Effect of Ho^3＋ Ion on Luminescent Property of CaGaeS4：Eu^2＋

The afterglow luminescent property and thermo-luminescence (TL) of CaGa2S4：Eu^2 , Ho^3 were systemateally investigated. The afterglow of Eu and Ho Co-doped CaGa2S4 shows a broadband emission at 552 nm, which is the same as that of Eu doped CaGa2S4 only. And the decay behavior of CaGa2S4 Eu^2 , Ho^3 was investigated, which shows that CaGa2S4: Eu^2 , Ho^3 is a phosphor with long after-glow, whereas the CaGazS4:Eu^2 is a phosphor with-out long afterglow. Comparison of TL curves and 3D-TL emission spectra of CaGa2S4:Eu^2 ,Ho^3 and Ca-C, a2S4:Eu^2 show that a new trap center is produced at about 80℃, which is the basic reason of CaGazS4:Eu^2 ,Ho^3 with long afterglow.     

Effects of Doping Trace Sm^3＋ and Gd^3＋ on Luminescent Character of Y2O2S：Eu^3＋

After trace Sm^3＋ ions and Gd^3＋ ions doping, the emission intensity of red phosphors Y2O2S： Eu^3 ＋ was enhanced and the voltage character （relation between emission intensity and excitation voltage） was improved while the other properties of physics and chemistry were not changed. The origins of enhancement and improvement are discussed. Probably the distortion and the defect of crystals are decreased by the substitution of Gd^3＋ for Y^3＋ instead of Eu^3＋ for Y^3＋ , and thus the Eu^3＋ crystal field is improved, and radiationless process and energy loss resulted from crystal defect are weakened, which leads to increased luminescence intensity and voltage character improvement. The overlapping fluorescent spectra of Y2O2S： Sm^3＋ emission and Y2O2S：Eu^3＋ excitation as well as Eu^3 ＋ excitation spectra transitions spectra lead to energy transfer from Sm^3 ＋ sensitization of Sm^3＋ ions fectively. containing Sm^3＋ excitation the possibility of resonance ions to Eu^3＋ ions, and the to Eu^3＋ ions is achieved effectively.     

Sol-Gel Synthesis and Luminescent Characteristic of Doped Eu^3 ＋ Silicate-Silica Phosphor

Silicagelphosphorsdopedrareearthionshave attractedgreatattentionofmanyresearchersdueto theseadvantages,suchashighersamplehomogeneity,purityandstable,efficientandenvironmentallyfriend lyphotoluminescencematrixmaterials,whichisless toxicleadtonetconversione…     

Citric Gel Synthesis and Luminescent Properties of Ce^3＋-Activated SrGa2O4 Phosphor

Ce^3＋-activated SrGa2O4 phosphor was synthesized by a method of citric gel,wherein citric acid served as a chelate agent,and the as-synthesized powder was calcined in a slightly reduced ambient.The crystallization characteristics of the sample varied with the calcining temperature.Compared with the phosphor prepared by the solid-state reaction,the phosphor synthesized by citric gel was calcined at a relatively lower temperature.Consequently,the volatilization of Ga2O3 during high-temperature calcining process was avoided.The typical double-peak emission of Ce^3＋ originated from 2D（5d）→4F5/2（4f）,and 2D（5d）→4F7/2（4f）was observed,and the intrinsic emission of SrGa2O4 host was much restricted.The emission intensity varied with the calcining temperature because the different crystallinity and the optimal concentration of Ce-dopant was determined at 3%.     

Study on Luminescence Properties and Crystal-Lattice Environment of Eu^2＋ in Sr4-xMgxSi3O8Cl4：Eu^2＋ Phosphor

According to the Van Uitert experimental equation, crystal-lattice environment of Eu^2 in the Sr4Si3O8C14 crystal was discussed. By adding Mg^2 to the host lattice, Sr4-xMgxSi3O8C14:Eu^2 was synthesized and the emission peak shifted from blue-green (488nm) to blue-violet (411nm) with the increase of amount of the magnesium which replaced the strontium. By analyzing the spectra of Sr4-xMgxSi3O8C14:Eu^2 the two Eu^2 emission centers were found because of the change of crystal-lattice environment in the host and the crystal structure was obtained by X-ray diffraction data.     

复合熔盐法合成Y2O3.Eu3+红色荧光粉

以草酸钇铕(Y2(C2O4)3:Eu3+)为前驱体,采用复合熔盐(NaCl+S+Na2CO3)协助焙烧法合成Y2O3:E.u3+红色荧光粉.利用XRD、SEM、光谱分析等测试和分析荧光粉粒径、颗粒形貌以及发光性能.主要考察复合熔盐配比、用量以及焙烧温度和时间对Y2O3:Eu3+荧光粉发光性能的影响.结果表明,NaCl在...     

Luminescent Properties of Green Phosphor Ca8Mg（SiO4 ）4 Cl2：EU^2＋ , DY^3＋ for LED Applications

The new phosphor calcium magnesium chlorosilicate, codoped with Eu^2＋ and Dy^3＋, was synthesized with the help of the high temperature solid state reaction in reducing atmosphere. The excitation and emission spectra were very similar to that of Ca8Mg（SiO4）4Cl2 ：Eu^2＋, and the Dy^3＋ concentration influenced the emission intensity of this phosphor. The intensity of Eu^2＋ and Dy^3＋ codoped CMSC was stronger than that of Eu^2＋ singly doped CMSC. The emission spectrum of the Dy^3＋ ion overlapped the absorption band of the Eu^2＋ ion, indicating that an energy transfer from Dy^3＋ to Eu^2＋ took place in CMSC：Eu^2＋, Dy^3＋ phosphor. The mechanism of the energy transfer from Dy^3＋ tO Eu^2＋, in this phosphor, might be resonant energy transfer.     

Research on Y2O3：Eu Phosphor Coated with In2O3

Y2O3：Eu red phosphor for FED application was prepared by high temperature solid-state reaction. The In2O3 coating by precipitation method to the phosphor was applied and the analyses of XRD, Zeta potential, SEM, EDS and low voltage cathodoluminescence （CL） were conducted for investigating the coating effect. The results showed that In2O3 coating promoted the low voltage CL of the phosphor efficiently. The promotion was possibly due to the enhancement of the surface conductivity of the phosphor grains.     

Luminescent characteristics of Ba3Y2（BO3）4：Eu^3＋ phosphor for white LED

The Ba3Y2（BO3）4：Eu^3＋ phosphor was synthesized using a high temperature solid-state reaction method and the luminescent characteristics were investigated. The emission spectrum exhibited one strong red emission at 613 nm, corresponding to the electric dipole 5D0-TF2 transition of Eu^3＋, under 365 nm excitation. The excitation spectrum of 613 nm indicated that the Ba3Y2（BO3）n：Eu^3＋ phosphor was effectively excited by ultraviolet （UV） （254, 365 and 400 nm） and blue （470 nm） light. The effect of Eu^3＋ concentration on the 613 nm emission of the Ba3Y2（BO3）n：Eu^3＋ phosphor was measured. The results showed that the emission intensity increased with increasing Eu^3＋ concentration, and then decreased. The CIE color coordinates of Ba3Y2（BO3）4：Eu^3＋ phosphor were x=0.641 and y=0.359 at 15 mol.% Eu^3＋.     

微波辐射法制备Y2O3:Eu3+红色荧光粉

通过正交试验确定了微波辐射法合成Y2O3:Eu3+红色荧光粉的最佳工艺条件,即升温速率20℃/min,煅烧温度1 240℃,保温时间60 min,此条件下所制备样品的相对亮度达107.0%.对样品进行物相、粒度及光谱分析,结果表明该样品为单一纯相Y2O3,粉末粒度均匀,D50为3.28μm,其最大发射光谱峰位于607 nm处,色坐标为x=0.653 3、y=0.342 4.     

Y2O3:Eu荧光粉的制备方法及性质研究进展

本文报道了近年来人们用来制备Y2O3:Eu粉末的多种方法(高温固相合成、微波热合成、溶胶-凝胶技术、共沉淀法、燃烧法、喷雾干燥法、高分子凝胶包膜法),并对各种合成方法所得产品的粒径、激发与发射光谱以及粉末的发光亮度做了分析和比较,同时对各种方法的特点进行了归纳和总结.     

Properties of red-emitting phosphors Sr2MgSi2O7:Eu3+ prepared by gel-combustion method assisted by microwave

Novel red-emitting phosphors Sr2MgSi2O7:Eu3+ were prepared by gel-combustion method assisted by microwave. The phase struc-ture and luminescent properties of as-synthesized phosphors were investigated by XRD and fluorescence spectrophotometer, respectively. The results showed that the as-synthesized sample was Sr2MgSi2O7 with tetragonal crystal structure. The excitation spectrum of Sr2MgSi2O7:Eu3+ was composed of two major parts: one was the broad band between 200 and 350 nm, which belonged to the charge transfer of Eu3+-O2-; the other consisted of a series of sharp lines between 350 and 450 nm, ascribed to the f-f transition of Eu3+. The emission spec-trum consisted of two emission peaks at 593 and 616 nm, which was attributed to 5D0→7F1 and 5D0→7F2 of Eu3+, respectively. The concen-tration of Eu3+ (x) had great effect on the emission intensity of Sr2-xMgSi2O7:Eu3+x. When x varied in the range of 0.04-0.18, the intensity of emission peaks at 593 and 616 nm increased gradually with the concentration of Eu3+ increasing. It was interesting that no concentration quenching occurred. Moreover, the luminescent intensity could be greatly enhanced with incorporation of charge compensator Li+ ions.     

Luminescent properties of Ca2SiO4:Eu3+ red phosphor for trichromatic white light emitting diodes

The luminescent properties of Eu3 doped Ca2SiO4 red phosphors synthesized by the flux fusion reaction method were investigated. It was found that the excitation spectrum included two regions: the weak excitation band below 325 nm and strong narrow peaks above 325 nm. The main peak of the excitation band was located at 400 nm. The peaks located at 290 nm were assigned to the combination of the charge transfer transition of O-Eu, peaks above 325 nm (325, 385, 400, 470, 511, and 539 nm) were assigned to the f–f transitions of Eu3 . The emission spectrum was dominated by the red peak located at 612 nm due to the electric dipole transition of 5D0–7F2. In addition, the ef- fects of the Eu3 content and charge compensators of Li , Na , K , and Cl– ions on the emission intensity were investigated. The experiment results suggested that the strongest emission was obtained when the concentration of the Eu3 ions was 0.3 mol–1, and Li ions gave the best improvement to enhance the emission intensity. Ca2SiO4:Eu3 , Li was thus suitable for low-cost trichromatic white light emitting diodes (WLED) based on UV InGaN chip.     

Y_2O_3-SiO_2∶Eu~(3 ),Bi~(3 )荧光材料的结构及性能研究

用溶胶—凝胶法 (Sol- gel法 )低温合成了 Y2 O3- Si O2 ∶ Eu3 ,Bi3 红色发光粉。 X射线实验研究发现 ,85 0℃时 ,样品晶体结构为 Y2 Si O5,属单斜晶系 (a=9.0 12 ,b=0 .979,c=6 .6 30 ) ,空间点群为 PI1 /C;SEM实验显示发光体为不规则片层结构 ;粒度分析表明 :发光体粒度分布均匀 ,平均粒度为 0 .79μm;T≥ 6 0 0℃时 ,发光体出现温度猝灭现象