硅对热轧低碳贝氏体钢组织和力学性能的影响

对不同硅含量的低碳贝氏体钢进行轧制,对轧制后的试样进行组织检验和拉伸试验,分析了该钢的显微组织和力学性能。结果表明:Si含量从1.0 wt%增加到1.5 wt%时,试样的微观组织基本相同,均为粒状贝氏体+M/A岛,其屈服强度、抗拉强度略有增加,伸长率基本相同,强度的增加主要来源于Si的固溶强化作用。Si含量从1.5wt%增加到2.0wt%时,该钢的显微组织明显变化,含硅2.0 wt%钢的显微组织为粒状贝氏体+板条马氏体+等轴铁素体,该钢的屈服强度及抗拉强度显著增加,但相比于含Si量1.5wt%的钢,伸长率、强塑积均下降,强度的提高主要是固溶强化、相变强化等的综合作用。比较三种低碳贝氏体钢,若只考虑钢的强度因素,则Si的添加量应达2.0 wt%;若只考虑钢种塑性及强塑积,则Si的添加量应为1.5 wt%。     

1Cr18Ni11Si4AlTi双相不锈钢的固溶组织与性能

对1Cr18Ni11Si4AlTi双相不锈钢进行了不同温度的固溶热处理试验,对材料的组织和性能与固溶处理之间的关系和影响规律进行了研究。结果表明:随着固溶温度的升高,材料中的析出相逐渐溶解,铁素体含量增加,屈服强度随着铁素体含量增加而提高,材料硬度呈现先降后升的趋势,1050 ℃固溶处理时硬度最低,当固溶温度达到和超过1100 ℃时,其显微组织逐渐粗化,铁素体含量明显增加,材料的屈服强度明显提高。     

成分差异对低成本热轧双相钢组织性能的影响

实验室真空感应炉冶炼C-Mn钢、Nb-Ti钢和含Cr钢,轧后采用三段式冷却工艺试制低成本热轧双相钢,分析了成分差异对热轧双相钢组织性能的影响。结果表明,三种成分均可得到铁素体和马氏体双相组织;三者比较而言,C-Mn钢的铁素体含量较高,塑性好,但强度级别低;由于Nb-Ti钢中微合金元素Nb的固溶拖曳作用抑制相变,铁素体含量低,但细晶强化作用提高了钢板的屈服强度,屈强比增加;含Cr钢显微组织中马氏体含量最高,抗拉强度随之增高,屈强比较Nb-Ti钢降低。     

氮对高电阻率高导磁不锈钢组织和性能的影响

采用SEM、EDS、拉伸及冲击试验,研究了氮对高电阻率高导磁不锈钢组织和性能的影响。结果表明,氮能显著扩大奥氏体相区,在1000℃保温1h油淬并在620℃回火后,含氮0.09%的试样与不含氮的试样相比在铁素体基体上出现少量马氏体,0.18%氮使原单相铁素体变为铁素体+马氏体双相组织,并且硬脆的σ相消失;添加0.09%和0.18%氮元素材料的强度和硬度均较未添加前有明显提高,材料的力学性能特别是冲击韧性得到显著改善。     

Si含量对DP-600级别热轧双相钢组织及性能的影响

采用光学显微镜、扫描电镜、纳米力学探针、透射电镜等技术对不同Si含量(0.03%和1.077%)的DP600级别热轧双相钢单向拉伸过程组织特征进行研究,分析了Si含量对相同工艺条件下双相钢显微组织特征,以及塑性变形过程中强化相与基体协调变形行为的影响。结果表明:Si作为一种铁素体形成元素,能够增加铁素体的形核率,具有细化铁素体晶粒的作用,可增加铁素体体积分数,分割并细化马氏体。Si含量的增加促进了C元素向马氏体富集,提升了单位体积马氏体的碳含量,使部分板条马氏体转变为孪晶马氏体,增加了马氏体硬度。由于Si对铁素体的净化作用,高Si实验钢中位错在铁素体中滑移时不易受到碳化物的钉扎作用。因此在相同工艺条件下,Si含量的增加可以提高双相钢的抗拉强度,提高硬度,降低屈强比。     

高品质热轧双相钢的开发

为了提高热轧双相钢的品质，研究了化学成分、轧制工艺、冷却工艺和不同季节水温等参数对热轧双相钢组织和性能的影响。结果表明，无Si成分设计显著提高了热轧双相钢的表面质量；较低的终轧温度和中间保温温度有利于获得更为细小的铁素体组织和弥散的马氏体组织；低的卷取温度（280 ℃）可以获得铁素体+马氏体双相组织；冷却水水温的降低显著提高马氏体含量并提高双相钢的强度。基于上述研究，邯钢实现了系列热轧双相钢的稳定生产，双相钢制作的汽车车轮性能良好。     

沿海建筑用00Cr25Ni7Mo4N双相不锈钢的热处理与性能

采用光学显微镜、扫描电镜、拉伸试验机和电化学工作站等,研究了固溶温度对00Cr25Ni7Mo4N双相不锈钢显微组织、力学性能和耐腐蚀性能的影响。结果表明,热轧和固溶温度为1025～1200℃时双相钢的显微组织都为铁素体+奥氏体双相组织,随着固溶温度升高,双相钢中α相含量不断增大,γ相含量不断减小,在固溶温度为1175℃时,双相钢中α∶γ相比例接近于1∶1;相较于热轧态双相钢,不同温度固溶处理后,双相钢的抗拉强度、规定塑性延伸强度和洛氏硬度有不同程度减小,而断后伸长率、断面收缩率和冲击吸收能量有不同程度增加;在固溶温度为1175℃时,双相钢的抗拉强度和规定塑性延伸强度较高,而断后伸长率、断面收缩率和冲击吸收能量都达到最大值。当固溶温度为1175℃时,双相钢的腐蚀电位最大、腐蚀电流密度最小,容抗弧半径和钝化膜电阻最大,弥散系数最接近于1,具有最佳的耐蚀性能。     

固溶处理对桥梁缆索用钢S31803组织和性能的影响

采用OM、XRD、常温力学性能测试等手段,研究了不同固溶处理对桥梁缆索用S31803双相不锈钢组织及力学性能的影响。结果表明:经950~1150℃固溶处理,随着温度的升高,S31803双相不锈钢组织中铁素体相含量不断增加,奥氏体相含量不断减少,当固溶温度为1050℃时,铁素体相/奥氏体相接近1∶1,组织晶粒最为细小。S31803双相不锈钢的抗拉强度、屈服强度、伸长率,随固溶温度升高均呈现先升高后降低的变化趋势。1050℃固溶保温2 h处理试样的抗拉强度765 MPa、屈服强度582 MPa、伸长率34.7%,综合力学性能最佳。     

高品质热轧双相钢的开发

为了提高热轧双相钢的品质,研究了化学成分、轧制工艺、冷却工艺和不同季节水温等参数对热轧双相钢组织和性能的影响。结果表明,无Si成分设计显著提高了热轧双相钢的表面质量;较低的终轧温度和中间保温温度有利于获得更为细小的铁素体组织和弥散的马氏体组织;低的卷取温度（280 ℃）可以获得铁素体+马氏体双相组织;冷却水水温的降低显著提高马氏体含量并提高双相钢的强度。基于上述研究,邯钢实现了系列热轧双相钢的稳定生产,双相钢制作的汽车车轮性能良好。     

马氏体体积分数对热轧双相钢力学性能和n值的影响

通过热轧和模拟超快冷试验,试制出780 MPa级热轧双相钢,研究了马氏体的含量、形貌、分布对热轧双相钢力学性能和n值的影响。结果表明,试验钢经850℃终轧后,组织为铁素体+马氏体,抗拉强度853 MPa,屈服强度464 MPa,屈强比0.54,伸长率19.5%,n值0.14,达到热轧DP780性能要求。在高马氏体含量下(28.2%),随着马氏体含量的增加,组织中的马氏体由弥散分布的片状马氏体逐渐转变为连续的板条状马氏体,马氏体的尺寸逐渐增加;而多边形铁素体部分转变为准多边形铁素体,铁素体尺寸逐渐减小。热轧双相钢的强度和屈强比逐渐提高,而伸长率和n值逐渐降低。     

Electrical conductivity of 1 : 1 and 2 : 1 clay minerals

The A.C. impedance plots were used as tools to analyze the electrical response of two varieties of Tunisian halloysite 1: 1 and illitic samples 2: 1 as a function of frequency at different temperatures (80–800°C). The real and imaginary parts of the complex impedance trace semicircles in the complex plane. Except for the illite, It-1, the second sample analyzed in this study, these plots give evidence for the presence of both bulk and grain boundary effect, above 600°C onwards. The bulk resistance of the materials decreases with the rise in temperature. Impedance Spectroscopy data reveal a non-Debye type of dielectric relaxation. The Nyquist plots show the negative temperature coefficient of resistance of both pure Tunisian illite and halloysite samples. The results of bulk electrical conductivity and its activation energy are presented for the two mineral clay samples. For illite It-1, the activation energy values estimated from the AC conductivity pattern and modulus pattern are very similar and suggest a possibility of a long-range mobility of charge carriers (ions) via hopping mechanism of electrical transport processes at higher temperature. On the other hand, for the halloysite sample provided from kasserine, (Ha-Kass), the modulus analysis admit that the electrical transport processes of the material are very likely of electronic nature. Relaxation frequencies follow an Arrhenius behavior with the activation energy values not comparable to those found for the electrical conductivity.     

A contribution to the crystallochemistry of ternary 1:1:1 and 1:1:2 rare earth intermetallic phases with Pb and Pd

The ternary alloys of the rare earths with lead and palladium were studied for the stoichiometric ratios 1:1:1 and 1:1:2 with respect to the structure of these alloys and their existence field. RPbPd (R = La, Ce, Pr, Nd, Sm, Gd, Tb, Dy, Y, Ho, Er, Tm, Yb) compounds have a hexagonal structure, hP9 Fe₂P type, while RPbPd₂ (R = Pr, Sm, Gd, Tb, Dy, Ho, Er, Yb) alloys have the cubic AlCu₂Mn-type structure (cF16, BiF₃ superstructure).     

有机阴离子转运多肽1B1的遗传药理学进展

人体存在多种类型的药物转运体,对于药物的吸收、分布和排泄起重要作用。参与药物跨膜转运的转运体功能受影响,将可能导致诸多临床药物的疗效、毒副作用甚至药物相互作用的发生。在各种影响因素中,遗传多态性所起的作用最为重要,可导致基因表达和蛋白功能发生改变。目前,阐明转运体基因的多态性以及基因型与表型之间的相互关系已成为应用遗传信息指导临床个体化用药的必要步骤。本文就肝脏有机阴离子转运多肽1B1(OATP1B1[OATP-C],编码基因SLCO1B1)基因多态性对药代动力学和药效动力学的影响及其临床意义等方面的进展作一综述。     

La1-xSrxCo1-yFeyO3材料制备及结构分析

以溶胶-凝胶法制备La1-xSrxCo1-yFeyO3粉体，对粉体在不同温度热处理后的晶体结构进行XRD表征，详细研究粉体的成分组成以及发生的结构转变。结果表明，凝胶前驱体粉体颗粒比表面增大有利于钙钛矿结构晶相形成；合成粉体受前驱体比表面程度影响形成两种具有不同空间群钙钛矿结构晶相，并且各晶相元素化学计量比不相同，两相体系较稳定。     

CYP1B1遗传多态性与个体化治疗

CYP1B1是细胞色素P450（cytochrome P450, CYP450s）家族成员,作为I相代谢酶,主要通过催化性激素、脂肪酸、维生素、褪黑素及外源性化学物质和药物的代谢,参与人体组织正常结构和生理功能的维持。研究发现,CYP1B1基因多态性会影响其蛋白表达水平和酶活性,对其催化的代谢过程产生影响,尤其是对性激素和外源物质的代谢过程的改变,与青光眼、各类癌症的发生发展及治疗密切相关。研究CYP1B1参与的机体代谢途径及基因多态性对其影响,有利于深入了解代谢途径的改变在相关疾病发生发展和药物治疗中的作用,加深对癌症、青光眼等疾病的认识,促进从基因层面检测和评估相关疾病的发生风险和预后,从而实现疾病的预防和早期发现,为个体化治疗提供依据,改善患者生存质量,延长生存期。本文拟就近五年CYP1B1参与的主要代谢途径及基因多态性对其影响的研究进展作一综述。     

La1-xSrxCo1-yFeyO3材料制备及结构分析

以溶胶-凝胶法制备La1-xSrxCo1-yFeyO3粉体,对粉体在不同温度热处理后的晶体结构进行XRD表征,详细研究粉体的成分组成以及发生的结构转变.结果表明,凝胶前驱体粉体颗粒比表面增大有利于钙钛矿结构晶相形成;合成粉体受前驱体比表面程度影响形成两种具有不同空间群钙钛矿结构晶相,并且各晶相元素化学计量比不相同,两相体系较稳定.     

Microstructures and mechanical properties of extruded Mg-1Mn-3.5Y and Mg-1Mn-1Y-2.5Nd alloys

Both Mg-1Mn-3.5Y and Mg-1Mn-1Y-2.5Nd alloys(mass fraction,%)were extruded at 380℃.Most of the(10 10) crystal planes in the Mg-1Mn-3.5Y alloy are parallel to the normal direction,while most of the(10 11)crystal planes in the Mg-1Mn-1Y-2.5Nd alloy are parallel to the normal direction.The tensile tests at room temperature,100℃ and 200℃ show that the Mg-1Mn-3.5Y alloy exhibits higher yield strength,but lower elongation to failure as compared with the Mg-1Mn-1Y-2.5Nd alloy. These differences in the tensile mechanical properties between the two alloys are mainly attributed to their different texture types and amount and distribution of the Mg24Y5 precipitates.The serration flow behavior is observed in the Mg-1Mn-1Y-2.5Nd alloy at 200℃,but does not occur in the Mg-1Mn-3.5Y alloy.The Mg-1Mn-3.5Y alloy shows the cleavage fracture mode,while the Mg-1Mn-1Y-2.5Nd alloy exhibits the dimple fracture mode.