Corrosion prevention of passivated iron in 0.1 M NaCl by coverage with an ultrathin polymer coating and healing treatment in 0.1 M NaNO3

An ultrathin, ordered and two-dimensional polymer coating was prepared on a passivated iron electrode by modification of 16-hydroxyhexadecanoate ion HO(CH₂)₁₅CO₂⁻ self-assembled monolayer with 1,2-bis(triethoxysilyl)ethane (C₂H₅O)₃Si(CH₂)₂Si(OC₂H₅)₃ and octadecyltriethoxysilane C₁₈H₃₇Si(OC₂H₅)₃. Subsequently, the electrode was healed in 0.1 M NaNO₃. Protection of passivated iron against passive film breakdown and corrosion of iron was examined by monitoring of the open-circuit potential and repeated polarization measurements of the polymer-coated and healed electrode in an aerated 0.1 M NaCl solution during immersion for many hours. Localized corrosion was markedly prevented by coverage with the polymer coating and the healing treatment in 0.1 M NaNO₃. Prominent protection of iron from corrosion in 0.1 M NaCl was observed before the breakdown occurred. The electrode surface covered with the healed passive film and polymer coating was analyzed by contact angle measurement, X-ray photoelectron spectroscopy and electron-probe microanalysis.     

An ultrathin polymer coating of carboxylate self-assembled monolayer adsorbed on passivated iron to prevent iron corrosion in 0.1 M Na2SO4

For preparing an ultrathin two-dimensional polymer coating adsorbed on passivated iron, a 16-hydroxyhexadecanoate ion HO(CH₂)₁₅CO₂⁻ self-assembled monolayer (SAM) was modified with 1,2-bis(triethoxysilyl)ethane (C₂H₅O)₃Si(CH₂)₂Si(OC₂H₅)₃ and octadecyltriethoxysilane C₁₈H₃₇Si(OC₂H₅)₃. Protection of passivated iron against passive film breakdown and corrosion of iron was investigated by monitoring of the open-circuit potential and repeated polarization measurements in an aerated 0.1 M Na₂SO₄ solution during immersion for many hours. The time required for passive film breakdown of the polymer-coated electrode was markedly higher in this solution than that of the passivated one, indicating protection of the passive film from breakdown by coverage with the polymer coating. The protective efficiencies of the passive film covered with the coating were extremely high, more than 99.9% in 0.1 M Na₂SO₄ before the passive film was broken down, showing prominent cooperative suppression of iron corrosion in the solution by coverage with the passive film and polymer coating. The polymer-coated surface was characterized by contact angle measurement and electron-probe microanalysis (EPMA). Prevention of passive film breakdown and iron corrosion for the polymer-coated electrode healed in 0.1 M NaNO₃ was also examined in 0.1 M Na₂SO₄.     

Protection of passivated iron from corrosion in 0.1 M KClO4 with and without Cl by coverage with a two-dimensional polymer film of carboxylate ion self-assembled monolayer

A film of two-dimensional polymer was prepared on an iron electrode passivated in a borate buffer solution at pH 8.49, derivatized with 16-hydroxyhexadecanoate ion and then modified with 1,2-bis(triethoxysilyl)ethane (C₂H₅O)₃Si(CH₂)₂Si(OC₂H₅)₃ and octadecyltriethoxysilane C₁₈H₃₇Si(OC₂H₅)₃. The protective ability of the polymer film adsorbed on passivated iron was examined by polarization measurement in oxygenated 0.1 M KClO₄ solutions with and without 1 × 10⁻⁴ and 1 × 10⁻³ M of Cl⁻. The values of the open-circuit potential, E_oc were monitored with the immersion time, t in these solutions. The E_oc value of the passivated electrode in 0.1 M KClO₄ was maintained high, more than −0.2 V/SCE in the initial region of t up to 10 h, indicating the presence of a passive film on the electrode. Thereafter, E_oc decreased to −0.4 V/SCE abruptly, exhibiting breakdown of the passive film. The value of the passivated electrode covered with the polymer film remained almost constant around −0.04 V/SCE during immersion for 45 h. The protective efficiency, P (%) of the polymer film on passivated iron was extremely high, more than 99.9% unless the passive film was broken down, indicating complete protection of iron against corrosion. The times for breakdown on the passivated electrode and polymer-coated one diminished with an increase in the concentration of Cl⁻. The polymer-coated surface was analyzed by electron-probe microanalysis after immersion in 0.1 M KClO₄ for 24 h.     

Complete protection of a passive film on iron from breakdown in a borate buffer containing 0.1 M of Cl by coverage with an ultrathin film of two-dimensional polymer

An ultrathin film of two-dimensional polymer was prepared on a passivated iron electrode by modification of a 16-hydroxyhexadecanoate ion self-assembled monolayer with 1,2-bis(triethoxysilyl)ethane (C₂H₅O)₃Si(CH₂)₂Si(OC₂H₅)₃ and octadecyltriethoxysilane C₁₈H₃₇Si(OC₂H₅)₃. This film prevented passive film breakdown examined by potentiodynamic anodic polarization of the coated electrode in the borate buffer solution containing 0.1 M of Cl⁻. Neither current spikes nor the pitting potential was observed in the passive and transpassive regions of polarization curve. The anodic current density was decreased in these regions markedly, implying hindrance to permeation of Cl⁻ and water through the film. Structure of the film was clarified by X-ray photoelectron and FTIR reflection spectroscopies and contact angle measurement with a drop of water. Electron-probe microanalysis of the passivated surface coated with the film after anodic polarization scanning up to the transpassive region revealed that the polymer film prevents pit initiation by an attack on the passive film with Cl⁻.     

Protection of passivated iron against corrosion in a 0.1 M NaNO3 solution by coverage with an ultrathin polymer coating of carboxylate SAM

An ultrathin, ordered and two-dimensional polymer coating was prepared on passivated iron by modification of 16-hydroxyhexadecanoate ion HO(CH₂)₁₅CO₂⁻ self-assembled monolayer (SAM) with 1,2-bis(triethoxysilyl)ethane (C₂H₅O)₃Si(CH₂)₂Si(OC₂H₅)₃ and octadecyltriethoxysilane C₁₈H₃₇Si(OC₂H₅)₃. Protection of passivated iron against passive film breakdown and corrosion of iron was examined by monitoring of the open-circuit potential and repeated polarization measurements in an aerated 0.1 M NaNO₃ solution during immersion for many hours. Passive film breakdown on the polymer-coated electrode in the solution was not observed during immersion for 480 h, whereas that of the passivated one occurred at 18.1 h, indicating protection of the passive film from breakdown by coverage with the polymer coating. The protective efficiencies of the passive film covered with the coating were extremely high, around 99.9% in the initial region of the immersion time up to 72 h and more than 98.3% thereafter, indicating prominent cooperative suppression of iron corrosion in 0.1 M NaNO₃ by coverage with the passive film and polymer coating. The polymer-coated surface was characterized by contact angle measurement and electron-probe microanalysis.     

Improvement of healing treatment with NaNO3 for a passivated iron electrode covered with an ultrathin polymer coating to prevent iron corrosion in some solutions containing aggressive anions

An ultrathin and ordered polymer coating was prepared on a passivated iron electrode by modification of a 16-hydroxyhexadecanoate ion self-assembled monolayer with 1,2-bis(triethoxysilyl)ethane (C₂H₅O)₃Si(CH₂)₂Si(OC₂H₅)₃ and octyltriethoxysilane C₈H₁₇Si(OC₂H₅)₃. Further, the passivated and polymer-coated electrode was healed by treatment in 1.0 M NaNO₃ for 4 h. Prevention of passive film breakdown and iron corrosion for the passivated, polymer-coated and healed electrode was examined by monitoring of the open-circuit potential and repeated polarization measurements in oxygenated 0.1 M KClO₄, 0.1 M Na₂SO₄ and 0.1 M NaCl for many hours. The values of the time for passive film breakdown, t_bd were >240, 22.2 and 9.5 h in these solutions, respectively. The protective efficiencies for the electrode were extremely high, more than 99.9% before t_bd, indicating complete protection of substrate iron against corrosion in these solutions, unless passive film breakdown occurred. The presence of on the passive surface by treatment in 1.0 M NaNO₃ was detected by X-ray photoelectron and FTIR reflection spectroscopies. The self-healing activity of adsorbed to suppress passive film breakdown was discussed.     

Direct modification of a passivated iron electrode with alkyltriethoxysilanes for preventing passive film breakdown in a borate buffer containing 0.1 M of chloride ion

A passive film on an iron electrode was modified with alkyltriethoxysilanes directly. In order to examine the protective ability of the modified passive film against breakdown, the pitting potential, E_pit was measured by anodic polarization of the modified electrode in a borate buffer solution (pH 8.49) containing 0.1 M of Cl⁻. The value of E_pit for the modified electrode shifted in the positive direction from that of the unmodified electrode, indicating prevention of passive film breakdown. The modified passive film was not broken down in the passive and transpassive regions of polarization curve in some cases. However, many current spikes appeared in the all curves of the modified electrodes. The modified surface of passivated electrode was characterized by X-ray photoelectron and FTIR reflection spectroscopies and contact angle measurement. There were defects and clusters of associated water within the modified film and hence, Cl⁻ could permeate through the defects, leading to appearance of current spikes and occurrence of breakdown.     

Prevention of passive film breakdown on iron in a borate buffer solution containing chloride ion by coverage with a self-assembled monolayer of hexadecanoate ion

Breakdown of a passive film on iron in a borate buffer solution (pH 8.49) containing 0.1 M of Cl⁻ was suppressed by coverage of the passive film surface with a self-assembled monolayer (SAM) of hexadecanoate ion C₁₅H₃₁CO₂⁻ (C₁₆A⁻). The pitting potential of an iron electrode previously passivated in the borate buffer at 0.50 V/SCE increased by treatment in an aqueous solution of sodium hexadecanoate for many hours, indicating protection of the passive film from breakdown caused by an attack on defects of the film with Cl⁻. No breakdown occurred over the potential range of the passive region by coverage with the SAM of C₁₆A⁻ in some cases. Structures of the passive film and the monolayer were characterized by X-ray photoelectron and Fourier transform infrared reflection spectroscopies and contact angle measurement with a drop of water.     

Self-assembled monolayers of carboxylate ions on passivated iron for preventing passive film breakdown

Self-assembled monolayers (SAMs) of carboxylate ions C_n−1H_2n−1CO₂⁻ (C_nA⁻) with the carbon number, n=12-18 and 16-hydroxyhexadecanoate ion HO(CH₂)₁₅CO₂⁻ (HOC₁₆A⁻) were prepared on an iron electrode previously passivated in a borate buffer at pH 8.49 by treatment in aqueous solutions of their sodium salts for many hours. Breakdown of the passive film on the electrode coated with the SAM was examined by anodic polarization measurement in the borate buffer containing 0.1 M of Cl⁻. The pitting potentials of the passivated electrodes coated with the SAMs of C_nA⁻ and HOC₁₆A⁻ shifted toward a more positive potential than that of the uncoated electrode, indicating prevention of passive film breakdown by blocking diffusion of Cl⁻ through the SAM to defects of the passive film. No breakdown was observed over the potential range of the passive region by coverage of the passive film with the SAM in some cases. The SAMs on the passive film were characterized by contact angle measurements and X-ray photoelectron and Fourier transform infrared reflection spectroscopies.     

Preparation of a two-dimensional polymer film on passivated iron by modification of a carboxylate ion self-assembled monolayer with alkyltriethoxysilanes for preventing passive film breakdown

The effect of an ultrathin, regularly arranged polymer film on prevention of passive film breakdown on iron in the presence of chloride ion was investigated. The film of two-dimensional polymer was prepared by modification of a 16-hydroxyhexadecanoate ion self-assembled monolayer adsorbed on a passivated iron electrode with 1,2-bis(triethoxysilyl)ethane(C₂H₅O)₃Si(CH₂)₂Si(OC₂H₅)₃ and octyltriethoxysilane C₈H₁₇Si(OC₂H₅)₃. The pitting potentials of the passivated electrodes bare and covered with the polymer film were determined by anodic polarization measurements in a borate buffer solution containing 0.1 M of Cl⁻. The pitting potential of the coated electrode was higher than that of the uncoated one, indicating prevention of passive film breakdown. No breakdown was observed over the potential range in the passive and transpassive regions by covering the passive film with the well-arranged two-dimensional polymer film. The film was characterized by X-ray photoelectron and FTIR reflection spectroscopies and measurement of the contact angle with a drop of water.     

Prevention of passive film breakdown on iron by coverage with one-dimensional polymer films of a carboxylate ion self-assembled monolayer modified with alkyltriethoxysilanes

A film composed of a one-dimensional polymer was fabricated by modification of a 16-hydroxyhexadecanoate ion HO(CH₂)₁₅CO₂⁻ self-assembled monolayer (SAM) adsorbed on a passivated iron electrode with octadecyltriethoxysilane C₁₈H₃₇Si(OC₂H₅)₃. The pitting potential, E_pit of the passivated electrode coated with this film was measured by anodic polarization in a borate buffer solution containing 0.1 M of Cl⁻. The E_pit value of the electrode coated with the film was markedly shifted from the value of the bare electrode in the positive direction, indicating prevention of passive film breakdown. No breakdown occurred over the potential range of passive region in some cases. Structure of the modified SAM was discussed by X-ray photoelectron and FTIR reflection spectroscopies and contact angle measurement of the electrode surface covered with the film. Suppression of Cl⁻ accumulation at a defect of the passive film was revealed by electron-probe microanalyses of the surfaces uncoated and coated with the SAM modified with octyltriethoxysilane C₈H₁₇Si(OC₂H₅)₃ after anodic polarization in the borate buffer containing Cl⁻.     

Preparation of ultrathin polymer coatings adsorbed on iron via a covalent bond by multistep modification of a hydroxymethylbenzene SAM with ethoxysilanes and alkanediol for preventing iron corrosion in 0.5 M NaCl

The film thickness, d of a p-hydroxymethylbenzene - C₆H₄CH₂OH (HOMB) self-assembled monolayer (SAM) adsorbed on iron via a covalent bond was increased by multistep modification with tetraethoxysilane (C₂H₅O)₄Si (TES) and 1,8-octanediol HO(CH₂)₈OH (C₈DO) and subsequently with 1,2-bis(triethoxysilyl)ethane (C₂H₅O)₃Si(CH₂)₂Si(OC₂H₅)₃ (BTESE) and akyltriethoxysilane C_nH_2n+1Si(OC₂H₅)₃ (C_nTES, n = 8 or 18). The protective ability of the film against iron corrosion was examined by polarization measurement of the iron electrode coated with the film in an oxygenated 0.5 M NaCl after immersion in the solution for many hours. The values of protective efficiency, P for the films, the HOMB SAM modified with TES and C₈DO twice and subsequently with BTESE and C_nTES were high, more than 81% at n = 8 and 85% at n = 18 in the range of the immersion time, t up to 240 h, respectively. The maximal P values of the respective films were 88.0% and 92.2%, of which approximate d values were 4.6 and 5.8 nm. The high protection of iron against corrosion was attributed to increases in the film thickness and interconnection between the adsorbed molecules with Si-O polymer linkages. The protective ability of the film was remarkably persistent during immersion in the solution for many hours. A slight enhancement of P was observed by additional modification of the modified HOMB SAM with C₈TES due to increases in interconnection and close packed arrangement. The formation of strong adsorption bonds, σ-covalent bond and back-donating π-bond, between the carbon atom of HOMB moiety and iron atom was discussed.     

Preparation of a one-dimensional polymer film on passivated iron by modification of a carboxylate ion self-assembled monolayer with octyltriethoxysilane for preventing passive film breakdown

A self-assembled monolayer (SAM) of 16-hydroxyhexadecanoate ion HO(CH₂)₁₅CO₂⁻(HOC₁₆A⁻) has been prepared on an iron electrode passivated in a borate buffer solution (pH 8.49) in the preceding paper. In this work, the HOC₁₆A⁻ SAM on the passivated electrode was modified with octyltriethoxysilane C₈H₁₇Si(OC₂H₅)₃ to form a film composed of one-dimensional polymer. Prevention of passive film breakdown was examined by anodic polarization measurements of the electrodes uncoated and coated with the modified SAM in the borate buffer containing 0.1 M of Cl⁻. The pitting potential, E_pit of the coated electrode shifted from that of the uncoated electrode in the positive direction, indicating prevention of passive film breakdown. The anodic current density was decreased in the passive and transpassive regions by coverage with the modified SAM. Neither current spikes nor E_pit was observed in the curve of the passive region in some cases, demonstrating complete protection of the passive film against breakdown in the Cl⁻ solution. The modified SAM on the electrode was characterized by X-ray photoelectron and FTIR reflection spectroscopies and contact angle measurement.     

Langmuir-Blodgett films of dococyltriethylammonium bromide and octadecanol on iron. Deposition and corrosion inhibitor performance in CO2 containing brine

The stability and compressibility of Langmuir films of dococyltriethylammonium bromide (C₂₂TAB) and 1-octadecanol (C₁₈OH) and their mixtures on water surfaces were first investigated. Langmuir-Blodgett films were transferred onto iron substrate. Their effect on corrosion of iron in carbon dioxide containing brine were investigated by electrochemical methods. The C₁₈OH formed a thin homogenous film with molecular area 19.4 Å² at 36 mN m⁻¹ at water surface. The films of C₂₂TAB and C₂₂TAB/C₁₈OH mixtures were less dense, with 31 Å² molecular area at 36 mN m⁻¹ at water surface. The corrosion rate of iron substrate was reduced by 95% by deposition film of C₁₈OH, while the corrosion rate of iron was reduced by 60% for films of C₂₂TAB and C₂₂TAB/C₁₈OH mixtures.     

Schiff bases of increasing complexity as mild steel corrosion inhibitors in 2 M HCl

The effect of three Schiff base compounds with increasing number of coordination sites, namely, 2-{(E)-[(2-hydroxyethyl)imino]methyl} phenol (I), 2-[(E)-({2-[(2-hydroxyethyl)amino]ethyl}imino)methyl]phenol (II) and 2,2′-{iminobis[ethane-2,1-diylnitrilo(E)methylylidene]}diphenol (III) have been investigated at 298 K by weight loss measurements, potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) methods. The inhibition efficiencies obtained from all methods employed are in good agreement. Results show compound III to be the best inhibitor with a mean efficiency of 93% at 10⁻² M additive concentration. Studies showed all three compounds to act as mixed type inhibitors.     

Synergistic effect of halide ions on improving corrosion inhibition behaviour of benzisothiozole-3-piperizine hydrochloride on mild steel in 0.5 M H2SO4 medium

The synergistic effect of iodide ions and benzisothiozole-3-piperizine hydrochloride (BITP) on corrosion inhibition of mild steel in 0.5 M H₂SO₄ solution has been studied by both chemical and electrochemical methods. The corrosion performance of BITP in 1.0 M HCl and 0.5 M H₂SO₄ media was examined and compared. The adsorption of BITP and its combination with iodide ions on mild steel surface followed Langmuir adsorption isotherm via chemisorption mechanism. The calculated values of synergism parameter (S_θ) were found to be greater than unity. This result clearly showed the existence of synergism between iodide ions and BITP molecules.     

Protection of iron against corrosion by coverage with ultrathin two-dimensional polymer films of a hydroxymethylbenzene self-assembled monolayer anchored by the formation of a covalent bond

Ultrathin films of two-dimensional polymers were prepared on an iron electrode by modification of a p-hydroxymethylbenzene p-HOCH₂C₆H₄ (HOMB) self-assembled monolayer (SAM) with 1,2-bis(triethoxysilyl)ethane (C₂H₅O)₃Si(CH₂)₂Si(OC₂H₅)₃ (BTESE) and alkyltriethoxysilanes C_nH_2n+1Si(OC₂H₅)₃ (C_nTES, n = 8 and 18). The electrode was derivatized by cathodic reduction of p-hydroxymethylbenzenediazonium tetrafluoroborate HOCH₂C₆H₄N₂BF₄ in an electrolytic acetonitrile solution below 10 °C for 1 h to form the SAM via a covalent bond between carbon and iron atoms. The protective ability of the polymer film against iron corrosion was determined by polarization measurement of the coated electrode in an oxygenated 0.5 M NaCl solution. The protective efficiencies of the polymer films prepared by modification with BTESE plus C₈TES and C₁₈TES were 63.9% and 68.5% after immersion in 0.5 M NaCl for 1.5 h, respectively. These values were higher than those of the one-dimensional polymer films prepared with the respective C_nTES. The film of the HOMB SAM modified with BTESE plus C₈TES was characterized by contact angle measurement using a drop of water and X-ray photoelectron and FTIR reflection spectroscopies. The films of the HOMB SAM modified with BTESE plus C₈TES and C₁₈TES were persistent during immersion of the coated electrodes in 0.5 M NaCl for many hours by far as compared with the alkanethiol SAM anchored on iron by the formation of a coordinate bond.     

The influence of the conditions of the ZrO2 passive film formation on its properties in 1 M NaOH

In this paper, results of the potentiodynamic-potentiostatic formation of a homogeneous, passive films of ZrO₂ onto a Zr electrode in 1 M NaOH solution at different potentials (2.0, 4.0, 6.0 and 8.0 V vs. SCE) are presented. The properties of such films were investigated by EIS measurements at different potentials. After fitting the EIS spectra by an appropriate equivalent circuit, the capacitance (C_pf) and resistance (R_pf) of these films were determined. All films were found to become insulators at the potentials equal and/or more positive than 2.0 V, with their thicknesses increasing linearly with the potential from about 7 nm at 2.0 V to about 20 nm at 8.0 V. In the potential range 0.8 V < E < 2.0 V a transition from a semiconducting to insulating behaviour has been recorded for all films (except for the one formed at 2.0 V). The donor densities (N_sc) for all films, as well as their flat band potentials (E_fb) and their thicknesses of the space charge layer (d_sc), were determined from the corresponding Mott-Schottky plots (MS) recorded in the potential range (0.0 V < E < 0.8 V), where all films behaved as n-type semiconductors.     

Experimental and theoretical calculations on corrosion inhibition of steel in 1 M H2SO4 by crown type polyethers

The corrosion inhibitive efficiencies of two crown type polyethers, namely dibenzo-bis-imino crown ether (C-1) and dibenzo-diaza crown ether (C-2), which are macrocyclic Schiff base and its reduced form (macrocyclic amine), respectively, for the steel in 1 M H₂SO₄ have been investigated by Tafel extrapolation and linear polarization methods. Corrosion and adsorption isotherm parameters were determined from current-potential curves. The studies show that C-1 and C-2 inhibit the corrosion of the steel in H₂SO₄ solution. Semiempirical AM1 method was used for theoretical calculations. The obtained results of these calculations for the compounds were found to be consistent with the experimental findings.     

Inhibition effect of methyl violet on the corrosion of cold rolled steel in 1.0 M HCl solution

The inhibition effect of methyl violet (MV) on the corrosion of cold rolled steel (CRS) in 1.0 M HCl solution at 20-50 °C was studied by weight loss, potentiodynamic polarization, electrochemical impedance spectroscopy (EIS), and scanning electron microscopy (SEM) methods. The results show that MV is an excellent inhibitor even with very low concentration, and the adsorption of MV on CRS surface obeys Langmuir adsorption isotherm. Potentiodynamic polarization curves reveal that MV behaves as a mixed-type inhibitor. EIS spectra exhibit one capacitive loop and confirm the inhibitive ability. The inhibition action of MV is also evidenced by SEM.