Effect of CrSi2 on the ablation resistance of a ZrSi2-Y2O3/SiC coating prepared by SAPS

To improve the ablation resistance of carbon/carbon (C/C) composites, a proportional amount of ZrSi₂-CrSi₂-Y₂O₃ mixed particles were deposited on the surface of SiC-coated C/C composites by supersonic air plasma spraying (SAPS) to form a ZrSi₂-CrSi₂-Y₂O₃/SiC coating. The microstructure and phase compositions of the coating were studied by SEM, EDS, XRD and its anti-ablation performance was tested by oxyacetylene torch. The experimental results showed that the ZrSi₂-CrSi₂-Y₂O₃ outer coating had a dense microstructure without obvious pores and microcracks, and the thickness reached approximately 150 μm. In the process of being eroded and scoured by the oxyacetylene flame, the coating exhibited excellent anti-ablation property, which was attributed to the mosaic microstructure formed by ZrO₂ and a Si-O-Cr liquid film on the coating surface. After experiencing an ablation time of 80 s, the linear ablation rate and the mass ablation rate of the coating were -1.0 ± 0.03 μm s^-1 and -0.16 ± 0.014 mg s^-1, respectively.     

Bimodal microstructure ZrB2-MoSi2 coating prepared by atmospheric plasma spraying for carbon/carbon composites against long-term ablation

To protect carbon/carbon composites against long-term ablation, a bimodal microstructure ZrB₂-MoSi₂ coating, consisting of an outer ZrB₂-MoSi₂ layer modified by Y₂O₃ and an inner basal ZrB₂-MoSi₂ layer, was prepared by atmospheric plasma spraying. The microstructure, phase composition and ablation resistance of the proposed coating were investigated in detail. Results showed that the bimodal coating maintained integrity in structure except for phase composition. There was no visible interlayer between the inner ZrB₂-MiSi₂ layer and the outer modified one. Mass ablation rate of the bimodal microstructure ZrB₂-MoSi₂ coated C/C composites was −2.02 × 10⁻³ g/s under an oxyacetylene flame ablation at 1873 K for 600 s, which exhibited better ablation resistance than a single ZrB₂-MoSi₂ coating. The excellent ablation resistance was ascribed to the positive effect of Y₂O₃, which not only pined in the glassy phase and alleviated the volatilization of SiO₂ glass phase by reacting with SiO₂ to form high viscosity of Y₂SiO₅, but also stabilized ZrO₂ and promoted its recrystallization and growth.     

Nanosized (Zr,Hf)O2 coating reinforced by AlN whiskers for the ablation protection of SiC coated C/C composites

In this work, AlN whisker-reinforced (Zr, Hf)O₂ coating was prepared on SiC coated carbon/carbon composites by sol-gel and plasma spraying methods. Its cyclic ablation resistance was evaluated using an oxyacetylene torch with a heat flux of 2.38 MW/m². After ablation, the coating showed apparently decreased crack sizes and quantity as compared with the one without AlN whisker addition, pointing out its better crack tolerance. Moreover, the coating had a thinner oxidized region based on the linear ablation rate (−0.042 µm/s), greatly lower than that of pure oxide coating (−0.922 µm/s). After detailed observation and characterization, probable protection mechanism was proposed.     

Ablation resistance of HfB2-SiC coating prepared by in-situ reaction method for SiC coated C/C composites

To improve the ablation resistance of SiC coating, HfB₂-SiC coating was prepared on SiC-coated carbon/carbon (C/C) composites by in-situ reaction method. Owing to the penetration of coating powders, there is no clear boundary between SiC coating and HfB₂-SiC coating. After oxyacetylene ablation for 60 s at heat flux of 2400 kW/m², the mass ablation rate and linear ablation rate of the coated C/C composites were only 0.147 mg/s and 0.267 µm/s, reduced by 21.8% and 60.0%, respectively, compared with SiC coated C/C composites. The good ablation resistance was attributed to the formation of multiple Hf-Si-O glassy layer including SiO₂, HfO₂ and HfSiO₄.     

Comparing ablation properties of NbC and NbC-25 mol.% ZrC coating on SiC-coated C/C composites

In this work, ablation properties of NbC and NbC-25 mol.% ZrC coating, deposited on SiC-coated C/C composites by supersonic atmospheric plasma spraying, were tested by an oxyacetylene torch. Results showed that, for NbC coating, an unexpected smooth liquid film mostly composed of niobium suboxides (such as NbO₂ and NbO), rather than pure Nb₂O₅, generated during ablation for 45 s. Mechanical erosion resulted from the molten SiO₂, and the relatively low viscosity of the outer oxide layer owing to insufficiently high melting point of niobium suboxides were the key factors for the failure mechanism of NbC coating. While NbC–ZrC coating abated for 90 s has a 97.49 and 66.53% decrease of linear and mass ablation rate relative to NbC coating ablated for 45 s, since ZrO₂ hindering the evaporation of SiO₂ droplets, and more thermal-stable Nb–O–Zr liquid film endow (NbC–ZrC)/SiC/C/C composites with an outstanding anti-ablation property.     

Preparation of carbon/carbon‐ultra high temperature ceramics composites with ultra high temperature ceramics coating

In order to increase the oxidation resistance of carbon/carbon (C/C) composites at long‐term high temperature, C/C‐Ultra High Temperature Ceramics composites (UHTCs) with a dual‐layer UHTCs oxidation coating was successfully designed and fabricated. The microstructure and ablation resistance were investigated and discussed. After ablation in arc‐heated wind tunnel with temperature being 2200°C for 1000s, the mass ablation rate and linear ablation rate were ?1.9 × 10^?2 mg/cm²s and 2.9 × 10^?5 mm/s, respectively. The formation of thermodynamically compatible oxide scale including ZrO₂ skeleton and SiO₂ or Zr–Si–O glass on the surface were mainly contributed to the excellent ablation resistance of the composite.     

Long-time ablation protection of carbon/carbon composites with different-La2O3-content modified ZrC coating

Long time oxidation protection at ultra-high temperatures or ablation protection has been a choke point for C/C composites. In this study, long time ablation protection of different-La₂O₃-content (5–30 vol.%) modified ZrC coating for SiC-coated carbon/carbon (C/C) composites was investigated. Results showed that ZrC coating with 15 vol.% La₂O₃ had good ablation resistance and could protect C/C composites for at least 700?s at 2160 °C. A high-thermal-stability and low-oxygen-diffusivity oxide scale containing m-ZrO₂ particles and molten phases with La_0.1Zr_0.9O_1.95 and La₂Zr₂O₇ was formed during ablation, offering the ablation protection. La could erode grain boundaries of ZrO₂ to refine ZrO₂ by short-circuit diffusion and m-ZrO₂ particles were retained due to less bulk diffusion than grain-boundary diffusion of La into ZrO₂. The erosion resulted in the formation of molten phases containing fine nano-ZrO₂, which served as viscous binder among m-ZrO₂ particles and crack sealer for the oxide scale.     

Oxidation resistance,ablation resistance and in situ ceramization mechanism of Al-coated carbon fiber/boron phenolic resin ceramizable composites modified with Ti3SiC2

Inherent defect of easy oxidation limited further application of carbon fiber/phenolic resin composites in hostile environments. Herein, a combined strategy of matrix modification and fiber coating was proposed to fabricate a novel ceramizable composite containing Al-coated carbon fibers and Ti₃SiC₂ toward thermal protection materials (TPM), which offered a promising solution to challenge facing long-term thermal protection and load-bearing subject to severe oxidation corrosion and ablation in hypersonic vehicle applications. Oxidation resistance, mechanical strength evolution, phase evolution, microstructure evolution and mechanical strength failure mechanism at elevated temperatures were studied based on thermogravimetric analysis, static ablation test, mechanical test, X-ray diffraction analysis, and scanning electron microscopy coupled with energy dispersive X-ray analysis. The resulting composites exhibited outstanding oxidation resistance, with residue yield at 1600 °C and flexural strength at 1400 °C as high as 87.7% and 31.7 MPa, respectively. It was found that dense multiphase ceramics formed by reactions between Ti₃SiC₂, O₂, pyrolytic carbon (PyC) and N₂, acted as oxygen barriers and self-healing agents during static ablation. Besides, the resulting composites exhibited satisfactory ablation resistance and the linear ablation rate was as low as 0.00853 mm/s. Furthermore, ablation mechanisms were revealed based on phase identification, microstructure characterization and thermodynamic calculation analysis. It was revealed that multiphase ceramics composed of PyC, Al coatings, Ti₃SiC₂, TiC, Al₂OC and AlB₂ contributed great to the ablation resistance during oxyacetylene ablation.     

Ablation behavior and mechanism of C/C–ZrC–SiC composites under an oxyacetylene torch at 3000 °C

C/C–ZrC–SiC composites with continuous ZrC–SiC ceramic matrix were prepared by a multistep technique of precursor infiltration and pyrolysis process. Ablation properties of the composites were tested under an oxyacetylene flame at 3000 °C for 120 s. The results show that the linear ablation rate of the composites was about an order lower than that of pure C/C and C/C–SiC composites as comparisons, and the mass of the C/C–ZrC–SiC composites increased after ablation. Three concentric ring regions with different coatings appeared on the surface of the ablated C/C–ZrC–SiC composites: (i) brim ablation region covered by a coating with layered structure including SiO₂ outer layer and ZrO₂–SiO₂ inner layer; (ii) transition ablation region, and (iii) center ablation region with molten ZrO₂ coating. Presence of these coatings which acted as an effective oxygen and heat barrier is the reason for the great ablation resistance of the composites.     

Evaluation of Rare‐Earth Modified ZrB2–SiC Ablation Resistance Using an Oxyacetylene Torch

Rare‐earth modified ZrB₂–SiC coatings were prepared via mechanical mixing Sm₂O₃ or Tm₂O₃ powders with spray‐dried ZrB₂, or by chemically doping samarium ions into spray‐dried ZrB₂. In either approach, SiC powders were also added and coatings were fabricated via shrouded air plasma spray. An oxyacetylene torch was utilized to evaluate the coatings under high heat flux conditions for hold times of 30 and 60 s. The resulting phases and microstructures were evaluated as a function of rare‐earth type, modification approach, and ablation time. A brittle m‐ZrO₂ scale was observed in the ZrB₂/SiC‐only coating after ablative tests; during cooling this scale detached from the unreacted coating. In contrast, rare‐earth modified coatings formed a protective oxide scale consisting primarily of either Sm_0.2Zr_0.8O_1.9 or Tm_0.2Zr_0.8O_1.9, along with small amount of m‐ZrO₂. These rare‐earth oxide scales displayed high thermal stability and remained adhered to the unreacted coating during heating and cooling, offering additional oxidation protection.     

Infrared radiative performance and anti-ablation behaviour of Sm2O3 modified ZrB2/SiC coatings

To improve the emissivity of ZrB₂/SiC coatings for serving in more serious environment, ZrB₂/SiC coatings with varying contents of high emissivity Sm₂O₃ were fabricated using atmospheric plasma spraying. The microstructure, infrared radiative performance and anti-ablation behaviour of the modified coatings were investigated. The results showed that as the content of Sm₂O₃ increased, the density of the coatings increased because of the low melting point of Sm₂O₃. When the content of Sm₂O₃ was 10 vol%, the coating had the highest emissivity in the 2.5–5 μm band at 1000 °C, up to 0.85, because of the oxygen vacancies promoting additional electronic transitions. Due to the high emissivity, the surface temperature of the coating modified with 10 vol% Sm₂O₃ decreased by 300 °C, which led to little volatilisation of the sealing phase. Further, the mass ablation ratio of the above coating was 3.19 × 10^?4 g/s, decreasing 31% compared to that of a ZrB₂/SiC coating. The formed dense surface structure of the coatings showed considerable oxygen obstructive effects. These findings indicate that the modified coatings show considerable anti-ablation performance, which provides effective anti-ablation protection for the C/C composite substrate.     

Enhanced bonding strength and thermal cycling performance of MoSi2–CrSi2–SiC–Si coating for carbon/carbon composites by surface modification via blasting treatment

Before the preparation of MoSi₂–CrSi₂–SiC–Si coating, blasting treatment of carbon/carbon (C/C) composites, as a surface modification method, was conducted under oxyacetylene torch. MoSi₂–CrSi₂–SiC–Si coating was prepared on the treated C/C composites by pack cementation, where an interlock interface was formed between the coating and the C/C substrate. After blasting treatment, the thermal expansion coefficient mismatch between the coating and C/C substrate was alleviated efficiently, and the bonding strength of the coating was increased by 45.6% and reached 26.2 MPa. To simulate the real working condition, thermal cycling test was conducted under oxyacetylene torch from 1600 °C to room temperature to construct an environment of combustion gas erosion. Due to the improvement of bonding strength and the alleviation of thermal expansion coefficient mismatch between the coating and the C/C substrate, thermal cycling performance of MoSi₂–CrSi₂–SiC–Si coating was enhanced. After 25 thermal cycles, the mass loss of the coated C/C composites without blasting treatment was up to 2.4%, and the C/C substrate was partially exposed. In contrast, the mass loss of the coated C/C composites with blasting treatment was only 1.1%.     

Ablation behavior of ZrB2–SiC protective coating for carbon/carbon composites

Ablation behavior of ZrB₂–SiC protective coating for carbon/carbon composites during oxyacetylene flame test at 2500 °C was investigated by analyzing the microstructure differentiation caused by the increasing intensity of ablation from the border to the center of the surface. After ablation, a continuous SiO₂ scale, a porous SiO₂ layer inlaid with fine ZrO₂ nuclei, and a continuous ZrO₂ scale respectively emerged in the border region, the transitional region, and the center region. In order to investigate the ablation microstructure in the initial stage, the sub-layer microstructure was characterized and found to be mainly formed by coral-like structures of ZrO₂, which showed huge difference with the continuous structure of ZrO₂ on the surface layer. A kinetic model concerning the thickness change induced by volatilization and oxidation during ablation was built to explain the different growth mechanisms of the continuous ZrO₂ scale and the coral-like ZrO₂ structure.     

Ultra-high temperature ceramic coating for carbon/carbon composites against ablation above 2000 K

To improve the ablation resistance of carbon/carbon composites at the temperature above 2000 K, a ZrB₂-SiC-ZrC ultra-high temperature ceramic coating was prepared by combination of supersonic atmosphere plasma spray (SAPS) and reaction melt infiltration. The micro-holes in ZrB₂-Si-ZrC coating prepared by SAPS were effectively filled and the compactness and interface compatibility between the coating and C/C composites was improved through the reaction melt infiltration process. The ultra-high temperature ceramic coating exhibited good ablation resistance under oxyacetylene torch ablation above 2000 K. After ablation for 120 s, the mass and linear ablation rates of the ZrB₂-SiC-ZrC coated C/C samples were only ?0.016 × 10^?3 g/s and 1.30 µm/s, respectively. Good ablation resistance of the ultra-high temperature ceramic coating is mainly attributed to the dense coating structure and the improvement of interface compatibility between the coating and C/C composites.     

WSi2 modified HfB2-SiC coating: Microstructure and ablation resistance

To enhance the ablation resistance of carbon/carbon composites, WSi₂ modified HfB₂-SiC coating was prepared by slurry dipping combined with vapor silicon infiltration. The effect of WSi₂ contents on the ablation performance of the coating was investigated. The results showed that the coating with 20 wt% WSi₂ had the best ablation resistance under oxyacetylene torch. During ablation, a dense Hf-Si-W-O oxide layer was covered on the coating surface, inhibiting the diffusion of oxygen. Additionally, WSi₂ with high emissivity and the formed W with good thermal conductivity played a role in reducing the ablation temperature. These effects contributed to the improvement of ablation performance.     

High temperature oxidation resistance of Y2O3 modified ZrB2-SiC coating for carbon/carbon composites

To protect carbon/carbon (C/C) composites from oxidation at high temperature, Y₂O₃ modified ZrB₂-SiC coating was fabricated on C/C composites by atmospheric plasma spraying. The microstructure and chemical composition of the coatings were characterized by SEM, EDS, and XRD. Experiment results showed that the coating with 10 wt% Y₂O₃ presented a relatively compact surface without evident holes and cracks. No peeling off occurred on the interface between the coating and substrate. The ZSY10 coating underwent oxidation at 1450 °C for 10 h with a mass loss of 5.77%, while that of ZS coating was as high as 16.79%. The existence of Y₂O₃ played an important role in inhibiting the phase transition of ZrO₂, thus avoiding the cracks caused by the volume expansion of the coating. Meanwhile, Y₂SiO₅ and ZrSiO₄ had a similar coefficient of thermal expansion (CTE), which could relieve the thermal stress inside the coating. The ceramic phases Y₂SiO₅, Y₂Si₂O₇ and ZrSiO₄ with high thermal stability and low oxygen permeability reduced the volatilization of SiO₂.     

Ablation behavior of single and alternate multilayered ZrC-SiC coatings under oxyacetylene torch

Based on the investigation of ablation behavior and thermal stress of the monolayered ZrC-SiC coatings with different SiC amounts, an alternate coating consisting of 4 sublayers with 10 and 70 vol.% SiC was prepared on SiC-coated carbon/carbon (C/C) composites through plasma spraying technique. Ablation tests were carried out under oxyacetylene torch with a heat flux of 2.38 MW/m². The alternate coating could offer 90 s ablation shield for C/C composites, providing superior ablation properties than all monolayered coatings. The improved ablation resistance is mostly induced by the fact that the outmost scale with abundant ZrO₂ particles was able to better endure the mechanical denudation from the torch. Moreover, due to the indirect contact with torch, the innermost sublayers were placed into relatively mild environment, thereby most of Si-based oxides could be retained and further hinder oxygen transport inward during ablation.     

A novel combination of precursor pyrolysis assisted sintering and rapid sintering for construction of multi-composition coatings to improve ablation resistance of SiOC ceramic modified carbon fiber needled felt preform composites

A double-layer coating composed of MoSi₂–SiO₂–SiC/ZrB₂–MoSi₂–SiC was designed and successfully constructed by a novel combination of precursor pyrolysis assisted sintering and rapid sintering to improve the ablation resistance of SiOC ceramic modified carbon fiber needled felt preform composites (CSs). The ZrB₂–MoSi₂–SiC inner layer coating was in relatively uniform distribution in the zone of 0–3 mm from the surface of CSs through the slurry/precursor infiltration in vacuum and SiOC precursor pyrolysis assisted sintering, which played a predominant role in improving oxidation and ablation resistance and maintaining the morphology of CSs. The MoSi₂–SiO₂–SiC outer layer coating was prepared by the spray and rapid sintering to further protect CSs from high-temperature oxidation. The ablation resistance of CSs coated with double-layer coating was evaluated by an oxygen-acetylene ablation test under the temperature of 1600–1800 °C with different ablation time of 1000 and 1500 s. The results revealed that the mass recession rates increased with the rise of ablation temperature and extension of ablation time, ranging from 0.47 g/(m²·s) to 0.98 g/(m²·s) at 1600–1800 °C for 1000 s and from 0.72 g/(m²·s) to 0.86 g/(m²·s) for 1000–1500 s at 1700 °C, while the linear recession rates showed negative values at 1700 °C due to the formation of oxides, such as SiO₂ and ZrO₂. The ablation mechanism of the double-layer coating was analyzed and found that a SiO₂–ZrO₂–Mo_4.8Si₃C_0.6 oxidation protection barrier would be formed during the ablation process to prevent the oxygen diffusion into the interior CSs, and this study provided a novel and effective way to fabricate high-temperature oxidation protective and ablation resistant coating.     

Effects of surface structure unit of 2D needled carbon fiber preform on the microstructure and ablation properties of C/C-ZrC-SiC composites

To investigate the effects of different structure units on the ablation properties of C/C-ZrC-SiC composites produced from 2D needled carbon fiber preforms as reinforcements, non-woven layer, short-cut fiber web and the surface of laminated layers of the composites were ablated by oxyacetylene flame respectively. Results showed that the formation ability of surface protective layer and the fiber orientation were the key factors, determining ablation properties of different structure units. Short-cut fiber web presented the best ablation resistance due to the forming of compactly integrated ZrO₂ self-protection coating because of its sufficient ceramic content. However, only scattered oxide particles formed on the ablated surface of non-woven layer, which resulted in serious erosion of carbon fibers and carbon matrices, leading to the poor ablation resistance. Compared with the non-woven layer perpendicular to the flame, the anti-ablation property was even worse when it paralleled to the flame.     

Ablation resistance of SiC‐modified ZrC coating prepared by SAPS for SiC‐coated carbon/carbon composites

This study evaluated the ablation resistance of ZrC/SiC coating for carbon/carbon (C/C) composites at different temperatures and heat fluxes, which improved the researches on ultra‐high temperature oxidation of ZrC/SiC system. Results showed that the protection of coating depended on temperature and heat flux. Ablation test for 120 seconds under heat flux of 2.4 MW/m² at 2270°C revealed a good ablation resistance, with the linear ablation rate reduced by 96.4% and the mass gain rate increased by 383.3% compared with those of pure ZrC coating. The good ablation resistance was attributed to the formation of dense oxide scale surface. SiC could improve the compactness of the oxide scale at this temperature by forming SiO₂. A dense scale could not form at 2105°C after ablation for 120 seconds, resulting in a dissatisfactory ablation resistance of the coating. After ablation for 120 seconds at 1738°C, the coating was integrated due to the protection of glassy SiO₂ encapsulated ZrO₂. The coating could not resist the strong shear force from the flame at heat flux of 4.2 MW/m² and was severely damaged after ablation for 60 seconds.