目的 探究TA+TB钛合金组合的线性摩擦焊（LFW）接头组织及力学性能特点。方法 进行了TA19/TB2异质接头LFW焊接试验。利用光学显微镜及扫描电镜观察分析了接头微观组织特征,利用拉伸试验机及显微硬度计测试分析了接头力学性能。结果 TA19侧焊缝区为动态再结晶形成的等轴细晶组织,晶内析出了针状α''及细小片层α,热力影响区晶粒发生了不同程度的变形,在近焊缝较宽范围内形成水平流线形貌;接头中部界面TA19侧形成了直径约为2~3 μm的细小等轴晶;TB2侧焊缝区由动态再结晶形成的等轴晶及部分变形晶粒组成,热力影响区晶粒变形程度较低未形成流线形貌。接头界面两侧组织特征具有不同程度的强化效果,TA19侧从母材区到界面显微硬度值逐渐增大,TB2侧焊缝及热力影响区显微硬度值略高于母材;接头拉伸强度与TB2母材相当。结论 说明TA19与TB2钛合金可通过LFW获得可靠连接。     

Ti17合金电子束焊接接头的性能及组织分析

分析了Ti17合金真空电子柬焊接接头的显微组织结构及其显微硬度分布规律,并结合室温和高温拉伸试验结果分析了焊接接头的力学性能。结果表明,用电子束焊接方法焊接的Ti17合金其焊缝区和热影响区显微组织为β相基体上分布着细长针状α相,母材为典型的α＋β双相网篮组织,焊后焊缝晶粒细化,焊接接头的焊缝区硬度最高,焊缝的抗拉强度和缺口敏感性均高于母材。     

Mg-Y-Nd-Zr镁合金焊接接头的显微组织与力学性能研究

目的研究Mg-Y-Nd-Zr镁合金焊接接头显微组织和力学性能。方法采用钨极氩弧焊工艺制备Mg-Y-Nd-Zr合金焊接接头,采用金相显微镜、扫描电子显微镜观察焊接接头显微组织,采用能谱测试主要合金元素含量,采用电子万能实验机测试焊接接头的力学性能,采用维氏硬度计测试焊接接头的硬度。结果Mg-Y-Nd-Zr合金母材、焊缝区与热影响区平均晶粒尺寸分别为80, 30, 95μm。焊接接头的抗拉强度、屈服强度和断后伸长率分别为295 MPa, 188 MPa和3.0%。结论 Mg-Y-Nd-Zr合金母材、焊缝和热影响区晶粒均为等轴晶,与母材相比,热影响区未发生晶粒粗化,焊缝区晶粒明显细化,析出相Mg24Y5增多。Mg-Y-Nd-Zr合金焊接接头经525℃×12 h固溶+225℃×12 h时效处理后,各区域的硬度差异不大。抗拉强度达到母材的93%,断后伸长率达到母材的67%。     

焊后热处理对TC11钛合金线性摩擦焊接头组织与性能的影响

焊后热处理可以改善线性摩擦焊接头的组织与性能。对TC11钛合金线性摩擦焊接头进行双重退火(950+530)℃处理，利用光学显微镜、扫描电子显微镜等微观分析技术研究双重退火对焊接接头组织的影响。结果表明：热处理后接头焊缝区的动态再结晶晶粒完全消失，被粗针状、条状和球状α相取代。热力影响区组织变形程度减小，晶粒长大，部分α组织球化。母材中次生α相长大，呈粗针及短棒状。接头焊缝区及热力影响区的晶粒取向在热处理后更加随机，择优取向明显降低。力学性能测试表明，焊后双重退火处理消除接头中心高硬度区，接头中心硬度较焊态接头硬度下降约50HV,热力影响区硬度较焊态接头硬度上升约30HV;焊后热处理对接头拉伸强度没有显著影响；热处理后接头冲击韧性达到61.3 J·cm^-2,相比焊态提高约80%,与母材的冲击韧性接近。     

高强低合金钢电子束焊接接头的组织与性能研究

采用电子束焊接了厚度为9 mm的15CrNi3MoV高强低合金钢试板,焊接接头成形良好,无内部缺陷,经热处理后焊接系数达到0.98以上。通过研究焊接接头组织和力学性能,发现热处理后,接头组织以贝氏体组织为主,在焊缝和热影响区粗晶区中出现索氏体组织,热影响区的细晶区存在粒状贝氏体组织,焊接接头的冲击韧性与母材相比得到提升;散焦修饰使原始焊缝的柱状晶碎化,能够改善焊缝处的显微硬度。     

铝合金搅拌摩擦对接焊接头组织与性能研究

研究了5083铝合金搅拌摩擦焊(FSW)焊接接头组织与性能,采用金相显微镜观察焊接接头各区域的微观组织,并对接头显微硬度和力学性能进行了测定。结果表明,5083铝合金搅拌摩擦焊焊核组织为动态再结晶生成的细小组织,强化相均匀分布;热机影响区由于动态再结晶和焊接热循环的双重作用,组织变化较大,晶粒有一定程度的长大,强化相有所细化;热影响区仅仅受到热循环作用,使得晶粒粗化和强化相出现聚集现象。搅拌摩擦焊接接头中心硬度与母材基本相当,热机影响区和热影响区由于焊接热输入的原因,使得硬度有所降低。搅拌摩擦焊室温拉伸性能和冲击性能不低于母材的,其中拉伸试样均断裂于母材,焊核室温冲击值达到母材的1.5倍以上,热影响区冲击值与母材的相当。     

Ti-23Al-14Nb-3V合金氩弧焊接头的显微组织及其力学性能

研究了预热对Ｔｉ－２３Ａｌ－１４Ｎｂ－３Ｖ合金焊接性，特别是对消除氩弧焊冷裂纹的作用以及对接头显微组织和力学性能的影响。结果表明，焊前预热可有效降低该合金的冷裂倾向。经预热处理后，焊缝区的结晶层状线消失，热影响区的硬度峰得到缓和，整个焊缝的显微硬度分布趋于均匀，但焊缝区的枝晶发生粗化，热影响区有所扩大。焊件接头的拉伸试验表明，预热可使焊缝区的接头强度系数增加，但无论预热与否，接头强度均低于母材强度，且不显示宏观塑性。     

TA23合金不同焊接方法接头组织性能研究

采用CMT、TIG和EBW焊对TA23合金进行焊接,对比分析了不同焊接方法下接头微观组织和力学性能的差异。结果表明,焊接热输入直接影响焊缝晶粒尺寸和焊接接头宽度,TIG焊缝晶粒尺寸最大,CMT次之,EBW最小;EBW接头宽度为5 mm,CMT接头宽度为7 mm,TIG接头达14 mm;3种焊接方法焊缝区域组织均由马氏体α相、片层状α相和残余β相组成,热影响区组织形态介于焊缝和母材组织形态之间;3种焊接方法焊缝区显微硬度和接头抗拉强度均大于母材,其中EBW焊缝区显微硬度值最大,TIG焊接头抗拉强度最高,CMT焊缝显微硬度和接头抗拉强度均居中。     

30CrMnSiNi2A与Q235异种钢焊接接头组织与性能分析

目的探讨30CrMnSiNi2A与Q235异种钢焊接接头的组织与性能。方法采用手工电弧焊对两者进行焊接,为了获得性能良好的焊接接头,焊前对其进行焊前预热,焊后对其进行焊后退火。通过X射线探伤检测,拉伸、冲击试验,显微硬度检测及光学显微镜金相分析等一系列工艺试验,对焊接接头进行研究。结果焊缝质量等级达到Ⅰ级;焊缝组织为先共析铁素体、针状铁素体、珠光体组织;30CrMnSiNi2A侧热影响区组织为回火索氏体,粗晶区组织片层厚度大于细晶区组织片层厚度;Q235侧热影响区由不完全重结晶区、细晶区、粗晶区组成。结论 30CrMnSiNi2A与Q235钢焊接后,获得了工艺性、力学性能良好的接头,可运用于2种材料焊接的实际生产。     

搅拌摩擦焊对Mg-Gd-Y-Zr合金组织与性能的影响

对一种Mg-Gd-Y-Zr合金cast-T6状态板片试样搅拌摩擦焊接后的组织与性能进行了研究。结果表明:Mg-Gd-Y-Zr合金的搅拌摩擦焊的焊核区发生动态再结晶,为等轴细晶,硬度值最高;热机影响区基体组织具有热变形特征,第二相会粗化、溶解,硬度值稍低;热影响区晶粒尺寸与母材相当,第二相粗化,硬度值低于母材。在本工作实验条件下,cast-T6铸件试样的焊接系数达0.91,且伸长率相对于母材有大幅度提高。断口形貌SEM分析显示,接头断裂模式为韧性断裂。     

Insertion of triangulated surfaces into a meccano tetrahedral discretization by means of mesh refinement and optimization procedures

In this paper, we present a new method for inserting several triangulated surfaces into an existing tetrahedral mesh generated by the meccano method. The result is a conformal mesh where each inserted surface is approximated by a set of faces of the final tetrahedral mesh. First, the tetrahedral mesh is refined around the inserted surfaces to capture their geometric features. Second, each immersed surface is approximated by a set of faces from the tetrahedral mesh. Third, following a novel approach, the nodes of the approximated surfaces are mapped to the corresponding immersed surface. Fourth, we untangle and smooth the mesh by optimizing a regularized shape distortion measure for tetrahedral elements in which we move all the nodes of the mesh, restricting the movement of the edge and surface nodes along the corresponding entity they belong to. The refining process allows approximating the immersed surface for any initial meccano tetrahedral mesh. Moreover, the proposed projection method avoids computational expensive geometric projections. Finally, the applied simultaneous untangling and smoothing process delivers a high‐quality mesh and ensures that the immersed surfaces are interpolated. Several examples are presented to assess the properties of the proposed method.     

Certification Institutions Expected to Update and Transfer Information on Present Standards

Standards are the basis for production enterprises to organize production, ex-factory inspection, trade (delivery) and technical exchanges, product certification, quality arbitration and supervision.……     

From Industry 4.0 to Research 4.0. Development of High Performance Fibers in the Light of Digitization

We associate a variety of innovations with the term ＂Industry 4.0＂. The pioneer of many 4.0 modifications forms the basisfor the trend towards the integrated di...     

Flow calorimeter for enthalpy increment measurements on condensed gases

A flow calorimeter for enthalpy increment measurements on condensed gases is presented. A better knowledge of the properties of the liquefied natural gas is needed, and therefore a liquid loop has been designed for our flow calorimeter. The fluid loop in the calorimeter is designed in order to avoid the two-phase region, since two phases would give compositional disturbances in the measurements. The avoidance of the two-phase region is made possible by increasing the pressure of the test fluid after the measurement section, then heating the fluid at super-critical pressure past the critical point. Finally, the fluid is throttled to the low-pressure gas state at the inlet condition of the compressor that circulates the fluid. To perform the pressure increase, a new cryogenic pump has been designed. To evaluate the new equipment, measurements were taken on liquid ethane over the temperature range 146–256 K at pressure between 0.9 and 5.1 MPa.     

Refrigerators Enter a New Era of Health Preservation Frestech initiates the establishment of China's first standard for household sterilization refrigerators

On November 30, 2007, the China Association for Standardization (CAS) held a press conference at Beijing Diaoyutai State Guest House. Leaders from the China Household Electric Appliance Research Institute, the China Household Electric Appliance Association, and the China Consumers' Association attended and made speeches.……     

Optimum-Simulation von Ernteprozessen

Zusammenfassung Bei der Gestaltung von Ernteprozessen — beispielsweise des Prozesses Mähdrusch, Körnertransport und -abnahme — als transportverbundene Fließarbeitsverfahren mit mindestens zwei verschiedenen Arbeitsmitteln gibt es einen großen Optimierungsspielraum. Solche Prozesse sind mehrstufige Bedienungsprozesse mit gemischter Anordnung der Bedienungseinrichtungen. Außerdem besitzen sie stark ausgeprägte räumliche Aspekte. Es wird vor allem gezeigt, welche Merkmale solcher Prozesse in Simulationsmodellen abgebildet sein müssen, welche Zielgrößen in Abhängigkeit von welchen Einflußgrößen unter Berücksichtigung welcher Prozeßbedingungen ermittelt werden sollten und wie der Bewertungsprozeß zur Ermittlung der gewünschten Informationen gestaltet werden muß.     

Roman iron and steel: A review

ABSTRACT

The production of ferrous metal increased during the Roman Late Republican period, Principate and Empire. The direct bloomery process was used to extract the metal from its ores using slag-tapping and slag-pit furnaces. The fuel was charcoal and an air blast was introduced by bellows-operated tuyères. Iron formed as a bloom, often as a spongy mass of metal, which contained impurities from the smelting process, including unreacted ore, fuel, slag and fragments from the furnace walls, while the metal was often inhomogeneous with varied carbon contents. Blooms were either smithed directly into bars or ingots or they were broken up, which also allowed the removal of gross impurities and a selection of pieces with similar properties to be made. These could then be forge-welded together and formed into characteristically shaped ingots. Making steel in the furnace seems to have been achieved: it depended on the ore and the furnace and conditions within it. Surface carburization was also carried out. Iron and steel were used extensively in construction and for tools and weapons. Fire welding was often used to add pieces of steel to make the edges of tools and weapons, which could be heat-treated by quenching to harden them.     

A study of centrifugal cast high boron high speed steel

In the present study a high‐boron high speed steel (HSS) roll material was designed. Many expensive alloy elements have been substituted by cheap boron alloy, and high‐boron high speed steel roll has been manufactured by centrifugal casting method. The microstructures, mechanical properties and wear resistance of centrifugal casting high‐boron high speed steel roll have been investigated by optical microscopy (OM), scanning electron microscopy (SEM), and X‐ray diffraction (XRD) analysis, hardness test, impact test and wear test. The results indicated that the solidification microstructures of high‐boron high speed steel roll consisted of M₂(B,C), (W,Mo)₂(B,C), M₃(B,C), M₂₃(B,C)₆ type borocarbides and martensite, a small amount of retained austenite. Borocarbides were continuously distributed over the grain boundary. After quenching from 1050 °C, local broken network appeared in partial borocarbides, and fine secondary borocarbide precipitated from the matrix. After tempering from 525 °C, the amount of precipitated borocarbide increased significantly. After heat treatment, the hardness of high‐boron high speed steel roll excelled 60 HRC, and its impact toughness excelled 8.0 J/cm². The single groove steel rolling amount of high‐boron high speed steel rolls increases by 500% than that of bainite cast iron roll, when the rolls are used in K₁ mill housing of bar mill.     

Thixotropy of Systems with Shear Thinning and Plastic Flow Behavior

The definition of the thixotropy is a decrease in viscosity with time in shear and a subsequent recovery of viscosity after the shear deformation is removed.We ...