Microwave Dielectric Properties of (111) Oriented Ferroelectric (Ba1 − xSrx)TiO3 Thin Films

Epitaxial (111) oriented ferroelectric (Ba_{1 ? x}Sr_x)TiO₃ (BST) films were deposited on MgO (111) single crystals using pulsed laser deposition. Structural properties of BST films were investigated using X-ray diffractometer. The dielectric properties of BST films were investigated under the dc bias field of 0–40 V using interdigital capacitors (IDT) fabricated by photolithography and etching process. The small signal dielectric properties of BST films were calculated by modified conformal mapping both the measured data using an impedance gain/phase analyzer and the reflection coefficient data measured using a HP 8510C vector network analyzer in 0.05–10 GHz at room temperature. The IDT capacitor based on (111) oriented BST film exhibits about 40% of capacitance change with an dc bias of 40 V which value is somewhat smaller than that of the IDT device based on (001) oriented BST film. But the dielectric quality factor value is about twice that of the device based on (001) oriented BST film.     

Frequency and Voltage Dependent Dielectric Properties of Ni-doped Ba0.6Sr0.4TiO3 Thin Films

Highly (100) preferred undoped and 1–5% Ni-doped Ba_1–xSr_xTiO₃ (BST) thin films were deposited onto MgO (100) single crystal substrate at 750°C using pulsed laser deposition. BST thin film-based interdigital capacitors (IDC) were prepared by standard photolithography process. The microwave properties of BST films were measured at 10 GHz. Ni-doped BST films showed better dielectric properties by exhibiting improved dielectric Q while retaining an appropriate capacitance tuning compared to undoped BST films. 1% Ni-doped BST film showed the maximum figure of merit of 2896.1. It is suggested that 1 mol% Ni doped BST film is an effective candidate for high performance tunable device applications.     

The resistance degradation of (Ba0.5Sr0.5)TiO3 thin films

Abstract

The leakage current and dielectric properties of (Ba_0.5Sr_0.5)TiO₃(BST) thin films prepared by pulsed laser deposition (PLD) were investigated. It was found that leakage currents for positive bias voltage were higher than that for negative bias voltage, which was attributed to the lattice mismatch between bottom Pt electrode and BST thin film. The time-dependent breakdown process under positive voltage was observed, which was interpreted as the increase of the internal electric field in the film near the bottom electrode. However, the internal electric field can be decreased and eventually recovered by applying negative bias voltage. It was found that internal electric field near the interface can influence the capacitance of the BST thin film capacitor. An explanation for the thickness effect of BST thin films was given.     

Synthesis and characterization of (BaxSr1−x)Ti1+yO3+z thin films and integration into microwave varactors and phase shifters

Abstract

Precise control of composition and microstructure is critical for the production of (Ba_xSr_1?x)Ti_1+yO_3+z (BST) dielectric thin films with the large dependence of permittivity on electric field, low losses, and high electrical breakdown fields that are required for successful integration of BST into tunable high frequency devices. Here we review recent results on composition-microstructure-electrical property relationships of polycrystalline BST films produced by magnetron sputter deposition, that are appropriate for microwave devices such as phase shifters. Films with controlled compositions were grown from a stoichiometric Ba_0.5Sr_0.5TiO₃ target by control of the background processing gas pressure. It was determined that the (Ba+Sr)/Ti ratios of these BST films could be adjusted from 0.73 to 0.98 by changing the total (Ar+O₂) process pressure, while the O₂/Ar ratio did not strongly affect the metal ion composition. Film crystalline structure and dielectric properties as a function of the (Ba+Sr)/Ti ratio are discussed. Optimized BST layers yielded capacitors with low dielectric losses (0.0047), among the best reported for sputtered BST, while still maintaining tunabili-ties suitable for device applications. These BST films were used to produce distributed-cir-cuit phase-shifters, using a discrete periodic loading of a coplanar waveguide with integrated BST varactors on high-resistivity silicon. Phase shifters yielding 30 degrees of phase shift per dB of insertion loss were demonstrated at 20GHz.     

Growth and Dielectric Properties of Ferroelectric BaTiO3 Thin Films for Cantilever-Type Microsensors

ABSTRACT

Ferroelectric BaTiO₃ (BTO) thin films were deposited on Si, silicon-on-insulator (SOI) and MgO substrates by pulsed laser deposition. The orientations of the films, polycrystalline and epitaxial phase, were controlled by the lattice mismatch between the BTO film and substrates. The structural properties and surface morphologies were examined using X-ray diffractometer and atomic force microscope. The dielectric properties of BTO films were investigated using metal-ferroelectric-metal (MFM) and interdigital co-planar capacitors. Conductive oxide layers, SrRuO₃(SRO) and La_0.5Sr_0.5CoO₃ (LSCO), were grown on Si and SOI substrates as bottom electrodes. For MFM capacitors based on Au/BTO/SRO/Si and Au/BTO/LSCO/SOI layer structures, a little asymmetric capacitance-voltage curves were obtained with about 36% capacitance tunability. The remanent polarizations were about 21 μC/cm² and the coercive fields were about 71 kV/cm. For an interdigital capacitor based on Au/BTO/MgO layer structure, a little lossy capacitance-voltage curve was obtained with about 64% capacitance tunability.     

The effects of the LaNiO3 interlayer in the preferential orientation and the dielectrical properties of Ba x Sr1− x TiO3 thin films

Ba _x Sr_1?x TiO₃ (BST) thin films were grown on different substrates with or without LaNiO₃ (LNO) layer by a modified sol–gel process. The BST thin films obtained have full perovskite phase with dense and crack-free surface. BST thin films on different substrates with LNO layer show (100) preferential orientation, the texture coefficient (TC) value is calculated to be about 42.7%, whereas those without LNO layer show a fairly reduced preferential orientation, the TC value is just about 24.8%. It is considered that the preferential orientation is induced by the interface stress between LNO and BST. Electrical property measurements showed that BST thin film with a LNO interlayer has lower capacitance and larger dielectric loss, which is due to smaller grains of the thin film.     

Characterization of Ni/Ce Co-Doped BST Thin Film Grown on LSCO/Pt Electrodes Prepared by Pulsed Laser Deposition

Perovskite (Ba_0.6Sr_0.4)TiO₃ (BST) thin films doped with Ni, Ce and Ni/Ce codopants were prepared on LSCO/Pt/SiO₂/Si substrates by pulsed laser deposition method. In this study, La_0.5Sr_0.5CoO₃ (LSCO) bottom electrodes were used to improve the crystallinity and dielectric properties of BST films. Single ion doped(1 mol%Ni doped,1 mol%Ce doped) BST films showed more improved crystallinity, smoother surface, and smaller grain size than that with 1 mol%Ni/1 mol%Ce. The dielectric constant and loss of Ni/Ce co-doped BST films were about 298 and 1.8%, respectively. In addition, tunability and figure of merit of co-doped BST films showed minimum values of approximately 9.3% and 5, respectively. With 1% Ni-doped BST thin films, results gave a tunability of 54.2% and a loss tangent of 1.8% while a figure of merit was 30. Correlation of the material properties with dielectric and tunable properties suggests the 1 mol%Ni-doped BST films are effective potential candidate for tunable device applications.     

Preparation of BST thin films on Pt electrode on Si wafer with down-flow LSMCVD reactor

Abstract

A novel type of down-flow LSMCVD (Liquid Source Mist CVD) reactor was developed to prepare a high dielectric BST thin film on Pt electrode on Si wafer. Barium acetate [Ba (OOCCH₃)₂], strontium acetate [Sr (OOCCH₃)₂], and titanium isoproxide [Ti (OC₃H₇ ⁱ )₄] were used as metal sources. Metal sources were dissolved in acetic acid, 1-butanol, or 2-methoxyethanol. BST [Ba/(Ba + Sr) = 0.7] film annealed on Pt/Ti/SiO₂/Si above 650°C was polycrystalline. BST film has a (110) preferred orientation with increasing temperature. Surface roughness of BST film and grain size increased with increasing temperature. The metal-oxygen bond was formed at 650°C as shown in the spectra of FTIR. The depth profiles of elements of BST thin films indicated a uniform composition throughout the film. BST films annealed at 750°C showed a dielectric constant and a tanδ of 390 (thickness: 150 nm) and 0.06 at a frequency of 100 kHz, respectively. The behavior of capacitance of the BST film with bias voltage showed paraelectric property. BST film annealed at 750°C had the leakage current density of 3.2 (μA/cm²) at a bias voltage of 2V.     

Structure and dielectric properties of Ca-doped (Ba0.7Sr0.3) TiO3 thin films fabricated by sol–gel method

A wide range of Ca-doped (Ba_0.7Sr_0.3)TiO₃ (BST) thin films (from 0 to 20 mol%) have been prepared on Pt/Ti/SiO₂/Si (100) substrates by sol–gel technique. The structural and dielectric properties of BST thin films were investigated as a function of Ca dopant concentration. The results showed that the microstructure and dielectric properties of the BST films were strongly dependent on the Ca contents. With the Ca dopant concentration increasing, the grain size, dielectric constant and dielectric loss of the BST thin films decreased. As the content of Ca dopant reaches 10 mol%, the dielectric constant, dielectric loss, tunability, the value of FOM and the leakage current density are 281, 0.0136, 16.7%, 12.3 and 5.5?×?10^?6 A/cm², respectively.     

DESIGN,FABRICATION AND MATERIAL PROPERTIES OF TEMPERATURE STABLE PERFORMANCE CONSISTENT TUNABLE DEVICES

ABSTRACT

The premier candidate active material for tunable microwave phase shifter devices is single composition, paraelectric BaSrTiO₃ (BST). However, there is concern that in practical applications the device performance will be compromised due to the temperature dependence of the BST based device capacitance. We report a device design which controls the magnitude and the sign of the temperature coefficient of capacitance (TCC) via a multilayer paraelectric BST/buffer layer/ferroelectric BST coplanar device structure. To realize this multilayer device structure we have designed, fabricated, and optimized a 10 mol% Al doped Ta₂O₅ barrier layer with low loss (tan δ = 0.004), moderate permittivity (?_r = 42.8), low TCC (?20 ppm/°C), and a low bias stability of capacitance (0.4%). The thin film integration of the barrier layer with the BST layers was optimized for structure, microstructure, interfacial/surface morphology, and dielectric properties as a function of Al doping concentration, annealing temperature, material growth and integration process parameters.     

Liquid source chemical vapor deposition of high-dielectric-constant (Ba,Sr)TiO3 films

High-dielectric-constant (Ba, Sr)TiO₃ [BST] films were deposited by the liquid source chemical vapor deposition (CVD) method. The system consisted of a single-wafer, low-pressure thermal CVD reactor, a vaporizer for liquid source materials, and a shower-type gas nozzle head, giving stable BST film deposition on a 6-in. diam. substrate with uniform thickness and uniform chemical composition ratio. The source materials employed were Ba(DPM)₂, Sr(DPM)₂, and TiO(DPM)₂ dissolved in tetrahydrofuran (THF), resulting in conformal step coverage of BST films at lowered substrate temperatures, where DPM denotes dipivaloylmethanate. Moreover, the two-step deposition technique was developed to restart protrusions formed on BST film surfaces at low temperatures, where the BST films consisted of a buffer layer and a main layer; the buffer layer was a layer about 60 Å thick of CVD-BST film annealed in N₂. Thus, the two-step CVD deposition of BST films on Pt and Ru electrodes achieved an equivalent SiO₂ thickness of t_eq ∼ 0.5 nm, a leakage current of J_L ∼ 1.0 × 10⁻⁸ A/cm² (at +1.1 V), and a dielectric loss of tan δ ∼ 0.01 at a total film thickness of 250 Å, along with conformal coverage of 80% for a trench with an aspect ratio of 0.65. Then, for BST films deposited on patterned electrodes 0.24 μm wide, 0.60 μm deep, and 0.15 μm high (each spaced by 0.14 μm), the capacitance was demonstrated to be increased without significant deterioration of the leakage current: the capacitance was increased in comparison with that for films on flat electrodes, by a factor corresponding to the increase in surface area due to sidewalls of storage-node-like pattern features. This capacitance increase reflects the most characteristic advantage of CVD, an excellent step coverage on microscopic pattern features. These electrical properties satisfy the specifications for capacitors for Gb-scale dynamic random access memories (DRAMs), giving a storage capacitance of more than 25 fF/cell for a stacked capacitor having a storage node 0.2 to 0.3 μm high. © 1998 Scripta Technica, Electr Eng Jpn, 125(1): 47–54, 1998     

STRESS CONTROLLED FERROELECTRIC (BA0.5Sr0.5)TiO3 THIN FILMS PREPARED ON GD2O3/SRTiO3(001) BY A PULSED LASER DEPOSITION

ABSTRACT

Stress controlled epitaxial ferroelectric Ba_0.5Sr_0.5TiO₃ (BST) films have been deposited on Gd₂O₃/SrTiO₃ by pulsed laser deposition with oxygen background pressure of 200 mTorr at the deposition temperature of 750°C. In order to control the stress in BST films, oxygen pressures for Gd₂O₃ buffer layers have been varied from 0.1 to 100 mTorr, while that of BST films have been fixed at 200 mTorr. It has been found that the lattice parameters of the BST films deposited on Gd₂O₃ were changed. Furthermore, microwave properties of co-planar waveguide (CPW) fabricated on BST films were investigated by a HP 8510C vector network analyzer from 1–20 GHz. Large dielectric tunabilities were observed from the CPW's fabricated on BST films deposited on Gd₂O₃ layers deposited at low and high oxygen pressures, 0.1 and 100 mTorr, respectively.     

The Effect of Stress on the Microwave Dielectric Properties of Ba0.5Sr0.5TiO3 Thin Films

Single phase, (1 0 0) epitaxial Ba_0.5Sr_0.5TiO₃ (BST) films have been deposited onto (1 0 0) LaAlO₃ and MgO substrates by pulsed laser deposition (PLD). The capacitance and dielectric losses of as-deposited and annealed films have been measured from 1–20 GHz as a function of electric field (0–80 kV/cm) at room temperature. The dielectric properties are strongly affected by the substrate type, post-deposition annealing time (6 h) and temperature (1200°C). For epitaxial BST films deposited onto MgO, it is observed that, after a post-deposition anneal the dielectric constant and the dielectric loss decreases. For epitaxial BST films deposited onto LAO, a post-deposition anneal (1000°C) results in an increase in the dielectric constant and an increase in the dielectric loss. The dc electric field induced change in the dielectric constant tends to increase with the dielectric constant and is largest for as-deposited films on MgO and post-deposited annealed films on LAO. In general, for epitaxial BST films, a large electric field effect is observed in films that have a large dielectric loss and a small electric field effect in films that have a low dielectric loss. High resolution X-ray diffraction measurements indicate that deposited film exhibit a significant tetragonal distortion which is strongly affected by a by a post deposition anneal. The observed differences in dielectric properties of the epitaxial BST films on MgO and LAO are attributed to the differences in film stress which arise as a consequence of the lattice mismatch between the film and the substrate and the differences in the thermal coefficient of expansion between the film and the substrate. A thin amorphous buffer layer of BST has been used to relieve stress induced by the lattice mismatch between the film and the substrate. Unlike epitaxial films, stress relieved films do not show an inverse relationship between dielectric tuning and Q (1/tan) and may be superior materials for tunable microwave devices.     

Iridium thin film as a bottom electrode for high dielectric (Ba,Sr)TiO3 capacitors

Abstract

We propose Ir thin films as new electrode materials for high dielectric BST capacitors. Ir was found to be superior to Pt in a number of aspects such as resistivity, adhesion and surface roughness. The Pt/BST/Ir/SiO₂/Si capacitors showed leakage currents as low as Pt/BST/Pt/SiO₂/Si ones, but higher capacitance resulted. For endurance properties with +5V unipolar pulse trains, the dielectric constant of BST films on Ir decreased by only 10% below its initial value after switching of 10⁹ cycles while that on Pt degraded by 30% after 10⁸ cycles. Ir bottom electrode effects on BST film properties were well explained by the formation of IrO₂ phases on the surface of Ir electrodes.     

Calculation of the intrinsic dead layers thicknesses from Au/Ba0.5Sr0.5TiO3/Pt thin film capacitors

Ferroelectric Ba_0.5Sr_0.5TiO₃ (BST) films were prepared on Pt/Ti/SiO₂/Si substrates by the sol-gel process. The films were spin-coated at 2000 rpm for 30 secs and then pyrolysed for 5 mins at the temperature of 350^∘C. This coating procedure was repeated for 3, 4, 5 and 6 times to obtain BST films with different thicknesses. After coating the films with the desired repetition times, the films were finally annealed in a conventional furnace at temperatures ranging from 600^∘C to 800^∘C with a 50^∘C interval in between. The films obtained with an annealing procedure of 750^∘C were polycrystalline with the presence of an impurity BaCO₃ phase. The capacitance and leakage current were measured and used to extract information on the metal-BST interface. With the series capacitance model and modified Schottky emission equation, the thickness of the dead layers for Au/BST and Pt/BST interfaces were calculated to be less than 6 nm and 5 nm, respectively.     

Microwave Tunable Properties of Ni-Doped (Ba0.5Sr0.5)TiO3 Thin Films Grown by Pulsed Laser Deposition

(Ba_0.5Sr_0.5)TiO₃ (BST) thin films were deposited by pulsed laser deposition (PLD) and investigated as a function of Ni dopant concentration in low and high frequency regions. In low frequency region (<10 MHz), the Ni-dopant concentration in BST films has a strong influence on the material properties including dielectric and tunable properties. Ni-doped (≤3 mol%) BST films showed denser, smoother morphologies and smaller grain sizes than those with 6 and 12 mol% Ni. Dielectric constant and loss of 3 mol% Ni-doped BST films were about 980 and 0.3%, respectively. In addition, tunability and figure of merit of 3 mol% doped BST films showed maximum values of approximately 39% and 108, respectively. In high frequency region (>1 GHz), the frequency tunability range at center frequency of undoped BST and 3 mol% Ni-doped BST coplanar waveguide (CPW) resonators showed 102 and 152 MHz, respectively at 30 V dc bias. The Ni-doped BST thin films are possible in applications of microwave tunable capacitors.     

Magnetron sputter-deposited multilayer (BaxSr1x)Ti1+yO3+z thin films for passive and active devices

Abstract

High permittivity (Ba_xSr_1?x)Ti_1+yO_3+z(BST) thin films are being investigated for integration into charge storage dielectrics and electric-field tunable elements for high frequency devices. For the latter application, it is desirable to have BST capacitors with high tunability and low losses. Therefore, we investigated the use of multilayer BST thin films consisting of very low dielectric loss BST/electrode interfacial layers ((Ba+Sr)/Ti = 0.73) sandwiching a high tunability, high permittivity primary BST layer ((Ba+Sr)/Ti = 0.9). BST capacitors with multiple layers of controlled composition can be effectively produced insitu by magnetron sputter deposition, using a single stoichiometric target and controlling the layer composition by changing the total process gas (Ar+O<₂) pressure. The layered BST film capacitors exhibit simultaneous low loss (tan Δ = 0.005), high tunability (76%), high charge storage energy density (34 J/cm³), low leakage, and high dielectric breakdown (>2.8 MV/cm).     

Planar and Parallel Dielectric Properties of Compositionally Graded (Ba,Sr)TiO3 Thin Films for Tunable Microwave Applications

Compositionally graded (Ba_x,Sr_{1 ? x})TiO₃ [BST] ferroelectric thin films have been received much attention in graded ferroelectric devices due to their unique properties, such as large pyroelectric coefficients, large polarization offset and small temperature coefficient of dielectric constant for microwave tunable devices. Compositionally graded BST thin films were deposited epitaxially on LaAlO₃ [LAO] and Nb-doped SrTiO₃ [STO:Nb] substrates by pulsed laser deposition. The planar and parallel dielectric properties of compositionally graded BST epitaxial thin films ware investigated in the frequency ranges of 100 Hz ～ 1 MHz as a function of the direction of the composition gradient with respect to the substrate at room temperature. The dielectric properties of the graded BST films depended strongly on the direction of the composition gradient with respect to the substrate. The graded ST → BT films grown on LAO and STO:Nb substrates exhibited a excellent dielectric properties than the graded BT → ST films.     

CHARACTERIZATIONS OF W-DOPED (Ba0.5Sr0.5)TiO3 THIN FILMS USING LaNiO3 ELECTRODE

ABSTRACT

The (Ba_0.5Sr_0.5)TiO₃ thin films were deposited onto LaNiO₃ by RF-magnetron sputtering at 550°C. The influence of W content on microstructure and electrical properties of BST films were investigated. The surface and grain size become smoother and smaller as the W content increased. Besides, the dielectric constant, tunability, dissipation factor, and leakage current decreased when the W content increased. The 1% W is the optimal doping concentration. The resultant BST film, with proper dielectric constant and leakage current, has a tunability of 32%, a dissipation factor of 0.006, a FOM value of 53.3 under applied field of 450 kV/cm.     

Influence of Y and Mn alternately doped order on the microstructures and dielectric properties of Ba0.6Sr0.4TiO3 films

ABSTRACT

The influences of Y and Mn alternately doped order on the microstructures and dielectric properties of the Ba_0.6Sr_0.4TiO₃ (BST) films were reported in this paper. The Y and Mn alternately doped BST films were designed as YBST/MnBST/… and MnBST/YBST…multilayer films orderly expressed as (Y/Mn)_M and (Mn/Y)_M for short, and prepared on Pt/Ti/SiO₂/Si wafers by an improved sol-gel method, where Y and Mn represent yttrium doped BST layer and manganese doped BST layer, and M is cycle unit, respectively. The microstructures of the alternately doped BST films were observed by SEM and the capacitance-voltage curves at 100 kHz or 1 MHz were measured by a HP4284A LCR meter and the dielectric properties in the range of 1GHz were measured by an E4991A impedance analyzer. Compared to Y or Mn doped multilayer BST film, (Y/Mn)_M and (Mn/Y)_M show higher dielectric tunability and lower dielectric loss with higher dielectric constant. Moreover, (Y/Mn)_M show better dielectric properties than (Mn/Y)_M because (Y/Mn)_M show granular microstructures independent of M, while the (Mn/Y)_M show granular microstructures when M is 2 and add to a surface layer of columnar microstructures on the granular microstructures when M is 4. The related mechanisms were obtained in terms of the XRD phase structures, the cross-sectional SEM microstructures and the AFM morphologies.