Prediction of threshold and ultra-low fatigue crack growth rates

A model was derived to predict the true threshold value for fatigue crack growth in the absence of crack closure. The model, based only on the tensile and cyclic properties of the material, was successfully verified against a set of experimental data on medium and high strength steels and one aluminium alloy. Good agreement with experimental results was also obtained for Region I of the $\text{d}\text{a/}\text{d}\text{N vs ΔK}$ curve using a fatigue crack growth rate equation based on the same model.Fatigue crack growth data obtained from the medium strength steel CK45 in the normalized state and two heat-treated conditions were analysed. Good data correlation was shown using a previously developed normalizing parameter, $\text{φ = (ΔK}{}^2\text{?ΔK}{}^2{}_{\mathrm{<mtext>th</mtext>}}\text{)/(K}{}^2{}_{\mathrm{<mtext>c</mtext>}}\text{?K}{}^2{}_{\mathrm{<mtext>max</mtext>}}\text{)}$, in the entire range of fatigue crack growth rates and for stress ratios ranging from 0.1 to 0.8.     

The influence of environment and stress ratio on fatigue crack growth at near threshold stress intensities in low-alloy steels

Fatigue crack propagation at low stress intensities has been studied in two low alloy steels in a variety of environments with particular emphasis being placed on the influence of stress ratio and strength level. It was found that fatigue crack growth rates are lower and threshold stress intensities ($\text{ΔK}{}_0$) are higher in vacuum than in humid, laboratory air but, in dry gaseous environments (argon, hydrogen and air) and at low stress ratio ($\text{R ~ 0.1}$), crack growth rates are faster and $\text{ΔK}{}_0$ values are lower than in laboratory air. However, the influence of stress ratio is considerably greater in laboratory air than in dry gaseous environments with the result that, at high stress ratio ($\text{R ~ 0.8}$) $\text{ΔK}{}_0$ values are similar in all environments examined. Increasing material strength level resulted in higher, near-threshold crack growth rates and a reduction in $\text{ΔK}{}_0$ in both dry and humid air environments. The results are discussed in terms of the influence of crack closure and environmental effects on fatigue crack growth behaviour. The importance of corrosion debris produced in fatigue cracks at low stress intensities is also discussed.     

A cumulative model of fatigue crack growth

A model of fatigue crack growth based on an analysis of elastic/plastic stress and strain at the crack tip is presented. It is shown that the fatigue crack growth rate can be calculated by means of the local stress/strain at the crack tip. The local stress and strain calculations are based on the general solutions given by Hutchinson, Rice and Rosengren. It is assumed that a small highly strained area existing at the crack tip is responsible for the fatigue crack growth. It is also assumed that the fatigue crack growth rate depends mainly on the width, x¹, of the highly strained zone and on the strain range, $\text{Δ?}{}^1$, within the zone. A relationship between stress intensity factor K and the local strain and stress has been developed. It is possible to calculate the local strain for a variety of crack problems. Then, the number of cycles N¹ required for material failure inside the highly strained zone is calculated. The fatigue crack growth rate is calculated as the ratio $\text{x}{}^1\text{N}{}^1$.The calculated fatigue crack growth rates were compared to the experimental ones. Two alloys steels and two aluminium alloys were analyzed. Good agreement between experimental and theoretical results is obtained.     

Crack tip closure and environmental crack propagation

Crack propagation rate, da/dN, and crack tip closure stress, σ_cc, in part-through crack fatigue specimens of aluminum alloys are drastically affected by gaseous environments. The present studies indicate that the crack closure reflects the influence of the environment on the plastic deformation at the crack tip, and, therefore, on the crack propagation rates. Postulating that da/dN is mainly determined by $\text{ΔK}{}_{\mathrm{eff}}\text{∝ (σ}{}_{\max }\text{?σ}{}_{\mathrm{cc}}\text{)}$ (instead of $\text{ΔK ∝ (σ}{}_{\max }\text{?σ}{}_{\min }\text{)}$, as is done traditionally) leads to the relationship $\text{da/dN = A(ΔK}{}_{\mathrm{eff}}\text{)}{}^{\mathrm{n}}$ in which $\text{A}$ and $\text{n}$ are virtually independent of the gaseous environment. The exponents are $\text{n ≈ 3.3}$ for Al 7075 T651 and $\text{n ≈ 3.1}$ for Al 2024 T351, respectively.     

Fatigue crack propagation behaviour of rotor and wheel materials used in steam turbines

The fatigue crack propagation characteristics of several rotor and wheel materials that are commonly used in rotating components of steam turbines were investigated. Particular emphasis was placed on the behaviour at near-threshold growth rates, ie below 10^?5 mm/cycle, approaching the fatigue-crack propagation threshold, $\text{ΔK}{}_{\mathrm{<mtext>th</mtext>}}$. The lifetimes of the cracks of interest lie mostly in this region, and it is also the region where few data are available.The effects of load ratio on the fatigue crack growth rates were examined, as well as the tensile, Charpy V-notch and fracture toughness properties of the rotor and wheel materials. The relationship between fatigue crack propagation behaviour and fractographic features was examined. Fatigue crack growth rate data, $\text{da/d}\text{N}$ vs stress intesity range $\text{ΔK}$, were fitted with a four parameter Weibull survivorship function. This curve fitting can be used for life estimation and establishment of $\text{ΔK}{}_{\mathrm{<mtext>th</mtext>}}$. The results show that load ratio and microstructure play a role in determining the fatigue crack threshold and fatigue crack growth behaviour.     

Cyclic analysis of a propagating crack and its correlation with fatigue crack growth

Stress and strain field of a propagating fatigue crack and the resulting crack opening and closing behavior were analysed. It was found that a propagating fatigue crack was closed at tensile external loads due to the cyclically induced residual stresses. Strain range value $\text{Δ?}{}_{\mathrm{y}}$ in the vicinity of the crack tip was found to be closely related with the effective stress intensity factor range $\text{ΔK}{}_{\mathrm{eff}}$ which was determined on the basts of the analytical crack opening and closing behavior at its tip. Application of this analysis to the non-propagating fatigue crack problem and the fatigue crack propagation problems under variable stress amplitude conditions revealed that both $\text{Δ?}{}_{\mathrm{y}}$ and $\text{ΔK}{}_{\mathrm{eff}}$ were essential parameters governing fatigue crack growth rate.     

Condition for stable growth of branched cracks

In order to clarify the reason why the stable growth of branched cracks occurs in delayed failure, while not in other subcritical crack propagation process such as fatigue, the stress intensity factor after crack branching in delayed failure was dropped to various values, and the propagation behavior of both cracks was investigated.The well balanced growth of branched cracks in delayed failure occurs only when the crack propagation velocity after crack branching belongs to the region II where the crack propagation velocity is constant independently of $\text{K}$. The fatigue cracks at the tips of artificially branched cracks, on the other hand, can not propagate stably, and only either crack propagates preferentially.The exponent in the crack propagation law ($\text{d}\text{a/}\text{d}\text{t =}\text{c}{}_1\text{K}{}^{\mathrm{<mtext>m</mtext>}}\text{or}\text{d}\text{a/}\text{d}\text{N =}\text{c}{}_2\text{(ΔK)}{}^{\mathrm{<mtext>m</mtext>}}$) expresses the degree of unbalance growth of branched cracks. The stable growth of branched cracks occurs only when the crack propagation velocity is constant independently of $\text{K}$ or $\text{ΔK}$, i.e. $\text{m}\text{= 0}$.     

On the cyclic behavior of cast and extruded aluminum alloys. Part B: Fractography

In a prior study [1], the fatigue crack propagation (FCP) response of a cast and an extruded aluminum alloy was examined as a function of mean stress and specimen orientation while crack closure data were collected. In this work, extensive electron fractographic studies were conducted on the previously generated fatigue fracture surfaces using both scanning and transmission electron microscopy. The threshold micromorphology revealed crisp, cleavage-like facets. Striation spacing measurements at intermediate and high $\text{Δ}\text{K}$ levels were obtained to determine microscopic growth rates; these measurements were seen to vary with $\text{R}$ ratio and were best correlated with $\text{ΔK}{}_{\mathrm{EFF}}$ rather than $\text{Δ}\text{K}{}_{\mathrm{APP}}$. Slope changes in the $\text{da/da-}\text{Δ}\text{K}$ plots were identified and attempts made to establish correlations between the associated plastic zone sizes and microstructural dimensions. Of particular note, a stage IIa to IIb transition in the extruded material was found to correspond to a micromechanism change from faceted growth to striated growth when the reversed plastic zone size was similar to the subgrain dimension.     

Fatigue crack propagation work coefficient—a material constant giving degree of resistance to fatigue crack growth

Study on fatigue crack growth in steels was carried out from energetic point of view, i.e. taking account of plastic work around the fatigue crack. Based on the examination of the relation between fatigue crack growth rate (da/dN) and the plastic work around the fatigue crack tip (W_0.02 in SUS304, Fe-3Si and HT 60 steels, a material constant-fatigue crack propagation work coefficient-Q_0.02 is proposed. It is the ratio of W_0.02 to da/dN and means the degree of the resistance to fatigue crack growth. Numerical expression of Q_0.02 by mechanical properties was derived, which is given by

$\text{Q}{}_{0.02}\text{=}\text{9.3x10}{}^1\text{(σ}{}_{\mathrm{y}}\text{+σ}{}_{0.2}\text{)}\text{σ}{}_{\mathrm{y}}{}^{1.3}$

Comparison of Q_0.02 of various steels showed that Q_0.02 of high strength steels is very small compared with that of low strength steels. Graphical representation of the relation between Q_0.02 and da/dN at various values of ΔK/σ_y for steels revealed that da/dN at given value of ΔK/σ_y increase with decreasing Q_0.02. It is shown that fatigue crack growth behaviour of a steel (da/dN-ΔK relation) can be obtained from the Q_0.02-da/dN diagram by knowing the mechanical properties. Discussion on design stress level of the steels is also given.     

Fatigue crack propagation in steels

From previous investigations of the mechanisms of both fracture and fatigue crack propagation, the static fracture model proposed by Lal and Weiss may be thought as reasonable for describing fatigue crack propagation in metals at both low and intermediate stress intensity factor ranges $\text{ΔK}$. Recent progress in fatigue crack propagation indicates that it is not only possible, but also necessary, to modify this static fracture model. Based on the modified static fracture model, the effective stress intensity factor range $\text{ΔK}{}_{\mathrm{eff}}$, which is defined as the difference between $\text{ΔK}$ and the fatigue crack propagation threshold value $\text{Δ}{}_{\mathrm{th}}$, is taken as the governing parameter for fatigue crack propagation. Utilising the estimates of the theoretical strengths of metals employed in industry, a new expression for fatigue crack propagation, which may be predicted from the tensile properties of the metals, has been derived. The correlation between the fatigue crack propagation rate and the tensile properties is thus revealed. The new expression fits the test results of fatigue crack propagation of steels below 10^?3 mm/cycle and indicates well the effect of stress ratio on the fatigue crack propagation rate.     

Some formulas for the crack opening stress level

Crack growth data for 2024-T3 sheet material were analysed with different formulas for $\text{ΔK}{}_{\mathrm{eff}}$ as a function fo the stress ratio $\text{R}$. The data covered $\text{R}$ values from ?1.0 to 0.54. A good correlation was obtained for $\text{ΔK}{}_{\mathrm{eff}}$/$\text{ΔK}$ = 0.55 + 0.33$\text{R}$ + 0.12$\text{R}{}^2$ The relation between log $\text{d}\text{a/}\text{d}\text{n}$ and log $\text{ΔK}{}_{\mathrm{eff}}$ was non-linear for high crack rates (> 1 μm/c).     

Fracture mechanics approach to fatigue crack initiation from deep notches

Fracture mechanics approach is applied to fatigue crack initiation at the tips of deep, blunt notches including those with very small notch-tip radius. The theoretical relations between the stress intensity range ΔK_ρ and the notch-tip radius ρ for a fixed life for crack initiation were derived based on the models of dislocation-dipole accumulation and blocked slip-band. Those are approximated by a simpler equation: $\text{ΔK}{}_{\mathrm{\rho }}\text{ΔK}{}_{\mathrm{o}}\text{= (1 + ρ/ρ0)}\text{1}\text{2}$ where ΔK₀ and ρ0 are material constants which are related to the fatigue strength of smooth specimens Δρ0 as $\text{Δρ0 =}\text{2ΔK}{}_0\text{(πρ0)}{}^{\mathrm{<mtext>1</mtext><mtext>2</mtext>}}$. The results of experiments done with bluntly notched compact tension specimens of a structural low-carbon steel agree with the above relation between $\text{ΔK}{}_{\mathrm{gr}}\text{ΔK}{}_{\mathrm{o}}$ and ρ/ρ_o. The method to predict ΔK_o, ρ_o and Δρ_o from the fatigue data of cracked and smooth specimens is proposed.     

The effect of temperature and R ratio on fatigue crack growth in A612 grade B steel

Fatigue-crack propagation rates in ASTM$\text{A612}$ Grade B steel were investigated at room temperature and ?100°F (?73°C) with $\text{R}\text{ratio}\text{= ?0.1}\text{and}\text{+0.67}$. The data were evaluated in terms of the crack propagation rates ($\text{d}\text{a/}\text{d}\text{N}$) as a function of the alternating stress intensition ($\text{ΔK}$), according to $\text{d}\text{a/}\text{d}\text{N = e+(v ? e)(? 1}\text{n}\text{(1 ?}\text{Δ}\text{K/K}{}_{\mathrm{b}}\text{))}{}^{\mathrm{t/k}}$. It was found that crack growth rates were increased due to increasing $\text{R}$ ratio. Also the dependence of crack growth rates on $\text{R}$ ratio is strongest at the lowest crack growth rates where a $\text{ΔK}$ fatigue threshold is established. Crack growth rates were decreased due to decreasing test temperature in the slow crack growth region. However, it was found that crack growth rates were increased due to decreasing test temperature in the fast crack growth region near the upper instability asymptote. Decreased test temperature and increased $\text{R}$ ratio interact synergistically to increase crack growth rates for the entire range of $\text{ΔK}$.     

Crack closure in 2219-T851 aluminum alloy

The effects of specimen thickness, stress ratio ($\text{R}$) and maximum stress intensity factor ($\text{K}{}_{\max }$) on crack closure (or opening) were studied using a 2219-T851 aluminum alloy. The crack length and the occurrence of crack closure were measured by an electrical potential method. The experimental work was carried out within the framework of linear-elastic fracture mechanics.The experimental results show that the onset of crack closure (or opening) dependes on $\text{R, K}{}_{\mathrm{<mtext>max</mtext>}}$), and specimen thickness. In terms of the “effective stress intensity range ratio” ($\text{U}$), as defined by Elber, the results show that $\text{U}$ tends to increase for increasing $\text{R}$, decrease for increasing $\text{K}{}_{\max }$, and decrease with increasing specimen thickness. From these trends, it is shown that the “effective stress intensity range” ($\text{ΔK}{}_{\mathrm{<mtext>eff</mtext>}}$) does not always increase with increasing stress intensity range ($\text{ΔK}$).The experimental results show that crack closure cannot fully account for the effects of stress ratio, specimen thickness and $\text{K}{}_{\max }$ on fatigue crack growth. The use of $\text{ΔK}{}_{\mathrm{<mtext>eff</mtext>}}$ as a parameter for characterizing the mechanical driving force for fatigue crack growth is questioned.     

On crack opening stress level in fatigue by Eddy current technique

Linear elastic fracture mechanics relates fatigue crack growth with the stress intensity factor at the crack tip. Presence of residual deformations at the tip of a fatigue crack reduces the crack tip stress intensification such that effective stress intensity range $\text{ΔK}{}_{\mathrm{e}}\text{= U · ΔK}$. In this paper use of eddy current technique is exhibited to find the values of test value of effective stress range factor $\text{U}{}_{\mathrm{test}}$. A reasonable comparison between computed and experimental results of $\text{U}{}_1$ and $\text{U}{}_{\mathrm{test}}$ on two Al alloys 6061-T6 and 6063-T6 has recommended the Eddy Current Technology for finding out the values of crack opening stress level under given loading conditions.     

A cumulative model of fatigue crack growth and the crack closure effect

A model of fatigue crack growth based on an analysis of elastic/plastic stress and strain at the crack tip is presented. It is shown that the fatigue crack growth rate can be calculated using the local stress/strain at the crack tip by assuming that a small highly strained area $\text{x}{}^1$, existing at the crack tip, is responsible for the fatigue crack growth, and that the fatigue crack growth may be regarded as the cumulation of successive crack re-initiations over a distance $\text{x}{}^1$. It is shown that crack closure can be modelled using the effective contact zone g behind the crack tip. The model allows the fatigue crack growth rate over the near threshold and linear ranges of the general da/dN versus ΔK curve to be calculated. The fatigue crack growth retardation due to overload and fatigue crack arrest can also be analysed in terms of g and $\text{x}{}^1$.Calculated fatigue crack growth rates are compared with experimental ones for low and high strength steel.     

A fracture mechanics analysis of ultrasonic fatigue

The method of ultrasonic fatigue finds increasing interest in materials science. Especially, fatigue crack growth rates near the threshold stress intensity range, $\text{ΔK}{}_0$, can be determined with this method in reasonable times providing no frequency and corrosion effects exist. But for an accurate application of this technique it is necessary to improve the testing systems and also the determination of the dynamic cyclic stress intensity range, $\text{ΔK}$. In this paper, fatigue crack growth experiments at ultrasonic frequencies with different mean stresses and also the calculation of the dynamic stress intensity range with finite elements are treated. On this basis fatigue crack growth curves at room temperature of the alloys Hastelloy X and IN 800 were measured and compared with results obtained at low frequencies. No significant influence of frequency could be found in these materials.     

Prior-to-failure extension of flaws under monotonic and pulsating loadings

An equation governing the prior to failure crack propagation is proposed. For a rate-sensitive solid containing two-dimensional crack and subject to the tensile mode of fracture the differential equations are integrated numerically for the loads increasing monotonically in time. The resulting integral curves gs = σ(l) and l= l(t), i.e. load vs crack length and length vs time, indicate that the growth of cracks in the subcritical range is strongly rate dependent.The fatigue growth, viewed as a sequence of slow growth periods, is simulated on EAI 380 analogue computer. The fourth power law proposed by Paris is confirmed only within certain range of high-cycle fatigue propagation and for a rate-insensitive solid. Otherwise, that is for a more pronounced rate dependency induced by viscosity of a solid and/or in the proximity of the final instability point the growth is markedly enhanced. For sufficiently small ratios of the applied stress intensity range ΔK to the toughness K_c, the suggested fatigue growth law consists of two terms, i.e.

$\text{d}\text{l}\text{d}\text{n}\text{=}\text{l}{}_1\text{12}\text{4}\text{ΔK}\text{K}{}_{\mathrm{c}}{}^4\text{+Cf}{}^{\mathrm{?1}}\text{ΔK}\text{K}{}_{\mathrm{c}}{}^2\text{, l}{}_1\text{=}\text{πK}{}^2{}_{\mathrm{c}}\text{8Y}{}^2$

First term is the familiar Paris expression while the second one accounts for the rate-dependent contribution; f denotes frequency and Y is the yield strength. Rate-sensitivity C is defined by eq. (1.13).     

A model for fatigue crack growth in a threshold region

The prediction of fatigue crack growth at very low ΔK values, and in particular for the threshold region, is important in design and in many engineering applications. A simple model for cyclic crack propagation in ductile materials is discussed and the expression

$\text{da}\text{dN}\text{=}\text{2}{}^{\mathrm{1+n}}\text{(1?2v)(ΔK}{}^2{}_{\mathrm{eff}}\text{?ΔK}{}^2{}_{\mathrm{c,eff}}\text{)}\text{4(1+n)π σ}{}^{\mathrm{1?n}}{}_{\mathrm{yc}}\text{E}{}^{\mathrm{1+n}}\text{?}{}^{\mathrm{1+n}}{}_{\mathrm{f}}$

developed. Here, n is the cyclic strain hardening exponent, σ_yc is cyclic yield, and ε_f is the true fracture strain. The model is successfully used in the analysis of fatigue data BS 4360-50D steel.