退火变脆Fe75Si10B15金属玻璃的脆韧性转变

研究了机械研磨对退火变脆Fe_(75)Si_(10)B_(15)金属玻璃的弛豫过程,晶化行为及脆韧性转变的影响。发现退火变脆的Fe_(75)Si_(10)B_(15)金属玻璃,经不同时间机械研磨,Curie温度T_C逐渐回落,总的弛像焓ΔH_?逐渐回升。在DSC曲线上观察到明显的玻璃转变温度T_(g_1)和一个附加的宽放热峰T_(x_1),随着研磨时间的增加,T_(x_1),T_(x_1),T_C同步降低,与T_(x_1)对应的放热面积ΔH_(x_1)逐渐增大,并在片状粒子表面形成切变带以及与其对应的剪切带,玻璃在退火过程中失掉的韧性逐渐得到恢复。     

Metastable magnetic behavior in La_(0.9)Tb_(0.1)MnO_3

The linear and nonlinear magnetizations of La_(0.9)Tb_(0.1)MnO_3 at low temperatures were reported in detail.The temperature dependence of magnetization shows peaks at 50,100 and 150 K,respectively.When LaMnO_3 is Tb-doped,its magnetic structure exhibits a canted antiparallel spin order.This is different from classical antiferromagnetic(AFM) in which the relaxation behavior takes place at about 150 K.At 50 K,Tb-doped LaMnO_3 exhibits canonical spin glass behavior,arising from the competition of exchange and super-exchange between spins.The peak at 100 K shows neither spin glass behavior nor canted AFM behavior.Its peak value increases with frequency increasing,and the transition temperature of the peak shifts to higher temperatures with frequency increasing.The study of aging behavior at 100 K shows a periodical variable metastability,which is ascribed to the competition between ferromagnetic(FM)-,AFM-and sinusoidal-order interactions.This work should shed a light on understanding the complex magnetic structure of the nerovskite oxides.     

结构弛豫对Zr_(64.13)Cu_(15.75)Ni_(10.12)Al_(10)块体非晶合金硬度和剪切带特征的影响

通过接近玻璃转变温度的等温退火获得不同弛豫状态的Zr64.13Cu15.75Ni10.12Al10块体非晶合金样品。利用维氏显微硬度计和洛氏硬度计研究结构弛豫对合金硬度和压痕周围剪切带特征的影响规律。结果表明:在590K等温退火处理使Zr64.13Cu15.75Ni10.12Al10块体非晶合金发生焓弛豫行为,其维氏显微硬度随退火时间的延长较快增加后趋于稳定,而大载荷洛氏硬度对结构弛豫不敏感。通过洛氏压痕周围剪切带特征的研究,定量比较了结构弛豫对剪切带间距、数量的影响规律。     

预退火时间与Fe68Ni1Al5Ga2P9.65B4.6Si3C6.75玻璃转变热力学参数的关系

采用DSC、XRD 检测方法,分析了经673 K((Tg-100 K)＜T＜Tg)不同时间(20,40,60 min)预退火处理后,Fe68Ni1Al5GazP9.65B4.6Si3C6.75非晶合金的玻璃转变温度Tg、起始晶化温度Tx、晶化峰温度Tp、玻璃转变过程中的比热容增量△Cp,g的变化以及经823 K晶化反应后的XRD图谱.结果表明:Fe68Ni1Al5Ga2P9.65B4.6Si3C6.75非晶合金的玻璃转变温度Tg和比热容增量△Cp,g随预退火时间的延长而逐步增加;起始晶化温度Tx和第一晶化峰温度Tp1随预退火时间呈现出逐渐减小的趋势;其晶化后样品衍射峰形貌相似,衍射峰的强度略有不同.利用结构弛豫理论对实验结果进行了分析.     

Mechanical relaxations of a (Zr77.5Ti22.5)55(Ni48Cu52)21.25Be23.75 amorphous alloy studied using dynamic mechanical analysis

The dynamic mechanical properties of a (Zr_77.5Ti_22.5)₅₅(Ni₄₈Cu₅₂)_21.25Be_23.75 amorphous alloy were investigated by frequency-dependent elastic moduli and isothermal multi-frequency measurements. The frequency-dependent loss modulus showed a relaxation behavior resulting from a glass transition, and the variation of the peak frequency was related to the Arrhenius equation. Isothermal multi-frequency measurement data were used to construct the master curves of the elastic moduli and tan δ by applying the time-temperature superposition principle. The temperature dependence of the shift factor was found to follow the Arrhenius relationship, and the activation energies for the low temperature relaxation and glass transition were approximately 156.6kJ/mol and 554kJ/mol, respectively. The glass transition temperature (T _g) was manifested by the crossover region of the shift factor dependence, and from the relationship between the shift factors and the temperature aboveT _g), the fragility index of this alloy was estimated.     

预退火时间对Pd40Cu30Ni10P20玻璃转变及晶化的影响

采用示差扫描量热(DSC)分析方法,测定了大块非晶合金Pd40Cu30Ni10P20经523 K((Tg-100 K)＜7＜Tg)不同时间(0～64 h)预退火后的玻璃转变温度7g、玻璃转变峰温度TM、起始晶化温度Tx、晶化峰的峰温Tp、晶化焓以及在玻璃转变过程中的比热容增量,并根据Kissinger公式计算了晶化的表观活化能.同时,测量了不同时间预退火后样品的显微硬度.结果表明:在玻璃转变温度以下的预退火处理使Pd40Cu30Ni10P20大块非晶合金的微观原子组态发生变化,从而影响了其随后的玻璃转变行为,但对晶化的影响不大.其显微硬度随预退火时间的延长而逐步增加后趋于稳定.并利用结构弛豫理论分析了预退火对玻璃转变、晶化和显微硬度的影响.     

HEAT CAPACITIES OF Fe_（40）Ni_（40）B_（20） GLASSY ALLOY MEASURED BY ENTHALPY METHOD

ＨＥＡＴＣＡＰＡＣＩＴＩＥＳＯＦＦｅ_（４０）Ｎｉ_（４０）Ｂ_（２０）ＧＬＡＳＳＹＡＬＬＯＹＭＥＡＳＵＲＥＤＢＹＥＮＴＨＡＬＰＹＭＥＴＨＯＤ￥ＪＩＡＮＧＱｉｎｇ;ＺＨＡＯＭｉｎｇ;ＬＩＪｉａｎｃｈｅｎ（ＪｉｌｉｎＵｎｉｖｅｒｓｉｔｙｏｆＴｅｃｈｎｏｌ?..     

Zr_(47)Cu_(44)Al_9大块非晶合金的变温晶化行为

利用示差扫描量热仪(DSC)研究了Zr_(47) Cu_(44)Al_9大块非晶合金在连续升温过程中的的变温晶化行为.利用Kissinger方法计算其特征温度表观激活能,利用Doyle方法计算其局域激活能.结果表明,Zr_(47) Cu_(44)Al_9大块非晶合金具有良好的热稳定性.利用Kissinger方法计算得到的其玻璃转变激活能E_g为390.2kJ/mol、晶化激活能E_x为325.1kJ/mol、晶化峰值的激活能E_p为299.5kJ/mol.随着加热速率的提高,各特征温度值向高温端移动,其晶化峰值温度所对应的晶化体积分数减小.局域激活能随着非晶晶化体积分数的增加而逐渐减小.     

DISACCOMMODATION OF INITIAL SUSCEPTIBILITY IN AMORPHOUS Fe_(90-x)Ni_xZr_(10) ALLOYS

The disaccommodation(DA)measurements of initial susceptibility were performed inamorphous Fe_(90-x)Ni_xZr_(10)(x=10,20,30)alloys.The DA was measured for two differentamorphous states:as-quenched and pretreated at 537 K for 45 min.For all the as-quenched samples,in the isochronal spectra of DA a well defined relaxation peak around350 K is accompanied by a samll but distinct peak near the Curie temperature ofFe_(90)Zr_(10) phase(T_c=230 K).The reversibility and annealing effect on DA are analyzedwithin the framework of two-level model.The fits of the theory to the experimentaldata of reversible relaxation processes gave a spectrum,of activation energies and pre-exponential factor.     

Study of relaxations in epoxy polymer by thermally stimulated depolarization current (TSDC) and dielectric relaxation spectroscopy (DRS)

Thermally stimulated depolarization current (TSDC) and dielectric relaxation spectroscopy (DRS) techniques were employed to study the relaxations and the conductivity phenomena in epoxy-based polymer. In addition to the primary α relaxation process associated with the glass–rubber transition, significant interfacial relaxation and ionic conduction process have been revealed. The ac conductivity is temperature and frequency dependent and shows a dc plateau at low frequencies. Above the glass transition temperature, dc conductivity is described by a Vogel–Tamman–Fulcher–Hesse (VFTH) equation while it shows Arrhenius behaviour at higher temperatures.     

稀土材料La—Ba—（Mn,Fe）—O的磁电输运特性探讨

研究制备了Ｌａ０．６７Ｂａ０．３３Ｍｎ１－ｘＦｅｘＯ３（ｘ＝０,０．０５,０．１）材料。结果表明：铁替换锰降低了材料的饱和磁化强度及居里温度,主要是因为Ｆｅ离子不参加双交换作用,同时Ｍｎ＾３＋－Ｏ＾３－Ｍｎ＾４＋的作用对随铁离子替代Ｍｎ＾３＋而数量减少,材料的铁磁作用随之减弱。铁替换降低了金属－半导体转换峰温度,相应提高了材料的零场电阻值。值得注意的是铁掺杂提高了大磁阻材料Ｌａ０．６７Ｂａ０．３３Ｍｎ１－ｘＦｅｘＯ３的低温性能,５Ｋ下磁阻比「Ｒ（６Ｔ）－Ｒ（０）」Ｒ（０）从ｘ＝０时的－４０％增加到ｘ＝０．１时的－６０％。本文同时利用迪尼模型对材料大磁阻效应进行了计算分析,发现理论计算曲线可以较好的反映实验上出现的金属－半导体转换峰现象,同时负的大磁阻效应现象也可从理论计算上得到证实。     

Effect of cold rolling on glass transition of Zr_(55)Al_(10)Ni_5Cu_(30) bulk metallic glass

Zr55Al10Ni5Cu30 bulk metallic glass was prepared through water-cooled copper mold suction casting, and was rolled up to 95% in thickness reduction. The structures and thermal stabilities of the as-cast and as-rolled specimens were examined by X-ray diffractometer and differential scanning calorimeter. As the thickness reduction increases, the crystallization onset temperature, peak temperature and the apparent activation energy of crystallization almost keep constant, while the glass transition temperature decreases from 681 to 671 K and the apparent activation energy of glass transition increases from (404±26) to (471±29) kJ/mol. The glass transition process is markedly affected by the rolling induced changes of microstructure and structural relaxation.     

Mg61Cu28Gd11和(Mg0.61Cu0.28Gd0.11)99.5Sb0.5非晶合金的晶化动力学和腐蚀行为（英文）

研究0.5%(摩尔分数)Sb的引入对Mg61Cu28Gd11块体非晶合金性能的影响。利用差热扫描量热仪测试样品的晶化动力学。结果表明:在等时加热的过程中,非晶合金的玻璃转变温度、起始晶化和峰值晶化温度都表现出对加热速率强的依赖性。基于Oawza方法可以确定非晶合金的起始晶化和峰值晶化激活能。Vogel-Fulcher-Tamman公式分析表明:含Sb元素的非晶合金具有更高的强度系数和更长的延迟时间。采用电化学极化和失重测试方法研究2种玻璃合金的腐蚀行为。与基体非晶合金相比,添加微量Sb降低了非晶合金的在含Cl-的碱性溶液中的钝化电流密度和腐蚀速率,表现出相比基体合金更为优越的耐蚀性。最后基于"点缺陷模型"进一步分析微量Sb元素对基体合金耐蚀性能的影响机理。     

Mechanical Relaxation of a Ti_(36.2)Zr_(30.3)Cu_(8.3)Fe_4Be_(21.2) Bulk Metallic Glass: Experiments and Theoretical Analysis

The dynamic mechanical relaxation behavior of Ti_(36.2)Zr_(30.3)Cu_(8.3)Fe_4Be_(21.2) bulk metallic glass with good glass-forming ability was investigated by mechanical spectroscopy. The mechanical relaxation behavior was analyzed in the framework of quasi-point defects model. The experimental results demonstrate that the atomic mobility of the metallic glass is closely associated with the correlation factor χ. The physical aging below the glass transition temperature T g shows a non-Debye relaxation behavior, which could be well described by stretched Kohlrausch exponential equation. The Kohlrausch exponent β_(aging) reflects the dynamic heterogeneities of the metallic glass. Both concentration of "defects" and atomic mobility decrease caused by the in situ successive heating during the mechanical spectroscopy experiments.     

压力对La-Al-(Cu,Ni)金属玻璃结构驰豫的影响

采用铜模吸铸法制备出La62.0Al15.7(Cu0.5Ni0.5)22.3大块金属玻璃,经高压处理后,用X射线衍射仪(XRD)和示差扫描量热计(DSC)对非晶的结构驰豫和晶化过程进行了研究.结果表明,非晶玻璃转变温度和第一晶化温度随着压力的增加,其先增加后减小,极大值出现在4.0 GPa的压力.这种现象归因于经过高压处理后玻璃转变温度区焓的变化,而焓的变化由基体缺陷激活体积引起自由体积变化所导致.此外,高压处理还影响玻璃的结晶过程.     

Structure relaxation and crystallization of Al83Ni10Ce7 metallic glass

Structure relaxation and crystallization of Al₈₃Ni₁₀Ce₇ metallic glass were studied by different scanning calorimetry (DSC) and X-ray diffraction (XRD). According to the DSC scan, it is interesting to find that the second exothermic peak changes with pre-annealing temperatures (below glass transition temperature), suggesting a change in the amorphous structure upon relaxation. Continuous heating crystallization and isothermal crystallization exhibit different crystallization mechanism of the present alloy. fcc-Al and a metastable phase precipitate simultaneously in the first stage crystallization during continuous heating; however, only a metastable phase precipitates during isothermal annealing below glass transition temperature (T_g).     

Fe55Ni2Cr12Mo10Y2B6C13块体非晶合金的热膨胀行为

本文采用铜模吸铸法制备直径为4mm的块体非晶合金Fe55 Ni2 Cr12 M010 Yo12 B6 C13,对非晶合金在298K-1073K温度区间的热膨胀行为进行了分析.非晶合金的膨胀系数在室温至接近玻璃转化温度区间没有发生明显的变化;当温度超过Tg后,由玻璃态进人过冷液相区,粘度急剧增加,膨胀系数增高;在T>Tg...     

Effect of melt cooling rate on glass transition kinetics and structural relaxation of Vit1 metallic glass

The thin ribbons and the bulk cylindrical rods with diameters of 2 mm and 10 mm of the Vit1 metallic glass (MG) were prepared by the single roller melt spinning method and the copper mold injection casting method, respectively. The cooling rates of the samples during melt solidification were evaluated. The glass transition behaviors of three groups of MG samples with different solidification cooling rates were studied by differential scanning calorimetry (DSC) at different heating rates. The effects of melt cooling rate on the glass transition kinetic parameters such as apparent activation energy (E) and fragility parameter (m) of the Vit1 MG were studied using the Kissinger and the Vogel-Fulcher-Tammann (VFT) equations. Additionally, the structural relaxation enthalpy (ΔH_rel) of three groups of MG samples was quantitatively analyzed by DSC through multi-step temperature rise and fall measurements. Results show that the melt cooling rate (R) has a significant effect on the glass transition kinetics and the structural relaxation of the Vit1 MG. As R decreases in the order of magnitude, the glass transition temperature (T_g), E, m, and ΔH_rel of the Vit1 MG gradually decreases. Furthermore, in the range of the experimental cooling rates, E, m, and ΔH_rel all have an approximately linear relationship with lgR.

     

Influence of Sb addition on Martensitic and Magnetic Transformation in β+γ Two-phase Based Co-Ni-Al Shape Memory Alloy

利用OM，SEM，EDX，XRD，DSC和VSM研究了用Sb替代Al对Co41Ni32Al27合金马氏体相变和磁性的影响．结果表明Co41Ni32Al26Sb1合金仍然生成L10型马氏体，其马氏体相变温度和Curie点与淬火温度成正比关系，淬火温度每升高10K，马氏体相变温度约提高9K，而Curie点约提高7．5K．相同淬火温度下Co41Ni32Al26Sb1合金的马氏体相变温度比Co41Ni32Al27合金约高70K，而Curie点也高出15K．Co41Ni32Al26Sb1在1623K热处理时出现共晶组织，发生部分熔化现象．特别重要的是C041Ni32A12eSbl合金的马氏体相变温度范围大幅度缩小，为20-28K，只有Co41Ni32Al27合金的一半，有利于获得大磁致应变．用平均s＋d总电子浓度和平均磁价电子数分别解释了马氏体相变温度和Curie点的变化．     

结构驰豫对Cu58.1Zr35.9AI6块状非晶合金弹性性能的影响

本文系统地研究了结构驰豫对Cu58.1Zr35.9AI6块状非晶合金弹性性能的影响.将Cu58.1Zr35.9AI6非晶合金在150℃、300℃、450℃分别保温1 h.测量退火样品的纵、横波声速,并推算其弹性性能.结果表明:随退火温度的升高,声速与弹性性能呈现逐渐增加的趋势.低温驰豫时声速与弹性性能变化缓慢,高温驰豫时增加明显.基于结构驰豫谱模型分析了上述现象的产生在于:提高温度,原子有足够的条件进行中程与长程扩散,通过发生原子的积聚重排,大量自由体积的湮灭,使非晶样品的有序度得到大大的改善.