Influence of Nd doping on microwave dielectric properties of SrTiO<Subscript>3</Subscript> ceramics

Sr_1?x Nd _x TiO₃ (x?=?0.08–0.14) ceramics were prepared by conventional solid-state methods. The analysis of crystal structure suggested Sr_1?x Nd _x TiO₃ ceramics appeared to form tetragonal perovskite structure. The relationship between charge compensation mechanism, microstructure feature and microwave dielectric properties were investigated. Trivalent Nd³⁺ substituting Sr²⁺ could effectively decrease oxygen vacancies. This reduction and relative density were critical to improve Q?×?f values of Sr_1?x Nd _x TiO₃ ceramics. For ε _r values, incorporation of Nd could restrain the rattling of Ti⁴⁺ cations and led to the reduction of dielectric constant. The τ _f values were strongly influenced by tilting of oxygen octahedral. The τ _f values decreased from 883 to 650 ppm/°C with x increasing from 0.08 to 0.14. A better microwave dielectric property was achieved for composition Sr_0.92Nd_0.08TiO₃ at 1460 °C: ε _r ?=?160, Q?×?f?=?6602 GHz, τ _f ?=?883 ppm/°C.     

Low temperature sintering and microwave dielectric properties of Zn<Subscript>3</Subscript>Mo<Subscript>2</Subscript>O<Subscript>9</Subscript> ceramic

Crystal structure and dielectric properties of Zn₃Mo₂O₉ ceramics prepared through a conventional solid-state reaction method were characterized. XRD and Raman analysis revealed that the Zn₃Mo₂O₉ crystallized in a monoclinic crystal structure and reminded stable up to1020 °C. Dense ceramics with high relative density (~ 92.3%) were obtained when sintered at 1000 °C and possessed good microwave dielectric properties with a relative permittivity (ε _r ) of 8.7, a quality factor (Q?×?f) of 23,400 GHz, and a negative temperature coefficient of resonance frequency (τ _f ) of around ??79 ppm/°C. With 5 wt% B₂O₃ addition, the sintering temperature of Zn₃Mo₂O₉ ceramic was successfully lowered to 900 °C and microwave dielectric properties with ε _r ?=?11.8, Q?×?f?=?20,000 GHz, and τ _f = ??79.5 ppm/°C were achieved.     

Enhancing the microwave dielectric properties of Sr<Subscript>2</Subscript>Ca<Subscript>3</Subscript>Ta<Subscript>4</Subscript>TiO<Subscript>17</Subscript> ceramics by Zr Substitution

The compositions in Sr₂Ca₃Ta₄Ti_1?xZr_xO₁₇ (0?≤?x?≤?0.12) series were designed and fabricated by solid state sintering method. All the compositions formed single phases and crystallized in an orthorhombic crystal structure. Zr substitution led to the enhancing of the microwave dielectric properties by tuning the τ_f value through zero and increased the Q_uf_o value from 12,540 to 14,970 GHz with a slight decrease in ε_r. In the present study, a good combination of ε_r ~?51, Q_uf_o ~?145,43 GHz and τ_f ~ 3 ppm/°C were obtained for Sr₂Ca₃Ta₄Ti_0.90Zr_0.1O₁₇ ceramic sintered at 1575 °C for 4 h.     

Solid-state reactions in the system Li<Subscript>2</Subscript>CO<Subscript>3</Subscript>-Na<Subscript>2</Subscript>CO<Subscript>3</Subscript>-Nb<Subscript>2</Subscript>O<Subscript>5</Subscript>-Ta<Subscript>2</Subscript>O<Subscript>5</Subscript>

The formation mechanisms of Li _x Na_{1 ?x} Ta _y Nb_{1 ? y} O₃ perovskite solid solutions in the Li₂CO₃-Na₂CO₃-Nb₂O₅-Ta₂O₅ system have been studied by x-ray diffraction, differential thermal analysis, thermogravimetry, IR spectroscopy, and mass spectrometry at temperatures from 300 to 1100°C. The results indicate that the synthesis of Li _x Na_{1 ? x} Ta _y Nb_{1 ? y} O₃ solid solutions involves a complex sequence of consecutive and parallel solid-state reactions. An optimized synthesis procedure for Li _x Na_{1 ? x} Ta _y Nb_{1 ? y} O₃ solid solutions is proposed.     

Very high thermal stability with excellent dielectric,and non-ohmics properties of Mg-doped CaCu<Subscript>3</Subscript>Ti<Subscript>4.2</Subscript>O<Subscript>12</Subscript> ceramics

In this work, the nominal CaCu_3?xMg_xTi_4.2O₁₂ (0.00, 0.05 and 0.10) ceramics were prepared by sintering pellets of their precursor powders obtained by a polymer pyrolysis solution method at 1100 °C for different sintering time of 8 and 12 h. Very low loss tangent (tanδ)?<?0.009–0.014 and giant dielectric constant (ε′) ～?1.1?×?10⁴–1.8?×?10⁴ with excellent temperature coefficient (Δε′) less than ±?15% in a temperature range of ??60 to 210 °C were achieved. These excellent performances suggested a potent application of the ceramics for high temperature X8R and X9R capacitors. It was found that tanδ values decreased with increasing Mg²⁺ dopants due to the increase of grain boundary resistance (R_gb) caused by the very high density of grain, resulting from the substitution of small ionic radius Mg²⁺ dopants in the structure. In addition, CaCu_3?xMg_xTi_4.2O₁₂ ceramics displayed non-linear characteristics with the significant enhancements of a non-linear coefficient (α) and a breakdown field (E_b) due to Mg²⁺doping. The high values of ε′ (14012), α (13.64) and E_b (5977.02 V/cm) with very low tanδ value (0.009) were obtained in a CaCu_2.90Mg_0.10Ti_4.2O₁₂ ceramic sintered at 1100 °C for 8 h.     

Ultralow thermal conductivity of cerium-doped Nd<Subscript>2</Subscript>Zr<Subscript>2</Subscript>O<Subscript>7</Subscript> over a wide doping range

In this paper, we report an ultralow thermal conductivity and a high-temperature phase stability of the (Nd_1?x Ce _x )₂Zr₂O_7+x system over the temperature range from room temperature to 1600 °C and over a wide composition range (0.2 ≤ x ≤ 0.8), and the (Nd_1?x Ce _x )₂Zr₂O_7+x system is therefore considered a strong candidate material for the fabrication of next-generation high-temperature thermal barrier coatings. The observed thermal conductivities (0.65–1.0 W/mK) are about 60–40% lower than those of undoped Nd₂Zr₂O₇ over the same temperature range (100–700 °C) and indicate a glass-like behavior. For comparison, the variation in the thermal conductivity with the temperature of the (Gd_1?x Ce _x )₂Zr₂O_7+x system with similar point defects was also measured, and the observed behavior was almost the same as that of undoped Gd₂Zr₂O₇ and was mostly determined by phonon–phonon scattering (λ ∝ 1/T). The effect of point defect scattering and strong phonon scattering sources (rattlers) on the thermal conductivity is also discussed in this paper. The results of this study suggest that the ultralow thermal conductivity of (Nd_1?x Ce _x )₂Zr₂O_7+x can be attributed to the presence of rattlers because of the large difference between the ionic radii of the Nd³⁺ and Ce⁴⁺ ions.     

Effect of Ni<Superscript>2+</Superscript> substitution on crystal structure and microwave dielectric properties for MgZrNb<Subscript>2</Subscript>O<Subscript>8</Subscript> ceramics

Monoclinic structured Mg_1?xNi_xZrNb₂O₈ (0?≤?x?≤?0.12) ceramics were synthesized for the first time through traditional solid-state reaction process and pure phase were obtained in all range. Rietveld refinement was used to analyze the crystal structure. With the increase of Ni²⁺ substitution amount, ε _r decreased, Q?×?f rose first then fell, τ _f shifted for the positive direction. Bond ionicity, lattice energy and bond energy were separately calculated to investigate the correlations with microwave dielectric properties. Typically, ceramics samples with the composition of Mg_0.92Ni_0.08ZrNb₂O₈ sintered at 1280 °C for 4 h exhibited the optimum microwave dielectric properties: ε _r ?=?24.58, Q?×?f?=?74534.1 GHz, τ _f ?=???49.11 ppm/°C, which could be a promising material for application.     

Crystal structure,microstructure and microwave dielectric properties of novel MgAl<Subscript>2</Subscript>Ti<Subscript>3</Subscript>O<Subscript>10</Subscript> ceramic

In the present work, a novel MgAl₂Ti₃O₁₀ ceramic was obtained using a traditional solid-state reaction method. X-ray diffraction and energy dispersive spectrometer showed that the main MgAl₂Ti₃O₁₀ phase was formed after sintered at 1300–1450 °C. With rising the sintering temperature from 1300 to 1450 °C, the bulk density (ρ), relative permittivity (ε _r ) and Q?×?f value firstly increased, reached the maximum values (3.61 g/cm³, 14.9, and 26,450 GHz) and then decreased. The temperature coefficient of resonator frequency (τ _f ) showed a slight change at a negative range of ??94.6 to ??83.7 ppm/°C. When the sintering temperature was 1400 °C, MgAl₂Ti₃O₁₀ ceramics exhibited the best microwave dielectric properties with Q?×?f?=?26,450 GHz, ε _r ?=?14.9 and τ _f ?=???83.7 ppm/°C.     

Effects of sintering temperature on the properties of Mn/Y codoped Ba<Subscript>0.67</Subscript>Sr<Subscript>0.33</Subscript>TiO<Subscript>3</Subscript> ceramics for tunable application

(Ba_0.67Sr_0.33)_1?3x/2Y _x Ti_1?y/2Mn _y O₃ [BST(Mn + Y), x = 0.006, y = 0.005] ceramics were fabricated by using citrate–nitrate combustion derived powder. Microstructure and dielectric properties of the BST(Mn + Y) ceramic samples were investigated within the sintering temperature ranged from 1220 to 1300 °C. Sintering temperature has a great influence on the microstructure and electrical properties of the ceramic samples. The dielectric properties, ferroelectric properties, and tunability are enhanced by optimizing sintering temperature. The relatively high tunability of 40 % (1.5 kV/mm DC field, 10 kHz) was obtained, and relatively low dielectric loss, <0.0052 (at 10 kHz, 20 °C) was acquired for BST(Mn + Y) samples sintered at 1275 °C for 3 h. Both the low dielectric loss and enhanced tunable properties of BST(Mn + Y) are useful for tunable devices application.     

Low temperature sintering and microwave dielectric properties of Li<Subscript>6</Subscript>Mg<Subscript>7</Subscript>Ti<Subscript>3</Subscript>O<Subscript>16</Subscript> ceramics with LiF additive for LTCC applications

Li₆Mg₇Ti₃O₁₆ ceramics were prepared by the conventional solid-state method with 1–5 wt% LiF as the sintering aid. Effects of LiF additions on the phase compositions, sintering characteristics, micro-structures and microwave dielectric properties of Li₆Mg₇Ti₃O₁₆ ceramics were investigated. The LiF addition could effectively lower the sintering temperature of Li₆Mg₇Ti₃O₁₆ ceramics from 1550 to 900 °C. For different LiF-doped compositions, the optimum dielectric permittivity (ε _r ) and quality factor (Q·f) values first increased and then decreased with the increase of LiF contents, whereas the temperature coefficient of resonant frequency (τ _f ) fluctuated between ??14.39 and ??8.21 ppm/°C. Typically, Li₆Mg₇Ti₃O₁₆ ceramics with 4 wt% LiF sintered at 900 °C exhibited excellent microwave dielectric properties of ε _r ?=?16.17, Q·f?=?80,921 GHz and τ _f ?=???8.21 ppm/°C, which are promising materials for the low temperature co-fired ceramics applications.     

The magnetic properties of BiY<Subscript>2</Subscript>Fe<Subscript>5</Subscript>O<Subscript>12</Subscript> nanoparticles doped with Cr ions

BiY₂Cr _x Fe_5?x O₁₂ (x = 0, 0.05, 0.1, 0.2, 0.3) nanocrystals were synthesized by using a sol-gel method. Samples were characterized by the powder X-ray diffraction (XRD), the thermal gravity analysis (TGA) and the differential thermal analysis (DTA), the vibrating sample magnetometer(VSM) and Mössbauer spectrums. The average sizes of the particles were determined by the Scherrer’s formula. The special Ms and Mössbauer spectra of BiY₂Cr _x Fe_5?x O₁₂ nanocrystals are researched at room temperature. It is seen that the special Mss of samples are initially increased with increasing Cr³⁺ content (x < 0.1), and decreased with increasing content of Cr³⁺ ions (x > 0.1).     

Growth and properties of LiCu<Subscript>2</Subscript>O<Subscript>2</Subscript>-NaCu<Subscript>2</Subscript>O<Subscript>2</Subscript> crystals

Platelike Li_{1 ? x} Na _x Cu₂O₂ single crystals up to 2 × 10 × 10 mm in dimensions have been grown by slowly cooling (1 ? x)Li₂CO₃·xNa₂O₂·4CuO melts in alundum crucibles in air. Li_{1 ? x} Na _x Cu₂O₂ solid solutions in the LiCu₂O₂-NaCu₂O₂ system have been shown to exist in the composition range 0.78 < x < 1. The temperature stability ranges of NaCu₂O₂ and LiCu₂O₂ are 780–930 and 890–1050°C, respectively. The Mössbauer spectra and electrical conductivity of the crystals have been measured.     

Structure and electrical properties of MnO doped (Ba<Subscript>0.96</Subscript>Ca<Subscript>0.04</Subscript>)(Ti<Subscript>0.92</Subscript>Sn<Subscript>0.08</Subscript>)O<Subscript>3</Subscript> lead free ceramics

In this work, (Ba_0.96Ca_0.04)(Ti_0.92Sn_0.08)O₃–xmol MnO (BCTS–xMn) lead-free piezoelectric ceramics were fabricated by the conventional solid-state technique. The composition dependence (0 ≤ x ≤ 3.0 %) of the microstructure, phase structure, and electrical properties was systematically investigated. An O–T phase structure was obtained in all ceramics, and the sintering behavior of the BCTS ceramics was gradually improved by doping MnO content. In addition, the relationship between poling temperature and piezoelectric activity was discussed. The ceramics with x = 1.5 % sintering at temperature of 1330 °C demonstrated an optimum electrical behavior: d ₃₃ ~ 475 pC/N, k _p ~ 50 %, ε _r ~ 4060, tanδ ~ 0.4 %, P _r ~ 10.3 μC/cm², E _c ~ 1.35 kV/mm, T _C ~ 82 °C, strain ~0.114 % and \(d_{33}^{*}\) ~ 525 pm/V. As a result, we achieved a preferable electric performance in BaTiO₃-based ceramics with lower sintering temperature, suggesting that the BCTS–xMn material system is a promising candidate for lead-free piezoelectric ceramics.     

Phases and morphotropic regions in the PbNb<Subscript>2/3</Subscript> Mg<Subscript>1/3</Subscript>O<Subscript>3</Subscript>-PbTiO<Subscript>3</Subscript> system

Ceramic samples of solid solutions (1 ? x) PbNb_2/3Mg_1/3O₃ · xPbTiO₃ (0 ≤ x ≤ 1.0, Δx = 0.0025–0.05) are prepared by the columbite method. A detailed x?T phase diagram of the system is constructed (isothermal join at 25°C), and dielectric, piezoelectric, and elastic properties are investigated. It is established that the region of the morphotropic phase transition is positioned in the range 0.28 < x ≤ 0.43 and consists of a series of narrower regions. Inside one phase (cubic, rhombohedral, tetragonal), regions are found in which a qualitative and quantitative difference in structural and electrical parameters is observed. An interpretation of the observed effects in the context of the defect structure of the objects is suggested.     

Enhanced magnetoelectric coupling in La-modified Bi<Subscript>5</Subscript>Co<Subscript>0.5</Subscript>Fe<Subscript>0.5</Subscript>Ti<Subscript>3</Subscript>O<Subscript>15</Subscript> multiferroic ceramics

Multiferroic properties of La-modified four-layered perovskite Bi_5?x La _x Fe_0.5Co_0.5Ti₃O₁₅ (0 ≤ x ≤ 1) ceramics were investigated, by analyzing the magnetodielectric effect, magneto-polarization response and magnetoelectric conversion. X-ray diffraction indicated the formation of pure Aurivillius ceramics, and Raman spectroscopy revealed the Bi ions displacement and the crystal structure variation. The enhancement of ferromagnetic and ferroelectric properties was observed in Bi_5?x La _x Fe_0.5Co_0.5Ti₃O₁₅ after La modification. The evidence for enhanced ME coupling was determined by magnetic field-induced marked variations in the dielectric constant and polarization. A maximum ME coefficient of 1.15 mV/cm·Oe was achieved in Bi_4.25La_0.75Fe_0.5Co_0.5Ti₃O₁₅ ceramic, which provides the possible promise for novel magnetoelectric device application.     

Magnetization reversal and tunable exchange bias behavior in Mn-substituted NiCr<Subscript>2</Subscript>O<Subscript>4</Subscript>

Single phase samples of Ni(Cr_1?xMn _x )₂O₄ (x = 0–0.50) were synthesized by using sol–gel route. Investigation of structural, magnetic, exchange bias and magnetization reversal properties was carried out in the bulk samples of Ni(Cr_1?xMn _x )₂O₄. Rietveld refinement of the X-ray diffraction patterns recorded at room temperature reveals the tetragonal structure for x = 0 sample with I4₁/amd space group and cubic structure for x ≥ 0.05 samples with \( {\text{Fd}\bar{3}\text{m}} \) space group. Magnetization measurements show that all samples exhibit ferrimagnetic behavior, and the transition temperature (T_C) is found to increase from 73 K for x = 0 to 138 K for x = 0.50. Mn substitution induces magnetization reversal behavior especially for 30 at% of Mn in NiCr₂O₄ system with a magnetic compensation temperature of 45 K. This magnetization reversal is explained in terms of different site occupation of Mn ions and the different temperature dependence of the magnetic moments of different sublattices. Study of exchange bias behavior in x = 0.10 and 0.30 samples reveals that they exhibit negative and tunable positive and negative exchange bias behavior, respectively. The magnitudes of maximum exchange bias field of these samples are found to be 640 and 5306 Oe, respectively. Exchange bias in x = 0.10 sample originates from the anisotropic exchange interaction between the ferrimagnetic and the antiferromagnetic components of magnetic moment. The tunable exchange bias behavior in x = 0.30 sample is explained in terms of change in domination of one sublattice moment over the other as the temperature is varied.     

Properties of fluorine-doped PbMg<Subscript>1/3</Subscript>Nb<Subscript>2/3</Subscript>O<Subscript>3</Subscript> ceramics

We report the first fluorine doping of lead magnesium niobate in the PbMg _{(1 + x)/3}Nb_{(2 ? x)/3}O_{3 ? x} F _x system in a wide composition range, x = 0.025 to 0.625. The fluorine content of the samples is shown to be substantially lower than the intended one because of the fluorine volatilization in the form of HF during synthesis and sintering in air. The ceramics consist of magnesium and lead oxides undetectable by x-ray diffraction, and a perovskite phase whose composition can be represented by the formula PbMg_{(1 + m)/3}Nb_{(2 ? m)/3}O_{3 ? m} F _m , where the fluorine content after sintering is m ≤ 0.12. The PbO and MgO contents of the ceramics depend on the starting mixture composition (x) and heat-treatment conditions (hydrogen fluoride and lead oxide volatilization). As a result of the low fluorine content, the diffraction patterns of the samples show no superlattice reflections, and their lattice parameter varies insignificantly with x. Data are presented on the temperaturedependent dielectric permittivity of ceramic samples sintered and annealed under different conditions.     

Strong up-conversion luminescence and electrical properties of SrBi<Subscript>4</Subscript>Ti<Subscript>4</Subscript>O<Subscript>15</Subscript> multifunctional ceramics by Er<Superscript>3+</Superscript> doping

Novel green-emitting piezoelectric ceramics of SrBi_4?x Er _x Ti₄O₁₅ (SBT-xEr) were prepared. Strong up-conversion with bright green (524 and 548 nm) and a relatively weak red (660 nm) emission bands were obtained under 980 nm excitation at room temperature, which is attributed to the intra 4f–4f electronic transition of (²H_11/2, ⁴S_3/2)–⁴I_15/2 and the transition from ⁴F_9/2 to ⁴I_15/2 of Er³⁺ ions, respectively. Simultaneously, Er³⁺ doping promotes the electrical properties. At 0.8 mol%Er, the optimal electric properties with high Curie temperature of T _c?~527?°C, large remanent polarization of 2P _r?~14.92 μC/cm² and piezoelectric constant of d ₃₃?~17 pC/N was achieved. As a multifunctional material, Er³⁺ doped SBT showed a great potential to be used in 3D-display, bio-imaging, solid state laser and optical temperature sensor.     

Structural and dielectric properties of PbMg<Subscript>1/3</Subscript>Nb<Subscript>2/3</Subscript>O<Subscript>3</Subscript>-PbZrO<Subscript>3</Subscript> solid solutions synthesized at high pressures and temperatures

(1 ? x)PbMg_1/3Nb_2/3O₃ · xPbZrO₃ (1 ? x)PMN · xPZ) solid solutions have been synthesized at a pressure of 5 GPa and temperatures from 1300 to 1700 K, and their structural and dielectric properties have been studied. The composition dependences of the average unit-cell parameter and dielectric permittivity for the solid solutions indicate that the PMN-PZ system has a morphotropic phase boundary near x = 0.65. The solid solutions have a cubic structure for x < 0.65, a rhombohedral structure in the range 0.65 < x < 0.9, and an orthorhombic structure (similar to that of PbZrO₃) for x > 0.9. The temperature and frequency dependences of dielectric permittivity suggest that the (1 ? x)PMN · xPZ samples with x < 0.65 consist of two ferroelectric phases: a relaxor with antipolar dipole order and a normal ferroelectric with a diffuse phase transition. The effect of annealing temperature on the ferroelectric state of the samples with x < 0.65 is examined. In the composition range 0.65 < x < 0.9, the samples have normal ferroelectric properties, independent of annealing temperature.     

Rare-earth-doped PbTiO<Subscript>3</Subscript>-PbZrO<Subscript>3</Subscript> solid solutions

(Pb_{1 ? x} Ln _x )(Zr_0.53Ti_0.47)O₃ and (Pb_{1 ? x} Ln _x )(Zr_0.65Ti_0.35)O₃ (x = 0.02, 0.06; Ln = La, Pr, Gd, Yb) solid solutions have been prepared by modified solid-state synthesis using organic-ligand precursors. The solid solutions have been characterized by thermal analysis, IR spectroscopy, x-ray powder diffraction, and atomic force microscopy. All of them have a rhombohedrally distorted perovskite structure (sp. gr. R3c).