TPU微孔薄膜织物防水透湿性能研究

研究了5种不同底布的涂TPU微孔薄膜织物的防水透湿性能.通过测试织物的毛细管高度、水滴接触角、沽湿面积比例及透湿量,对比了5种织物的性能差异.发现织物底布的结构越紧密,其防水性能越好,沾湿性能越差,透湿性能越差.双层复合TPU微孔薄膜织物的防水性能优于3层复合织物,而其沾湿性能较3层复合织物差.透湿性还随织物底布厚度的增加而减弱.     

防水透湿PU膜层压复合机织物的性能研究

以涤纶机织物、热熔胶TPU(热塑性聚氨酯)弹性体和高透PU(聚氨酯)膜为基材,采用层压复合的方法制备防水透湿复合织物,测试涤纶机织物、高透PU膜及复合织物的拉伸、悬垂、透气及防水透湿性能,讨论不同TPU用量、温度及复合压力对复合织物各项性能的影响。研究结果表明:涤纶机织物与PU膜复合后,在一定程度上能提高复合织物的拉伸断裂强力,但悬垂性比涤纶机织物有所降低,防水效果明显比涤纶机织物要好,透湿、透气效果比高透PU膜要小。当TPU用量为22 g/m2,复合压力为5MPa,复合温度为80℃时,复合织物的复合效果最好。     

防水透湿织物服用性能的影响因素分析

探讨防水透湿织物重要服用性能的影响因素。制造了46种不同面料或里料、不同复合方式(涂层及层压)、不同组合方式的防水透湿织物,对其防风保暖性、透湿性、防水性及抗撕破性进行了测试与分析。结果表明:相同面料的涂层及膜层压织物保暖性相差不大;厚重蓬松里料对层压织物主要起保暖作用;轻薄透里料对层压织物的膜具有保护作用;微孔膜层压织物的透湿性最好,湿法与转移涂层织物的透湿性较好;防水透湿织物的抗沾水能力主要取决于面料的抗沾水性,抗渗水性主要取决于层压膜或涂层的抗渗水性;伸缩性较大的面料利于提高防水透湿织物的撕裂强力,复合伸缩性较大的里料可以增大三层层压织物的撕裂强力。认为在户外运动服装面料的设计开发中应针对需要选择合适的面料、里料以及处理方式。     

防水透湿层压织物制作工艺探索

采用点胶法制作防水透湿层压织物,细化探索施胶和压烫工艺,得出层压织物的制作条件,并表征所制含膜防水透湿织物的黏结强度、透气和透湿性能。结果表明,在熔胶温度215℃、施胶压强0.34 MPa、开胶时间0.004 s的条件下,控制压烫温度、时间分别为125℃、25 s[聚四氟乙烯(PTFE)膜],125℃、35 s[聚氨酯(PU)膜]和115℃、45 s(PTFE/PU膜),所制织物的黏结强度最大;其中,PU织物的剥离强度达23.68 N/2.5 cm,PTFE织物的透湿性超过8 000 g/(m2·24 h),PTFE/PU膜制品的防风性最佳,透湿性介于两种单组分膜织物之间。     

开发拒液纺织品的3种新途径

介绍了通过 3种不同途径开发的新型拒液纺织品 :①采用不同的纤维原料、织物组织结构、密度和化学后整理工艺 ,开发既具有较高拒液性能、又有较好透湿性能的新型医用血液屏蔽织物 ;②制备具有良好防水透湿性能聚偏氟乙烯微孔膜 ,再与织物复合 ,开发既能满足防水需要、又有透湿性的新型防水透湿织物 ;③采用电子束辐照后与丙烯酸单体接枝改性的方法 ,开发遇水能拒水 (抗浸 )、干态时又有良好透湿性的智能型抗浸织物     

户外睡袋用面料防水透湿性能的评价

户外睡袋用面料对防水性能和透湿性能的要求很高。文章针对市场上已有的高密面料、涂层面料和覆膜面料3类共20种户外睡袋面料进行调研,并对面料的表面抗湿性能、抗渗水性能和透湿性能进行评价。结果表明:覆膜面料和高密压光面料的表面抗湿性最好,沾水度评级在4～5级;覆膜面料的抗渗水性最好,静水压值大于等于30 kPa,其中PU覆膜面料和PTFE两层覆膜面料静水压值大于50 kPa;高密面料的透湿性能最好,透湿量最高超过6 000 g/(m~2·d),PTFE覆膜面料的透湿性能也较好,透湿量接近4 000 g/(m~2·d)。     

抗菌剂对层压织物防水透湿及抗菌性能的影响

TPU膜复合织物分别以锦纶、涤纶及棉为基布贴合高透湿909TPU薄膜。对复合织物进行DF纳米银抗菌整理,测试整理前后层压复合织物对金黄色葡萄球菌(Staphylococcus aureus ATCC 29213)、大肠杆菌(Escherchia coli ATCC 8739)的抗菌性能,以及整理前后复合织物的防水透湿及剥离强度等户外服装面料主要服用性能的变化。实验表明,采用新的DF纳米银抗菌剂添加整理工艺,方法简便、可行,且织物的抗菌性能显著提高,整理对复合织物原有的防水透湿及剥离强度影响较小。     

丝素/聚氨酯防水透湿涂层剂的制备及其应用

为改善涂层织物的防水透湿性能,采用丝素共混改性水性聚氨酯,制备了丝素/聚氨酯复合涂层剂,用于涤纶织物的涂层整理.利用红外光谱、X射线衍射、热重分析对丝素/聚氨酯共混膜的结构、性能进行表征,研究了丝素粒径及其质量分数对涂层防水透湿性能的影响.结果表明:丝素与聚氨酯之间存在着氢键作用,丝素的加入提高了聚氨酯体系的热稳定性.当粒径为5 μm的丝素粉体质量分数为20％时,涂层织物的透湿量达到3000 g/m2.d-1以上,静水压值保持在3000 Pa以上.与单一聚氨酯涂层整理的织物相比,丝素改性聚氨酯涂层整理织物的透湿性得到显著改善,且具有良好的耐洗性和断裂强力.     

聚氨酯/二氧化硅复合超细纤维膜的制备及其防水透湿性能

为制备具有防水透湿性能的超细纤维膜,在聚氨酯(PU)纺丝液中添加疏水二氧化硅(SiO₂)颗粒,制备PU/SiO₂复合超细纤维膜。通过软件模拟分析了纺丝液浓度和纤维膜厚度对纤维膜孔径的影响,根据静态水接触角、静水压、透气率和透湿率分析了复合超细纤维膜的防水透湿性能,并讨论了不同质量分数SiO₂对PU/SiO₂复合超细纤维膜防水透湿性能的影响。结果表明:复合纤维膜的孔径随着纺丝液浓度的增加而增加,随着纤维膜厚度的增加而减少;当SiO₂质量分数为9%、PU质量分数为18%时,PU/SiO₂复合纤维膜的静态水接触角达到131°,静水压为6.4 kPa,透气率为33.4 mm/s,透湿率为8.065 kg/(m²·d);该条件下复合纤维膜断裂应力为4.16 MPa,断裂伸长率为184%,与纯PU膜相比具有较好的尺寸稳定性。     

层压防水透湿针织物的性能测试分析与研究

以PTFE微孔薄膜复合针织物为例,在试验测试的基础上,采用对比分析的方法,对PTFE微孔薄膜复合针织物和复合前的普通织物的各项服用性能进行了研究.得出这种层压防水透湿织物在服用性能方面的优越性和缺陷;对层压防水透湿织物的进一步研究和产品开发具有一定的参考建议.     

防水透湿织物性能

研究不同材料用不同方法加工的防水透湿织物，如亲水性薄膜、进口的微孔薄膜、微孔涂层织物、亲水性涂层织物的耐静水压性能和透湿性能，并探讨水洗对这些性能的影响。     

DF纳米银抗菌剂对复合织物性能影响的研究

TPU膜复合织物分别以锦纶、涤纶及棉为基布贴合高透湿909TPU薄膜。复合织物进行DF纳米银抗菌整理,测试整理前后层压复合面料对金黄色葡萄球菌(Staphylococcus aureus ATCC 29213)、大肠杆菌(Escherchia coli ATCC 8739)的抗菌性能,以及整理前后复合织物的防水透湿及剥离强度等户外服装面料主要服用性能的变化。研究表明,采用新的DF纳米银抗菌剂添加整理工艺,方法简便,生产可行,且面料的抗菌性能显著提高,整理对复合面料原有的防水透湿及剥离强度影响较小。     

多孔绵材料层对防水透湿复合织物性能的影响

为开发新型防水透湿保暖型层压复合织物,选用多孔绵、热塑性聚氨酯（TPU）薄膜,以机织物为面层,摇粒绒为基材,利用湿固化聚氨酯热熔胶（PUR）黏合剂,通过2 或3 次层压复合试制系列复合织物样品。观察并分析了含多孔绵材料层复合织物横截面形貌结构,研究了多孔绵材料对层压复合织物防水、透湿、保暖等主要功效的影响,同时分析了多孔绵膜层压复合织物的剥离强度。结果表明,所制备的多孔绵膜层压复合织物在防水、透湿、剥离强度等基本不变的情况下,保暖率提高了0%左右,基本解决在极地寒域服装面料保暖性能不足的问题。     

Investigation on permeability and moisture management properties of different denim fabrics after repeated laundering

The physiological comfort determined by air permeability and moisture management properties of fabrics is influenced by various constructional parameters of the fabric which give woven fabric a porous structure. Evaporation of sweat during wear has the potential to cool the body besides restricting the additional weight of sweat being absorbed by the fabric. In this study, comfort characteristics of denim fabrics with different weft yarn of cotton, polyester and core spun Lycra have been discussed. Effect of enzyme washing and repeated laundering on air permeability, moisture management and drying rate has also been discussed. It was observed that air permeability and water vapour permeability of unwashed denim fabrics with cotton weft yarn are significantly higher than the fabric with polyester and Lycra cotton weft yarns. The wetting time is higher for cotton and Lycra cotton yarn fabrics. One-way transport index is highest for Lycra cotton weft fabrics and lowest for fabrics with polyester weft. Fabrics with polyester weft yarns show highest spreading rate, spreading radius and drying rate due to better wicking and hydrophobic nature of polyester fibres.     

Waterproof and moisture permeable coating of polyester fabrics using a novel waterborne polyurethane agent modified with silk fibroin and polyvinylpyrrolidone

A novel waterproof and moisture-permeable coating agent was prepared by modifying a waterborne polyurethane (WPU) agent with silk fibroin (SF) and polyvinylpyrrolidone (PVP), and the PVP/SF/WPU blended agent was applied in polyester fabric coating to achieve a desirable waterproof and breathable effect. The PVP/SF/WPU film prepared by the novel coating agent was characterized with Fourier transform infrared (FT-IR), scanning electron microscope (SEM), thermogravimetry (TG) and X-ray diffraction (XRD) techniques, and the moisture permeability and water repellency of the PVP/SF/WPU coated polyester fabrics were evaluated. The results showed that the thermostability of the blended film was increased compared to the single WPU film, and the compatibility of SF and polyurethane was improved with adding PVP component; the moisture permeability and waterproof of the PVP/SF/WPU coated polyester fabrics were improved significantly. The optimized recipe of the PVP/SF/WPU-coating agent was as follows: 10 wt.%SF (with particle size of 5 μm), 4 wt.% PVP, 4 wt.% cross-linking agent TF694A, and 2 wt.% Thickener TF601. The water vapor transmission rate and hydrostatic pressure value of the PVP/SF/WPU coated polyester fabric reached 5,031 g/ (m² 24 h) and 493 mm H₂O, respectively. The physical and mechanical properties of the coated fabric were not considerably affected.     

纳米二氧化硅改性水性聚氨酯防水透湿涂层织物的制备及其性能

为提升水性聚氨酯涂层织物的防水透湿功能,采用R972疏水型气相纳米二氧化硅对水性聚氨酯进行共混改性,以涂层的方式对纯棉针织物进行整理。利用红外光谱仪、扫描电子显微镜和超景深显微镜对纳米二氧化硅水性聚氨酯复合涂层的结构和形貌进行表征。研究了纳米二氧化硅质量分数对织物防水透湿性能的影响。结果表明:疏水型气相纳米二氧化硅可以在水性聚氨酯体系中发挥良好的纳米效应,并且对水性聚氨酯涂层膜的结构并无较大影响;当纳米二氧化硅质量分数为1.5%时,涂层膜的吸水率降低55.4%,涂层织物的透湿量增加54.7%,耐静水压和接触角分别增大86%和131.4%,同时复合涂层的力学性能也得到了显著改善。     

功能性防水透湿涂层织物性能及其影响因素

制造防水透湿织物的方法一般有高密织物生产路线和涂层整理生产路线。介绍了国内外防水透湿织物的开发过程、性能要求、防水透湿整理原理、透湿性的测试及计算方法,并对这两种路线生产的织物的透湿性进行比较;重点分析了亲水型防水透湿涂层织物性能的优越性及影响因素。     

聚四氟乙烯防水透湿层压织物的研制与开发

阐述了研制的聚四氟乙烯防水透湿层压织物生产的技术关键，介绍了该产品的国内外应用和开发概况，认为有必要加强这一高科技产品的研究和开发力度。