粘合树脂A250在子午线轮胎带束层胶中的应用

试验研究以粘合树脂A250替代间苯二酚在子午线轮胎带束层胶中的应用效果.结果表明,在子午线轮胎带束层胶配方中,采用2.5份粘合树脂A250替代1.5份间苯二酚,并采用快速促进剂NS,减小癸酸钴用量,胶料的加工安全性提高,硫化速度降低不明显;硫化胶各项物理性能变化不大,热空气老化后的撕裂强度明显提高,老化后胶料与钢丝帘线的粘合性能保持较高水平.     

粘合树脂Elaztobond A250在全钢载重子午线轮胎带束层胶中的应用

试验研究粘合树脂Elaztobond A250在全钢载重子午线轮胎带束层胶中的应用。结果表明,在全钢载重子午线轮胎带束层胶中以2份粘合树脂Elaztobond A250替代1.5份间苯二酚,以促进剂NS等量替代促进剂NOBS,胶料的工艺性能和硫化胶的物理性能变化不大,老化后胶料与钢丝帘线的H抽出力略有提高,成品轮胎的强度和耐久性能均超过国家标准要求,具有明显的环保优势。     

粘合树脂Elaztobond A250在全钢载重子午线轮胎带束层胶中的应用

试验研究粘合树脂Elaztobond A250在全钢载重子午线轮胎带束层胶中的应用。结果表明,在全钢载重子午线轮胎带束层胶中以2份粘合树脂Elaztobond A250替代L5份问苯二酚,以促进剂NS等量替代促进剂NOBS,胶料的工艺性能和硫化胶的物理性能变化不大,老化后胶料与钢丝帘线的H抽出力略有提高,成品轮胎的强度和耐久性能均超过国家标准要求,具有明显的环保优势。     

粘合树脂PN759在半钢子午线轮胎带束层胶中的应用

试验研究粘合树脂PN759等量替代预分散间苯二酚在半钢子午线轮胎带束层胶中的应用效果。结果表明,在半钢子午线轮胎带束层胶中以粘合树脂PN759等量替代预分散间苯二酚,并以1.2份促进剂NS替代1.4份促进剂DZ,硫化胶的300%定伸应力略有下降,粘合性能略有提高,成品轮胎的高速和耐久性能均达到国家标准要求。     

粘合树脂PN759在全钢载重子午线轮胎胎体胶中的应用

试验研究粘合树脂PN759替代间苯二酚在全钢载重子午线轮胎胎体胶中的应用效果.结果表明,在全钢载重子午线轮胎胎体胶中,以粘合树脂PN759等量替代间苯二酚,同时以促进剂NS减量替代促进剂DZ,可以保证胶料的加工安全性、硫化特性和物理性能达到使用间苯二酚的水平,提高成品轮胎的耐久性能,降低原材料成本,解决了胶料在混炼和加工过程中出现的冒烟问题.     

几种粘合促进剂在全钢子午线轮胎中的应用

研究间苯二酚、间甲树脂、酚醛树脂3种粘合促进剂在全钢子午线轮胎胎体中的应用。结果表明：间苯二酚硫化胶的邵尔A型硬度和定伸应力较大,酚醛树脂和间甲树脂硫化胶的撕裂强度和拉断伸长率较大;酚醛树脂硫化胶与钢丝帘线的初始抽出力较高,老化后,间苯二酚和间甲树脂硫化胶与钢丝帘线的抽出力和抽出力保持率较高;酚醛树脂硫化胶压缩生热和60℃时的损耗因子明显高于间苯二酚和间甲树脂硫化胶。在实际生产中,应根据原料特性与应用性能调整配方与优化工艺,以获得最佳的综合性能。     

粘合树脂在全钢子午线轮胎胎体胶中的应用

研究了三种酚醛树脂替代间苯二酚后全钢子午线轮胎胎体胶的硫化性能、力学性能、动态力学性能以及老化前后与钢丝的粘合性能。结果表明,使用酚醛树脂替代间苯二酚后,胶料的门尼黏度增加,焦烧时间延长;除树脂TYC-0219使硫化时间明显延长外,其余相差不大;硫化胶的拉伸强度、定伸应力稍有降低,其他力学性能变化不大;贮能模量、损耗因子都有所下降;胶料与镀铜钢丝间的抽出力明显增大,相对于使用间苯二酚,树脂A250、TYC-0219和B-20-S使抽出力分别增加32%、24%和22%。热空气老化后,三种替代树脂的增粘效果仍然明显高于间苯二酚;经盐水介质老化后,树脂A250的增粘效果下降较大。     

粘合树脂PN760在全钢载重子午线轮胎钢丝胶中的应用

研究粘合树脂PN760在全钢载重子午线轮胎钢丝胶中的应用。结果表明:在钢丝胶中以粘合树脂PN760替代间苯二酚,胶料的门尼粘度增大,门尼焦烧时间缩短,t90延长;硫化胶的物理性能变化不大,粘合性能提高;成品轮胎的耐久性能提高,可减少环境污染。     

间苯二酚-甲醛树脂HT1005在全钢载重子午线轮胎钢丝粘合胶中的应用

研究国产间苯二酚-甲醛树脂HT1005在全钢载重子午线轮胎钢丝粘合胶中的应用,并与普通间苯二酚和进口同类产品B-20-S进行对比。结果表明:以HT1005树脂替代间苯二酚用于钢丝粘合胶中,胶料的门尼焦烧时间和t90延长,硫化胶的物理性能和粘合性能提高,可有效解决胶料在加工过程中的冒烟问题,减少环境污染;加入HT1005树脂的胶料综合性能与加入B-20-S树脂的胶料基本相当。     

改性间苯二酣-甲醒树脂在全钢载重子午线轮胎带束层胶中的应用

研究改性间苯二酚-甲醛树脂B-20-WS或A250等量替代间苯二酚在全钢载重子午线轮胎带束层胶中的应用。结果表明:以B-20-WS或A250树脂等量替代间苯二酚后,胶料的门尼焦烧时间延长,硫化速度加快;硫化胶的定伸应力减小,拉伸强度和粘合力增大;成品轮胎的耐久性能提高,可减少环境污染。     

粘合增进剂NMP-ZD在载重斜交轮胎中的应用

对粘合增进剂NMP-ZD在载重斜交轮胎缓冲胶和外层帘布胶配方中的应用进行试验。结果表明，在原生产配方的基础上，缓冲层胶中添加1.5份间苯二酚和2．5份粘合增进剂NMP—ZD，外层帘布胶中添加1.2份间苯二酚和2份粘合增进剂NMP-ZD，胶料的粘合性能和耐热老化性能提高，轮胎的内在质量得到改善，使用寿命延长。     

Investigation of the effects of adhesion promoters on the adhesion properties of rubber/steel cord by a new testing technique

The effects of adhesion promoters, cobalt decanoate and PN759 (modified resorcinol) on the static and dynamic adhesion properties of rubber/steel cord in a carcass recipe are examined. A new testing method with special rubber/steel cord specimens was developed. It was found that cobalt decanoate could improve the static adhesion and favored the dynamic adhesion of rubber/steel cord so that adhesive failure mainly occurred in rubber phase. A resorcinol‐formaldehyde‐silica promoting system was deleterious to adhesion stability, but improved initial adhesion strength. PN759 improved the dynamic mechanical properties compared with resorcinol for the carcass vulcanizates at strains less than 10%. PN759 instead of resorcinol slightly improved the static and dynamic adhesion and the probability that adhesion failure occurred in the interphase was similar to that occurring in the rubber phase. The dynamic “pull‐out forces” for samples with 1.0 phr cobalt decanoate first increased and then decreased with the increase in the number of fatigue cycles and reached a maximum at 100,000 fatigue cycles. The covered rubber on the “pulled‐out” cord after fatigue appeared to form a screw thread form and the greater pull‐out force corresponded to more uniform and narrower screw threads. SEM images indicated that un‐dispersed filler agglomerates could be the initiating factor for adhesive failure. © 2013 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2014 , 131, 39460.     

改性白炭黑对NR/ENR共混胶力学性能的影响

研究了沉淀法白炭黑对NR/ENR共混胶力学性能的影响。结果表明,随着未改性白炭黑用量的增加,共混胶力学性能先升高后降低,未改性白炭黑用量为5～10份时共混胶力学性能较好;Si-69,KH-550和间苯二酚六次甲基四胺(PY)对白炭黑都有很好的改性效果,其中Si-69和KH-550用量分别为2.7份时改性效果最佳,PY(间苯二酚和六次甲基四胺用量比为40/60的络合物)用量为1份时改性效果最好。     

大比表面积活性氧化锌在轮胎肩垫胶中的应用

研究了大比表面积活性氧化锌在轮胎肩垫胶中的应用效果。试验结果表明 ,用 5份大比表面积活性氧化锌替代 8份普通氧化锌 ,胶料的门尼粘度略有下降 ,焦烧时间和t10 稍有延长 ,t90 缩短 ;硫化胶的邵尔A型硬度、拉伸强度、30 0 %定伸应力和撕裂强度均有所提高 ,而扯断伸长率和固特里奇生热有所降低 ;采用试验配方生产的轮胎成品性能明显提高 ,且配方成本下降     

粘合体系对全钢载重子午线轮胎胎体钢丝粘合胶性能的影响

研究3种粘合体系对全钢载重子午线轮胎胎体钢丝粘合胶性能的影响。试验结果表明,单独使用钴盐粘合体系,癸酸钻用量以0．5和1份为宜;单独使用间一甲粘合体系,间苯二酚-80用量以1．25份、粘合剂RA用量以4和5份为宜;两种粘合体系配合使用进行配方优选,钴盐用量为0．5份,间苯二酚-80用量为1．25份,粘合剂RA用量为4份,胶料的各项性能达到最优。采用优选配方进行生产,胶料的工艺性能良好,成品轮胎耐久性能超过国家标准要求。     

反式聚异戊二烯/纳米碳化硅形状记忆复合材料的制备与性能

以反式聚异戊二烯（TPI）为基质,研究了纳米碳化硅用量对碳化硅/TPI形状记忆复合材料硫化特性、物理机械性能、热性能及形状记忆性能的影响。结果表明,随着碳化硅用量的增加,复合材料的焦烧时间和正硫化时间都逐渐缩短;拉伸强度呈现先增大后减小的趋势,硬度逐渐增大;结晶度逐渐降低,从纯TPI的16.5%下降至碳化硅用量20份（质量,下同）时的13.9%;碳化硅用量为10份时复合材料的单向形状记忆性能最好,而其双向形状记忆行为在应力为250 kPa时的形状回复率达到了最大值79.1%。     

次氯化血红素的合成

以氯化血红素为原料,用间苯二酚还原合成了次氯化血红素。讨论了反应温度、反应时间、间苯二酚用量对次氯化血红素产率的影响,并进行了正交优化实验。在反应时间45min、反应温度165℃、m(氯化血红素)∶m(间苯二酚)=1∶5的最佳反应条件下,次氯化血红素产率可达97.8%,与最近的报道相比产率提高了约55%。传统方法需在高温下加入乙醚,既不方便,又很危险,该文以研磨水洗法取代乙醚溶解法实现了这一反应,安全、经济、简便。产物进行了精制和表征。