Synthesis of nanocrystalline xCuFe2O4-(1 − x)BiFeO3 magnetoelectric composite by chemical method

xCuFe₂O₄-(1 − x)BiFeO₃ spinel-perovskite nanocomposites with x = 0.1, 0.2, 0.3 and 0.4 were prepared using citrate precursor method. X-ray diffraction (XRD) analysis showed phase formation of xCuFe₂O₄-(1 − x)BiFeO₃ calcined at 500 °C. Transmission electron microscopy (TEM) shows formation of nanocrystallites of xCuFe₂O₄-(1 − x)BiFeO₃ with an average particle size of 40 nm. Variation of dielectric constant and dielectric loss with frequency showed dispersion in the low frequency range. Coercivity, saturation magnetization and squareness have been found to vary with concentration of ferrite phase and annealing temperature due to the increase in crystallite size. Squareness and coercivity increased with an increase in annealing temperature up to 500 °C and then decreased with a further increase in temperature to 600 °C. Magnetoelectric effect of the nanocomposites was found to be strongly depending on the magnetic bias and magnetic field frequency.     

Investigation of BiFeO3 modified PbTiO3-Bi(MgZr)O3-based complex perovskite ceramics

Bismuth containing crystalline solutions of (1 − x)Bi(MgZr)_0.5O₃-xPbTiO₃ (BMZ-PT) and [(BiFeO₃)_y − (BiMg_0.5Zr_0.5)_1−y]_x − [PbTiO₃]_1−x (BMZ-BF-PT) have been developed using conventional ceramic technology. X-ray diffraction analysis reveals that both the systems possess a perovskite structure, in which tetragonal to rhombohedral phase transformation appears for x = 0.55 in BMZ-PT and y = 0.20 in BMZ-BF-PT systems. SEM photographs reveal a uniform grain size distribution in the solid solution matrix with the presence of ferroelectric domains in few of the compositions. Ferroelectric hysteresis (polarization-electric field, P-E) loops reveal that increase in BiFeO₃ in BMZ-PT systems results in a decrease in residual polarization of the system with change and distortion in the shape of the (P-E) loops.     

Dielectric properties of (1−x)(Mg0.95Co0.05)TiO3-xCaTiO3 ceramic system at microwave frequency

The microwave dielectric properties and the microstructures of the (1−x)MgTiO₃-xCaTiO₃ ceramic system were investigated. With partial replacement of Mg by Co, dielectric properties of the (1−x)(Mg_0.95Co_0.05)TiO₃-xCaTiO₃ ceramics can be promoted. The microwave dielectric properties are strongly correlated with the sintering temperature. At 1275°C, the 0.95(Mg_0.95Co_0.05)TiO₃-0.05CaTiO₃ ceramics possesses excellent microwave dielectric properties: a dielectric constant ε_r of 20.3, a Q×f value of 107 000 ( at 7 GHz) and a τ_f value of −22.8 ppm/°C. By appropriately adjusting the x value in the (1−x)(Mg_0.95Co_0.05)TiO₃-xCaTiO₃ ceramic system, zero τ_f value can be achieved. With x=0.07, a dielectric constant ε_γ of 21.6, a Q×f value of 92 000 (at 7 GHz) and a τ_f value of −1.8 ppm/°C was obtained for 0.93(Mg_0.95Co_0.05)TiO₃-0.07CaTiO₃ ceramics sintered at 1275°C for 4 h.     

Effect of Nb substitution on the structural, dielectric and magnetic properties of multiferroic BiFe1−xNbxO3 ceramics

Polycrystalline BiFe_1−xNb_xO₃ ceramics have been synthesized by standard solid-state reaction method. The effect of Nb substitution on the dielectric, magnetic and magnetoelectric properties of the BiFeO₃ multiferroic perovskite was studied. X-ray diffraction pattern revealed that all the samples with x = 0.00-0.10 showed rhombohedral perovskite structure. We obtained single phase upto doping concentration of x = 0.05 and with further increase in Nb concentration, some impurity peaks appeared. An anomaly in the dielectric constant (?) and dielectric loss (tan (δ)) in the vicinity of the antiferromagnetic Néel temperature (T_N) was observed. Nb substitution reduced the antiferromagnetic Néel temperature (T_N) in BiFe_1−xNb_xO₃. Proper amount of Nb could decrease the dielectric loss. Magnetic hysteresis loops measured at 5 K/300 K and temperature dependent magnetization curves indicated ferromagnetism in Nb substituted BiFeO₃ ceramics. The room temperature magnetic moment was found to increase with increase in Nb concentration. The dependence of dielectric constant on the magnetic field is an evidence of magnetoelectric coupling in BiFe_1−xNb_xO₃ ceramics.     

Effect of BiFeO3 additions on the dielectric and piezoelectric properties of (K0.44Na0.52Li0.04)(Nb0.84Ta0.1Sb0.06)O3 ceramics

(1 − x) (K_0.44Na_0.52Li_0.04)(Nb_0.84Ta_0.1Sb_0.06)O₃ − x BiFeO₃ (x = 0, 0.002, 0.004, 0.006, 0.008, 0.01) lead-free piezoelectric ceramics were prepared by the conventional ceramic processing. The compositional dependence of the phase structure and the electrical properties of the ceramics were studied. A morphotropic phase boundary between the orthorhombic and tetragonal phases was identified in the composition range of 0.004 < x < 0.006. The ceramics near the morphotropic phase boundary exhibit a strong compositional dependence and enhanced piezoelectric properties. The ceramics with 0.6 mol.% BiFeO₃ exhibit good electrical properties (d₃₃ ∼ 246 pC/N, k_p ∼ 43%, T_c ∼ 285 °C, ?_r ∼ 1871, and tan δ ∼ 1.96%). These results show that the (1 − x) (K_0.44Na_0.52Li_0.04)(Nb_0.84Ta_0.1Sb_0.06)O₃ − x BiFeO₃ ceramic is a promising lead-free piezoelectric material for applications in different devices.     

Enhanced multiferroic properties and tunable magnetic behavior in multiferroic BiFeO3-Bi0.5Na0.5TiO3 solid solutions

A series of multiferroic (1−x)BiFeO₃−x(Bi_0.5Na_0.5)TiO₃ (BF-BNT) (x = 0 − 0.6) solid solution ceramics were prepared by a sol-gel method. The XRD results show that increasing BNT content induce a gradual phase transformation from rhombohedral to pseudocubic structure near x = 0.4. Compared with pure BiFeO₃, superior multiferroic properties are obtained for x = 0.3 with remnant polarization P_r = 1.49 μC/cm² and saturated magnetization M_s = 0.51 emu/g. Importantly, the paramagnetic (PM) to ferromagnetic (FM) transition is observed for the solutions, and the Curie temperature (T_C) can be tuned by varying the content of BNT. This observed FM ordering is discussed in terms of the possible existence of the long-range superexchange interaction of Fe³⁺-O-Ti-O-Fe³⁺ in the chemically ordered regions.     

Structural studies of BiFeO3 modified BMZ-PT ceramics

Bismuth perovskites have been attracting attention as a family of piezoelectric ceramics in place of the widely used Pb (Zr, Ti)O₃ (PZT) system. The advantages of bismuth perovskites over PZT are environmentally more-friendly materials, a higher mechanical strength and Curie temperature. Most recently BiMgZrO₃-PbTiO₃ has been reported to be high temperature morphotropic phase boundary (MPB) piezoelectric with appreciably good ferroelectric and piezoelectric properties.Bismuth containing crystalline solutions [(BiMgZrO₃)_1−y-(BiFeO₃)_y]_x-(PbTiO₃)_1−x, (BMZ-BF-PT) have been synthesized by high temperature solid-state reaction technique. The crystalline symmetry varied with the composition, indicating good solid-state solubility of BMZ and BF with PT. X-ray diffraction (XRD) reveals that BMZ-BF-PT has a single-phase perovskite structure. The Morphotropic Phase Boundary (MPB) of BMZ-PT system lies in the region x = 0.55 to x = 0.6 which is supported by the transformation from tetragonal to rhombohedral phase. The SEM photographs reveal the uniform distribution of grains in the matrix. Variation of dielectric parameters with frequency (at room temperature) exhibit typical dielectric behavior for all compositions.     

Electrical conduction, dielectric behavior and magnetoelectric effect in (x)BaTiO3 + (1 − x)Ni0.94Co0.01Mn0.05Fe2O4 ME composites

Electrical and magnetoelectric properties of magnetoelectric (ME) composites containing barium titanate as electrical component and a mixed Ni-Co-Mn ferrite as the magnetic component are reported. The ME composites with a general formula (x)BaTiO₃ + (1 − x)Ni_0.94Co_0.01Mn_0.05Fe₂O₄ where x varies as 0, 0.55, 0.70, 0.85 and 1 were prepared by standard double sintering ceramic method. The presence of both the phases was confirmed by X-ray diffraction technique. The dc resistivity was measured as a function of temperature. The variation of dielectric constant (?) and loss tangent (tan δ) with frequency (100 Hz-1 MHz) and with temperature was studied. The conduction is explained on the basis of small polaron model based on ac conductivity measurements. The static value of ME conversion factor i.e. dc (ME)_H was studied as function of intensity of magnetic field. The changes were observed in dielectric properties as well as ME effect as the molar ratio of the components was varied. A maximum value of ME conversion factor of 610 μV/cm Oe was observed in the case of a composite containing 15 mol% ferrite phase.     

Microstructure and microwave dielectric characteristics of (1 − x)Ba(Zn1/3Ta2/3)O3-xBaTi4O9 ceramics

(1 − x)Ba(Zn_1/3Ta_2/3)O₃-xBaTi₄O₉ (0.1 ≤ x ≤ 0.85) composites are prepared by mixing 1150 °C-calcined BaTi₄O₉ with 1150 °C-calcined Ba(Zn_1/3Ta_2/3)O₃ powders. The crystal structure, microwave dielectric properties and sinterabilites of the (1 − x)Ba(Zn_1/3Ta_2/3)O₃-xBaTi₄O₉ ceramics have been investigated. X-ray diffraction patterns reveal that BaTi₄O₉, ordered and disordered Ba(Zn_1/3Ta_2/3)O₃ phases exist independently over the whole compositional range. The sintering temperatures of (1 − x)Ba(Zn_1/3Ta_2/3)O₃-xBaTi₄O₉ ceramics are about 1240 - 1320 °C and obviously lower than those of Ba(Zn_1/3Ta_2/3)O₃ ceramics. The dielectric constants (?_r) and the temperature coefficient of resonant frequency (τ_f) of (1 − x)Ba(Zn_1/3Ta_2/3)O₃-xBaTi₄O₉ ceramics increase with the increase of BaTi₄O₉ content. Nevertheless, the bulk densities and the quality values (Q × f) of (1 − x)Ba(Zn_1/3Ta_2/3)O₃-xBaTi₄O₉ ceramics increase with the increase of Ba(Zn_1/3Ta_2/3)O₃ content. The results are attributed to the higher density and quality value of Ba(Zn_1/3Ta_2/3)O₃ ceramics, the better grain growth, and the densification of sintered specimens added a small BaTi₄O₉ content. The (1 − x)Ba(Zn_1/3Ta_2/3)O₃-xBaTi₄O₉ ceramic with x = 0.1 sintered at 1320 °C exhibits a ?_r value of 31.5, a maximum Q × f value of 68500 GHz and a minimum τ_f value of 4.1 ppm/°C.     

Optimized microwave dielectric properties of Co- and Ca-substituted Mg0.6Zn0.4TiO3

The system of (1 − y)(Mg_0.6Zn_0.4)_1−xCo_xTiO₃-yCaTiO₃ was investigated to optimize its microwave dielectric properties by adopting appropriate contents of Co and Ca and by controlling sintering conditions. The effect of Co substitution was to enhance densification and Qf value, while the addition of CaTiO₃ resulted in increases of dielectric constant and TCF. As an optimal compositions, 0.93(Mg_0.6Zn_0.4)_0.95Co_0.05TiO₃-0.07CaTiO₃ successfully demonstrated a dielectric constant of 23.04, a Qf of 79,460 GHz and a TCF value of +1.4 ppm/°C after firing at a relatively lower sintering temperature of 1200 °C. The increase of sintering temperature beyond 1200 °C tended to degrade overall microwave dielectric properties presumably due to Zn volatilization as evidenced by the presence of a Zn-deficient phase (MgTi₂O₅) at 1400 °C. An attempt to establish the correlation between microstructure characteristics and dielectric properties was made in this dielectric system where the extensive range of firing temperature up to 1400 °C was evaluated.     

Dielectric properties of B2O3-doped (1 − x)LaAlO3-xSrTiO3 ceramic system at microwave frequency

The effects of B₂O₃ addition on the microwave dielectric properties and the microstructures of (1−x)LaAlO₃-xSrTiO₃ ceramics prepared by conventional solid-state routes have been investigated. Doping with 0.25 wt.% B₂O₃ can effectively promote the densification and the microwave dielectric properties of (1−x)LaAlO₃-xSrTiO₃ ceramics. It is found that LaAlO₃-SrTiO₃ ceramics can be sintered at 1400°C due to the liquid phase effect of a B₂O₃ addition observed by scanning electronic microscopy (SEM). The dielectric constant as well as the Q×f value decreases with increasing B₂O₃ content. At 1460°C, 0.46LaAlO₃-0.54SrTiO₃ ceramics with 0.25 wt.% B₂O₃ addition possesses a dielectric constant (ε_r) of 35, a Q×f value of 38,000 (at 7 GHz) and a temperature coefficients of resonant frequency (τ_f) of −1 ppm/°C.     

Locating the normal to relaxor phase boundary in Ba(Ti1−xHfx)O3 ceramics

In this article, we report our studies on the relaxor behavior of Ba(Ti_1−xHf_x)O₃ ceramics, made with close compositions between 0.20 ≤ x ≤ 0.30, to locate the hafnium concentration boundary for the normal to relaxor crossover. X-ray diffraction followed by Rietveld refinement shows the occurrence of single-phase cubic structure for the synthesized Ba(Ti_1−xHf_x)O₃ ceramics. Temperature and frequency dependence of the real (?′) and imaginary (?″) parts of the dielectric permittivity has been studied in the temperature range of 90-350 K at frequencies of 0.1, 1, 10, and 100 kHz. A diffuse phase transition accompanying frequency dispersion is observed in the permittivity versus temperature plots revealing the occurrence of relaxor ferroelectric behavior. The T_m verses Hf concentration plot shows a discontinuous jump and change in the slope at x = 0.23. Quantitative characterization based on phenomenological models has also been presented. The plausible mechanism of the relaxor behavior has been discussed. Substitution of Hf⁴⁺ for Ti⁴⁺ in BaTiO₃ reduces the long-range polar ordering yielding a diffuse ferroelectric phase transition.     

Dielectric properties of Ba(Ti1 − xZrx)O3 solid solutions

This paper reports the structural and dielectric properties of Ba(Ti_1 − xZr_x)O₃ (x = 0-0.3) ceramics. Single-phase solid solutions of the samples were determined by X-ray diffraction. Microscopic observation by scanning electron microscope revealed dense, single-phase microstructure with large grains (20-60 μm). The evolution of dielectric behavior from a sharp ferroelectric peak (for x ≤ 0.08) to a round dielectric peak (for 0.15 ≤ x ≤ 0.25) with pinched phase transitions and successively to a ferroelectric relaxor (for x = 0.3) was observed with increasing Zr concentration. Compared with pure BaTiO₃, broaden dielectric peaks with high dielectric constant of 25,000-40,000 and reasonably low loss (tanδ: 0.01-0.06) in the Ba(Ti_1 − xZr_x)O₃ ceramics have been observed, indicating great application potential as a dielectric material.     

SmAlO3-modified (K0.5Na0.5)0.95Li0.05Sb0.05Nb0.95O3 lead-free ceramics with a wide sintering temperature range

Lead-free ceramics (1 − x)(K_0.5Na_0.5)_0.95Li_0.05Sb_0.05Nb_0.95O₃-xSmAlO₃ (KNLNS-xSA) were prepared by conventional sintering technique. The phase structure, dielectric and piezoelectric properties of the ceramics were investigated. All compositions show a main perovskite structure, exhibiting room-temperature symmetries of tetragonal at x ≤ 0.0075, of pseudo-cubic at x = 0.0100. The Curie temperature of KNLNS-xSA ceramics decreases with increasing SmAlO₃ content. Moreover, the addition of SmAlO₃ can effectively broaden the sintering temperature range of the ceramics. The KNLNS-xSA ceramic with x = 0.0050 has an excellent electrical behavior of piezoelectric coefficient d₃₃ = 226 pC/N, planar mode electromechanical coupling coefficient k_p = 38%, dielectric loss tan δ = 3.0%, mechanical quality factor Q_m = 60, and Curie temperature T_C = 327 °C, suggesting that this material could be a promising lead-free piezoelectric candidate for piezoelectric applications.     

Dielectric and pyroelectric anisotropy in melt-quenched BaBi2(Nb1 − xVx)2O9 ceramics

The (0 0 l) textured BaBi₂(Nb_1 − xV_x)₂O₉ (where x = 0, 0.03, 0.07, 0.1 and 0.13) ceramics were fabricated via the conventional melt-quenching technique followed by high temperature heat-treatment (800-1000 °C range). The influence of vanadium content and sintering temperature on the texture development and relative density were investigated. The samples corresponding to the composition x = 0.1 sintered at 1000 °C for 10 h exhibited the maximum orientation of about 67%. The Scanning electron microscopic studies revealed the presence of platy grains having the a-b planes perpendicular the pressing axis. The dielectric constant and the pyroelectric co-efficient values in the direction perpendicular to the pressing axis were higher. The anisotropy in the dielectric constant is about 100 (at 100 kHz) at the dielectric maximum temperature and anisotropy in the pyroelectric co-efficient is about 50 μC cm⁻² °C⁻¹ in the vicinity of pyroelectric anomaly for the sample corresponding to the composition x = 0.1 sintered at 1000 °C. Higher values of the dielectric loss and electrical conductivity were observed in the direction perpendicular to the pressing axis which is attributed to the high oxygen ion conduction in the a-b planes.     

(1 − x)PNZ-xBT ceramics derived from mechanochemically synthesized powders

Nanosized (1−x)Pb(Zn_1/3Nb_2/3)O₃-xBaTiO₃ (PZN-BT, x=0.05, 0.10, 0.15, 0.20, 0.25, and 0.30) powders were synthesized directly from their corresponding oxide mixture via a high-energy ball milling process. Almost single phase was achieved in the composition range of PZN-BT. The grain size estimated from SEM observation was about 50 nm, being in good agreement with that (20 nm) calculated from XRD patterns. PZN-BT ceramics were also obtained by sintering the synthesized powders at 1050°C for 1 h. The grain size of the final ceramics decreases from 4.5 to 1.2 μm as BT content increases from 0.05 to 0.30. The properties, such as microstructure, lattice constant, phase composition, dielectric constant as a function of composition of the PZN-BT ceramics, were investigated and discussed.     

Influence of sintering temperature on piezoelectric properties of (K0.5Na0.5)NbO3-LiNbO3 lead-free piezoelectric ceramics

Lead-free piezoelectric ceramics (1 − x)(K_0.5Na_0.5)NbO₃-xLiNbO₃ have been synthesized by traditional ceramics process without cold-isostatic pressing. The effect of the content of LiNbO₃ and the sintering temperature on the phase structure, the microstructure and piezoelectric properties of (1 − x)(K_0.5Na_0.5)NbO₃-xLiNbO₃ ceramics were investigated. The result shows that the phase structure transforms from the orthorhombic phase to tetragonal phase with the increase of the content of LiNbO₃, and the orthorhombic and tetragonal phase co-exist in (K_0.5Na_0.5)NbO₃-LiNbO₃ ceramics when the content of LiNbO₃ is about 0.06 mol. The sintering temperature of (1 − x)(K_0.5Na_0.5)NbO₃-xLiNbO₃ decreases with the increase of the content of LiNbO₃. The optimum composition for (1 − x)(K_0.5Na_0.5)NbO₃-xLiNbO₃ ceramics is 0.94(K_0.5Na_0.5)NbO₃-0.06LiNbO₃. The optimum sintering temperature of 0.94(K_0.5Na_0.5)NbO₃-0.06LiNbO₃ ceramics is 1080 °C. Piezoelectric properties of 0.94 (K_0.5Na_0.5)NbO₃-0.06LiNbO₃ ceramics under the optimum sintering temperature are piezoelectric constant d₃₃ of 215 pC/N, planar electromechanical coupling factor k_p of 0.41, thickness electromechanical coupling factor k_t of 0.48, the mechanical quality factor Q_m of 80, the dielectric constant of 530 and the Curie temperature T_c = 450 °C, respectively. The results indicate that 0.94(K_0.5Na_0.5)NbO₃-0.06LiNbO₃ piezoelectric ceramics is a promising candidate for lead-free piezoelectric ceramics.     

Modified tunable dielectric properties by addition of MgO on BaZr0.25Ti0.75O3 ceramics

Phase composition, microstructure and tunable dielectric properties of (1 − x)BaZr_0.25Ti_0.75O₃-xMgO (BZTM) composite ceramics fabricated by solid-state reaction were investigated. It was found Mg not only existed in the matrix as MgO, there was also trace amount of Mg²⁺ ions dissolved in the BZT grains, which led to Curie temperature of the BZTM composites ceramics shifting to below −100 °C. Dielectric permittivity of the BZTM composite ceramics was reduced from thousands to hundreds by manipulating the content of MgO. Johnson's phenomenological equation based on Devonshire's theory was used to describe the nonlinear dielectric permittivity of the ceramics with increasing applied DC field. With increasing content of MgO, anharmonic constant α_(T) increased monotonously. Dielectric permittivity was 672, while dielectric tunability was as high as 30.0% at 30 kV/cm and dielectric loss was around 0.0016 for the 0.6BaZr_0.25Ti_0.75O₃-0.4MgO sample at 10 kHz and room temperature.     

Synthesis, low-temperature sintering and the dielectric properties of the ZnO-(1 − x)TiO2-xSnO2 (x = 0.04-0.2)

ZnO-(1 − x)TiO₂-xSnO₂ (x = 0.04-0.2) ceramics were prepared by conventional mixed-oxide method combined with a chemical processing. Fine particle powders were prepared by chemical processing to activate the formation of compound and to improve the sinterability. One wt.% of V₂O₅ and B₂O₃ with the mole ratios of 3:1 were used to lower the sintering temperature of ceramics. The effect of Sn content on phase structure and dielectric properties were investigated. The results show that the substituting Sn for Ti accelerates the hexagonal phase transition to cubic phase, and an inverse spinel structure Zn₂(Ti_1−xSn_x)O₄ solid solution forms. The best dielectric properties obtained at x = 0.12. The ZnO-0.88TiO₂-0.12SnO₂ ceramics sintered at 900 °C exhibit a good dielectric property: ?_r = 29 and tan δ = 9.86 × 10⁻⁵. Due to their good dielectric properties, low firing characteristics, ZnO-(1 − x)TiO₂-xSnO₂ (x = 0.04-0.2) can serve as the promising microwave dielectric capacitor.     

New dielectric material system of x(Mg0.95Zn0.05Ti)O3-(1 − x)Ca0.8Sm0.4/3TiO3 at microwave frequency

The microstructures and the microwave dielectric properties of the x(Mg_0.95Zn_0.05)TiO₃-(1 − x) Ca_0.8Sm_0.4/3TiO₃ ceramic system were investigated. In order to achieve a temperature-stable material, we studied a method of combining a positive temperature coefficient material with a negative one. Ca_0.8Sm_0.4/3TiO₃ has dielectric properties of dielectric constant ε_r ~ 120, Q × f value ~ 13,800 GHz and a large positive τ_f value ~ 400 ppm/°C. (Mg_0.95Zn_0.05)TiO₃ possesses high dielectric constant (ε_r ~ 16.21), high quality factor (Q × f value ~ 210,000 at 9 GHz) and negative τ_f value (− 59 ppm/°C). Sintering at 1300 °C with x = 0.9, 0.9(Mg_0.95Zn_0.05Ti)O₃ − 0.1 Ca_0.8Sm_0.4/3TiO₃ has a dielectric constant (ε_r) of 22.7, a Q × f value of 124,000 GHz and a temperature coefficient of resonant frequency (τ_f) of − 6.3 ppm/°C.