(Fe50Co50)73.5Cu1Nb3Si13.5B9合金的微观结构及软磁性能

研究了(Fe50Co50)73.5Cu1Nb3Si13.5B9合金晶化过程中的微观结构及形成纳米晶后的合金软磁性能,发现在FINEMET合金基础上,用Co置换1/2含量Fe形成的(Fe50Co50)73.5Cu1Nb3Si13.5B9非晶合金具有相对较高居里温度Tc≈450℃,460℃退火处理后(Fe50Co50)73.5Cu1Nb3Si13.5B9合金形成均匀纳米晶组织,晶粒度约为20nm.     

用Co部分置换Fe对Fe73.5Cu1Nb3Si13.5B9合金高频磁性的影响

研究了(Fe100-xCox)73 5Cu1Nb3Si13.5B9(x=0、50)纳米晶软磁合金的高频磁特性.结果表明,用Co部分置换Fe后,仍可形成纳米晶结构,并且可以显著提高合金的高频特性.与典型的Fe73.5Cu1Nb3Si13.5B9纳米晶软磁合金相比,其复数磁导率实部μ略有下降,但表征损耗的复数磁导率虚部μ"却大幅度降低,从而可显著提高软磁材料的截止使用频率fr及品质因数Q,本文初步探讨了在Fe73 5Cu1Nb3Si13.5B9合金基础上,用Co置换Fe而使高频特性得到改善的机理.     

纳米晶Fe73.5Cu1Nb3Si13.5B9磁粉芯的磁性能研究

利用球磨纳米晶Ｆｅ７３．５Ｃｕ１Ｎｂ３Ｓｉ１３．５Ｂ９合金得到的粉末压制成磁粉芯,研究其磁性。结果表明,在测量的频率范围内（１ｋＨｚ－１００ｋＨｚ）,该粉芯的磁导率几乎不随频率变化的而变化;粉芯的品质因数Ｑ随的增加而增加,在较高频率时有着比坡莫合金粉芯还要高的值,具有应用价值。推导出磁粉芯的静态磁导率的表达式发现分芯的磁导率与磁粉芯的密度有着密切的密度愈大,磁粉芯的静态磁导率愈高。     

Fe/Fe_(73.5)Cu_1Nb_3Si_(13.5)B_9纳米晶磁粉芯研究

采用Fe粉复合FeCuNbSiB纳米晶粉体制备了磁粉芯,并讨论了退火温度、Fe粉复合量、纳米晶粉体粒度以及绝缘剂等对磁粉芯磁性能的影响.结果表明,在200～350℃和350～400℃内退火,随着温度的升高,μ_e均呈先增大后减小,375℃时达到最佳;当复合Fe粉后,发现其软磁性能得到了明显改善, Fe粉量为40%时,μ_e达到最大,且在100kHz～1MHz内,频率稳定性良好,其中心频率在500kHz附近,并随Fe粉量的增加而向低频发生偏移.纳米晶粉体的粒度越大,磁粉芯的磁性能越好;粉体粒度为100～200目时,其μ_e达到最大.当375℃退火,由有机绝缘剂、40%(质量分数)Fe粉、100～200目纳米晶粉制备的磁粉芯,其μ_e达52.72、损耗Pu为0.01317J/m~3、Bs为3.92×10~(-3)T、Br=6.48×10~(-5)T、H_c为1.28A/m.     

等温退火Fe73.5Cu1Mo3Si13.5B9合金的纳米晶结构及其与起…

本文用ＸＲＤ和ＴＥＭ研究了Ｆｅ７３．５Ｃｕ１Ｍｏ３Ｓｉ１３．５Ｂ９非晶合金在５２０℃２０－１２０ｍｉｎ退火后形成的纳米晶结构。结果表明，晶化相为局部具有ＤＯ３超结构的α－Ｆｅ（Ｓｉ），尺寸约为１４ｎｍ，α－Ｆｅ（Ｓｉ）晶粒由ＤＯ３有序区和序区组成。随退火时间的延长，α－Ｆｅ（Ｓｉ）的体积分数，Ｓｉ含量及ＤＯ３有序区尺寸增加。在退火时间为６０ｍｉｎ时，残余非晶相处于一特殊结构状态。α－Ｆｅ（Ｓｉ）相     

(FeCo)73.5Cu1Nb3S15.5B7纳米晶合金晶化过程的研究

采用四探针法和X射线衍射技术研究了(FeCo)73.5CuiNb3Si15.5B7合金在定速升温过程相对电阻率与结构的变化.实验发现在电阻率快速上升的温度范围与晶化的第一阶段有关,是由纳米尺寸bcc的α-Fe(Si)固溶体形成引起的.在晶化发生的第二阶段,剩余非晶相转变为硼化物(Fe3B和Fe23B6)相,电阻率有所下降.     

电脉冲快速退火Fe73.5Cu1Mo3Si13.5B9合金的组织与磁性能

采用电脉冲快速退火实现了非晶合金Ｆｅ７３．５Ｃｕ１Ｍｏ３Ｓｉ１３．５的纳米晶化。显微组织分析与磁性能测定结果表明,该合金经适当工艺的脉冲电流处理可得到较常规法晶粒密度更高、晶粒尺寸更小、软磁性能更优的纳米晶材料。基于随机无规磁各向异性模型,阐明了该合金的软磁性能与其显微结构的关系。     

Fe78Si9B13非晶合金磁芯封装及其软磁性能

研究了Fe78Si9B13非晶合金磁芯进行环氧封装及封装后对非晶合金磁芯软磁性能的影响。结果表明对磁芯进行环氧封装,有效改善磁芯的机械强度同时,能改善带材表面的平整度,在带材表面形成一层绝缘层,显著降低了非晶合金磁芯高频下的损耗值,封装后的非晶合金磁芯在Bm=1T,f=1kHz下,损耗值比封装前下降了14%。综合考虑机械强度大小、磁化难易、损耗高低等因素,封装胶浓度为2%时封装效果最佳。     

Fe70Cr8Mo2Si5B15非晶合金SPS烧结及磁性能

研究了SPS烧结温度对球磨熔体快淬Fe70Cr8Mo2Si5B15粉末的烧结块体合金组织结构与磁性能的影响.结果表明(1)在30MPa/5min条件下,当烧结温度从850℃提高至1000℃时,样品相对密度从95.8%增加到98.9%;(2)烧结样品主要组成相为α-Fe相,尚存在少量的第二相金属间化合物,且其α-Fe相平均粒晶尺寸处于纳米级范围;(3)随着烧结温度的提高,这些样品合金的比饱和磁化强度σs增加,矫顽力Hc随之降低.     

电脉冲快速退火Fe_(73.5)Cu_1Mo_3Si_(13.5)B_9合金的组织与磁性能

采用电脉冲快速退火实现了非晶合金Ｆｅ７３．５Ｃｕ１Ｍｏ３Ｓｉ１３．５Ｂ９的纳米晶化。显微组织分析与磁性能测定结果表明,该合金经适当工艺的脉冲电流处理可得到较常规法晶粒密度更高、晶粒尺寸更小、软磁性能更优的纳米晶材料。基于随机无规磁各向异性模型,阐明了该合金的软磁性能与其显微结构的关系     

应力退火对Fe73.5Cu1Nb3Si13.5B9纳米晶合金磁性能的影响

采用一种新的退火方式,将Fe73．5Cu1Nb3Si13．5B9合金薄带在铜环上卷绕成铁芯,研究在这种方式的退火过程中Fe73．5Cu1Nb3Si13．5B9合金薄带晶化时产生的张应力对其磁性的影响．结果表明：与普通退火相比,这种张应力使退火后合金的剩磁Br明显下降（最低为0.22T）,形成的感生磁各向异性的易轴垂直于张应力的方向．这种横向感生磁各向异性起因于纳米bccFe（Si）晶粒内通过内应力和负的磁滞伸缩引起的磁弹性作用。     

Si含量对纳米晶Fe_(87-x)Cu_1Nb_3Si_xB_9合金磁性能的影响

研究了Si含量对Fe87-xCu1Nb3SixB9合金经不同方式退火后磁性能的影响。结果表明:随Si含量的增加,Fe87-xCu1Nb3SixB9合金经普通退火后软磁性能逐渐得到优化;经磁退火后可感生出单轴磁各向异性,且磁退火特征随Si含量的增加而逐渐明显。根据横磁退火实验结果计算出的感生磁各向异性值Ku,则由26.7J/m3(Si=9.5at%)降低至14.1J/m3(Si=13.5at%)。由实验数据的分析认为Fe87-xCu1Nb3SixB9合金在高Si含量时经普通退火或纵磁退火后呈现优异的软磁特性,归因于析出的α-Fe(Si)相晶粒具有小的磁晶各向异性K1,从而导致合金具有更低的有效磁各向异性常数K所至。     

Fe73．5Cu1Nb3Si13．5B9纳米晶磁粉芯磁性能研究

用Fe73.5Cu1Nb3Si13.5B9纳米晶粉体,加入一定量的塑化剂,通过模压成型方法制备磁粉芯.实验结果表明,在一定粒度范围内,磁导率μ随粉体粒度增大而增大,品质因数Q,随着粒度的增大而减小,且在一定频率范围内,μ呈现良好的频率稳定性;塑化剂质量百分含量α越大,μ越小.当α=6.5%时,μ达到最大值31.8.0～300kHz范围内,α与Q成反比;300～1000kHz范围内,α与Q成正比例关系;磁导率μ随着成型压力的增加而提高,相反,压力越大,Q值越小;磁导率随着磁粉芯测试温度的提高逐渐减小,0≤f≤700kHz范围内,温度升高,Q降低,700kHz≤f≤1000kHz范围内时,温度升高,Q值升高;随退火温度的增加,μ和Q均呈现先增大后减小的趋势.     

Influence of annealing on the crystallographic structure and some magnetic properties of the Fe73.5Cu1Nb3-xUxSi13.5B9 nanocrystalline alloys

The influence of annealing on the structure and some magnetic properties of Fe73.5Cu1Nb3-xUxSi13.5B9 (x=1, 2, 3) alloys has been studied. The results confirmed the nanocrystalline character of these alloys in the temperature range 550–650 °C. The influence of the uranium content on the structural stability has been observed for annealing treatment at high temperature, i.e. at about 700 °C. The coercive field strongly depended both on the annealing temperature and on the uranium content. A minimum value of Hc was observed after annealing at 550 °C. Core losses of all alloys in the nanocrystalline state decreased with increasing uranium content. © 1998 Kluwer Academic Publishers     

Study of the crystallization kinetics in amorphous Fe73.5Cu1Nb3Si13.5B9 alloy

The kinetics of the crystallization of Fe_73.5Cu₁Nb₃Si_13.5B₉ amorphous alloy was studied using Mössbauer spectroscopy and X-ray diffractometry. During isothermal annealing of the samples, two phases were observed: a crystalline D0₃-FeSi alloy with fine grains and an amorphous phase enriched with niobium, boron and copper. It was found that the growth rate of the particles of the crystalline alloy was controlled by diffusion. For longer annealing time or at higher annealing temperature the growth process was found to be suppressed, probably by the niobium atoms. The activation energy obtained for the crystallization was about 143 kJ mol^–1.     

Fe86Zr5.5 Nb5.5 B3非晶合金的超高压烧结成型

为了获得致密的块状Fe86Zr55Nb55B3纳米晶合金,研究了高压快速烧结工艺参数对样品致密度和α-Fe相晶粒尺寸的影响.结果表明:快淬球磨破碎非晶粉末在5.5 GPa/3min烧结条件下,当Pw=1150 W后,可获得相对密度为98.3%、单相α-Fe纳米晶(16.3 nm)块体合金,且随着Pw和t的增加,样品相对密度和α-Fe相晶粒尺寸均略有增加,样品典型的比饱和磁化强度σs和矫顽力Hc分别为119.6 emu/g,63.8 Oe.     

纳米晶复合Nd9.5Fe81-xCoxZr3B6.5永磁材料磁性能的研究

采用熔体快淬及晶化退火工艺制备了Nd9.5Fe81-xCoxZr3B6.5(x=0、2、5、8、10)纳米晶合金条带,研究了Co的添加对快淬合金磁性能和居里温度的影响.结果表明,适量Co元素的添加能够有效降低各相晶粒的尺寸,增强了软、硬磁相晶粒的交换耦合作用,从而提高了合金的磁性能.Co含量为5%(原子分数)的合金,经670℃/4min的晶化处理后所得到的最佳磁性能为`Br=0.90T,jHc=588kA/m,(BH)max=117kJ/m3.     

Structure modification and recovery of amorphous Fe73.5Si13.5B9Nb3Cu1 magnetic ribbons after autoclave treatment: SAXS and thermodynamic analysis

The structure, crystallization kinetics and magnetic property of as-quenched Fe_(73.5)Si_(13.5)B_9Nb_3Cu_1 amorphous ribbon(R0) as well as ribbons after autoclave treatment at 100°C and 150°C(R1 and R2) have been systematically studied by various techniques. With increasing autoclave treatment temperature,the measured structural, kinetic and magnetic parameters of samples increase firstly, i.e. R0 R1; and then decrease or recover to the as-quenched sample, i.e. R2 R1 or R2 ≈ R0. These results indicate that the SROs in R1 samples increased by transforming from fcc to bcc structure during the autoclave treatment and that the autoclave treatment can decrease the large radius(r_M) MRO(medium range order),but increase the small rMMRO. The measured structural, thermal and magnetic parameters of R2 sample have a tendency to recover toward as-quenched R0 sample. The thermal and magnetic parameters of samples after solely annealing treatment at higher temperature have no obvious recover phenomenon.The uneven actions of pressure and temperature in autoclave treatment may be helpful for us to search a new method to improve the magnetic properties of Fe-based glasses.