阔叶木浆对工业滤纸原纸透气度和孔径的影响

阔叶木浆较低的价格和对孔径的控制能力使得其在工业滤纸的生产中广泛应用,但阔叶木浆的纤维相对较短、细,对滤纸透气性能限制较大。实际生产经验显示,随着阔叶木浆加入量的提高,滤纸孔径逐渐缩小,透气度大幅降低。准确的确定阔叶木浆加入量,能够合理控制孔径和透气度的范围,同时可以充分利用阔叶木浆价格较低的优势,有效降低生产成本。实验结果显示:阔叶木浆的加入量与滤纸孔径和透气度均呈现出反比例函数图像,并可以求出关系式。     

定量对双层空气复合滤纸原纸性能的影响

双层复合滤纸的设计对双层复合空气滤纸原纸的性能具有重要的影响。研究了不同总定量及不同定量比的双层复合空气滤纸原纸,探究定量变化对双层复合空气滤纸原纸性能的影响。结果表明,随着总定量的增加,孔径减小,透气度减小,过滤效率增加,容尘量减小;120g/m2时过滤效率为99.68%,容尘量为117g/m2;改变复合滤纸定量比,容尘量先上升后下降,过滤效率基本不变,结合载尘纸样内部结构图,定量比1∶3为最佳值;与单层滤纸相比,复合滤纸过滤效率高于单层滤纸,最大差值为0.1%。     

麦草浆中木素含量对其MFC增强性能的影响

实验自制3种不同木素含量的麦草浆及相应的微纤化纤维素（MFC）产品,并以MFC为增强剂用于漂白化学热磨机械浆（BCTMP）抄片,探究其对BCTMP浆张强度性能的影响。结果表明,麦草浆中木素含量对用其制备的MFC产品增强性能具有显著影响,将木素含量分别为24.04%、11.82%和3.84%的麦草浆制得的MFC按用量5%添加到BCTMP中,手抄片裂断长分别为1.96、2.56和2.53 km,当MFC用量增至20%时,手抄片裂断长分别增加到2.48、4.17和4.61 km,低木素含量麦草浆制备的MFC增强性能更显著;扫描电子显微镜（SEM）、X射线光电子能谱仪（XPS）、扫描电子显微镜-能谱仪（SEM-EDS）等定量分析结果进一步证明,麦草浆中的木素是通过抑制MFC制备过程中微纤丝的形成以及影响MFC表面活性羟基相对含量2方面作用共同影响MFC的增强性能。     

阳离子试剂对织物染色整理影响的研究

本文针对纤维素织物阳离子化后对织物染色后整理的影响作了初步探讨，结果表明，阳离子化整理可减少大量的有色废液，同时又能提高后整理性能。     

超声处理对制备竹浆微纤化纤维素的影响

以漂白竹浆为原料,采用中性2,2,6,6-四甲基哌啶-氮-氧化物(TEMPO)微波氧化预处理,然后在浆浓0.6%下结合超声波处理将竹浆纤维素分离解纤为微纤化纤维素(MFC)。通过表观分散性观察、透射电子显微镜(TEM)、傅里叶变换红外吸收光谱(FI-TR)和X射线衍射仪(XRD)对不同超声时间所制备的MFC的分散特性、形态特征、化学结构、结晶度和晶型结构进行表征分析。结果表明,超声2 h可以得到分散性好、完全透明的MFC,其直径分布均一(5~15 nm),而长度在微米级;超声处理不会改变纤维素的化学结构和晶体类型,但对其结晶度有一定的影响,超声1.5 h其结晶度最高66.97%,超声2.5 h后其结晶度剧烈下降至39.16%。     

匀度指数对碳纸原纸强度与孔隙特性的影响研究

本研究以碳纤维为原料,通过改变分散剂种类制备具有不同匀度性能的碳纸原纸,考察了碳纤维浆料的分散稳定性及其均匀性变化规律,探讨了匀度指数与透气度、抗张强度、孔隙率等指标之间的关系。结果表明,与单一APAM、TOCNs和PU分散剂相比,质量分数0.1% APAM和1.0% PU复合的分散剂体系制备的碳纤维浆料分散稳定性和均匀性得到改善,该复合分散剂制备碳纸原纸匀度指数最好,为10.32。随着匀度指数的减小,碳纸原纸厚度偏差从21.76 mm降至0.96 mm,抗张强度从0.15 kN/m增加到1.68 kN/m,孔隙率从93.5%下降到90.5%,透气度从1 658.9 L/(m²·s)下降到1 171.5 L/(m²·s)。     

MFC负载铁离子催化对纸浆纤维的芬顿表面氧化作用研究

将富含铁离子的微纤化纤维素(MFC-铁离子)吸附于漂白硫酸盐针叶木浆纤维表面,然后对纸浆纤维表面进行芬顿氧化;通过激光扫描共聚焦显微镜(LSCM)间接检测纤维上芬顿反应产生的羟基自由基(·OH),使用扫描电子显微镜(SEM)和能谱仪(EDS)检测纤维上铁元素的分布;评价了在相同打浆转数下,芬顿表面氧化处理对纤维素平均聚合度(DP)、纤维形态及成纸抗张指数和撕裂指数的影响。结果表明,芬顿表面氧化预处理产生的·OH主要分布在纸浆纤维表面,并且基本保留了纤维平均长度;与原浆相比,芬顿表面氧化浆的纤维素平均DP仅下降约4.9%,打浆转数8000转时,成纸抗张指数和撕裂指数较原浆成纸分别提高了20.9%和25.7%。     

苎麻织物阳离子化改性及其染色工艺的研究

笔者对苎麻织物的阳离子化改性工艺、改性织物的染色工艺,以及改性和染色一浴法工艺等都进行了全面、深入的研究,而且还从白度值、断裂强力、改性剂用量、阳离子化度、匀染性及加工成本等多方面对各种改性处理方式作了综合比较。通过本文的研究,揭示了影响阳离子化改性和染色的各种因素,从而筛选出了较佳的改性和染色条件,以及较佳的改性处理方式。此外,试验结果还表明,只要阳离子化剂选择得当,那么改性和染色同浴进行也是可能的,而且苎麻织物阳离子化改性和染色一浴法的轧烘焙工艺尚具有较大的实用价值和经济价值。研究结果对于苎麻、棉、粘胶及丝绸等含活泼氢纤维的改性和染色实践都具有重要的指导作用。     

阳离子对CMC溶液流变特性的影响研究

CMC具有典型的聚电解质效应,外源性离子强度及离子种类会使其流变性质产生影响.本文通过高级旋转流变仪详细研究了不同盐(包括一价阳离子Na+、K+及二价阳离子Ca2、Mg2+)及不同离子强度(离子浓度为0％～1％)对CMC水溶液流变特性的影响.通过实验发现,Na+、K+、Ca2+及Mg2+明显影响CMC溶液的零剪切粘度、黏度、剪切稀化指数、黏度衰减特性及黏弹性特性(包括弹性模量G,、黏性模量G”及损耗正切tan (ddlta)),并从微观结构上进行详细解析.同时,通过对CMC溶液进行频率扫描,研究了低频区与高频区的弹性模量与黏性模量随阳离子添加量的变化规律.另外,本文应用浊度仪及色度仪分别测定CMC溶液的浊度以及色度(包括L、a及b),研究了阳离子及其不同浓度对CMC水溶液浊度及色度特性的影响.     

纳米纤维素对小麦淀粉糊化和流变特性的影响

将不同比例微晶纤维素(microcrystalline cellulose,MCC)、纳米晶体纤维素(nanocrystaline cellulose,NCC)、纳米纤化纤维素(nanofibrillated cellulose,NFC)与小麦淀粉(wheat starch,WS)复配,对比研究纳米纤维素对小麦淀粉糊化...     

纳米微纤化纤维素在纸张增强与涂布中的应用

用漂白亚硫酸盐竹浆制备纳米微纤化纤维素(MFC),将MFC与漂白硫酸盐蔗渣浆、漂白针叶木浆以及漂白阔叶木浆混合抄片,探讨了浆内添加MFC对纸张物理强度性能的影响;同时在相同条件下,对MFC和阳离子淀粉的涂布效果进行比较.结果表明,在低涂布量时,MFC涂布的纸张表面强度要高于阳离子淀粉涂布的纸张.     

Lignin-containing Microfibrillated Cellulose Prepared from Corncob Residue via Calcium Hydroxide Co-grinding and Its Application in Paper Reinforcement

In this study, lignin-containing microfibrillated cellulose (MFC) was prepared from corncob residue after xylose extraction via co-grinding with calcium hydroxide. The product was then compared with the MFC obtained by direct grinding and applied to strengthen paper. The chemical composition and morphological structure analysis results showed that the corncob residue can be used to prepare lignin-containing MFC and does not require further purification. Moreover, the co-grinding with calcium hydroxide is easier to fibrillate corncob residue. The MFC obtained by co-grinding with calcium hydroxide had a higher aspect ratio, and its surface was coated with calcium carbonate nanoparticles. MFCs obtained by both the methods mentioned above had an obvious strengthening effect on paper. Compared with the paper without MFC, the tensile index, elongation, burst index, and folding strength of the paper with MFC obtained by co-grinding with calcium hydroxide significantly increased by 17.5%, 22.1%, 19.5%, and 157.1%, respectively. This study provides a novel idea for the utilization of corncob residue, which may enhance the value and promote the comprehensive utilization of corn by-products.     

滤纸多层复合对透气率的影响

研究多层复合滤纸和单层滤纸间透气率的关系。通过将单层湿纸页按一定顺序紧密叠合在一起并放入弧形干燥器内干燥的方法形成多层复合滤纸,探讨当各层纤维为单一纤维和多种纤维复配两种情况下的2层和3层复合滤纸的透气率与各单层滤纸透气率之间的关系,并从理论上推导出多层复合滤纸和单层滤纸间透气率存在如下关系:1/T=1/T1+1/T2+…+1/Tn,这对多层复合滤纸的研究有一定的指导意义。     

用圆网纸机生产高效真空吸尘器纸袋原纸的工艺研究

研究了采用圆网纸机生产高效真空吸尘器纸袋原纸的生产工艺。从纤维配比、浆料处理、化学助剂添加、表面施胶工艺及圆网纸机生产实际操作等方面考虑,采用单因素实验探讨各因素对生产高效真空吸尘器纸袋原纸的影响。研究结果表明,用圆网纸机生产高效真空吸尘器纸袋原纸的基本工艺条件为:石头牌南方松针叶木浆和涤纶纤维(12 mm,1.67 dtex)配比为75∶25;浆料只疏解不打浆;湿强剂(PAE)用量为0.6%;表面施胶采用质量比为1∶1的氧化淀粉(OS)与羧甲基纤维素(CMC)的混合胶液,胶液浓度为4%。     

活性炭孔隙结构对活性炭过滤纸吸附性能的影响

用氮气吸附法、扫描电镜对4种不同活性炭(木质活性炭AC1、AC2,煤质活性炭AC3,椰壳质活性炭AC4)的孔隙结构进行表征,通过抄纸方法制备活性炭过滤纸,用亚甲基蓝和苯酚吸附效率表征活性炭过滤纸的吸附性能,研究了活性炭孔隙结构对过滤纸吸附性能的影响.结果表明,两种木质活性炭的比表面积和总的孔容积较高,分别为1054 m2/g、1.165 cm3/g和1125 m2/g、1.083 cm3/g;4种活性炭微孔平均孔径相差不大,但两种木质活性炭的大中孔平均孔径较大;其中,木质活性炭AC2的微孔和大中孔孔容积均较大,孔径在0.64、1.2和2.3 nm附近的孔隙发达,具有较强的选择性吸收能力,用其抄造的过滤纸对亚甲基蓝和苯酚均有较好的吸附效率,3次过滤吸附效率分别为92.2%和93.8%.     

建筑模板原纸特性及生产工艺

主要介绍了建筑模板原纸的特性及生产工艺技术。     

纺织用纸线原纸的研究

分析了进口纸线原纸的纤维形态、组成及配比;测定了原纸的各项物理性能指标;研究了在针叶木浆中配加棉浆、细菌纤维以及水溶性PVA纤维对纸张强度性能的影响.结果表明当纤维配比为木浆纤维棉浆纤维细菌纤维水溶性纤维=81∶10∶7∶2,且分散剂PEO用量0.07%,湿强剂PAE用量1.8%,CMC用量0.3%时,纸线原纸的主要物理性能为干抗张指数71.10 N·m/g,湿抗张指数30.03N·m/g,撕裂指数8.01 mN·m2/g,耐折度460次、伸长率2.46%.     

多因素对纸张孔隙结构和渗透性能的影响研究

纸张的微观孔隙结构直接影响其性能。为实现对纸张结构的调控,本研究以棉浆、阔叶木浆和针叶木浆为原料,利用毛细管流动孔径分析仪研究纤维种类、打浆度和定量对纸张孔隙结构和渗透性能的影响。结果表明,随着打浆度和定量的增大,3种纤维原料抄造纸张的孔径都逐渐减小,孔径分布范围和峰值也随之往更小的孔径方向变化,渗透性能下降;相比于定量因素,打浆对纸张孔径及其分布影响更大,进而影响纸张的渗透性能。上述研究结果有助于实现对纸张结构的调控,推进多孔纸基材料的设计和开发。     

原纸表面施胶液对铜版纸表面强度的影响

探讨了原纸表面施胶液的变化对铜版纸表面强度的影响。结果表明:增加表面施胶液中氧化淀粉浓度,施胶量增加,施胶胶膜厚度增加,原纸抗张指数、平滑度、白度均有所提高,Cobb值下降,铜版纸表面强度拉毛值显著增加;增加表面施胶液中表面施胶剂用量,原纸Cobb值下降,抗张指数、平滑度均提高,白度没有变化,对铜版纸表面强度影响较小。