木素在Na2SO3处理及H2O2漂白中的发色行为

通过定量研究磨木木素色团在Na2SO3处理及H2O2漂白中的发色效果,揭示木素在CTMP化学预处理及漂白过程中的发色行为。研究发现,邻醌和邻酚金属螯合物是Na2SO3处理及H2O2漂白木素的主要颜色来源。共轭羰基对木素颜色不构成主要影响;限制金属离子的引入,可有效地提高CTMP浆的漂白性能。     

三倍体毛白杨木材特性分析及CTMP制浆

对三倍体毛白杨全材和心材的化学组成差异,CTMP制浆的影响因素,特别是化学处理过程的工艺参数对CTMP制浆的影响进行了研究。三倍体毛白杨全材的综纤维素含量高于心材,而木素和苯醇抽出物的含量低于心材。NaOH用量影响着白度、得率、筛渣、羧基和磺酸基含量、松厚度和浆料强度;Na2SO3用量主要影响白度和磺酸基含量;提高温度能够增加浆料的强度,而延长化学预处理时间可以降低浆料中纤维束（筛渣）。三倍体毛白杨CTMP在碱性过氧化氲漂白过程中具有良好的可漂性。     

木素在Na2SO3处理及H2O2漂白中的发色行为

通过定量研究磨木木素色团在Na2SO3处理及H2o2漂白中的发色效果,揭示木素在CTMP化学预处理及漂白过程中的发色行为.研究发现,邻醌和邻酚金属螯合物是Na2SO3处理及H2O2漂白木素的主要颜色来源,共轭羰基对木素颜色不构成主要影响;限制金属离子的引入,可有效地提高CTMP浆的漂白性能.     

改进玉米秸秆化学预处理提高后续生物酶解糖化效率的研究

采用NaOH、NaOH+AQ、NaOH+Na2SO3、H2SO4+Na2SO3、NaOH+Na2S以及H2SO4预处理玉米秸秆,通过改变最高温度和药品用量考察了不同处理方式对酶解效率及总糖得率的影响。结果表明:在相同处理条件下,采用NaOH+Na2SO3预处理有利于提高后续的酶解效率及总糖得率。在140℃及10%用碱量时,碱性亚硫酸钠法的处理效果最佳,聚葡萄糖和聚木糖的酶解效率分别达到84.7%和81.1%。基于初始原料的总糖得率约为0.44g/g初始秸秆,相比同样条件的单一NaOH预处理提高了13.5%。     

蓝桉材性对CTMP质量的影响

以从2个人工林地选择的蓝桉为原料,评价其是否适用于生产高质量的高得率浆。蓝桉木片先经Na2O3预处理后再磨浆制取CTMP。CTMP浆料特性与木材的化学和物理性能密切相关。结果表明,木材中的苯．醇抽出物含量与CTMP白度呈线性关系;木材中木素含量与CTMP浆张紧度具有相关性：1％NaOH抽出物含量与浆料得率呈相反趋势。浆料经光热处理后再测定返黄值发现,热诱导返黄对CTMP浆张的影响较小,可满足印刷纸的需要。此外,浆料返黄值与抽出物含量成反比,通过添加抗氧化刺可以减轻浆张的返黄。     

预处理条件对柳桉磺化化机浆性能的影响

探讨预处理奈件对柳桉磺化化机浆物理性能指标的影响，试验表明，NaOH用量、Na2SO3用量、磺化温度和保温时间对纸浆强度、白度和得率影响较大，对柳按而言，最佳的预处理条件为：NaOH用量为4％，Na2SO3用量为5％，磺化温度为120℃，保温时间为120min。     

麦草制取低污染的SCMP和CTMP的研究

本文对麦草制取低污染SCMP和CTMP进行了初步研究。探讨了浓废液循环利用对SCMP性质的影响和SCMP的稀洗涤废液用于制取麦草CTMP的适宜条件。结果表明：麦草制取SCMP的适宜条件：Na2SO3用量15％，磺化温度130℃，升温时间60min，保温时间45min，磺化浆得率82．0％，成浆裂断长3．45km，撕裂指数8．32mNm^2／g。在较优条件下进行浓废液循环利用对浆料性质影响不大，稀洗涤废液用于制取麦草CTMP是可行的，在适宜化学处理条件下（Na2SO3用量4％，NaOH用量3％，最高温度125℃，保温时间30min）制得CTMP的得率87．1％，裂断长2．48km，撕裂指数6．91mN·m^2／g。     

绿液预处理杨木硫酸盐法蒸煮脱木素反应历程研究

采用碱回收绿液对杨木木片进行预处理,研究了预处理后硫酸盐法蒸煮过程中脱木素反应历程及NaOH的消耗过程。研究表明,采用绿液预处理后,杨木木片得率为73.1%,木素脱除率为32.54%。预处理后的蒸煮过程中,在初始脱木素段,木素脱除率为14.52%;在大量脱木素段,木素脱除率为42.62%;残余脱木素段,木素脱除率仅为3.41%。这3个阶段的木素脱除率比传统硫酸盐法分别降低了3.55、19.38和9.11个百分点。NaOH几乎全部消耗在蒸煮初期和大量脱木素段,这2个阶段NaOH分别消耗了57.71%和42.29%;Na2S质量浓度在蒸煮初期逐渐减小,蒸煮的中后期又逐渐增大。绿液预处理硫酸盐法蒸煮不仅能提高脱木素选择性,还能提高蒸煮后浆料得率（达到50.8%）,比传统硫酸盐法浆料得率（47.9%）提高2.9个百分点。     

大叶相思制CTMP及配抄箱纸板

对大叶相思木材的纤维形态、化学组分进行了分析,并对木材制CTMP及其配抄纸板进行了研究。结果表明,此种木材虽纤维长度偏短,但纤维系含量较高,壁腔比小,木素含量高,采用NaOH和Na2SO3 混合液浸渍的一般磨浆工艺能生产出高得率的CTMP,配抄箱纸要的以质量符合国家要求。     

国产挤压撕裂机的生产运行

挤压撕裂机是在CTMP和APMP(PRC-APMP)等化机浆生产工艺中对原料进行化学预处理挤压浸渍段的关键设备,已广泛地应用于木片的挤压撕裂,通过该设备大压缩比的强力挤压作用可使木片被撕裂压馈,增加了物料与药液接触的表面积,同时又可去除木片中部分水分、空气和树脂等物质,减少化学药品渗透的阻力和降低后续物料化学处理的药品消耗,使物料在高密度和高干度膨胀下利用海绵效应充分均匀地吸收化学药品,为后续生产工艺创造条件.汶瑞机械(山东)有限公司在吸收消化国外先进技术,自主开发出JS30型挤压撕裂机,并投入连续化大生产运行.     

桉木化机浆性能的改善

研究了桉木化学机械浆制浆过程中的预处理条件对纸浆物理性能及漂白性能的影响，并对改善桉木化机浆质量性能的途径进行了探索。结果表明加强药液对木片的预浸渍，可提高纸浆白度和纸浆中磺酸基含量。采用两段ＮａＯＨ—Ｎａ２ＳＯ３预处理方法可提高纸浆强度、白度及可漂性能。     

Chemische Eigenschaften von TMP und CTMP, hergestellt aus Kiefernholz und UF-Harz-gebundenen mitteldichten Faserplatten (MDF)

Thermo-mechanical (TMP) and chemo-thermo-mechanical pulps (CTMP) were prepared from pine wood and from UF-bonded MDF made from pine wood. For preparing TMP pine chips as well as UF-bonded MDF were digested under pressure at 170 °C. Thereafter, the digested chips and MDF were defibrated at 170 °C using a single disc refiner. CTMP was prepared from pine wood with 0.25% NaOH (based on dry wood) under the conditions set forth above. CTMP was also made from MDF under two conditions using 0.15% sodium hydroxide (% based on dry MDF) and a mixture of sodium sulphite (1%) and sodium hydroxide (0.25%). The pulps show distinct differences in their properties: TMP from UF-bonded MDF shows lower extractive content in cold and hot water, lower pH-value and higher buffering capacity towards alkali of the cold water extractives than the CTMP counterpart. Moreover, CTMP prepared by using sodium hydroxide alone as a pulping agent increases the content of formate and acetate ions in the cold water extractives. The use of a mixture of sodium sulfite and sodium hydroxide as a pulping agent decreases, however, significantly the content of formate and acetate ions in the cold water extractives. This may be due to the buffering action of sodium sulfite. In general, CTMP decreases the formaldehyde release of the fibres, as measured by the flask method. In presence of sodium sulfite as a pulping agent for recycled MDF, the formaldehyde release is slashed to almost 30% of its original value. The formaldehyde release of CTMP from UF-bonded boards seems to be in the same range as that of TMP from virgin wood.      

化学预处理对慈竹化机浆制浆漂白性能的影响

对氢氧化钠和中性亚硫酸钠两种化学预处理方式的慈竹化机浆的制浆、漂白性能进行了研究。氢氧化钠预处理,原浆白度较深;中性亚硫酸钠预处理,原浆白度较浅。不同预处理方式引起的浆料原始白度差异,可以—直保持到过氧化氢漂白以后,后者比前者白度高出11％-12％ISO。不同预处理方式,相同过氧化氢水平漂白时,对应的最佳用碱量不同;10％H2O2漂白时,氢氧化钠预处理的最佳碱用量为6％,中性亚硫酸钠预处理的最佳碱用量为7％。中性亚硫酸钠预处理浆料的漂白性能优于氢氧化钠预处理,抗张指数及耐破指数高20％-40％;撕裂指数高出10％～20％。在本文研究的化学品用量范围内,中性亚硫酸钠预处理方式优于氢氧化钠预处理方式。     

杨木NaOH浸渍渗透特性研究

通过自制设备对杨木NaOH浸渍渗透过程进行了实验研究。结果表明,杨木NaOH浸渍过程纵向边材渗透性能明显优于心材,而横向渗透差异较小;横向渗透为逐层渗透过程,单位渗透体积量与渗透时间呈线性关系;纵向渗透过程可分为快速渗透阶段(第一阶段)和慢速渗透阶段(第二阶段)两个阶段。在本实验条件下适当提高浸渍温度和NaOH浓度均能不同程度地改善浸渍渗透效果,而木块厚度和含水率对渗透过程均有不同程度的负面影响。     

绿竹改良APMP制浆的研究

对绿竹改良APMP制浆工艺进行研究,通过对影响预处理,预浸渍以及漂白工艺的各因素进行分析研究,得出：影响化学预处理的主要因素是温度和Na2SO3用量,其最佳工艺为Na2SO3 10%,NaOH用量2%,保温时间120min,温度130℃;预浸渍最佳工艺为H2O2用量3%,NaOH用量4%,温度70℃,时间60 min,EDTA用量0.1%,Na2SiO3用量4%,MgSO4用量0.05%,浸渍浆浓20%;最佳漂白工艺为H2O2用量3%,NaOH用量1%,温度70℃,时间80 min,EDTA用量0.1%,Na2SiO3用量4%,MgSO4用量0.05%,漂白浆浓25%。在最佳工艺条件下,可以得到APMP浆得率为74.24%,成纸裂断长为3.15 km,撕裂指数为5.83 mN.m2/g,白度为62.4%ISO。     

芦竹磺化化机浆工艺条件的探讨

对芦竹SCMP工艺条件进行了研究 ,实验结果表明 :不同预处理条件及盘磨间隙对芦竹SCMP浆性能影响很大。在弱碱条件下 (1%NaOH用量 ) ,Na2 SO3用量 15 % ,最高温度 15 0℃ ,升温保温 1h左右的预处理条件是适宜的 ;高浓磨浆时 ,建议采用 0 .3、0 .1、0 .1mm的盘磨间隙进行三段磨解 ,磨浆浓度 15 %