Study of LiFePO4 cathode materials coated with high surface area carbon

LiFePO₄ is a potential cathode material for 4 V lithium-ion batteries. Carbon-coated lithium iron phosphates were prepared using a high surface area carbon to react precursors through a solid-state process, during which LiFePO₄ particles were embedded in amorphous carbon. The carbonaceous materials were synthesized by the pyrolysis of peanut shells under argon, where they were carbonized in a two-step process that occurred between 573 and 873 K. The shells were also treated with a proprietary porogenic agent with the goal of altering the pore structure and surface area of the pyrolysis products. The electrochemical properties of the as-prepared LiFePO₄/C composite cathode materials were systematically characterized by X-ray diffraction, scanning electron microscope, element mapping, energy dispersive spectroscopy, Raman spectroscopy, and total organic carbon (TOC) analysis. In LiFePO₄/C composites, the carbon not only increases rate capability, but also stabilizes capacity. In fact, the capacity of the composites increased with the specific surface area of carbon. The best result was observed with a composite made of 8.0 wt.% with a specific surface area of 2099 m² g⁻¹. When high surface area carbon was used as a carbon source to produce LiFePO₄, overall conductivity increased from 10⁻⁸ to 10⁻⁴ S cm⁻¹, because the inhibition of particle growth during the final sintering process led to greater specific capacity, improved cycling properties and better rate capability compared to a pure olivine LiFePO₄ material.     

Morphology and electrical properties of carbon coated LiFePO4 cathode materials

Core-shell LiFePO₄@C composites were synthesized successfully from FePO₄/C precursor using the polyvinyl alcohol (PVA) as the reducing agent, followed by a chemical vapor deposition (CVD) assisted solid-state reaction in the presence of Li₂CO₃. Some physical and chemical properties of the products were characterized by X-ray powder diffraction (XRD), Raman, SEM, TEM techniques. The effect of morphology and electrochemical properties of the composites were thoroughly investigated. XRD patterns showed that LiFePO₄ has an order olivine structure with space group of Pnma. TEM micrographs exhibited that the LiFePO₄ particles encapsulated with 3-nm thick carbon shells. The powders were homogeneous with grain size of about 0.8 μm. Compared with those synthesized by traditional organic carbon source mixed method, LiFePO₄@C composite synthesized by CVD method exhibited better discharge capacity at initial 155.4 and 135.8 mAh g⁻¹ at 0.1C and 1C rate, respectively. It is revealed that the carbon layer coated on the surface of LiFePO₄ and the amorphous carbon wrapping and connecting the particles enhanced the electronic conductivity and rate performances of the cathode materials.     

Formation mechanism of LiFePO4/C composite powders investigated by X-ray absorption spectroscopy

The local structure and oxidation states for both the precursors and the LiFePO₄/C composite powders were investigated by X-ray absorption spectroscopy (XAS) to provide a deep insight into their formation mechanism. It was found that the local structure and oxidation states of the precursors and the synthesized LiFePO₄/C powders as well as the electrochemical properties of the synthesized powders were strongly influenced by the R ratio (R: molar ratio of citric acid to total metal ions). The oxidation states of iron ions of the precursors for R = 1 and 0.75 consist mainly of Fe(II) and traces of Fe(III). However, the oxidation state of iron ions of the precursor for R = 0.5 comprises mainly of Fe(III). The oxidation state of iron ions of all the synthesized powders is Fe(II). The structure of the precursors and the synthesized powders for R = 1 and 0.75 is more ordering than that for R = 0.5. It is in good agreement with the observation of the cation mixing obtained from the Riteveld analysis of the XRD data. The better the electrochemical performance is, the more ordering the structure or the less the cation mixing. However, the effect of the R values on the carbon content is also essential for the electrochemical properties of the synthesized LiFePO₄/C composite powders. Increasing the carbon content leads to the increase in the electronic conductivity but impedes the Li⁺ ion diffusion of the composite materials. Consequently, the powders synthesized at the optimal R ratio of 0.75 exhibited the highest initial capacity, about 150 mAh g⁻¹ when cycled at 1/40 C rate at room temperature. The structural scheme of the precursors and the synthesized powders and the formation mechanism of the LiFePO₄/C composite powders are also addressed in this work.     

Synthesis and electrochemical properties of olivine LiFePO4 prepared by a carbothermal reduction method

LiFePO₄/C composite cathode material was prepared by carbothermal reduction method, which uses NH₄H₂PO₄, Li₂CO₃ and cheap Fe₂O₃ as starting materials, acetylene black and glucose as carbon sources. The precursor of LiFePO₄/C was characterized by differential thermal analysis and thermogravimetry. X-ray diffraction (XRD), scanning electron microscopy (SEM) micrographs showed that the LiFePO₄/C is olivine-type phase, and the addition of the carbon reduced the LiFePO₄ grain size. The carbon is dispersed between the grains, ensuring a good electronic contact. The products sintered at 700 °C for 8 h with glucose as carbon source possessed excellent electrochemical performance. The synthesized LiFePO₄ composites showed a high electrochemical capacity of 159.3 mAh g⁻¹ at 0.1 C rate, and the capacity fading is only 2.2% after 30 cycles.     

Synthesis and electrochemical characterization of carbon-coated nanocrystalline LiFePO4 prepared by polyacrylates-pyrolysis route

A carbon-coated nanocrystalline LiFePO₄ cathode material was synthesized by pyrolysis of polyacrylate precursor containing Li⁺, Fe³⁺ and PO₄⁻. The powder X-ray diffraction (XRD) and high-resolution TEM micrographs revealed that the LiFePO₄/C composite as prepared has a core-shell structure with pure olivine LiFePO₄ crystallites as cores and intimate carbon coating as a shell layer. Between the composite particulates, there exists a carbon matrix binding the nanocrystallites together into micrometer particles. The electrochemical measurements demonstrated that the LiFePO₄/C composite with an appropriate carbon content can deliver a very high discharge capacity of 157 mAh g⁻¹ (>92% of the theoretical capacity of LiFePO₄) with 95% of its initial capacity after 30 cycles. Since this preparation method uses less costly materials and operates in mild synthetic conditions, it may provide a feasible way for industrial production of the LiFePO₄/C cathode materials for the lithium-ion batteries.     

Enhancement of electrochemical performance of lithium dry polymer battery with LiFePO4/carbon composite cathode

LiFePO₄/carbon composite electrode was prepared and applied to the dry polymer electrolyte. Enhanced low-temperature performance of LiFePO₄ was achieved by modifying the interface between LiFePO₄ and polymer electrolyte. The molecular weight of the polymer and the salt concentration as the Li/O ratio were optimized at 3 × 10⁵ and 1/10, respectively. Impedance analysis revealed that a small resistive component occurred in the frequency range of the charge transfer process. The reversible capacity of the laminate cell was 140 mAh g⁻¹ (C/20) and 110 mAh g⁻¹ (C/2) at 40 °C, which is comparable to the performance in the liquid electrolyte system.     

Morphological characterization of LiFePO4/C composite cathode materials synthesized via a carboxylic acid route

A new type of LiFePO₄/C composite surrounded by a web containing both amorphous and crystalline carbon phases was synthesized by incorporating malonic acid as a carbon source using a high temperature solid-state method. SEM, TEM/SAED/EDS and HRTEM were used to analyze surface morphology and confirmed for the first time that crystalline carbon was present in LiFePO₄/C composites. The composite was effective in enhancing the electrochemical properties such as capacity and rate capability, because its active component consists of nanometer-sized particles containing pores with a wide range of sizes. An EDS elemental map showed that carbon was uniformly distributed on the surface of the composite crystalline particles. TEM/EDS results clearly show a dark region that is LiFePO₄ with a trace of carbon and a gray region that is carbon only. To evaluate the materials’ electrochemical properties, galvanostatic cycling and conductivity measurements were performed. The best cell performance was delivered by the material coated with 60 wt.% malonic acid, which delivered first cycle discharge capacity of 149 mAh g⁻¹ at a C/5 rate and sustained 222 cycles at 80% of capacity retention. When carboxylic acid was used as a carbon source to produce LiFePO₄, overall conductivity increased from 10⁻⁵ to 10⁻⁴ S cm⁻¹, since particle growth was prevented during the final sintering process.     

The effect of carbon coating thickness on the capacity of LiFePO4/C composite cathodes

Two types of carbon source and precursor mixing pellets were employed simultaneously to prepare the LiFePO₄/C composite materials: Type I using the LiFePO₄ precursor with 20 wt.% polystyrene (PS) as a primary carbon source, and Type II using the LiFePO₄ precursor with 50 wt.% malonic acid as a secondary carbon vapor source. During final sintering, a Type I pellet was placed down-stream and Type II precursor pellet(s) was(were) placed upstream next to a Type I precursor pellet in a quartz-tube furnace. The carbon-coated product of the sintered Type I precursor pellet was obtained by using both PS and malonic acid as carbon sources. When two Type II pellets were used as a carbon vapor source (defined as Product-2), a more uniform film between 4 and 8 nm was formed, as shown in the TEM images. In the absence of a secondary carbon source (defined as Product-0), the discharge capacity of Product-0 was 137 mAh g⁻¹ with 100 cycles at a 0.2C-rate, but Product-2 demonstrated a high capacity of 151 mAh g⁻¹ with 400 cycles. Our results indicate that electrochemical properties of LiFePO₄ are correlated to the amount of carbon and its coating thickness and uniformity.     

Synthesis and characterization of Carbon Nano Fiber/LiFePO4 composites for Li-ion batteries

Carbon Nano Fibers (CNFs) coated with LiFePO₄ particles have been prepared by a non-aqueous sol–gel technique. The functionalization of the CNFs by HNO₃ acid treatment has been confirmed by Raman and XPS analyses. The samples pure LiFePO₄ and LiFePO₄–CNF have been characterized by XRD, SEM, RAMAN, XPS and electrochemical analysis. The LiFePO₄–CNF sample shows better electrochemical performance compared to as-prepared LiFePO₄. LiFePO₄–CNF (10 wt.%) delivers a higher specific capacity (∼140 mAh g⁻¹) than LiFePO₄ with carbon black (25 wt.%) added after synthesis (∼120 mAh g⁻¹) at 0.1C.     

Effects of carbon coating and iron phosphides on the electrochemical properties of LiFePO4/C

Carbon coated LiFePO₄ (LiFePO₄/C) with different contents of high electron conductive iron phosphide phase was synthesized by an aqueous sol–gel method in a reductive sintering atmosphere. Different synthesis parameters were used for adjusting the microstructure and phase compositions of the products. The effects of the carbon coating and iron phosphides on the electrochemical properties of the LiFePO₄/C electrodes were studied by means of testing the discharge capacities at rates of 0.1–5C (1C = 170 mAh g⁻¹) and analyzing the CV curves. The results show that carbon coating in a content of 1.5 wt.% derived from the carbon source of ethylene glycol greatly decreases the particle size of LiFePO₄ in one order in the specific surface area, and significantly improves the rate capability of LiFePO₄. The effect of the content of FeP on the capacity of the carbon coated LiFePO₄ was different at different discharge rates. Increasing the content of FeP from 1.2 to 3.7 wt.% slightly decreases the capacity of LiFePO₄/C at low discharge rate (0.1C and 1C), but obviously increases the capacity of LiFePO₄/C when the discharge rate is increased to 5C. For the carbon free sample, even it also has 1.8 wt.% FeP, it still possesses poor capacity due to the large particle size of LiFePO₄ and the lack of conductivity. And too much iron phosphides lowers the discharge capacity of the electrode since they are inert for the deinsertion/insertion of lithium ion.     

New freeze-drying method for LiFePO4 synthesis

The freeze-drying method is proposed as an effective synthesis process for the obtaining of LiFePO₄/C composites. The citric acid is used as a complexing agent and carbon source. After the low temperature annealing, the freeze-dried solution leads to a homogeneous carbon covered LiFePO₄ sample. The chemical characterization of the material included ICP and elemental analysis, infrared spectroscopy, X-ray diffraction, magnetic measurements and thermal analysis. SEM and TEM microscopies indicate an aggregate morphology with tiny particles of lithium iron phosphate inside a carbon matrix. Impedance spectroscopy showed a 8.0 × 10⁻⁷ S cm⁻¹ conductivity value. Cyclic voltammetry graphics displayed the two peaks corresponding to the Fe(II)/Fe(III) reaction and demonstrated the good reversibility of the material. The specific capacity value obtained at C/40 rate was 164 mAh g⁻¹, with a slight decrease on greater C-rates reaching 146 mAh g⁻¹ at C/1. The capacity retention study has evidenced good properties, with retention over 97% of the maximum values in the first 50 cycles, which allows an effective performance of the freeze-dried sample as cathodic material in lithium-ion batteries.     

Synthesis of LiFePO4/C composite with high-rate performance by starch sol assisted rheological phase method

LiFePO₄/C composite was synthesized at 600 °C in an Ar atmosphere by a soluble starch sol assisted rheological phase method using home-made amorphous nano-FePO₄ as the iron source. XRD, SEM and TEM observations show that the LiFePO₄/C composite has good crystallinity, ultrafine sphere-like particles of 100-200 nm size and in situ carbon. The synthesized LiFePO₄ could inherit the morphology of FePO₄ precursor. The electrochemical performance of the LiFePO₄ by galvanostatic cycling studies demonstrates excellent high-rate cycle stability. The Li/LiFePO₄ cell displays a high initial discharge capacity of more than 157 mAh g⁻¹ at 0.2C and a little discharge capacity decreases from the first to the 80th cycle (>98.3%). Remarkably, even at a high current density of 30C, the cell still presents good cycle retention.     

LiFePO4 with enhanced performance synthesized by a novel synthetic route

Pure LiFePO₄ was synthesized by heating an amorphous LiFePO₄. The amorphous LiFePO₄ obtained through lithiation of FePO₄·xH₂O by using oxalic acid as a novel reducing agent at room temperature. FePO₄·xH₂O was prepared through co-precipitation by employing FeSO₄·7H₂O and H₃PO₄ as raw materials. X-ray diffraction (XRD), scanning electron microscopy (SEM) observations showed that LiFePO₄ composites with fine particle sizes between 100 nm and 200 nm, and with homogenous sizes distribution. The electrochemical performance of LiFePO₄ powder synthesized at 500 °C were evaluated using coin cells by galvanostatic charge/discharge. The synthesized LiFePO₄ composites showed a high electrochemical capacity of 166 mAh g⁻¹ at the 0.1C rate, and possessed a favorable capacity cycling maintenance at the 0.1C, 0.2C, 0.5C and 1C rate.     

Conductive additive content balance in Li-ion battery cathodes: Commercial carbon blacks vs. in situ carbon from LiFePO4/C composites

Two samples of commercial conducting carbon black and the carbon generated in situ during LiFePO₄/C composite synthesis from citric acid are studied, with the aim of finding out whether carbon from the composite can fulfil the same function as carbon black in the electrode blend for a Li-ion battery. For this purpose, the carbon samples are analyzed by several techniques, such as X-ray diffraction, Raman spectroscopy, transmission electron microscopy, granulometry, BET specific area and conductivity measurements. Different cathode compositions and component proportions are tested for pellet and cast electrodes. Electrochemical results show that a moderate reduction of commercial carbon black content in both kinds of cathodes, by adding more LiFePO₄/C composite, enhanced the electrochemical behaviour by around 10%. In situ generated carbon can partially replace commercial conducting carbon black because its high specific surface probably enhances electrolyte penetration into the cathode, but it is always necessary to maintain a minimum amount of carbon black that provides better conductivity in order to obtain a good electrochemical response.     

Novel synthesis of LiFePO4-Li3V2(PO4)3 composite cathode material by aqueous precipitation and lithiation

LiFePO₄-Li₃V₂(PO₄)₃ composite cathode material is synthesized by aqueous precipitation of FeVO₄·xH₂O from Fe(NO₃)₃ and NH₄VO₃, following chemical reduction and lithiation with oxalic acid as the reducer and carbon source. Samples are characterized by XRD, SEM and TEM. XRD pattern of the compound synthesized at 700 °C indicates olivine-type LiFePO₄ and monoclinic Li₃V₂(PO₄)₃ are co-existed. TEM image exhibits that LiFePO₄-Li₃V₂(PO₄)₃ particles are encapsulated with a carbon shell 5-10 nm in thickness. The LiFePO₄-Li₃V₂(PO₄)₃ compound cathode shows good electrochemical performance, and its discharge capacity is about 139.1 at 0.1 C, 135.5 at 1 C and 116 mA h g⁻¹ at 3 C after 30 cycles.     

LiFePO4/carbon cathode materials prepared by ultrasonic spray pyrolysis

Small crystallites LiFePO₄ powder with conducting carbon coating can be synthesized by ultrasonic spray pyrolysis. Cheaper trivalent iron ion is used as the precursor. The pure olivine phase can be prepared with the duplex process of spray pyrolysis (synthesized at 450, 550 or 650 °C) and subsequent heat-treatment (at 650 °C for 4 h). The results indicate that the pyrolysis temperature of 450 °C is appropriate for best results. The carbon coating on the LiFePO₄ surface is critical to the electrochemical performance of LiFePO₄ cathode materials of the lithium secondary battery, since the carbon coating does not only increase the electronic conductivity via carbon on the surface of particles, but also enhance the ion mobility of lithium ion due to prohibiting the grain growth during post-heat-treatment. The carbon of 15 wt.% evenly distributed on the final LiFePO₄ powders can get the highest initial discharge capacity of 150 mA h g⁻¹ at C/10 and 50 °C.     

A study on the electrochemical characteristics of LiFePO4 cathode for lithium polymer batteries by hydrothermal method

Phospho-olivine LiFePO₄ cathode materials were prepared by hydrothermal reaction at 150 °C. Carbon black was added to enhance the electrical conductivity of LiFePO₄. LiFePO₄-C powders (0, 3, 5 and 10 wt.%) were characterized by X-ray diffraction (XRD) and transmission electron microscope (TEM). LiFePO₄-C/solid polymer electrolyte (SPE)/Li cells were characterized electrochemically by charge/discharge experiments at a constant current density of 0.1 mA cm⁻² in a range between 2.5 and 4.3 V vs. Li/Li⁺, cyclic voltammetry (CV) and ac impedance spectroscopy. The results showed that initial discharge capacity of LiFePO₄ was 104 mAh g⁻¹. The discharge capacity of LiFePO₄-C/SPE/Li cell with 5 wt.% carbon black was 128 mAh g⁻¹ at the first cycle and 127 mAh g⁻¹ after 30 cycles, respectively. It was demonstrated that cycling performance of LiFePO₄-C/SPE/Li cells was better than that of LiFePO₄/SPE/Li cells.     

Synthesis of carbon-coated LiFePO4 nanoparticles with high rate performance in lithium secondary batteries

A novel preparation technique was developed for synthesizing carbon-coated LiFePO₄ nanoparticles through a combination of spray pyrolysis (SP) with wet ball milling (WBM) followed by heat treatment. Using this technique, the preparation of carbon-coated LiFePO₄ nanoparticles was investigated for a wide range of process parameters such as ball-milling time and ball-to-powder ratio. The effect of process parameters on the physical and electrochemical properties of the LiFePO₄/C composite was then discussed through the results of X-ray diffraction (XRD) analysis, field-emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), the Brunauer-Emmet-Teller (BET) method and the use of an electrochemical cell of Li|1 M LiClO₄ in EC:DEC = 1:1|LiFePO₄. The carbon-coated LiFePO₄ nanoparticles were prepared at 500 °C by SP and then milled at a rotating speed of 800 rpm, a ball-to-powder ratio of 40/0.5 and a ball-milling time of 3 h in an Ar atmosphere followed by heat treatment at 600 °C for 4 h in a N₂ + 3% H₂ atmosphere. SEM observation revealed that the particle size of LiFePO₄ was significantly affected by the process parameters. Furthermore, TEM observation revealed that the LiFePO₄ nanoparticles with a geometric mean diameter of 146 nm were coated with a thin carbon layer of several nanometers by the present method. Electrochemical measurement demonstrated that cells containing carbon-coated LiFePO₄ nanoparticles could deliver markedly improved battery performance in terms of discharge capacity, cycling stability and rate capability. The cells exhibited first discharge capacities of 165 mAh g⁻¹ at 0.1 C, 130 mAh g⁻¹ at 5 C, 105 mAh g⁻¹ at 20 C and 75 mAh g⁻¹ at 60 C with no capacity fading after 100 cycles.     

Physical and electrochemical properties of LiFePO4 nanoparticles synthesized by a combination of spray pyrolysis with wet ball-milling

A novel preparation technique was developed to synthesize LiFePO₄ nanoparticles through a combination of spray pyrolysis (SP) with wet ball-milling (WBM). Using this technique, the preparation of LiFePO₄ nanoparticles was investigated for a wide range of process parameters such as ball-milling time and sintering temperature. The effect of process parameters on the physical and electrochemical properties of LiFePO₄ was then discussed through analysis using by X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), the Brunauer–Emmet–Teller (BET) method, Raman spectroscopy and using an electrochemical cell of Li|1 M LiClO₄ in EC:DEC = 1:1|LiFePO₄. LiFePO₄ nanoparticles with a geometric mean diameter of 58 nm were prepared at a rotating speed of 800 rpm and a ball-milling time of 12 h in an Ar atmosphere followed by heat treatment at 500 °C for 4 h in a N₂ + 3% H₂ atmosphere. The sample delivered first discharge capacities of 164 and 100 mAh g⁻¹ at charge–discharge rates of 0.1 and 10 C in the test cells, respectively. The electrochemical properties of LiFePO₄ nanoparticles were strongly affected by the formation of Fe₂P, Fe₃P and α-Fe₂O₃ at higher charge–discharge rates.     

Synthesis and effect of forming Fe2P phase on the physics and electrochemical properties of LiFePO4/C materials

Series LiFePO₄/C materials have been prepared by a so-called reformative solid-coordination method, which uses citric acid as the coordination agent and carbon source. A monodenate coordination band of –COO-M was proved to form gradually and that would help to disperse Li⁺ or Fe²⁺ among the homogeneous gel during the grinding process. Impure phase Fe₂P was detected out among the LiFePO₄/C composites with increasing annealed temperature. The remnant coating carbon was considered to be the reductive under the pure nitrogen gas. The amounts of carbon, particle size and morphology were investigated in detail and all the results showed to be related to the formation of Fe₂P. The electro-conductive Fe₂P phase among LiFePO₄/C composites acts as important role in increasing electronic conductivity and evidently improves the electrochemical performance of LiFePO₄/C including the less polarization phenomenon, comparatively high reversible capability, stable cycling performance and slight trend of less loss of rate capability.