粉煤灰在建筑材料领域的应用分析

介绍了粉煤灰的理化性质和建材应用机理,分析了其目前应用于高活性粉煤灰水泥混合材料、绿色高性能高掺量粉煤灰混凝土、高掺量粉煤灰烧结砖、衬砌材料、生产轻集料和空心砌块等建材领域的特点,说明使用粉煤灰作建筑材料不仅能节约资源、降低生产成本和工程造价,而且能够生产出性能优良的建筑材料。     

建筑垃圾、粉煤灰双掺对压制成型水泥基材料性能影响的研究

针对建筑垃圾、粉煤灰双掺在压制成型水泥基材料的应用进行研究,探索了建筑垃圾取代全部河砂、粉煤灰以不同掺量取代水泥时对水泥基材料强度和耐久性的影响规律。研究结果表明:在建筑垃圾取代全部河砂的前提下,掺有粉煤灰的水泥基材料强度随粉煤灰掺量的增加而降低;随着养护龄期的延长,水泥基材料的强度增长率随着粉煤灰掺量的增加呈增加趋势。在耐久性能方面,粉煤灰掺量≤50%时,满足D100的抗冻等级指标,掺量达到66.7%时,只能满足D50的抗冻等级指标。     

矿渣与粉煤灰掺量对高延性水泥基复合材料力学性能与应变硬化特性的影响

高延性水泥基复合材料(High Ductility Cementitious Composites,HDCC)是指在弯曲和拉伸荷载作用下具有应变硬化特性的水泥基复合材料,具有单轴拉伸延性好,耐久性能优异等优点。在材料设计中用大掺量的粉煤灰来替代水泥,以实现更加优异的高延性。本文研究了在聚乙烯醇(polyvinyl alcohol,PVA)纤维体积掺量为1.2%和1.4%时,同时掺入高炉矿渣与粉煤灰制备高延性水泥基复合材料,通过改变高炉矿渣与粉煤灰的掺量,得到试件的抗压强度、抗折强度与弯曲韧性,用以对比矿渣与粉煤灰不同质量比例对高延性水泥基复合材料力学性能、弯曲韧性和表面裂纹特征的影响规律。结果显示,当矿渣和粉煤灰掺量分别为总胶凝材料质量的40%和10%时,试件呈现出良好的应变硬化与多缝开裂特性,最大挠度达到10.79mm,极限拉应变为1.26%,裂纹数量达到14条。表明了矿渣的掺入有利于在保证高延性水泥基复合材料具有应变硬化特性的前提下,可以有效提高高延性水泥基复合材料中的强度和弯曲韧性,对于此类材料的工程应用十分有益。     

生产优质高掺量粉煤灰水泥的技术途径

以一立窑水泥厂的生产实际为例,论述生产优质高掺量粉煤灰水泥的技术途径。采用低铁、高硫配方、应用串级粉磨工艺、掺加高温煅烧石膏是提高粉煤灰掺量,改善水泥性能的有效措施。     

高掺量粉煤灰水泥的研制

粉煤灰水泥早期强度低,加之磨细粉煤灰供应不足,妨碍了它的生产和应用。国家标准规定:无筋干硬性砼和砂浆中,粉煤灰不宜超过40％。采用复合外加剂,能提高原状粉煤灰的掺量及早期强度,配制出>40％的高掺量粉煤灰水泥。试验证明,掺30％～50％的粉煤灰水泥在     

粉煤灰影响海水海洋骨料水泥基材料抗压强度试验研究

通过试验测定不同粉煤灰掺量下的海水水泥净浆、海水海砂砂浆以及海水海洋骨料混凝土的抗压强度,研究粉煤灰掺量对海水海洋骨料水泥基材料抗压强度的影响。试验结果表明,随着粉煤灰掺量的增加,海水水泥净浆和海水海砂砂浆的抗压强度逐渐降低,海水海洋骨料混凝土抗压强度表现为先增大后减小。粉煤灰掺量对海水海洋骨料水泥基材料抗压强度的影响规律与粉煤灰掺量对淡水河砂水泥基材料抗压强度的影响规律基本一致,但影响程度略小于淡水河砂水泥基材料。     

低等级粉煤灰的活化及应用研究

采用物理活化与化学活化相结合的高效复合活化技术对低等级粉煤灰进行活化可得到高活性粉煤灰,该粉煤灰广泛应用于生产高掺量粉煤灰水泥、新型墙体材料、干混砂浆及高性能绿色混凝土中。     

水泥-膨胀剂-粉煤灰复合胶凝材料膨胀与强度发展的协调性研究

研究了水泥-膨胀剂二元复合胶凝材料和水泥-膨胀剂-粉煤灰三元复合胶凝材料,这两种胶凝材料可以用于制备具有良好体积稳定性的高性能膨胀混凝土。研究表明:存在一个最优辅助胶凝材料掺量组合,在此条件下胶凝材料具有良好的膨胀与强度的协调性,在水泥-膨胀剂体系中,膨胀剂掺量范围在6%~12%,其中掺6%~8%适用于配制补偿收缩混凝土,掺8%~12%适用于填充性混凝土。在水泥-膨胀剂-低钙粉煤灰体系中,CSA合理掺量范围为8%~12%;在水泥-膨胀剂-高钙粉煤灰体系中,合理掺量范围是6%~8%。粉煤灰的掺入可以削减由于膨胀剂过量而导致过高的限制膨胀率,从而避免由此造成的膨胀破坏现象,低钙粉煤灰的作用优于高钙粉煤灰。     

银川地区粉煤灰水泥土的力学特性试验研究

针对银川周边高矿化度湖泊相软土地基水泥土桩法处理问题,在软土天然含水量下,固定水泥掺量,应用搅拌法制备边长70.7 mm的立方体试件,标准条件养护,通过SANS万能材料试验机测定试件的强度和变形,通过扫描电子显微镜SEM进行微观结构分析,试验研究高掺量粉煤灰水泥土的应力-应变关系,强度随粉煤灰掺量、含水量、胶水比和龄期等因素变化的规律,并进行相关性分析,揭示作用机理。研究表明:在高掺粉煤灰条件下,水泥土的强度显著提高,且后期有很高的增长率,粉煤灰与水泥的最优掺量比约为3,主要作用机理为粉煤灰的水化效应和填充效应;水泥土的强度与粉煤灰掺量、胶水比、含水量之间近似为线性关系,其与胶水比的相关性最好。     

采用激发剂与助磨剂磨制粉煤灰硅酸盐水泥

通过RHJ-(B)激发剂与助磨剂(即：复合外加剂)生产粉煤灰硅酸盐水泥的应用研究,实现以廉价粉煤灰代替矿渣作水泥混合材,且在增加粉煤灰掺量前提下,提高水泥质量和产量,降低电耗,达到预期应用效果,取得了显著经济效益。     

KSC轻质隔墙板施工技术

KSC轻质隔墙板作为一种新型施工材料,拥有轻质、高强、隔音、隔热、防潮、防火等诸多特点,广泛适用于框架、高层、超高层结构建筑分户内隔墙。其采用纤维石、粉煤灰、工业废渣、建筑垃圾等为原材料,实现了资源综合利用;基于传统建材,其减轻了楼房荷载、降低了工程造价,有效增加了实用面积;在施工中安装便捷可提高施工效率。     

建筑固体废弃物治理全生命周期环境影响评价—以废旧粘土砖为例

为定量评价建筑固体废弃物治理的环境影响,基于生命周期评价（LCA）理论和建筑工程环境表现评价系统（BEPAS）,综合考虑废弃物治理过程的环境代价以及再生材料的环境收益,以净环境代价为指标,建立了建筑固体废弃物治理环境影响评价框架。根据实际案例,定量评价了废旧粘土砖几种典型治理方式的环境影响,结果表明:填埋的净环境代价较高,其次是重复利用,而再生利用的代价相对较低;在再生利用方式中,净环境代价从小到大依次为水泥混合料、混凝土砌块原料、免烧砌筑水泥原料、混凝土骨料、烧砖瓦原料,其中烧砖瓦原料的净环境代价为正值,即所得到环境收益不足以弥补其环境代价。     

Manufacture of high heat conductivity resistant clay bricks containing perlite

Different methods have been investigated for achieving heat insulation in the buildings. Manufacturing of high heat conductivity resistant construction materials is an important part of these research efforts. Perlite is an extremely useful material for heat insulation and 70% of the world reserves are located in Turkey. Nearly 65% of the perlite produced today is consumed by the construction industry. Its thermal, lightness, and acoustic insulation properties make perlite an excellent material to be used as lightweight aggregate in brick manufacturing. High heat resistant brick can be produced by adding perlite into the clay in conventional brick manufacturing. In this investigation perlite of Eski?ehir region and clay were collated and fired to form high heat conductivity resistant material. Binding materials such as cement, gypsum, lime, bitumen and clay were used for manufacturing perlite brick. Bricks in standard sizes manufactured at different perlite–clay ratios and unit weight, compressive strength, volume reduction and heat conductivity values were obtained. Then the mixture with the best combination of the properties was determined and cost optimization was described. Results were examined according to combination properties, and specialties of perlite bricks were determined at various weights. As a result, the best mixture was determined as the one containing 30% perlite.     

砂浆掺废弃砖粉的应用研究

废弃砖块在建筑垃圾中有着重要的比重,将废弃砖块磨成细粉资源化再利用是解决建筑垃圾的重要途径。为了提高对建筑垃圾的利用率,文中分析了废弃砖粉的化学成分、吸水率、含水率,并对不同掺量下砖粉的砂浆强度进行了试验,结果显示砖粉的主要化学成分与硅酸盐水泥的基本一致,废弃砖粉可以作为一定的胶凝材料替代部分水泥,掺有废弃砖粉的砂浆对砂浆的延性有一定的改善作用,但是砖粉具有一定的吸水率,随着砖粉粒径的逐渐减小,砖粉的吸水率逐渐增大。     

Potential use of stockpiled circulating fluidized bed combustion ashes in manufacturing compressed earth bricks

There is currently 123 million tons of coal combustion by-products produced in US each year. Among these include fly ash, bottom ash, boiler slag, and flue gas desulphurization material. Of that approximately 40% are utilized as a construction material in cement manufacturing, roadway construction, and others. However, the utilization of some ashes such as those produced by fluidized bed combustion has been limited due to their inherent high sulfate and carbon content. This paper is aimed at the evaluation of the potential use of stockpiled circulating fluidized bed combustion ash (SCFBCA) to develop compressed earth brick (CEB). Laboratory tests were conducted to determine the physical, chemical, and mineralogical properties with respect to SCFBCA. A series of tests were carried out to evaluate the properties of the bricks related to filler and binder types on compressive strength, density, and absorption. Test results indicate that SCFBCA can be used to manufacture CEB. Subordinately, test results may provide a means to reduce a waste disposal problem while providing the brick industry with a new, useful, low cost raw material.     

黏土砖微粉的应用研究

介绍了一种建筑垃圾处理过程中大量黏土砖的资源化利用方法。将建筑垃圾筛分、分选、破碎后得到黏土砖颗粒,利用球磨设备将黏土砖颗粒粉磨半小时后得到微粉,在砂浆、砌块等采用干硬性混凝土为原料的生产中作为掺合料代替部分水泥,通过采用醇胺类激发剂激发黏土砖微粉的活性,提高其后期强度,可提高建筑垃圾的资源化利用率,并降低产品的生产成本。     

蒸压粉煤灰砖的生产工艺研究

实心粘土砖自国家实行限制使用后出现了许多替代产品,粉煤灰砖是较为突出的产品之一。一方面,粉煤灰砖发展前景好,另一方面,粉煤灰排放量急剧增长但利用率低。针对这一问题提出大力发展蒸压粉煤灰砖的生产研究及应用、打造＂绿色建材＂的观点,分析了蒸压粉煤灰砖的原材料选择要点及生产工艺,并从性能、成本、应用及社会效益等方面对其发展前...     

蒸压灰砂多孔砖的研制及应用

介绍蒸压灰砂多孔砖的研制目标和砖型的设计原则,在样砖的基础上进行方案的优化选择;阐述蒸压灰砂多孔砖的生产工艺、成型主机特点、综合性能和部分试验情况,并将蒸压灰砂多孔砖与实心砖的生产成本进行对比分析,总结工程应用经验。     

水泥稳定建筑垃圾的路用性能研究

为节约建筑材料,对水泥稳定建筑垃圾混合料的抗压强度、劈裂强度、抗压回弹模量、抗冻性能等路用技术性能进行了系统的试验研究,结果表明,水泥稳定建筑垃圾具有较高的强度、刚度和较好的抗冻性能,其各项技术性能满足现行规范的要求,可以作为各级公路的底基层或基层材料。     

混凝土多孔砖在漳州生产与应用的调研分析

混凝土多孔砖是以水泥为胶结材料，砂、石等为主要集料，加水搅拌成型，养护制成的一种多排小孔的混凝土砖。本文介绍了制作混凝土多孔砖的原材料、配合比、生产工艺、产品性能及在漳州生产与应用情况的调研分析。