11 t铸锭帽口绝热板和保护渣对H13钢成坯率的影响

针对钢厂热作模具钢H13成坯率低的冶金质量问题,对影响成坯率的相关质量进行了统计分析,得出因帽口保温性能差所造成的疏松缺陷占不合格钢锭总量的58%~76%。通过将SiO₂绝热板的体积密度和导热率分别由1.65 g/cm³和0.317 W/(m·K)降至0.87 g/cm³和0.21 W/(m·K),优化低碳复合保护渣的组成,使其熔点和粘度分别由原来的1258℃和1.8 Pa·s降至1147℃和0.9 Pa·s,使钢锭平均成坯率由原来的75%提高至80%。     

Cr含量对G18CrMo2-6钢组织和性能的影响

通过热处理试验、微观组织表征和力学性能检测,对比研究了在不同Cr含量的情况下,G18CrMo2-6钢微观组织形貌、力学性能的变化.结果表明,随着合金元素Cr含量增加,同一温度退火热处理后G18CrMo2-6钢中铁素体体积分数减少,贝氏体增多,从而导致材料强度升高;但是Cr含量的增加还会导致该类材料退火产生的贝氏体中马氏...     

氩气流量、渣系和加Al粉对1Cr21Ni5Ti钢保护气氛重熔锭[Ti]的影响

生产试验了氩气流量（15~45 L/min）,三元（/%:63CaF₂,27Al₂O₃,10CaO）、四元（/%:53CaF₂,22Al₂O₃,20CaO,5MgO）和五元（/%:50CaF₂,22Al₂O₃,20CaO,5MgO,3TiO₂）渣系和重熔过程加Al粉对3 t保护气氛重熔1Cr21Ni5Ti钢锭[/%:0.09~0.14C,≤0.80Mn,≤0.80Si,≤0.025S,≤0.035P,4.8~5.8Ni,20~22Cr,5×（C-0.02~ 0.65Ti]中[Ti]的影响。结果表明,增加氩气流量,采用五元渣系和重熔过程均匀加入Al粉可使重熔锭平均钛的烧损△[Ti]≤0.15%。采用优化工艺在6 t保护气氛电渣炉,填充比0.58,电流12 500~13 500 A,电压40~43 V,,氩气流量30 L/min,重熔1Cr21Ni5Ti钢的结果表明,电渣锭成分稳定,C含量0.090%~0.091%;Ti含量0.46%~0.52%。      

冷处理温度对1Cr20Co6Ni2WMoV钢组织和力学性能的影响

马氏体热强钢1Cr20Co6Ni2WMoV用真空感应炉冶炼,锭重22.5 kg并锻成中16 mm棒材。试样经 1060℃1h油冷淬火, -70℃或-192℃2h空冷的冷处理,640 ℃3 h空冷回火处理。试验结果表明, 1Cr20Co6Ni2WMoV钢在热处理后的组织由高密度位错的回火板条马氏体、残余奥氏体、δ-铁素体和M₂₃C₆组成。 随冷处理温度由-70 ℃降至-192℃,晶界上M₂₃C₆析出数量增多,晶内位错密度升高,残余奥氏体含量降低,钢 的抗拉强度和屈服强度分别由1045 MPa和715 MPa提高至1090 MPa和760 MPa。     

铸锭加热和锻后热处理工艺对18CrNiMo7-6钢Ф540mm棒材带状的影响

试验18CrNiMo7-6重型齿轮钢(/%:0.165C,0.59Mn,0.24Si,0.006S,0.008P,1.56Ni,1.71Cr,0.28Mo,0.034M,0.0129N)的生产流程为60 t UHP EAF-LF-VD-12.5 t铸锭工艺。试验研究了钢锭加热工艺(1 200~1 220℃,7-8 h~13-15 h),锻材完全退火(900℃12 h,≤80℃/h至650℃50 h,空冷)、等温退火(900℃12 h,空冷至650℃50 h,空冷)和正火(900℃12 h,空冷)工艺对Φ540 mm锻材带状组织的影响。结果表明,钢锭1 200~1 220℃7-8 h加热,锻材经完全退火、等温退火或正火处理后其带状级别分别为4.0,3.5和3.0,钢锭经1 200~1 220℃13-15 h加热,锻材经正火处理后其带状级别为2.5,为最佳工艺。     

冷拔变形量对30CrMnSiNi2A六角材晶粒度及脱碳判定的影响

分析30CrMnSiNi2A钢冷拔六角材总脱碳不合原因,结果表明：当冷拔一次拔制变形量处于临界变形区间时,经690℃退火后冷变形区域晶粒较为粗大,影响总脱碳判定。当冷拔一次拔制变形量在21%～30%时,经热处理后冷变形区域再结晶晶粒得到细化。从而消除因变形量处于临界变形区间导致拔制退火后晶粒粗大而影响总脱碳判定准确性。通过生产实践将冷拔一次变形量控制在20%～25%,并降低退火温度到630℃,生产的S22 mm六角材总脱碳满足标准要求,且脱碳层改善效果明显。     

6流非对称40t中间包挡墙和挡坝对帘线钢盘条夹杂物的影响

通过工业试验研究了6流非对称40t中间包不加挡墙、加挡墙和同时加挡墙挡坝对82A帘线钢Φ5.5 mm盘条夹杂物数量和尺寸的影响。金相检验和电解夹杂物分析结果表明,中间包不加挡墙,近流盘条中夹杂物数量多且尺寸大;加挡墙后,近流盘条中夹杂物数量明显减少且尺寸减小,但远流盘条中夹杂物数量增多且尺寸较大;当加挡墙和挡坝,远流和近流盘条中夹杂物数量和尺寸均明显下降。     

退火温度对刃具钢6CrW2Si组织和硬度的影响

为满足用户加工硬度的特殊需求(硬度≤210HBW),降低6CrW2Si钢硬度,本文利用连轧厂实际辊底式退火炉进行了不同退火温度的退火试验,并借助金相显微镜对不同退火温度下的组织进行了分析,以确定最佳的退火温度。结果表明:6CrW2Si的退火硬度与退火温度有关,随着退火温度的升高,硬度先下降后上升,当退火温度为810℃时,钢材平均硬度值最低(193 HBW左右),球化组织为均匀的球化珠光体组织。     

Si含量对超超临界汽轮机转子钢30Cr2Ni4MoV组织和性能的影响

30Cr2Ni4MoV钢(%:0.15～0.16C、0.03～0.45Si、0.12～0.14Mn、0.005P、0.005～0.006S、1.62～1.72Cr、3.60～3.63Ni、0.52～0.53Mo、0.07V、≤0.005A1)由10kg真空感应炉冶炼,锻后经930℃空冷+900℃空冷+640℃空冷处理,再经850℃水淬+600℃回火调质处理。试验结果表明,当钢中的Si含量由0.03%增加至0.45%时,钢中马氏体量增加,晶粒更为粗大;钢的抗拉和屈服强度分别从922～936 MPa和868～873 MPa增至1015～1028 MPa和950～959 MPa,但平均冲击功由205 J降至154 J。     

时效处理对超级双相不锈钢00Cr29Ni6Mo2N组织和耐点蚀性的影响

采用扫描电镜和X射线能谱仪研究了00Cr29Ni6Mo2N超级双相不锈钢1080℃30 min固溶+650～1000℃60 min时效后的显微组织.试验结果表明,在奥氏体和铁素体相界面上析出了Cr2N和σ相两种析出相,同时发现少量的Cr2N在铁素体相内.Cr2N析出优先于σ相,增加时效温度和时间对Cr2N的析出量没有显...     

钢锭本体帽口的试验研究

基于帽口高度对钢锭内部质量的影响,开展了钢锭本体帽口的试验。研究结果表明：本体帽口对提高钢锭内部质量、提高钢板探伤合格率有着非常明显的作用。但钢锭最终质量还受前步冶炼、精炼、真空处理等工艺的影响,单靠采用本体帽口不可能完全解决钢锭探伤问题。     

3 t模铸钢锭大截面帽口充填技术

大冶特殊钢公司的模铸锭重 3ｔ,经 85 0初轧机开坯 ,对原锭型的模铸钢 ,在满足现有锭机工程能力又不做大的工艺调整的条件下 ,模铸钢帽口部采用大截面充填技术对提高成坯率效果显著 ,钢质量稳定 ,改善了操作人员的劳动条件。1　 3ｔ锭模改型的可行性原钢锭锭身设计合理 ,能充分发挥锭机配套能力 ,但锭型帽口部容积较大 (设计值 1 3 .78% ) ,是影响成坯率提高的主要因素 ,对此 ,提出了对其进行改型研制的设想。在改型研制中遵循的原则是 :(1 )不增加投入 ;(2 )立足现有锭机配套条件 ,对现行生产的钢锭参数进行实测 ;(3 )保证改型后的钢锭质量…     

Improvement in Quality and Yield of the Low Alloy Steel Ingot Casting Through Modified Mould Design

The internal quality and yield in 4 ton steel ingot of 40cmd8 grade was studied by comparing its solidification in a square cross-section mould with a slender rectangular cross-section mould, using FEM simulation. The model predicted various solidification aspects like fluid flow, thermal and solidification profiles, mushy zone, local solidification time, porosity and piping for both the molds. The convective flow of the molten metal during solidification showed higher velocity in square ingot than rectangular ingot under similar conditions due to lower surface area to volume ratio that affected the heat transfer in the rectangular ingot. Higher amount of air gap between the ingot and the mould was formed in rectangular ingots. Lower microsegregation as measured in terms of local solidification time was observed in rectangular ingot. Based on microstructure parameters such as thermal gradient and rate of solidification, it was found that the square ingot had more equiaxed zone than rectangular ingot. The rectangular ingot solidified at a faster rate and showed more propensity for core porosity than the square ingot. The ingot yield was improved by 3.6% through mould shape modification from square to rectangular. Model was validated to limited extent by carrying out a typical experiment with square mould.     

换底锭模的设计与生产

阐述了开发新型锭模的必要性和换底锭模的创新设计思路，扼要介绍了换底锭模的生产方法及其使用效果。设计的换底锭模由锭模本体和活动组件两大部分组成。该模优势：易损坏的部位可以更换；应用于铁合金浇注可比常规产品延长使用寿命5倍以上；单位铁水消耗的锭模费用可降低75％。     

模厚比K值对钢锭模热应力分布的影响

采用热光弹法与有限元法，研究了３．０ｔ矩形弧边钢锭模模口角部厚度变化对钢锭模热应力分布的影响，并进行优化设计，使钢锭模的使用寿命提高１倍。     

3.16 t SCM822H齿轮钢锭红送入炉温度对钢材表面质量的影响

3．16t 0．20C-1．20Cr—0．4Mo齿轮钢锭—火成材红送工艺实践表明，当进入加热炉时铸锭的温度为800～900℃时，因相变组织应力和脆性AlN的大量析出，使Φ140～160mm钢材表面出现裂纹。而入炉时钢锭表面温度高于950℃和低于700℃时，因避免了上述不利因素，成品材的表面质量良好。     

B25.6t镇沸两用锭型成坯率的统计分析

通过对Ｂ２５．６ｔ这一目前国内自行设计的最大锭型的成坯率进行统计分析，证明该锭型投入生产后，能有效地节约能源，提高设备生产能力，扩大产品规格等，可提高成坯率及成材率，收到显著的经济效益。     

塑料模具钢大型预硬化模块的研究

系统研究了LF+VD精炼工艺、钢锭模设计、氩气保护浇注工艺、大型钢锭高温扩散工艺、锻造工艺、淬火工艺及高温回火工艺等因素对718钢大型预硬化模块材料纯净度和硬度均匀性的影响规律。结果显示：LF和VD精炼过程中炉渣碱度分别保持在3.5～4.0和3.0～3.5,精炼后钢中w[S]控制到0.003%,T[O]为12×10-6;28t钢锭模尾锥形状和入口倒角优化设计后,尾部夹杂废品率由6.81%降低到1.55%;通过试验确定氩气流量按4～8 m3/h控制;大型钢锭高温扩散后,模块低倍组织的偏析和硬度偏差分别由≤3.0级和≤5.0HRC提高到≤2.0级和≤3.5HRC;采用FM法代替平砧拔长,模块低倍组织疏松和超声波探伤检验分别由≤3.0级和C/d提高到≤2.0级和D/d;采用水-空控时淬火和电加热回火炉回火对规格为650 mm×1 080 mm的模块进行预硬化处理,模块横断面硬度偏差≤3.5HRC。     

Influence of Mould and Insulation Design on Soundness of Tool Steel Ingot by Numerical Simulation

 The solidification of 4. 4 t cold work tool steel ingot type X210Cr12 was simulated by Magma software. By the reduction of ingot height, solidification modeling and pouring of a new 3 t ingot were performed and decreasing the porosity formation potential in 3 t ingot in comparison with 4. 4 t ingot on the basis of Niyama criterion was observed which was in good accordance with experimental data. In order to produce sound ingot, a new 2. 8 t ingot mould was designed which includes some parameteric changes in mould such as mould slope, slenderness ratio, mould concavity radius, fillet radius of mould internal corners and feeding diameter to ingot upper diameter ratio. Furthermore, the effects of insulating between kokil and feeding ring and also insulating the outer surface of feeding ring as well as insulating the outer surface of one third of kokil upper part on centerline porosity formation were investigated in both 2. 8 and 4. 4 t ingots. The results show that the ingot which was produced in new designed 2. 8 t mould has a better Niyama pattern and the centerline porosities were eliminated.