溴化十六烷基吡啶在HCl中对冷轧钢的缓蚀作用

用失重法研究了在1.0 mol/L HCl中20~50℃时溴化十六烷基吡啶(HDPB)在冷轧钢表面上的吸附及缓蚀作用。结果表明,HDPB对钢具有良好的缓蚀作用,缓蚀率随缓蚀剂浓度和温度的增加而增大;HDPB在钢表面的吸附符合Langmuir吸附模型。求出了相应的吸附热力学参数(吸附自由能ΔG0,吸附焓ΔH0,吸附熵ΔS0),并根据这些参数详细讨论了缓蚀作用机理。     

氢氟酸溶液中溴化十六烷基吡啶在碳钢表面吸附热力学研究

采用失重法研究了不同温度下不同质量浓度的溴化十六烷基吡啶在3%的氢氟酸介质中对碳钢的缓蚀作用。结果表明,溴化十六烷基吡啶在3%的氢氟酸介质中对碳钢的腐蚀具有良好的抑制作用。溴化十六烷基吡啶在碳钢片表面的吸附规律基本服从Langmuir等温式。采用Sekine方法处理实验数据,获得了吸附系数、焓变、熵变、自由能变等相关热力学参数。     

溴代十六烷基吡啶对冷轧钢在柠檬酸中的缓蚀性能

通过失重法、电化学阻抗谱(EIS)、动电位极化曲线和扫描电子显微镜(SEM)研究了溴代十六烷基吡啶(HDPB)在0.10 mol/L柠檬酸(H₃C₆H₅O₇)溶液中对冷轧钢的缓蚀性能。结果表明,20℃时30 mg/L HDPB的缓蚀率为83.3%,缓蚀率与缓蚀剂浓度呈正相关,而与温度呈负相关,HDPB在冷轧钢表面遵循Langmuir吸附等温式,各温度的标准吸附Gibbs自由能(ΔG⁰)在-34～-29 kJ/mol范围,且吸附过程为标准吸附熵(ΔS⁰)减小的放热过程。HDPB为混合抑制型缓蚀剂,阴、阳两极的腐蚀电流密度随HDPB浓度增大而不断减小。Nyquist图谱由容抗弧和感抗弧构成,添加HDPB后电荷转移电阻增大。SEM微观形貌进一步证实了HPDB有效抑制了柠檬酸对冷轧钢表面的腐蚀。     

HCl中有机染料在钢表面的吸附及缓蚀作用

用失重法研究了在1.0 mol/LHCl中5种有机染料——丽春红S(PS)、俾士麦棕Y(BBY)、玫瑰桃红R(BR)、橙黄G(OG)和橙黄IV(OIV)在冷轧钢表面的吸附及缓蚀作用。结果表明:染料PS和BBY具有中等程度的缓蚀作用,且在钢表面的吸附符合Temkin吸附模型;其余3种染料BR、OG和OIV的缓蚀性能较差。5种染料的缓蚀率排序为:PS>BBY>BR>OG>OIV。     

溴化十六烷基吡啶在硫酸溶液中对钢的缓蚀性能研究

采用失重法、动电位极化曲线、电化学阻抗谱(EIS)、扫描电子显微镜(SEM)及原子力显微镜(AFM)研究了阳离子表面活性剂溴化十六烷基吡啶(HDPB)在1.0 mol/L H2SO4溶液中对冷轧钢的缓蚀性能.结果表明:HDPB具有良好的缓蚀性能,缓蚀率随缓蚀剂浓度和温度的增加而增大,50℃时100 mg/L HDPB的最大缓蚀率可高达98.2％.HDPB属于混合抑制型缓蚀剂,添加HDPB后电荷转移电阻显著增大,且SEM与AFM的微观形貌进一步证实了HDPB有效减缓了冷轧钢表面的腐蚀程度.     

盐酸中烯丙基硫脲在钢表面的吸附及缓蚀作用

用失重法研究了在1.0 mol/L 盐酸中20～50℃烯丙基硫脲(ATU)在冷轧钢表面上的吸附及缓蚀作用.结果表明:ATU对钢具有良好的缓蚀作用,在钢表面的吸附符合Langmuir吸附模型.通过吸附理论和动力学Arrhenius公式分别求出了相应的吸附热力学参数(吸附自由能△G°, 吸附热△H°, 吸附熵△S°)和动力学参数表观活化能Ea,并根据这些参数详细讨论了缓蚀作用机理.     

溴化十五烷基吡啶的电位滴定法测定

<正> 溴化十五烷基毗啶(Pentadecyl Pyridine Bromide,简写为PPB)是一种季铵盐型阳离子表面活性剂,由棕榈酸溴化后再与吡啶加成而制得。它在制药工业中用作提取金霉素、青霉素时的破乳剂、蛋白沉淀剂,在纺织等行业也有应用。高含量的PPB(如工业品的纯度)依有关厂家的企业标准用碘量法测定,低含量     

盐酸中原儿茶醛在钢表面的吸附及缓蚀作用

用失重法和动电位极化曲线法研究了在1.0mol/L HCl中20~50℃原儿茶醛(3,4-二羟基苯甲醛)在冷轧钢表面上的吸附及缓蚀作用.结果表明:原儿茶醛具有中等程度的缓蚀作用,为混合抑制型缓蚀剂,缓蚀率随原儿茶醛的浓度增加而增大,但随温度的增加而减小;原儿茶醛在钢表面的吸附符合Freundlich吸附模型.通过吸附理论和动力学Arrhenius公式求出了相应的吸附热力学参数(吸附自由能ΔG°,吸附热ΔH°,吸附熵ΔS°)和动力学参数表观活化能Ea,并根据这些参数详细讨论了缓蚀作用机理.     

表面活性剂在HCl中对钢的缓蚀协同效应

用失重法和电化学法研究了在1.0 mol/L HCl中阴离子表面活性剂油酸钠(SO)和非离子表面活性剂聚乙二醇辛基苯基醚(OP)对冷轧钢的缓蚀协同作用.研究结果表明,单独的SO和OP对冷轧钢具有一定的缓蚀作用,为混合型缓蚀剂,且在钢表面的吸附符合Temkin吸附模型.当两者复配后产生了明显的缓蚀协同效应,最大缓蚀率可达92%.     

溴化十六烷基吡啶光度法测定微量锡

在０．３ｍｏｌ／Ｌ的硫酸介质中，于溴化十六烷基吡啶存在下，形成锡－苯芴酮－溴化十六烷基吡啶橙红色三元络合物，其吸收波长为５１０ｎｍ，摩尔吸光系数为ε５１０＝１．０７×１０＾５Ｌ·ｍｏｌ＾－１·ｃｍ＾－１样品标准偏差Ｓ〈０．０３％，锡含量在０－８μｇ／５０ｍｌ内符合比尔定律。本法已成功地动用于多金属矿分析。     

H_2SO_4介质中KI在冷轧钢表面的吸附及缓蚀作用

用失重法和电化学法研究了在1.0~6.0 mol/LH2SO4介质中,20~60℃时K I在冷轧钢表面上的吸附及缓蚀作用。结果表明,K I在H2SO4中具有非常好的缓蚀作用,为混合抑制型缓蚀剂,最大缓蚀率超过98%;K I在钢表面的吸附符合Langmu ir吸附模型。通过吸附热力学和动力学公式分别求出了相应的吸附热力学参数(吸附自由能ΔG0,吸附热ΔH0,吸附熵ΔS0)和动力学参数(腐蚀速度常数k,腐蚀动力学参数B),并根据这些参数详细讨论了缓蚀作用机理。     

邻菲罗啉与溴离子对磷酸溶液中冷轧钢的缓蚀研究

研究了在2．0-9．0mol／L磷酸溶液体系中,邻菲罗啉单体及邻菲罗啉与溴离子复配对冷轧钢的缓蚀行为。结果表明邻菲罗啉单体对冷轧钢在磷酸溶液中缓蚀性能有限,但当与0．03mol／L溴离子复配时,表现出强烈的协同缓蚀效应,且该复配缓蚀剂尤其适用于高浓度磷酸体系,单体及复配缓蚀剂在冷轧钢表面的吸附均符合Langmuir吸附模型,吸附热、吸附熵、吉布斯自由能和吸附平衡常数等热力学参数以及表观活化能、指前因子等动力学参数也一并求得。     

Experimental and Quantum Chemical Studies on Corrosion Inhibition Performance of Thiazolidinedione Derivatives for Mild Steel in Hydrochloric Acid Solution

In the present investigation, two thiazolidinedione derivatives, 5-[(2-(3,4,5-trimethoxyphenyl)-6-phenylimidazo[2,1-b][1,3,4]thiadiazol-5-yl)methylidene]-1,3-thiazolidine-2,4-dione (Inh I) and 5-[2-(3,4,5-trimethoxyphenyl)-6-(4-methoxylphenyl)-imidazo[2,1-b][1,3,4]thiadiazol-5-yl)methylidene]-1,3-thiazolidine-2,4-dione (Inh II) were synthesized and investigated as inhibitors for mild steel corrosion in 15% HCl solution using the weight loss, electrochemical polarization, and electrochemical impedance spectroscopy (EIS) techniques. It was found that the inhibition efficiency of these inhibitors increased with increasing concentration. The effect of temperature on the corrosion rate was investigated, and some thermodynamic parameters were calculated. Polarization studies showed that both studied inhibitors were of mixed type in nature. The adsorption of inhibitors on the mild steel surface in acid solution was found to obey the Langmuir adsorption isotherm. Scanning electron microscopy (SEM) was performed on inhibited and uninhibited mild steel samples to characterize the surface. The semi-empirical AM1 method was employed for theoretical calculation of highest (E _HOMO), and lowest unoccupied molecular orbital (E _LUMO) energy levels, energy gap (E _LUMO ? E _HOMO), dipole moment (μ), global hardness (γ), softness (σ), binding energy, molecular surface area, chemical potential (Pi), and the fraction of electrons transferred from the inhibitor molecule to the metal surface (ΔN). The results were found to be consistent with the experimental findings.     

硫酸溶液中KCl在冷轧钢表面的吸附及缓蚀作用

用失重法研究了在1.0~7.0 mol/L H2SO4中20~60℃时,KCl在冷轧钢表面上的吸附及缓蚀作用。结果表明:KCl在H2SO4中对冷轧钢具有中等程度的缓蚀作用,缓蚀率随KCl和H2SO4介质的浓度增加而增大,而随温度的变化缓蚀率排序为:50℃>30℃>40℃>60℃>20℃;KCl在钢表面的吸附符合Temkin吸附模型。通过Mathur经验动力学公式求出了腐蚀速度常数k和腐蚀动力学参数B,并根据这些参数详细讨论了缓蚀作用机理。     

棉竹竹叶提取物在HCl中对钢和铝的缓蚀作用

采用失重法和动电位极化曲线首次研究了棉竹竹叶提取物在1.0 mol/LHCl溶液中对冷轧钢和工业纯铝的缓蚀作用。结果表明：棉竹竹叶提取物对冷轧钢具有非常好的缓蚀作用,最大缓蚀率达95%,且在钢表面的吸附符合Langmuir吸附等温式;对铝具有中等程度的缓蚀作用,最大缓蚀率仅为55%,在铝表面的吸附也服从Langmuir吸附模型。极化曲线表明竹叶缓蚀剂为混合抑制型缓蚀剂。     

H3PO4中染料中性红对钢的缓蚀性能

用失重法研究了染料中性红对冷轧钢在1.0 mol/LH3PO4溶液中的缓蚀作用。结果表明：中性红对冷轧钢在1.0 mol/LH3PO4溶液中具有良好的缓蚀作用。缓蚀率先随缓蚀剂浓度的增加而增大,后减小,存在浓度极值现象;缓蚀率随温度的升高而增大。在吸附区间（25～150 mg/L）中性红在钢表面的吸附符合Temkin吸附等温式。通过热力学基本公式求出了相应的吸附热力学（吸附自由能△G0,吸附焓△H0,吸附熵△S0）;根据这些参数讨论了缓蚀作用机理。     

H2SO4中聚乙二醇20000在钢表面的吸附及缓蚀作用

用失重法研究了在1.0mol/L H2SO4中20-50℃聚乙二醇20000（PEG-20000）在冷轧钢表面上的吸附及缓蚀作用。结果表明：PEG-20000对钢具有良好的缓蚀作用,缓蚀率随缓蚀剂浓度的增加而增大;但随温度的增加而增大。PEG-20000在钢表面的吸附符合Langmuir吸附模型。通过吸附热力学和动力学公式分别求出了相应的吸附热力学参数（吸附自由能ΔG,°吸附焓ΔH°,吸附熵ΔS°）和动力学参数表观活化能Ea,并根据这些吸附参数详细讨论了缓蚀作用机理。     

H_2SO_4中聚乙二醇20000在钢表面的吸附及缓蚀作用

用失重法研究了在1.0mol/L H2SO4中20~50℃聚乙二醇20000(PEG-20000)在冷轧钢表面上的吸附及缓蚀作用。结果表明:PEG-20000对钢具有良好的缓蚀作用,缓蚀率随缓蚀剂浓度的增加而增大;但随温度的增加而增大。PEG-20000在钢表面的吸附符合Langmuir吸附模型。通过吸附热力学和动力学公式分别求出了相应的吸附热力学参数(吸附自由能ΔG,°吸附焓ΔH°,吸附熵ΔS°)和动力学参数表观活化能Ea,并根据这些吸附参数详细讨论了缓蚀作用机理。     

盐酸中硝氮黄染料在钢表面的吸附及缓蚀作用

用失重法研究了在1.0 mol/L HCl中染料类化合物硝氮黄(NY)在冷轧钢表面上的吸附及缓蚀作用。结果表明,NY对冷轧钢具有中等程度的缓蚀作用,缓蚀率随NY的浓度增加而增大,而随温度的增加而减小;NY在钢表面的吸附符合Temkin吸附模型。通过吸附理论求出了相应的吸附热力学参数(吸附自由能ΔG0,吸附热ΔH0,吸附熵ΔS0),并根据这些参数详细讨论了吸附和缓蚀作用机理。