漏口附近存在明显腐蚀痕迹,裂纹沿横向扩展,裂纹尖端圆钝,裂纹尖端腐蚀产物中N元素重量百分比达到24.11%。折烟角水冷壁管泄漏原因为：SNCR喷枪中尿素水溶液喷洒到水冷壁管,并在高温下分解、反应形成腐蚀性介质,使得金属管子发生化学腐蚀,现场鳍片与管子焊接质量较差,腐蚀介质在焊缝与母材交界处沉积浓缩,加快腐蚀速率;同时,尿素溶液温度为50℃,直接喷洒到高温水冷壁管子,冷热交替形成热交变应力,在腐蚀严重部位产生热疲劳裂纹,腐蚀又促进裂纹的扩展,进而发生泄漏。     

集箱短管接头角焊缝埋弧焊工艺试验研究

为提高锅炉集箱短管角接接头焊接机械化程度及角焊缝质量,上海锅炉厂有限公司创新性地采用"内孔氩弧焊+埋弧焊"工艺方法,并与合作方联合开发"集箱短管接头角焊缝埋弧焊设备"。通过对高端材料、几种规格和不同坡口型式的短管接头进行的大量焊接试验,最终确定了最佳的坡口型式及焊接工艺规范参数,且获得了焊缝表面成型美观、接头质量可靠等性质优良的焊接接头,生产效率大大提升,为工厂生产应用和大面积推广打下了基础。     

T23水冷壁管排鳍片焊缝裂纹的分析

SA213-T23钢因具有良好的高温蠕变强度和焊接工艺性能,而被电站锅炉广泛采用,但SA213-T23用于百万等级螺旋水冷壁,因焊接应力、热校正等因素造成管子与扁钢角焊缝中心出现裂纹.主要对该钢种应用在螺旋水冷壁鳍片管时,角焊缝产生结晶裂纹的形成原因及防止措施进行研究.     

伸出15mm SA-213 T22换热管与堆焊Inconel 600管板焊接工艺研究

换热管材质SA-213 T22,管板基材为SA-336 F22Cl3,管板堆焊层为Inconel 600,管端伸出长度15mm,管孔开45°坡口,坡口深2.5mm,对于此结构形式的管子管板焊相关研究较少,本文针对此种结构形式管子-管板焊进行焊接工艺研究。分析主要工艺参数对焊接质量的影响,进行渗透检查、宏观检查,焊脚尺寸测量。最终得出最优焊接工艺参数,钨极伸出长度约17mm、保护气流量25-30L/min时可同时解决焊接可达性和熔池保护效果的矛盾。首层焊缝采用自熔焊可保证根部焊透,其余焊层采用填丝焊接,焊缝成形美观,焊接质量稳定。角焊缝焊脚尺寸满足相关标准要求。     

列管式圆筒形水冷壁制造工艺研究

列管式圆筒形膜式水冷壁作为IGCC气化炉内件中的重要部件,需由大量的扁钢与管子拼接后制成圆筒形,单个圆筒形膜式壁沿圆周方向有300～700余条纵向焊缝,焊接工作量大、变形控制困难.通过焊接和压制试验,对圆筒形水冷壁加工和变形控制工艺进行研究,得出了合适的列管式筒形水冷壁制造工艺.     

超超临界火力发电厂机组主蒸汽管SA335-P92钢焊接工艺研究

简述了超超临界机组锅炉主蒸汽管SA335-P92钢的性能特点,并分析其焊接特性。为获得满足超超临界火力发电机组主蒸汽管SA335-P92钢的焊接接头性能,详细介绍了应采取的焊接工艺措施。实践证明,通过严格执行施焊工艺,控制现场施工环境,可以获得满足使用性能要求的焊接接头。     

换热器管子与管板焊缝焊接工艺评定中的检验要求

本文根据换热器管子和管板焊缝中角焊厚度、溶深和焊透、管孔间隙、管子和管板角焊缝探伤等,全面介绍了目前在换热器管与板焊焊接工艺评定中的这些检验项目和要求．     

Unerroric of control of mutual compliance of the efficiency of hydrogen engines of unmanned vehicles in the conditions of mass production

The issues related to the reliability of hydrogen engines of unmanned vehicles and increasing the efficiency of using hydrogen as fuel when using the method of its production during the decomposition of hydrogen-containing molecules of liquid-phase organic compounds in a plasma discharge under the action of intense ultrasonic exposure are considered. Experiments have shown that as a result of decomposition in the acoustoplasma discharge of liquid hydrocarbons, solid-phase carbon-containing products are formed, chemical transformations occur in the liquid phase and hydrogen-containing combustible gas is formed. Hydrogen-containing gas can be used as fuel immediately after synthesis, i.e. it does not require separation, since in addition to hydrogen it contains only impurities of CO₂ and water vapor. The purpose of the study is to formalize the basic conditions for tightening the control of mutual compliance with the efficiency of hydrogen engines of the same series in the conditions of their mass production. Methods of mathematical statistics and hardware-software modeling were used in the study. The term “unerroric of quality mutual compliance control” is introduced to describe a set of hardware and software tools for such control. The principle of in-depth testing of the technical condition of such engines of one series is described in a multidimensional formulation of the quality control problem for three of their operating parameters at once. The conditions for increasing the mutual correspondence of the measured values of such parameters in the conditions of serial production of hydrogen engines are formalized.     

小型锅炉烟尘测试时锅炉出力的计算

锅炉烟尘测试时,必须对锅炉出力进行测试。但监测中,许多小型锅炉往往不具备相关的计量装置和仪表,为解决这一问题,文章提出了用烟气量和空气过剩系数来计算锅炉的出力的公式,在实际使用中,该方法简单易行,其结果和实测值具有很好的一致怀。     

气门锁夹槽位置检测

气门圆弧形锁夹槽中心至杆端面以及至盘锥面量规线的距离(如图1中L、H). 在过程检验中如用普通量具难以测量,如用仪器测量则速度慢,效率低.为便于生产过程控制,确保工序质量,我们采用锁夹槽定位,用标准件比较测量的专用检具(如图2)进行测量.为保证锁夹槽定位准确以适应不同型号的气门,并防止气门测量时轴向窜动和左右摆动,采用了V型定位叉,使锁夹槽以四点定位,V型叉口的宽度,根据锁夹槽圆弧半径大小确定:约为圆弧的三分之二处(图3,图4).     

煤焦混烧时粉尘化学成分和比电阻对静电除尘效率的影响

文章介绍了在煤焦混粉燃烧的情况下，粉尘化学成分和粉尘比电阻的变化对静电除尘器效率的影响。     

关于发展天然气电厂的讨论

世界发电燃料结构在不断的转换过程中。18世纪60年代从薪柴转到煤炭,19世纪到20世纪初大量发展燃煤电厂;20世纪20年代又从煤炭转向石油和天然气,20年代上半叶又大量发展燃油电厂;20世纪末由于天然气生产的发展,天然气因环境影响小,受到工业发达国家的青睐,加速发展天然气电厂。我国70年代初和90年代曾两次发展燃油电厂,由于石油危机和石油价格暴涨而受到制约,不得不实行以煤代油,改造燃油电厂。现在似乎认为燃油电厂不能再搞,但又出现发展燃气电厂的热流,发展燃气电厂确实是当今的世界潮流,但是同当年发展燃油电厂一样,要研究是否符合中国的国情?     

活塞车床设计方案探讨--ECK25异形活塞车床设计分析

本文从新型活塞设计的趋势及其对活塞车床的功能要求，讨论活塞车床的设计方案，并从机床功能、造型和宜人性上进行分析。     

中国煤炭地下气化技术的发展

本文综述了煤炭地下汽化技术的国内外发展现状,对我国“长通道、大断面”煤炭地下气化新工艺给予了技术经济评述,并提出了发展煤炭地下汽化技术的政策建议。     

分选机制砂对混凝土性能影响试验研究

平江抽水蓄能电站泵送混凝土使用的花岗岩为主的人工细骨料,云母含量较高.通过分选工艺降低游离云母的机制砂配制混凝土,性能试验结果表明:分选后机制砂混凝土拌和物混凝土用水量减少,混凝土工作性能提高,混凝土的抗冻性能得到改善.     

提高日光温室太阳能利用率的措施

根据天文学,气象学,地理学的基本原理,在实验的基础上提出了日光温室提高太阳能利用率的措施。     

固体热辐射Yong性能分析

本文对漫灰均温物体在常物性条件下对外辐射传热的Ｙｏｎｇ值计算建立了数学模型。通过与物体内能Ｙｏｎｇ公式的数值计算比较,得出了辐射能量的Ｙｏｎｇ值不大于内能Ｙｏｎｇ值的结论。从初步的热射Ｙｏｎｇ值计算公式发现。Ｙｏｎｇ与物体表面辐射率有关。