竹炭包膜尿素和常用氮肥的氮素淋失特征研究

通过土壤淋溶试验,探讨了竹炭包膜尿素和常用氮肥的氮素淋失特点以及施用不同氮肥对土壤性质的影响。结果表明,不同氮肥施入土壤后其氮素淋失率有很大的差异,其中硝酸钾的淋失率最高,其次为尿素,碳铵的淋失率最低。竹炭包膜尿素因具有养分缓慢释放的特点,其氮素淋失率较尿素低9.93%~16.27%。施用竹炭包膜尿素所引起土壤盐基离子的淋失量远低于施用速溶性氮肥;不同氮肥淋洗后对土壤pH值变化的影响差异较大,竹炭包膜尿素对土壤pH值变化的影响较小。施肥淋洗后,除了硝酸钾处理外,其余处理土壤的速效氮含量均比淋洗前高,两种竹炭包膜尿素处理土壤的速效氮含量均高于尿素处理;土壤介质对氮素的淋失率有较大的影响,供试氮肥在砂土中的氮素淋失率远高于其在石灰岩风化土中的淋失率。     

竹炭包膜尿素在土壤中的氨挥发损失及其影响因素

采用"静态吸收法"研究了自制竹炭包膜尿素(BCCU)在土壤中的氨挥发损失情况,以及施肥量、土壤含水量、土壤温度和土壤类型等因素对氨挥发损失的影响。结果表明,自制的竹炭包膜尿素氨挥发损失量显著减少。在每千克土壤中,施氮600 mg时,两种包膜氮肥氨挥发损失量分别比尿素减少31.8%和19.3%;施氮1 000 mg时,两种包膜氮肥氨挥发损失量分别比尿素减少21.82%和16.66%。在两个施肥水平下,供试氮肥的氨挥发损失量随时间的变化关系均可用Elovich动力学方程Yt=a blnt来描述。土壤含水量和温度等对氮肥氨挥发有较大的影响,氨挥发量随着含水量和温度的上升而递增。     

环渤海盐碱化潮土区小麦-玉米轮作体系氮肥用量对氮肥利用率的影响

采用田间小区试验,研究了环渤海盐碱化潮土区高、中、低产田小麦-玉米最佳施氮量,以及不同施氮水平对小麦-玉米产量、氮肥贡献率和氮肥利用率的影响。结果表明:对于高、中、低产田,小麦的适宜施氮量分别为225,225,180kg/hm2,玉米的适宜施氮量分别为225,180,135kg/hm2;氮肥贡献率在低产田和中产田上大于高产田;氮肥吸收利用率为低产田>中产田>高产田,氮肥吸收利用率和氮肥偏生产力随氮肥用量增加而降低;高、中、低产田土壤供氮能力在冬小麦茬口分别为82.2%,77.8%,76.8%,在夏玉米茬口分别为81.9%,77.7%,75.9%。     

竹炭纤维的性能及应用

介绍了竹炭纤维的结构与制备工艺,具有自调湿、吸湿快干、蓄热保暖、抗菌、吸附除臭、保健等优异性能,并总结了竹炭纤维在服装、家纺、医用以及产业用领域的应用。竹炭纤维是竹材有效利用的一个全新发展方向,是一种新型的环保材料,具有广阔的发展前景。     

竹炭涤纶纤维的染色技术研究

通过单因素分析和正交实验方法研究竹炭涤纶纤维的染色工艺,确定其最佳染色工艺条件为：染色温度95℃、染色时间50min、浴比1：100、pH值4．结果表明：采用该最佳工艺染色后的竹炭涤纶纤维色泽鲜艳,色谱齐全,色牢度及负离子释放性能良好．     

大气气溶胶离子溶出特性的研究

大气气溶胶酸碱特性呈现出明显的季节变化，冬季SO4^2-、NH4^ 要明显高于夏季，大致是夏季的2－3倍，其他离子变化不大。SO4^2-为IP中的主要阴离子，占总阴离子的70％以上，NH4^ 为IP中的主要阳离子，约占总量的40％－50％。各离子质量分数之间有很好的相关关系，特别是硫酸根与铵根，说明这两个离子的来源比较类似。可吸入尘与大颗粒气溶胶在去离子水水浸之后溶液的pH值存在着很好的相关性，相关系数达到0．99以上；同时IP粒子与＞10μm气溶胶在用去离子水及不同的酸性溶液浸取之后，所得浸出液的pH值也成很好的相关关系。气溶胶中主要的碱性离子Ca^2 和Mg^2 随着浸取液pH值的变小，溶解度会有相应的增加，特别是Ca^2 ，用pH4．00的酸溶液浸取比用去离子水浸取的溶出率可增加20％左右，说明气溶胶在酸雨的形成过程中起中和作用。     

竹炭粘胶纤维的性能研究

利用电子显微镜对竹炭粘胶纤维的微观结构进行观察,发现其纵向具有凹槽,纤维内部存在大量空隙;红外光谱研究表明其具有明显的CO2吸收峰;物理性能研究发现其断裂强度较低,回潮率较高;利用铜氨溶液法测定其聚合度,结果证明其聚合度为380.     

水质对面质的影响

研究了水的硬度，ｐＨ值面团性能，产品质量的影响，为制面工艺和制面中的质量控制提供了理论依据。     

竹炭的吸附性能及应用研究进展

竹炭是一种多孔、比表面积大的新型炭材料,其价廉易得、吸附性能好,在污水处理方面已经得到了广泛的应用.探讨了竹炭预处理、吸附动力学、吸附热力学和吸附的影响因子,介绍了竹炭在水环境中的应用.竹炭作为一种清洁环保的材料,其应用将会越来越广泛.     

玉米淀粉基缓释膜生物降解性的测定

以玉米淀粉与聚乙烯醇为原料,在交联剂的作用下,制得包膜料液,用此料液给尿素涂膜,制得包膜尿素。通过生物降解实验,验证了它的环保性。结果表明,此包膜尿素缓释性能良好,且有保水性,抗结块性。此包膜材料具有成本低、可生物降解、无环境污染等特点。     

竹原纤维与竹浆纤维结构和热性能的比较

应用扫描电镜（SEM）、红外光谱（FTIR）、X-射线衍射等测试手段对竹原纤维和竹浆纤维的结构进行了研究。确认竹原纤维属于典型的纤维素Ⅰ结构，竹浆纤维属于纤维素Ⅱ结构，竹原纤维的结晶度和热稳定性均高于竹浆纤维。     

Synthesis and performance of polyurethane coated urea as slow/controlled release fertilizer

Polyurethane coated urea slow/controlled release fertilizer was prepared based on urea granules, isocyanate, polyols and paraffin. Isocyanate reacted with polyols to synthesize the polyurethane skin layer on urea granules surface. Paraffin serves as a lubricant during syntheses of polyurethane skin layers. The structure and nutrient release characteristics of the polyurethane skin layers were investigated by FTIR, SEM and TG. Urea nitrogen slow-release behavior of the polyurethane coated urea was tested. The experimental results indicated that compact and dense polyurethane skin layers with a thickness of 10-15 μm were formed on urea surface, the urea nitrogen slow-release time can reach 40-50 days. Paraffin proves to play a key role in inhibiting water to penetrate into urea, but excessive addition would decrease the polyurethane crosslinking density.     

处理氮肥厂氨氮废水的树脂筛选及动力学特征

采用上海汇脂树脂厂的3种强酸性阳离子交换树脂001×7,D61和D001,研究了树脂对模拟氮肥厂废水(氨氮、Ca2+,Mg2+的质量浓度分别为915,120,70mg/L)中氨氮的Freundlich和Lagergren吸附等温式,在30～50min内树脂对氨氮的吸附基本达到平衡,等温线均符合Freundlich模式,根据吸附等温模型,树脂结构特征和再生等评价方法筛选出用D61树脂去除该废水中的高浓度氨氮效果较好;并研究了D61树脂的动力学特征.结果表明:D61树脂对氨氮的吸附在初期快速反应阶段(前20min)既符合拟一级Lagergren反应动力学模型又符合拟二级Lagergren反应动力学模型,而整个过程理论分析采用拟二级Lagergren反应动力学模型较好,实际应用时采用拟一级Lagergren反应动力学模型速率较快,因而更具有实际意义.     

光催化竹炭纤维针织物光催化降解亚甲基蓝的研究

为了开发新型功能型织物,研究了光催化竹炭纤维织物对亚甲基蓝溶液的光催化降解效果,分析了反应时间、亚甲基蓝溶液的初始浓度、pH值、光源中心与液面间距离等因素对亚甲基蓝溶液光催化降解效果的影响。结果表明,光催化竹炭纤维针织物在紫外线的照射下对亚甲基蓝溶液产生明显的降解效果,其去除率可达67.02%;亚甲基蓝溶液的初始浓度越低,降解效果越好;亚甲基蓝溶液的初始pH值越高,降解效果越好;光源中心与液面间距较小时织物的光催化降解效果较好。因此,光催化竹炭纤维针织物可用作过滤、污水处理材料等。     

重组竹材三面和四面受火炭化性能试验

重组竹作为一种新型的建筑结构材料应用日益广泛,但同木材相似的可燃性导致重组竹结构抗火设计方法亟待补充和完善.为研究重组竹材多面受火炭化性能,依据ISO 834火灾试验方法进行了4组16根重组竹构件三面和四面受火试验,分析截面尺寸、受火时间以及不同受火面对炭化深度和炭化速度的影响.结果表明,由于炭化层隔热作用,随着受火时间增加重组竹构件炭化速度逐渐减小;火灾作用下构件截面有效面积减小,角部区域因承受双向热传递而由棱角变为圆角形,圆角区和非圆角区炭化深度差异明显;通过对比重组竹材多面炭化非圆角区炭化深度与单面受火炭化深度,前者较后者增加明显,引入多面炭化因子进一步修正计算模型;为简化抗火设计,通过对比多种木材,考虑圆角区影响提出重组竹材多面受火条件下名义炭化速度为0.7 mm/min,为重组竹结构灾后剩余截面计算提供重要参数依据.     

温室栽培对包膜尿素养分利用性研究

以桐油为包膜材料,制备包膜肥料,研究"温室无土栽培对桐油包膜肥料养分释放性",同时进行烟草的温室无土栽培试验,研究其氮素的利用率.结果表明:桐油包膜尿素的养分释放性,在第1 d低于普通尿素59.6%;其氮素利用率高于普通尿素10.8%.结论:桐油包膜尿素具有很好的养分释放性和利用率.     

漳河灌区农田氮磷淋失特性

进行农田土壤渗漏及伴随的N和P淋失的研究是十分重要的,这对于制定合理的水肥管理措施和保护人类的生存环境具有十分重要的意义.选取湖北省漳河灌区的水旱作物(水稻和玉米)作为研究对象,对两种作物在不同处理方式下土壤N和P渗漏淋失的规律及其主要影响因素进行了深入分析.试验结果表明:不同的土地利用方式的土壤有不同的特性,对N和P淋失影响显著;灌溉方式直接影响渗漏量,对N和P淋失有一定影响;在作物生育期的不同阶段,N和P淋失存在显著差异;不同的降雨条件和地形地势差异也会对N和P淋失产生一定影响.