Electrochemical performance of SrF2-coated LiNi1/3Co1/3Mn1/3O2 cathode materials for Li-ion batteries

SrF₂-coated LiNi_1/3Co_1/3Mn_1/3O₂ cathode materials with improved cycling performance over 2.5–4.6 V were investigated. The structural and electrochemical properties of the materials were studied using X-ray diffraction (XRD), scanning electron microscope (SEM), charge–discharge tests and electrochemical impedance spectra (EIS). The results showed that the crystalline SrF₂ with about 10–50 nm particle size is uniformly coated on the surface of LiNi_1/3Co_1/3Mn_1/3O₂ particles. As the coating amount increased from 0.0 to 2.0 mol%, the initial capacity and rate capability of the coated LiNi_1/3Co_1/3Mn_1/3O₂ decreased slightly owing to the increase of the charge-transfer resistance; however, the cycling stability was improved by suppressing the increase of the resistance during cycling. 4.0 mol% SrF₂-coated LiNi_1/3Co_1/3Mn_1/3O₂ showed remarkable decrease of the initial capacity. 2.0 mol% coated sample exhibited the best electrochemical performance. It presented an initial discharge capacity of 165.7 mAh g⁻¹, and a capacity retention of 86.9% after 50 cycles at 4.6 V cut-off cycling.     

Cycle life improvement of ZrO2-coated spherical LiNi1/3Co1/3Mn1/3O2 cathode material for lithium ion batteries

A modified synthesis process was developed based on co-precipitation method followed by spray drying process. In this process, a spherical shaped (Co_1/3Ni_1/3Mn_1/3)(OH)₂ precursor was synthesized by co-precipitation and pre-heated at 500 °C to form a high structural stability spinel (CoNiMn)O₄ to maintain its shape for further processing. The spherical LiNi_1/3Co_1/3Mn_1/3O₂ was then prepared by spray drying process using spherical spinel (CoNiMn)O₄. LiNi_1/3Co_1/3Mn_1/3O₂ powders were then modified by coating their surface with a uniform and nano-sized layer of ZrO₂. The ZrO₂-coated LiNi_1/3Co_1/3Mn_1/3O₂ material exhibited an improved rate capability and cycling stability under a high cut-off voltage of 4.5 V. X-ray diffraction (XRD) measurements revealed that the material had a well-ordered layered structure and Zr was not doped into the LiNi_1/3Co_1/3Mn_1/3O₂. Electrochemical impedance spectroscopy measurements showed that the coated material has stable cell resistance regardless of cycle number. The interrupt charging/discharging test indicated that the ZrO₂ coating can suppress the polarization effects during the charging and discharging process. From these results, it is believed that the improved cycling performance of ZrO₂-coated LiNi_1/3Co_1/3Mn_1/3O₂ is attributed to the ability of ZrO₂ layer in preventing direct contact of the active material with the electrolyte resulting in a decrease of electrolyte decomposition reactions.     

Preparation and electrochemical characterization of single-crystalline spherical LiNi1/3Co1/3Mn1/3O2 powders cathode material for Li-ion batteries

LiNi_1/3Co_1/3Mn_1/3O₂ has aroused much interest as a new generation of cathode material for Li-ion batteries, due to its great advantages in capacity, stability, low cost and low toxicity, etc. Here we report a novel single-crystalline spherical LiNi_1/3Co_1/3Mn_1/3O₂ material that is prepared by a convenient rheological phase reaction route. The X-ray powder diffraction, scanning electron microscopy and transmission electron microscopy indicate that the particles are highly dispersed with spherical morphologies and diameters of about 1-4 μm, and more interestingly, they show a perfect single-crystalline nature, which is not usual according to the crystal growth theories and may bring extra benefits to applications. Electrochemical tests show good performance of the material in both the capacity and cycling stability as cathode material in a model cell.     

Synthesis of LiNi1/3Co1/3Mn1/3O2 as a cathode material for lithium battery by the rheological phase method

LiNi_1/3Co_1/3Mn_1/3O₂ is prepared by a rheological phase method. Homogeneous precursor derived from this method is calcined at 800 °C for 20 h in air, which results in the impressive differences in the morphology properties and electrochemical behaviors of LiNi_1/3Co_1/3Mn_1/3O₂ in contrast to that obtained by a solid-state method. The microscopic structural features of LiNi_1/3Co_1/3Mn_1/3O₂ are investigated using scanning electron microscopy (SEM), X-ray diffraction (XRD). The electrochemical properties of LiNi_1/3Co_1/3Mn_1/3O₂ are carried out by charge–discharge cycling test. All experiments show that the microscopic structural features and the morphology properties are deeply related with the electrochemical performances. The obtained results suggest that the rheological phase method may become an effective route to prepare LiNi_1/3Co_1/3Mn_1/3O₂ cathode materials for lithium battery.     

Synthesis and characterization of submicron-sized LiNi1/3Co1/3Mn1/3O2 by a simple self-propagating solid-state metathesis method

Submicron-sized LiNi_1/3Co_1/3Mn_1/3O₂ cathode materials were synthesized using a simple self-propagating solid-state metathesis method with the help of ball milling and the following calcination. A mixture of Li(ac)·2H₂O, Ni(ac)₂·4H₂O, Co(ac)₂·4H₂O, Mn(ac)₂·4H₂O (ac = acetate) and excess H₂C₂O₄·2H₂O was used as starting material without any solvent. XRD analyses indicate that the LiNi_1/3Co_1/3Mn_1/3O₂ materials were formed with typical hexagonal structure. The FESEM images show that the primary particle size of the LiNi_1/3Co_1/3Mn_1/3O₂ materials gradually increases from about 100 nm at 700 °C to 200–500 nm at 950 °C with increasing calcination temperature. Among the synthesized materials, the LiNi_1/3Co_1/3Mn_1/3O₂ material calcined at 900 °C exhibits excellent electrochemical performance. The steady discharge capacities of the material cycled at 1 C (160 mA g⁻¹) rate are at about 140 mAh g⁻¹ after 100 cycles in the voltage range 3–4.5 V (versus Li⁺/Li) and the capacity retention is about 87% at the 350th cycle.     

Investigation of LiNi1/3Co1/3Mn1/3O2 cathode particles after 300 discharge/charge cycling in a lithium-ion battery by analytical TEM

Using analytical transmission electron microscopy (TEM) techniques reveal a zigzag layer on surface of the cycled particles of LiNi_1/3Co_1/3Mn_1/3O₂ cathode after 300 discharge/charge cycles. The Ni, Mn content in the zigzag layer of the cycled particle has decreased rapidly from interior to edge of the zigzag layer of the cycled particles. The structure of LiNi_1/3Co_1/3Mn_1/3O₂ oxide was gradually destructed from hexagonal cell with P3₁12 at interior region to fcc lattice of α-NaFeO₂ at edge of the zigzag layer of the cycled particles. These experimental data provide the compositional and structural origins of the capacity decrease in the Li-ion battery.     

Synthesis and characterization of LiNi0.6Mn0.4−xCoxO2 as cathode materials for Li-ion batteries

LiNi_0.6Co_xMn_0.4−xO₂ (x = 0.05, 0.10, 0.15, 0.2) cathode materials are prepared, and their structural and electrochemical properties are investigated using X-ray diffraction (XRD), scanning electron microscope (SEM), X-ray photoelectron spectroscopy (XPS), differential scanning calorimetric (DSC) and charge–discharge test. The results show that well-ordering layered LiNi_0.6Co_xMn_0.4−xO₂ (x = 0.05, 0.10, 0.15, 0.2) cathode materials are successfully prepared in air at 850 °C. The increase of the Co content in LiNi_0.6Mn_0.4−xCo_xO₂ leads to the acceleration of the grain growth, the increase of the initial discharge capacity and the deterioration of the cycling performance of LiNi_0.6Mn_0.4−xCo_xO₂. It also leads to the enhancement of the ratio Ni³⁺/Ni²⁺ in LiNi_0.6Co_xMn_0.4−xO₂, which is approved by the XPS analysis, resulting in the increase of the phase transition during cycling. This is speculated to be main reason for the deteriotion of the cycling performance. All synthesized LiNi_0.6Co_xMn_0.4−xO₂ samples charged at 4.3 V show exothermic peaks with an onset temperature of larger than 255 °C, and give out less than 400 J g⁻¹ of total heat flow associated with the peaks in DSC analysis profile, exhibiting better thermal stability. LiNi_0.6Co_0.05Mn_0.35O₂ with low Co content and good thermal stability presents a capacity of 156.6 mAh g⁻¹ and 98.5% of initial capacity retention after 50 cycles, showing to be a promising cathode materials for Li-ion batteries.     

Structural changes and thermal stability of charged LiNi1/3Co1/3Mn1/3O2 cathode material for Li-ion batteries studied by time-resolved XRD

Structural changes and their relationship with thermal stability of charged Li_0.33Ni_1/3Co_1/3Mn_1/3O₂ cathode samples have been studied using time-resolved X-ray diffraction (TR-XRD) in a wide temperature from 25 to 600 °C with and without the presence of electrolyte in comparison with Li_0.27Ni_0.8Co_0.15Al_0.05O₂ cathodes. Unique phase transition behavior during heating is found for the Li_0.33Ni_1/3Co_1/3Mn_1/3O₂ cathode samples: when no electrolyte is present, the initial layered structure changes first to a LiM₂O₄-type spinel, and then to a M₃O₄-type spinel and remains in this structure up to 600 °C. For the Li_0.33Ni_1/3Co_1/3Mn_1/3O₂ cathode sample with electrolyte, additional phase transition from the M₃O₄-type spinel to the MO-type rock salt phase takes place from about 400 to 441 °C together with the formation of metallic phase at about 460 °C. The major difference between this type of phase transitions and that for Li_0.27Ni_0.8Co_0.15Al_0.05O₂ in the presence of electrolyte is the delayed phase transition from the spinel-type to the rock salt-type phase by stretching the temperature range of spinel phases from about 20 to 140 °C. This unique behavior is considered as the key factor of the better thermal stability of the Li_1−xNi_1/3Co_1/3Mn_1/3O₂ cathode materials.     

Effect of Ag additive on the performance of LiNi1/3Co1/3Mn1/3O2 cathode material for lithium ion battery

The LiNi_1/3Co_1/3Mn_1/3O₂/Ag composite used for cathode material of lithium ion battery was prepared by thermal decomposition of AgNO₃ added to commercial LiNi_1/3Co_1/3Mn_1/3O₂ powders to improve the electrochemical performance of LiNi_1/3Mn_1/3Co_1/3O₂. Structure and morphology analysis showed that Ag particles were dispersed on the surface of LiNi_1/3Co_1/3Mn_1/3O₂ instead of entering the crystal structure. The results of charge–discharge tests showed that Ag additive could improve the cycle performance and high-rate discharge capability of LiNi_1/3Mn_1/3Co_1/3O₂. Extended analysis indicated that Ag was unstable in the commercial electrolyte at high potential. The improved electrochemical performance caused by Ag additive was associated not only with the enhancement of electrical conductivity of the material and the lower polarization of the cell, but also with the increased “c” parameter of LiNi_1/3Mn_1/3Co_1/3O₂ after repeated charge/discharge cycles and the compact and protective SEI layer formed on the surface of LiNi_1/3Mn_1/3Co_1/3O₂.     

Study of the surface modification of LiNi1/3Co1/3Mn1/3O2 cathode material for lithium ion battery

The surface of LiNi_1/3Co_1/3Mn_1/3O₂ (LNMCO) particles has been studied for material synthesized at 900 °C by a two-step process from a mixture of LiOH·H₂O and metal oxalate [(Ni_1/3Co_1/3Mn_1/3)C₂O₄] obtained by co-precipitation. Samples have been characterized by X-ray diffraction (XRD), high-resolution transmission electron microscope (HRTEM), Raman scattering (RS) spectroscopy, and magnetic measurements. We have investigated the effect of the heat treatment of particles at 600 °C with organic substances such as sucrose and starch. HRTEM images and RS spectra indicate that the surface of particles has been modified. The annealing does not lead to any carbon coating but it leads to the crystallization of the thin disordered layer on the surface of LiNi_1/3Co_1/3Mn_1/3O₂. The beneficial effect has been tested on the electrochemical properties of the LiNi_1/3Co_1/3Mn_1/3O₂ cathode materials. The capacity at 10C-rate is enhanced by 20% for post-treated LNMCO particles at 600 °C for half-an-hour.     

Physical and electrochemical properties of spherical Li1+x(Ni1/3Co1/3Mn1/3)1−xO2 cathode materials

A (Ni_1/3Co_1/3Mn_1/3)CO₃ precursor with an uniform, spherical morphology was prepared by coprecipitation using a continuously stirred tank reactor method. The as-prepared spherical (Ni_1/3Co_1/3Mn_1/3)CO₃ precursor served to produce dense, spherical Li_1+x(Ni_1/3Co_1/3Mn_1/3)_1−xO₂ (0 ≤ x ≤ 0.15) cathode materials. These Li-rich cathodes were also prepared by a second synthesis route that involved the use of an M₃O₄ (M = Ni_1/3Co_1/3Mn_1/3) spinel compound, itself obtained from the carbonate (Ni_1/3Co_1/3Mn_1/3)CO₃ precursor. In both cases, the final Li_1+x(Ni_1/3Co_1/3Mn_1/3)_1−xO₂ products were highly uniform, having a narrow particle size distribution (10-μm average particle size) as a result of the homogeneity and spherical morphology of the starting mixed-metal carbonate precursor. The rate capability of the Li_1+x(Ni_1/3Co_1/3Mn_1/3)_1−xO₂ electrode materials, which was significantly improved with increased lithium content, was found to be better in the case of the denser materials made from the spinel precursor compound. This result suggests that spherical morphology, high density, and increased lithium content were key factors in enabling the high rate capabilities, and hence the power performances, of the Li-rich Li_1+x(Ni_1/3Co_1/3Mn_1/3)_1−xO₂ cathodes.     

Structural and transport properties of LixNi1−y−zCoyMnzO2 cathode materials

In this work structural and transport properties of layered LiNi_1−y−zCo_yMn_zO₂ (y = 0.25, 0.35, 0.5 and z = 0.1) cathode materials are presented. In the considered group of oxides, LiNi_1−y−zCo_yMn_zO₂, there is no clear correlation between electrical conductivity and the a parameter (M-M distance in the octahedra layers). A non-monotonic modification of electrical properties of Li_xNi_0.65Co_0.25Mn_0.1O₂ cathode materials is observed upon lithium deintercalation.     

Nonflammable electrolyte for 3-V lithium-ion battery with spinel materials LiNi0.5Mn1.5O4 and Li4Ti5O12

The compatibility between dimethyl methylphosphonate (DMMP)-based electrolyte of 1 M LiPF₆/EC + DMC + DMMP (1:1:2 wt.) and spinel materials Li₄Ti₅O₁₂ and LiNi_0.5Mn_1.5O₄ was reviewed, respectively. The cell performance and impedance of 3-V LiNi_0.5Mn_1.5O₄/Li₄Ti₅O₁₂ lithium-ion cell with the DMMP-based nonflammable electrolyte was compared with the baseline electrolyte of 1 M LiPF₆/EC + DMC (1:1 wt.). The nonflammable DMMP-based electrolyte exhibited good compatibility with spinel Li₄Ti₅O₁₂ anode and high-voltage LiNi_0.5Mn_1.5O₄ cathode, and acceptable cycling performance in the LiNi_0.5Mn_1.5O₄/Li₄Ti₅O₁₂ full-cell, except for the higher impedance than that in the baseline electrolyte. All of the results disclosed that the 3 V LiNi_0.5Mn_1.5O₄/Li₄Ti₅O₁₂ lithium-ion battery was a promising choice for the nonflammable DMMP-based electrolyte.     

Structural and transport properties of layered Li1+x(Mn1/3Co1/3Ni1/3)1−xO2 oxides prepared by a soft chemistry method

In this work structural and transport properties of layered Li_1+x(Mn_1/3Co_1/3Ni_1/3)_1−xO₂ oxides (x = 0; 0.03; 0.06) prepared by a “soft chemistry” method are presented. The excessive lithium was found to significantly improve transport properties of the materials, a corresponding linear decrease of the unit cell parameters was observed. The electrical conductivity of Li_1.03(Mn_1/3Co_1/3Ni_1/3)_0.97O₂ composition was high enough to use this material in a form of a pellet, without any additives, in lithium batteries and characterize structural and transport properties of deintercalated Li_1.03−y(Mn_1/3Co_1/3Ni_1/3)_0.97O₂ compounds. For deintercalated samples a linear increase of the lattice parameter c together with a linear decrease of the parameter a with the increasing deintercalation degree occurred, but only up to 0.4-0.5 mol of extracted lithium. Further deintercalation showed a reversal of the trend. Electrical conductivity measurements performed of Li_1.03−y(Mn_1/3Co_1/3Ni_1/3)_0.97O₂ samples (y = 0.1; 0.3; 0.5; 0.6) showed an ongoing improvement, almost two orders of magnitude, in relation to the starting composition. Additionally, OCV measurements, discharge characteristics and lithium diffusion coefficient measurements were performed for Li/Li⁺/Li_1.03−y(Mn_1/3Co_1/3Ni_1/3)_0.97O₂ cells.     

Structural and electrochemical characterization of xLi[Li1/3Mn2/3]O2·(1 − x)Li[Ni1/3Mn1/3Co1/3]O2 (0 ≤ x ≤ 0.9) as cathode materials for lithium ion batteries

A series of cathode materials with molecular notation of xLi[Li_1/3Mn_2/3]O₂·(1 − x)Li[Ni_1/3Mn_1/3Co_1/3]O₂ (0 ≤ x ≤ 0.9) were synthesized by combination of co-precipitation and solid state calcination method. The prepared materials were characterized by X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) techniques, and their electrochemical performances were investigated. The results showed that sample 0.6Li[Li_1/3Mn_2/3]O₂·0.4Li[Ni_1/3Mn_1/3Co_1/3]O₂ (x = 0.6) delivers the highest capacity and shows good capacity-retention, which delivers a capacity ∼250 mAh g⁻¹ between 2.0 and 4.8 V at 18 mA g⁻¹.     

Studies on the low-heating solid-state reaction method to synthesize LiNi1/3Co1/3Mn1/3O2 cathode materials

The low-heating solid-state method has been adopted to synthesize LiNi_1/3Co_1/3Mn_1/3O₂ materials. The final product, with homogeneous phase and smooth crystals indicated by XRD and SEM results, can be synthesized at 700 °C, much lower than the synthesis temperatures of co-precipitation method. The reaction process and microstructure of precursor has been investigated by IR spectrum. By comparative studies with the mixture of CH₃COOLi and (Ni, Co, Mn)(C₂O₄), it is testified that the precursor is homogeneous, rather than a mixture. The decomposition process and the reaction energy have been studied to investigate the reaction mechanism of the precursor when heated at high temperature. The as-synthesized LiNi_1/3Co_1/3Mn_1/3O₂ exhibits excellent electrochemical properties, exhibiting initial specific capacity of 167 mAh g⁻¹ with stable cyclic performance.     

An amorphous LiCo1/3Mn1/3Ni1/3O2 thin film deposited on NASICON-type electrolyte for all-solid-state Li-ion batteries

Amorphous LiCo_1/3Mn_1/3Ni_1/3O₂ thin films were deposited on the NASICON-type Li-ion conducting glass ceramics, Li_1+x+yAl_xTi_2−xSi_yP_3−yO₁₂ (LATSP), by radio frequency (RF) magnetron sputtering below 130 °C. The amorphous films were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The Li/PEO₁₈-Li(CF₃SO₂)₂N/LATSP/LiCo_1/3Mn_1/3Ni_1/3O₂/Au all-solid-state cells were fabricated to investigate the electrochemical performance of the amorphous films. It was found that the low-temperature deposited amorphous cathode film shows a high discharge voltage and a high discharge capacity of around 130 mAh g⁻¹.     

Electrochemical effects of ALD surface modification on combustion synthesized LiNi1/3Mn1/3Co1/3O2 as a layered-cathode material

Combustion synthesized Li(Ni_1/3Mn_1/3Co_1/3)O₂ particles are coated with thin, conformal layers of Al₂O₃ by atomic layer deposition (ALD). XRD, Raman, and FTIR are used to confirm that no change to the bulk, local structure occurs after coating. Electrochemical impedance spectroscopy (EIS) results indicate that the surface of the Li(Ni_1/3Mn_1/3Co_1/3)O₂ are protected from dissolution and HF attack after only 4-layers, or ∼8.8 Å of alumina. Electrochemical performance at an upper cutoff of 4.5 V is greatly enhanced after the growth of Al₂O₃ surface film. Capacity retention is increased from 65% to 91% after 100 cycles at a rate of C/2 with the addition of only two atomic layers. Due to the conformal coating, the effects on Li(Ni_1/3Mn_1/3Co_1/3)O₂ overpotential and capacity are negligible below six ALD-layers. We propose that the use of ALD for coating on Li(Ni_1/3Mn_1/3Co_1/3)O₂ particles makes the material a stronger replacement candidate for LiCoO₂ as a positive electrode in lithium ion batteries.     

Thermal and electrochemical characterization of MCMB/LiNi1/3Co1/3Mn1/3O2 using LiBoB as an electrolyte additive

The gas generation associated with the use of the lithium bis(oxalate)borate—(LiBoB) based electrolyte at the elevated temperature were detected in the pouch cell (MCMB/LiNi_1/3Co_1/3Mn_1/3O₂ with 10% excess Li), which might prevent the LiBoB usage as a salt. However, the cell capacity retention was improved significantly, from 87 to 96% at elevated temperature, when using LiBoB as an electrolyte additive. The capacity fade during cycling is discussed using dQ/dE, area specific impedance, and frequency response analysis results. Most of the capacity loss in the cell is associated with the rise in the cell impedance. Moreover, results from the differential scanning calorimetry indicate that the thermal stability of the negative electrode with the solid electrolyte interface (SEI) formed by the reduction of the LiBoB additive was greatly improved compared with that obtained from the reduction of LiPF₆-based electrolyte without additive. In this case, the onset temperature of the breakdown of the LiBoB-based SEI is 150 °C which is higher than that of the conventional electrolyte without additive. Furthermore, the total heat generated between 60 and 170 °C is reduced from 213 to 70 J g⁻¹ when using LiBoB as electrolyte additive compared to the one without additive. In addition, the thermal stability of the charged LiNi_1/3Co_1/3Mn_1/3O₂ with 10% excess Li was not affected when using LiBoB as an electrolyte additive.     

Electrochemical performance of spinel LiMn2O4 cathode materials made by flame-assisted spray technology

Spinel lithium manganese oxide LiMn₂O₄ powders were synthesized by a flame-assisted spray technology (FAST) with a precursor solution consisting of stoichiometric amounts of LiNO₃ and Mn(NO₃)₂·4H₂O dissolved in methanol. The as-synthesized LiMn₂O₄ particles were non-agglomerated, and nanocrystalline. A small amount of Mn₃O₄was detected in the as-synthesized powder due to the decomposition of spinel LiMn₂O₄ at the high flame temperature. The impurity phase was removed with a post-annealing heat-treatment wherein the grain size of the annealed powder was 33 nm. The charge/discharge curves of both powders matched the characteristic plateaus of spinel LiMn₂O₄ at 3 V and 4 V vs. Li. However, the annealed powder showed a higher initial discharge capacity of 115 mAh g⁻¹ at 4 V. The test cell with annealed powder showed good rate capability between a voltage of 3.0 and 4.3 V and a first cycle coulombic efficiency of 96%. The low coulombic efficiency from capacity fading may be due to oxygen defects in the annealed powder. The results suggest that FAST holds potential for rapid production of uniform cathode materials with low-cost nitrate precursors and minimal energy input.