Magnetic and Magnetocaloric Properties of Er2TiMnO7 Compound

Magnetic properties and magnetocaloric effects of the Er₂TiMnO₇ compound have been evaluated by magnetization and heat capacity measurements. The reversible magnetic-entropy change is found to be just above the boiling point of helium and hydrogen liquefaction temperature range of 2 to 50 K. The magnetocaloric behavior estimated from specific heat data is confirmed by adiabatic magnetization above 2 K, and indicates that Er₂TiMnO₇ is a potential candidate for application in magnetic refrigeration in the low-temperature range.     

溶胶凝胶法合成Li4.4Al0.4S0.6O4-xLi2O及电导性能*

用溶胶-凝胶法制备了Li.4.4A;0.4Si0.6O4-xLi2O(x=0.00～0.50)离子导体材料,并用DTA-TG、XRD、及交流阻抗等技术对样品进行了测试,结果发现用溶胶-凝胶法可降低Li4.4Al0.4Si0.6O4的合成温度;随Li2O的掺入可增强基质材料的致密性并提高了其离子的导电性能.     

Magnetic Properties and Magnetocaloric (MC) Effects in the Antiferromagnetic Gd2NiGa3 Compound

Journal of Superconductivity and Novel Magnetism - The magnetocaloric (MC) properties in various magnetic materials were well determined within last three decades due to its own potential...     

羟基磷灰石涂层材料的制备及其性能表征

设计并采用类似搪瓷涂覆的工艺制备了羟基磷灰石－Ｔｉ６Ａｌ４Ｖ复合材料．使用ＸＲＤ、ＳＥＭ对复合材料的相组成和显微结构进行分析和表征,在模拟体液中观察了获得材料的生物相容性．结果表明;在涂层中,羟基磷灰石粒子均匀地分散在玻璃基体中,它们保持原有的晶格结构,未发生相分解等现象．烧成温度对中间层玻璃涂层的显微结构有着较为明显的影响．中间层玻璃涂层与钛合金的结合强度或不小于２９．７３ＭＰａ,远高于等离子喷涂,达到使用要求．在模拟体液中浸泡一段时间后,ＸＰＳ分析表明复合材料表面有新生羟基磷灰石粒子析出,表明复合涂层有优良的生物相容性．     

Optical and Low-Temperature Magnetocaloric Properties of HoCr0.5Mn0.5O3 Compound

Journal of Superconductivity and Novel Magnetism - The optical, magnetic and magnetocaloric properties of HoCr0.5Mn0.5O3 compound have been investigated thoroughly. A multicolour photoluminescence...     

Investigation on Magnetic and Magnetocaloric Properties of DySe2

Journal of Superconductivity and Novel Magnetism - The magnetization measurements have been performed to bring out the magnetic and magnetocaloric properties of polycrystalline DySe2 system...     

Al掺杂浓度对Hf0.5 Zr0.5 O2薄膜铁电性能的影响

采用脉冲激光沉积法(Pulsed laser deposition,PLD)在Pt/Ti/SiO2/Si衬底上制备TiN/Al掺杂Hf0.5 Zr0.5 O2/TiN的MIM(金属-绝缘体-金属)结构薄膜电容器.对Al掺杂浓度为0％ ～4％(摩尔分数)的Al:Hf0.5 Zr0.5 O2薄膜的微观结构以及电学性能进行了研究,在此基础上,还研究了退火温度对Al:Hf0.5 Zr0.5 O2薄膜的影响.测试结果表明,随着Al掺杂浓度的增大和退火温度的降低,四方相更加稳定,电滞回线更加细窄,剩余极化强度减小.退火温度为500℃时,掺杂浓度为1.03％(摩尔分数)的Al:Hf0.5 Zr0.5 O2薄膜中将诱导出类似反铁电薄膜具有的双电滞回线特性,储能密度更高.分析结果表明,这些变化均是由于Al:Hf0.5 Zr0.5 O2薄膜内四方相与正交相之间发生的场致可逆相变以及氧空位的再分布.     

双钙钛矿化合物Sr_2FeMoO_6的制备及其电磁特性研究

采用溶胶一凝胶法在不同烧结温度下制备了双钙钛矿结构化合物Sr_2FeMoO_6,研究了烧结温度对样品B位阳离子的有序度和饱和磁化强度的影响,测量了样品电阻率随温度变化的曲线.X射线衍射实验表明,所有样品中无杂相产生,晶体结构均为四方结构.样品的有序度随烧结温度的升高而增大,而有序度越高的样品饱和磁化强度也越大;样品在30000Oe磁场下的导电行为呈现出由半导体导电行为(低温区T≈10～80K)向金属导电行为(高温区了T≈80～300K)的转变.     

细晶Ba0.6Sr0.4TiO3(BST)陶瓷材料的制备与介电性能

采用改进的Sol-gel工艺和传统烧结技术制备了晶粒尺寸在0.15～10μm的Ba0.6Sr0.4TiO3(BST)陶瓷,观察了样品的显微结构,并对样品的介电性能进行了测试,分析了晶粒尺寸对材料介电性能的影响.实验结果表明:改进的Sol-gel工艺和两步烧结法可以有效地控制Ba0.6Sr0.4TiO3(BST)陶瓷的晶粒尺寸.晶粒尺寸的降低,材料的介电常数也随之下降,介电峰呈现明显的铁电-顺电弥散相变;但当陶瓷的晶粒尺寸＜1 μm,介电常数出现峰值,铁电相变温区变窄.     

Magnetothermal Properties and Magnetocaloric Effect in R3Co11B4

Journal of Superconductivity and Novel Magnetism - We present a study on the magnetic properties and magnetocaloric effect (MCE) in R3Co11B4, where R?=?Pr, Nd, Tb, Dy, and Ho. The...     

Ti6Al4V-TiN和Ti6Al4V-TiN-TiC生物梯度材料的血液相容性评价

采用体外试验法对Ti6Al4V-TiN和Ti6Al4V-TiC生物梯度材料及其它几种常用人工心脏瓣膜材料的体外动态凝血时间、溶血率、血小板消耗率进行了测定,并对这几种材料的血液相容性进行了对比,得到以下结论.(1)以动态凝血时间为指标,有LTI碳＞DLC膜＞TiN＞TiC＞Ti6Al4V.(2)以血小板消耗率为指标,有LTI碳＞DLC膜＞TiN＞Ti6Al4V＞TiC.(3)以溶血率为指标,有LTI碳＞DLC膜＞TiN＞TiC＞Ti6Al4V.     

氩气雾化Ti6Al4V预合金粉末的制备及特性研究

采用氧气雾化法制备出Ti6Al4V预合金粉末,并对粉末的粒度分布、形貌和微观结构进行了研究.结果表明:所制备的粉末颗粒细小,粒度呈正态分布.粉末大部分为球形或近球形,粉末表面为近似六边形胞状组织,大颗粒粉末表面相对较为粗糙,并伴有少量的卫星颗粒,小颗粒粉末表面光滑,并且没有黏附卫星颗粒.粉末的内部组织呈现为胞状结构,组织细小均匀.粉末主要由α相胞晶和细针状马氏体α ′组成,这都是快速凝固所形成的;随着粉末粒度的减小,针状相数量和尺寸减小,并且部分发生球化形成细小的球化相.粉末表面存在一定的成分偏析以及碳、氧元素污染,氧化膜的厚度约为30μm.     

Ti-6Al-4V表面超声滚压制备Al_2O_3膜层的微观组织及性能研究

运用超声滚压处理(USRP)的方法,在Ti-6Al-4V合金表面制得一层Al2O3薄膜。利用SEM、XRD、光学干涉仪及显微硬度计分析了超声滚压处理后试样表面层的微观组织和性能。结果表明:加入Al2O3粉末进行USRP后可以在基体金属表面形成厚度约为7μm的Al2O3膜层,且结合处基体金属存在残余压应力和塑性变形。相对于母材,处理后试样表面粗糙度降低50%,表面硬度提高98%。同时,处理后试样表面层存在残余压应力场,最大压应力值为-687MPa,位于最表层,残余压应力深度为420μm。加入Al2O3粉末的USRP后的试样,既利用表面Al2O3的加入进一步提高其表面硬度,同时保留了USRP的优势。     

氦离子注入对Ti6Al4V合金组织和力学性能的影响

在室温和400～700℃条件下,采用 1×1017ions/cm2注入剂量和200keV加速电压对 Ti6Al4V合金进行了氦离子注入.分别采用纳米硬度仪和X射线衍射方法对Ti6Al4V合金的氦离子注入表面层(≤700nm)进行了纳米硬度、弹性模量测试和物相分析.结果表明:在室温至600℃范围内,氦离子注入温度越高,Ti6Al4V合金注入层的硬度也越高,而其弹性模量则变小.氦离子注入温度为700℃时,Ti6Al4V合金发生了软化,其弹性模量也有所提高.氦离子注入引起的硬化现象与点缺陷和Ti6Al4V合金中β相的析出有关,而软化现象则与β相的粗化和γ-TiH相的形成有关.     

通孔构型Ti6Al4V/Ti2AlC-TiAl基叠层复合板材的组织和性能

将Ti-Al-TiC混合粉末和通孔构型TC4钛合金箔(Ti6Al4V)依次叠放装入模具,采用放电等离子烧结技术( SPS)制备了珍珠层结构Ti6Al4V/Ti2 AlC-TiAl基叠层复合板材.采用XRD、SEM、EBSD等测试手段分析相组成及微观结构,测试其室温力学性能,研究其强韧化及断裂机理.结果表明,Ti2 AlC理论生成量为10% (质量分数)时,复合板材在垂直于叠层方向弯曲强度和断裂韧性达到最大值,分别为645. 77 MPa和25. 06 MPa· m1/2 .通孔构型TC4钛合金强韧层设计改变了裂纹扩展路径,使裂纹扩展驱动力不断被削弱,同时第二相Ti2 AlC对裂纹扩展也产生阻碍作用,从而提高了TiAl基叠层复合板材的综合力学性能.     

Effects of the Substitution of 30 % Pr for La on the Magnetic Properties and Magnetocaloric Effect in LaFe 1 1 . 5 Si 1 . 5 B 0 . 2

Magnetic properties and magnetocaloric effect (MCE) in LaFe_11.5Si_1.5 B _0.2 have been investigated by substituting 30 % Pr for La. It is found that the substitution of 30 % Pr for La leads to a reduction in Curie temperature (T _C) from 200 to 190 K. The characteristic of the itinerant electron metamagnetic (IEM) transition above T _C becomes more prominent with the substitution of 30 % Pr for La. The maximum magnetic entropy change (?ΔS _M) is remarkably enhanced from 13.0 to 17.9 J/kg·K under a field change of 0–3 T, and correspondingly, the values of refrigerant capacity (RC) for LaFe_11.5Si_1.5 B _0.2 and La_0.7Pr_0.3Fe_11.5Si_1.5 B _0.2 are 167 and 224 J/kg, respectively. The large ?ΔS _M and the high RC in a low magnetic field indicate that La_0.7Pr_0.3Fe_11.5Si_1.5 B _0.2 may be a promising candidate for magnetic refrigeration material near 200 K