Superior dehydrogenation performance of nanoscale lithium borohydride modified with fluorographite

A significant enhancement in the dehydrogenation performance of LiBH₄ is achieved by modifying with fluorographite (FGi). In-depth investigations show that the dehydrogenation thermodynamics and kinetics of LiBH₄ are strongly improved by ball milling LiBH₄ with FGi. The ball-milled LiBH₄–FGi (mass ratio of 1:1) composite starts to release hydrogen without impurity gas at around 180 °C, and obtains a hydrogen desorption capacity of 7.2 wt% below 200 °C in seconds, which is improved dramatically compared with pristine ball-milled LiBH₄. Microscopic morphology indicates that numerous ∼90 nm spots formed on the surface of FGi. Based on the microstructure analyses combined with hydrogen storage performances, the prominent effect of FGi is largely attributed to the nano-modifying effect and the exothermic reaction between LiBH₄ and FGi during the dehydrogenation process. Furthermore, partial reversibility of the LiBH₄–FGi composite has been demonstrated and the mechanism underlying the cycling capacity loss is discussed. The use of FGi may shed light on future study on searching for new strategies to improve both the thermodynamics and kinetics of light-metal complex hydrides.     

Enhanced hydrogen storage properties of TiN–LiAlH4 composite

The hydrogen storage properties of LiAlH₄ doped efficient TiN catalyst were systematically investigated. We observe that TiN catalyst enhances the dehydrogenation kinetics and decreases the dehydrogenation temperature of LiAlH₄. The dehydrogenation behaviors of 2%TiN–LiAlH₄ are investigated using temperature programmed desorption (TPD), differential scanning calorimetry (DSC) and fourier transform infrared spectroscopy (FTIR). Interestingly, the onset hydrogen desorption temperature of 2%TiN–LiAlH₄ sample gets lowered from 151.0 °C to 90.0 °C with a faster kinetics, and the dehydrogenation rate reached a maximum value at 137.2 °C. By adding a small amount of as-prepared TiN, approximately 7.1 wt% of hydrogen can be released from the LiAlH₄ at 130 °C. Interestingly, the result of the FTIR indicates that the 2%TiN–LiAlH₄ maybe restore hydrogen under 5.5 MPa hydrogen. Moreover, 2%TiN–LiAlH₄ displayed a substantially reduced activation energy for LiAlH₄ dehydrogenation.     

Enhancement of the H2 desorption properties of LiAlH4 doping with NiCo2O4 nanorods

Lithium aluminum hydride (LiAlH₄) is considered as an attractive candidate for hydrogen storage owing to its favorable thermodynamics and high hydrogen storage capacity. However, its reaction kinetics and thermodynamics have to be improved for the practical application. In our present work, we have systematically investigated the effect of NiCo₂O₄ (NCO) additive on the dehydrogenation properties and microstructure refinement in LiAlH₄. The dehydrogenation kinetics of LiAlH₄ can be significantly increased with the increase of NiCo₂O₄ content and dehydrogenation temperature. The 2 mol% NiCo₂O₄-doped LiAlH₄ (2% NCO–LiAlH₄) exhibits the superior dehydrogenation performances, which releases 4.95 wt% H₂ at 130 °C and 6.47 wt% H₂ at 150 °C within 150 min. In contrast, the undoped LiAlH₄ sample just releases <1 wt% H₂ after 150 min. About 3.7 wt.% of hydrogen can be released from 2% NCO–LiAlH₄ at 90 °C, where total 7.10 wt% of hydrogen is released at 150 °C. Moreover, 2% NCO–LiAlH₄ displayed remarkably reduced activation energy for the dehydrogenation of LiAlH₄.     

LiAlH4–ZrCl4 mixtures for hydrogen release at near room temperature

The dehydrogenation temperature of LiAlH₄ was significantly reduced by the production of mixtures with ZrCl₄. Stoichiometric 4:1, and 5 mol % mixtures of LiAlH₄ and ZrCl₄ were produced by ball milling at room temperature and ?196 °C, and tested for dehydrogenation at low temperature. Cryogenic ball-milling resulted in an effective way to produce reactive mixtures for hydrogen release; because of achieving small aggregates size (5–20 μm) in 10 min of cryomilling while preventing substantial decomposition during preparation. Dehydrogenation reaction in the mixtures LiAlH₄/ZrCl₄ started around 31–47 °C under different heating rates. Partial dehydrogenation was proved at 70 °C: 4.4 wt % for the 5 mol% ZrCl₄–LiAlH₄ mixture, and 3.4 wt % for the best 4:1 stoichiometric mixture. Complete dehydrogenation up to 250 °C released 6.4 wt% and 4.1 wt%, respectively. Dehydrogenation reactions are exothermic, and the LiAlH₄/ZrCl₄ mixtures are unstable and difficult to handle. The activation energy of the exothermic reactions was estimated as 113.5 ± 9.8 kJ/mol and 40.6 ± 6.6 kJ/mol for 4LiAlH₄+ZrCl₄ and 5%mol ZrCl₄+LiAlH₄ samples milled in cryogenic conditions, respectively. The dehydrogenation pathway was changed in the LiAlH₄/ZrCl₄ mixtures as compared to pure LiAlH₄. Dehydrogenation reaction is proposed to form Al, LiCl, Zr, and H₂ as main products. Modification of the dehydrogenation reaction of LiAlH₄ was achieved at the cost of reducing the total hydrogen release capacity.     

Significantly improved dehydrogenation of LiAlH4 catalysed with TiO2 nanopowder

The effects of TiO₂ nanopowder addition on the dehydrogenation behaviour of LiAlH₄ have been studied. The 5 wt.% TiO₂-added LiAlH₄ sample showed a significant improvement in dehydrogenation rate compared to that of undoped LiAlH₄, with the dehydrogenation temperature reduced from 150 °C to 60 °C. Kinetic desorption results show that the added LiAlH₄ released about 5.2 wt% hydrogen within 30 min at 100 °C, while the as-received LiAlH₄ just released below 0.2 wt.% hydrogen within same time at 120 °C. From the Arrhenius plot of the hydrogen desorption kinetics, the apparent activation energy is 114 kJ/mol for pure LiAlH₄ and 49 kJ/mol for the 5 wt.% TiO₂ added LiAlH₄, indicating that TiO₂ nanopowder adding significantly decreased the activation energy for hydrogen desorption of LiAlH₄. X-ray diffraction and Fourier transform infrared analysis show that there is no phase change in the cell volume or on the Al-H bonds of the LiAlH₄ due to admixture of TiO₂ after milling. X-ray photoelectron spectroscopy results show no changes in the Ti 2p spectra for TiO₂ after milling and after dehydrogenation. The improved dehydrogenation behaviour of LiAlH₄ in the presence of TiO₂ is believed to be due to the high defect density introduced at the surfaces of the TiO₂ particles during the milling process.     

Improved reversible hydrogen storage of LiAlH4 by nano-sized TiH2

Transition metal halides are mostly used as dopants to improve the hydrogen storage properties of LiAlH₄, but they will cause hydrogen capacity loss because of their relatively high molecular weights and reactions with LiAlH₄. To overcome these drawbacks, active nano-sized TiH₂ (TiH₂^nano) prepared by reactive ball milling is used to dope LiAlH₄. It shows superior catalytic effect on the dehydrogenation of LiAlH₄ compared to commercial TiH₂. TiH₂^nano-doped LiAlH₄ starts to release hydrogen at 75 °C, which is 80 °C lower than the onset dehydrogenation temperature of commercial LiAlH₄. About 6.3 wt.% H₂ can be released isothermally at 100 °C (800 min) or at 120 °C (150 min). The apparent activation energies of the first two dehydrogenation reactions of LiAlH₄ are reduced by about 20 and 24 kJ mol⁻¹, respectively. Meanwhile, the regeneration of LiAlH₄ is realized through extracting the solvent from LiAlH₄·4THF, which is obtained by ball milling the dehydrogenated products of TiH₂^nano-doped LiAlH₄ in the presence of THF and 5 MPa H₂. This suggests that TiH₂ is also an effective catalyst for the formation of LiAlH₄·4THF.     

Catalytic effects of FGO-Ni addition on the dehydrogenation properties of LiAlH4

LiAlH₄ is an ideal hydrogen storage material with a theoretical hydrogen storage capacity of 10.6 wt%. In order to reduce the hydrogen release temperature and increase the hydrogen release amount of LiAlH₄, multilayer graphene oxide and nickel (FGO-Ni) composite catalyst were prepared by physical ball milling and doped into LiAlH₄. The effect of FGO-Ni composite catalyst on the dehydrogenation performance of LiAlH₄ was studied by pressure-composition-temperature apparatus, scanning electron microscope (SEM) and X-ray diffractometer. The results show that, compared with pure LiAlH₄, the hydrogen release time of LiAlH₄ doped with 9 wt%FGO-3wt%Ni is obviously shortened about 90min at 150 °C and the hydrogen release amount of LiAlH₄ doped with 9 wt%FGO-3wt%Ni also increased 1.8 wt%. Importantly, the dehydrogenation amount of LiAlH₄ (9 wt%FGO)-3wt% could reach 4 wt% at 135 °C which was 4 times higher than that of the pure LiAlH₄. At the same temperature, the hydrogen release of pure LiAlH₄ was only 0.84 wt%. In contrast, doping FGO-Ni composite catalyst reduces the hydrogen release temperature of LiAlH₄ and weakens the hydrogen release barrier. Forthermore, SEM results showed that doping FGO-Ni reduced the agglomeration between LiAlH₄ particles and increased the specific surface area of the sample, which improving the hydrogen release properties of LiAlH₄.     

Enhancing the dehydrogenation properties of LiAlH4 using K2NiF6 as additive

Lithium alanate (LiAlH₄) is a material that can be potentially used for solid-state hydrogen storage due to its high hydrogen content (10.5 wt%). Nevertheless, a high desorption temperature, slow desorption kinetic, and irreversibility have restricted the application of LiAlH₄ as a solid-state hydrogen storage material. Hence, to lower the decomposition temperature and to boost the dehydrogenation kinetic, in this study, we applied K₂NiF₆ as an additive to LiAlH₄. The addition of K₂NiF₆ showed an excellent improvement of the LiAlH₄ dehydrogenation properties. After adding 10 wt% K₂NiF₆, the initial decomposition temperature of LiAlH₄ within the first two dehydrogenation steps was lowered to 90 °C and 156 °C, respectively, that is 50 °C and 27 °C lower than that of the аs-milled LiAlH₄. In terms of dehydrogenation kinetics, the dehydrogenation rate of K₂NiF₆-doped LiAlH₄ sample was significantly higher as compared to аs-milled LiAlH₄. The K₂NiF₆-doped LiAlH₄ sample can release 3.07 wt% hydrogen within 90 min, while the milled LiAlH₄ merely release 0.19 wt% hydrogen during the same period. According to the Arrhenius plot, the apparent activation energies for the desorption process of K₂NiF₆-doped LiAlH₄ are 75.0 kJ/mol for the first stage and 88.0 kJ/mol for the second stage. These activation energies are lower compared to the undoped LiAlH₄. The morphology study showed that the LiAlH₄ particles become smaller and less agglomerated when K₂NiF₆ is added. The in situ formation of new phases of AlNi and LiF during the dehydrogenation process, as well as a reduction in particle size, is believed to be essential contributors in improving the LiAlH₄ dehydrogenation characteristics.     

LiBH4–VCl3 and LiAlH4–VCl3 mixtures prepared in soft milling conditions for hydrogen release at low temperature

Mixtures of LiBH₄/VCl₃ and LiAlH₄/VCl₃ in 5:1, 3:1, and 5% mol stoichiometries were prepared and tested for hydrogen release. The mixtures were prepared in 10 min of ball milling at room temperature or with cryogenic (N₂-liquid) cooling. The mixtures demonstrated diverse hydrogen release levels, but all of them started releasing hydrogen at low temperatures (33–66 °C) with a change in the reaction pathway as compared to pure LiBH₄ or LiAlH₄. The driving force for that is the formation of the stable salt LiCl. The best material was the 5% mol VCl₃ + LiAlH₄ cryogenic mixture because of the low-temperature dehydrogenation onset of 34 °C; and the dehydrogenation level of 5.1 wt.%, and 6.4 wt.% that was achieved upon heating at 100 °C and 250 °C, respectively.     

Significantly improved dehydrogenation of LiAlH4 destabilized by K2TiF6

The effects of K₂TiF₆ on the dehydrogenation properties of LiAlH₄ were investigated by solid-state ball milling. The onset decomposition temperature of 0.8 mol% K₂TiF₆ doped LiAlH₄ is as low as 65 °C that 85 °C lower than that of pristine LiAlH₄. Isothermal dehydrogenation properties of the doped LiAlH₄ were studied by PCT (pressure–composition–temperature). The results show that, for the 0.8 mol% K₂TiF₆ doped LiAlH₄ that dehydrogenated at 90 °C, 4.4 wt% and 6.0 wt% of hydrogen can be released in 60 min and 300 min, respectively. When temperature was increased to 120 °C, the doped LiAlH₄ can finish its first two dehydrogenation steps in 170 min. DSC results show that the apparent activation energy (E_a) for the first two dehydrogenation steps of LiAlH₄ are both reduced, and XRD results suggest that TiH₂, Al₃Ti, LiF and KH are in situ formed, which are responsible for the improved dehydrogenation properties of LiAlH₄.     

Catalytic effects of MgFe2O4 addition on the dehydrogenation properties of LiAlH4

Study on the catalytic roles of MgFe₂O₄ on the dehydrogenation performance of LiAlH₄ was carried out for the first time. Notable improvement on the dehydrogenation of LiAlH₄–MgFe₂O₄ compound was observed. The initial decomposition temperatures for the catalyzed LiAlH₄ were decreased to 95 °C and 145 °C for the first and second stage reactions, which were 48 °C and 28 °C lower than the milled LiAlH₄. As for the desorption kinetics performance, the MgFe₂O₄ doped-LiAlH₄ sample was able to desorb faster with a value of 3.5 wt% of hydrogen in 30 min (90 °C) while the undoped LiAlH₄ was only able to desorb 0.1 wt% of hydrogen. The activation energy determined from the Kissinger analysis for the first two desorption reactions were 73 kJ/mol and 97 kJ/mol; which were 31 and 17 kJ/mol lower as compared to the milled LiAlH₄. The X-ray diffraction result suggested that the MgFe₂O₄ had promoted significant improvements by reducing the LiAlH₄ decomposition temperature and faster desorption kinetics through the formation of active species of Fe, LiFeO₂ and MgO that were formed during the heating process.     

Dehydrogenation properties of doped LiAlH4 compacts for hydrogen generator applications

Lithium aluminum hydride (LiAlH₄) is an attractive hydrogen source for fuel cell systems due to its high hydrogen storage capacity and the moderate dehydrogenation conditions. In this contribution, TiCl₃- and ZrCl₄-doped LiAlH₄ powders are prepared and pelletized under different compaction pressures in a uniaxial press. At constant 80 °C and a hydrogen partial pressure of 0.1 MPa, the maximal hydrogen release of suchlike LiAlH₄ compacts amounts to 6.64 wt.%-H₂ (gravimetric capacity) and 53.88 g-H₂ l⁻¹ (volumetric capacity). The hydrogen release properties of the doped LiAlH₄ compacts are studied systematically under variation of the compaction pressure, temperature and hydrogen partial pressure. Furthermore, the volume change of doped LiAlH₄ compacts during dehydrogenation as well as their short-term storability are investigated (shelf life).     

Thermal decomposition of LiAlH4 chemically mixed with Lithium amide and transition metal chlorides

Thermogravimetric analysis of LiAlH₄ chemically mixed with different additives is reported for the application of hydrogen storage. Here, we illustrated the dehydrogenation properties of combined LiAlH₄/LiNH₂ (2:1) mixture and LiAlH₄ wet-doped with different transition metals (Sc, Ti, and V) in their chloride forms. Thermal gravimetric analysis of LiAlH₄/LiNH₂ system released 7.9 wt.% of hydrogen in three decomposition steps at temperatures between 75 and 280 °C under a heating ramp of 5 °C min⁻¹. The LiAlH₄ doped with transition metals showed the decrease of decomposition temperature down to 30–40 °C for both 1st and 2nd dehydrogenation steps as compared to as-received LiAlH₄. The catalytic activity in lowering the dehydrogenation temperature of LiAlH₄ doped with transition metals increases in the order of pure LiAlH₄ < V < Ti < Sc. The X-ray diffraction analysis, field emission scanning electron microscopy, and Fourier transformation infra-red spectroscopy techniques were carried out in support of the thermogravimetric results.     

Hydrogen desorption properties of MgH2/LiAlH4 composites

The hydrogen desorption properties of MgH₂–LiAlH₄ composites obtained by mechanical milling for different milling times have been investigated by Thermal Desorption Spectroscopy (TDS) and correlated to the sample microstructure and morphology analysed by X-ray Diffraction (XRD) and Scanning Electron Microscopy (SEM). The MgH₂–LiAlH₄ composites show improved hydrogen desorption properties in comparison with both as-received and ball-milled MgH₂. Mixing of MgH₂ with small amount of LiAlH₄ (5 wt.%) using short mechanical milling (15 min) shifts, in fact, the hydrogen desorption peak to lower temperature than those observed with both as-received and milled MgH₂ samples. Longer mixing times of the MgH₂–LiAlH₄ composites (30 and 60 min) reduce the catalytic activity of the LiAlH₄ additive as revealed by the shift of the hydrogen desorption peak to higher temperatures.     

Improved hydrogen desorption in lithium alanate by addition of SWCNT-metallic catalyst composite

A LiAlH₄/single walled carbon nanotube (SWCNT) composite system was prepared by mechanical milling and its hydrogen storage properties investigated. The SWCNT - metallic particle addition resulted in both a decreased decomposition temperature and enhanced desorption kinetics compared to pure LiAlH₄. The decomposition temperature of the 5 wt.% SWCNT-added LiAlH₄ sample was reduced to 80 °C and 130 °C for the first and second stage, respectively, compared with 150 °C and 180 °C for as-received LiAlH₄. In terms of the desorption kinetics, the 5 wt.% SWCNT-added LiAlH₄ sample released about 4.0 wt.% hydrogen at 90 °C after 40 min dehydrogenation, while the as-milled LiAlH₄ sample released less than 0.3 wt.% hydrogen for the same temperature and time. Differential scanning calorimetry measurements indicate that enthalpies of decomposition in LiAlH₄ decrease with added SWCNTs. The apparent activation energy for hydrogen desorption was decreased from 116 kJ/mol for as-received LiAlH₄ to 61 kJ/mol by the addition of 5 wt.% SWCNTs. It is believed that the significant improvement in dehydrogenation behaviour of SWCNT-added LiAlH₄ is due to the combined influence of the SWCNT structure itself and the catalytic role of the metallic particles contained in the SWCNTs. In addition, the different effects of the SWCNTs and the metallic catalysts contained in the SWCNTs were also investigated, and the possible mechanism is discussed.     

Effects of REF3 (RE = Y,La, Ce) additives on dehydrogenation properties of LiAlH4

The catalytic effects of rare earth fluoride REF₃ (RE = Y, La, Ce) additives on the dehydrogenation properties of LiAlH₄ were carefully investigated in the present work. The results showed that the dehydrogenation behaviors of LiAlH₄ were significantly altered by the addition of 5 mol% REF₃ through ball milling. The destabilization ability of these catalysts on LiAlH₄ has the order: CeF₃>LaF₃>YF₃. For instance, the temperature programmed desorption (TPD) analyses showed that the onset dehydrogenation temperature of CeF₃ doped LiAlH₄ was sharply reduced by 90 °C compared to that of pristine LiAlH₄. Based on differential scanning calorimetry (DSC) analyses, the dehydriding activation energies of the CeF₃ doped LiAlH₄ sample were 40.9 kJ/mol H₂ and 77.2 kJ/mol H₂ for the first and second dehydrogenation stages, respectively, which decreased about 40.0 kJ/mol H₂ and 60.3 kJ/mol H₂ compared with those of pure LiAlH₄. In addition, the sample doped with CeF₃ showed the fastest dehydrogenation rate among the REF₃ doped LiAlH₄ samples at both 125 °C and 150 °C during the isothermal desorption. The phase changes in REF₃ doped LiAlH₄ samples during ball milling and dehydrogenation were examined using X-ray diffraction and the mechanisms related to the catalytic effects of REF₃ were proposed.     

Enabling easy and efficient hydrogen release below 80 °C from NaBH4 with multi-hydroxyl xylitol

NaBH₄ has been widely considered as a low-cost hydrogen storage material with high gravimetric hydrogen capacity of about 10 wt%. However, its strong thermodynamic stability severely hinders the application of NaBH₄ to obtain hydrogen. In this study, multi-hydroxyl xylitol, for the first time, was chosen as a protic hydrogen carrier to destabilize and react with NaBH₄. The NaBH₄-xylitol composites were easily prepared through hand-milling, which leads to the fast liberation of hydrogen from moderate temperatures lower than 80 °C with more than 3.6 wt% hydrogen desorption capacity. Besides, over 80% of hydrogen could be efficiently released in NaBH₄-xylitol composite. The dehydrogenation process is proved to be completely impurity-free and controllable by altering the NaBH₄/xylitol ratios and operating temperatures. The reaction between NaBH₄ and xylitol is investigated to be similar to an alcoholysis procedure, however no observable liquid phase takes place before and after the dehydrogenation of NaBH₄-xylitol composite, showing a great potential to produce hydrogen under low temperatures through solid-state carriers.     

Enhanced hydrogen storage performance of LiAlH4-MgH2-TiF3 composite

The mutual destabilization of LiAlH₄ and MgH₂ in the reactive hydride composite LiAlH₄-MgH₂ is attributed to the formation of intermediate compounds, including Li-Mg and Mg-Al alloys, upon dehydrogenation. TiF₃ was doped into the composite for promoting this interaction and thus enhancing the hydrogen sorption properties. Experimental analysis on the LiAlH₄-MgH₂-TiF₃ composite was performed via temperature-programmed desorption (TPD), differential scanning calorimetry (DSC), isothermal sorption, pressure-composition isotherms (PCI), and powder X-ray diffraction (XRD). For LiAlH₄-MgH₂-TiF₃ composite (mole ratio 1:1:0.05), the dehydrogenation temperature range starts from about 60 °C, which is 100 °C lower than for LiAlH₄-MgH₂. At 300 °C, the LiAlH₄-MgH₂-TiF₃ composite can desorb 2.48 wt% hydrogen in 10 min during its second stage dehydrogenation, corresponding to the decomposition of MgH₂. In contrast, 20 min was required for the LiAlH₄-MgH₂ sample to release so much hydrogen capacity under the same conditions. The hydrogen absorption properties of the LiAlH₄-MgH₂-TiF₃ composite were also improved significantly as compared to the LiAlH₄-MgH₂ composite. A hydrogen absorption capacity of 2.68 wt% under 300 °C and 20 atm H₂ pressure was reached after 5 min in the LiAlH₄-MgH₂-TiF₃ composite, which is larger than that of LiAlH₄-MgH₂ (1.75 wt%). XRD results show that the MgH₂ and LiH were reformed after rehydrogenation.     

Enhanced hydrogen storage properties of 4MgH2 + LiAlH4 composite system by doping with Fe2O3 nanopowder

In this paper, the hydrogen storage properties and reaction mechanism of the 4MgH₂ + LiAlH₄ composite system with the addition of Fe₂O₃ nanopowder were investigated. Temperature-programmed-desorption results show that the addition of 5 wt.% Fe₂O₃ to the 4MgH₂ + LiAlH₄ composite system improves the onset desorption temperature to 95 °C and 270 °C for the first two dehydrogenation stage, which is lower 40 °C and 10 °C than the undoped composite. The dehydrogenation and rehydrogenation kinetics of 5 wt.% Fe₂O₃-doped 4MgH₂ + LiAlH₄ composite were also improved significantly as compared to the undoped composite. Differential scanning calorimetry measurements indicate that the enthalpy change in the 4MgH₂–LiAlH₄ composite system was unaffected by the addition of Fe₂O₃ nanopowder. The Kissinger analysis demonstrated that the apparent activation energy of the 4MgH₂ + LiAlH₄ composite (125.6 kJ/mol) was reduced to 117.1 kJ/mol after doping with 5 wt.% Fe₂O₃. Meanwhile, the X-ray diffraction analysis shows the formation of a new phase of Li₂Fe₃O₄ in the doped composite after the dehydrogenation and rehydrogenation process. It is believed that Li₂Fe₃O₄ acts as an actual catalyst in the 4MgH₂ + LiAlH₄ + 5 wt.% Fe₂O₃ composite which may promote the interaction of MgH₂ and LiAlH₄ and thus accelerate the hydrogen sorption performance of the MgH₂ + LiAlH₄ composite system.     

Ti-doped LiAlH4 for hydrogen storage: Rehydrogenation process,reaction conditions and microstructure evolution during cycling

One-step rehydrogenation of Ti-doped LiAlH₄ from its dehydrogenated precursor (Ti-doped LiH/Al), proceeds in Me₂O solution under mild conditions (25 °C; 50–100 bar H₂). The formation process, the effects of reaction conditions (temperature and H₂ pressure) on the yield of LiAlH₄, and the microstructure evolution during hydrogenation–dehydrogenation cycles were investigated comprehensively. No evidence was obtained for the intermediate Li₃AlH₆ in the product. Higher temperatures adversely affect the yield and stability of the Ti-doped LiAlH₄ product. High hydrogen pressure favors the formation of LiAlH₄ but the influence of pressure in the range 50–100 bar is slight if other variables are maintained constant. The cycling performance depends on the microstructure of the material: larger particle size; lower surface area; and the formation of less active Ti clusters and Ti–Al alloys upon cycling correspond to a decrease in cycling performance. Incorporation of an extra ball milling stage before each rehydrogenation significantly improves the cycling performance.